• KCI Concrete Journal
• /
• 제14권4호
• /
• pp.171-177
• /
• 2002

Antifungal agents are used to impart antibacterial or bactericidal properties to commodities and various articles used in industries and can be classified into two broad groups i.e organic and inorganic. Inorganic antifungal agents comprise of Ag, Zn, or Cu, etc. These elements tend to exhibit high level of antifungal activities, non-uniform dispersion in substrates, and have poor properties in expensive and cheap adhesiveness. In this study, the organic antifungal agent was used for the purpose of investigating the antifungal activity of antifungal agent activated-cement mortar (AACM) on the aspergilus niger of various fungus which can be easily discovered in the interiors and exteriors of buildings. In addition, an experiment on the basic physical properties of AACM such as compressive and flexural strength was carried out. The conclusion of this investigation revealed that a dosage increase of antifungal agent exhibits a high inhibitory effect on the aspergilus niger, and although there is a slight decrease in the strength of AACM, the strength of AACM was almost equal to that of inactivated cement mortar.

• 한국초전도ㆍ저온공학회논문지
• /
• 제5권2호
• /
• pp.41-45
• /
• 2003

Resistance distribution in thin film type SFCL elements of different shunt layer thickness was investigated. The 300 nm thick film of 2 inch diameter was coated with a gold layer and patterned into 2 mm wide meander lines. The shunt layer thickness was varied by ion milling the shunt layer with Ar ions, and also by having the shunt layer grown in different thickness. The SFCL element was subjected to simulated AC fault current for measurements. It was immersed in liquid nitrogenduring the experiment. The resistance distribution was not affected by the shunt layer thickness at applied voltages that brought the temperature of the elements to similar values. This result could be explained with the concept of heat transfer from the film to the surroundings. The resistance distribution was independent of the shunt layer thickness because thick sapphire substrates of high thermal conductivity dominated the thermal conductance of the elements.

• Progress in Superconductivity
• /
• 제6권2호
• /
• pp.108-112
• /
• 2005

We investigated temperature behavior of superconducting fault current limiters (SFCLs) during quenches. Knowledge on temperature behavior during quenches is important to the design of SFCLs, because the temperature of SFCLs is related to their stability. SFCLs were fabricated by patterning $Au/YBa_2Cu_3O_7$ thin films grown on sapphire substrates into meander lines by photolithography. A gold film grown on the back side of the substrate was patterned into a meander line, and used as a temperature sensor. The front meander line was subjected to simulated AC fault currents, and the back line to DC current. They were immersed in liquid nitrogen during the experiment for effective cooling. Overall, temperature at the back side of SFCLs was close to that at the front side. It was closer at the beginning of faults, and at lower applied voltages. Temperature distribution at the back side was even except at the edge, as at the front side. These results tell that the whole SFCL was heated to similar degree during quenches, and that effective cooling of SFCLs at the back side is as important to the stability of SFCLs as at the front side. The results could be explained with the concept of heat transfer within the film.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1999년도 추계학술대회 논문집 학회본부 C
• /
• pp.873-875
• /
• 1999

We have fabricated good quality superconducting $YBa_{2}Cu_{3}O_{7-\delta}$ thin films on Hastelloy(Ni-Cr-Mo alloys) metallic substrate with $CeO_2$ and $BaTiO_3$ buffer layers in-situ by pulsed laser deposition in a multi-target processing chamber. We have chosen $CeO_2$ as a buffer layer which has cubic structure of $5.41{\AA}$ lattice parameter and only 0.2% of lattice mismatch with YBCO. $CeO_2$ layer may be helpful for power transmission due to its conducting property. In order to enhance the crystallization of YBCO films on metallic substrates. we deposited $CeO_2$ and $BaTiO_3$ buffer layers at various temperatures. The YBCO superconducting tape fabricated with $BaTiO_3$ and $CeO_2$ buffer layers shows 85K of transition temperature and about $8.4{\times}10^4A/cm^2$ of critical current density at 77K.

• 한국축산식품학회지
• /
• 제27권1호
• /
• pp.102-109
• /
• 2007

Lactobacillus salivarius subsp. salivarius CNU27 possessed a high level of ${\alpha}$-galactosidase activity. Purified ${\alpha}$-galactosidase was obtained after sonication of harvested cell pellet followed by DEAE-Sephadex A-50 and Mono Q anion exchange chromatography. The specific activity of the purified enzyme was 8,994 units/mg protein which is 17.09 times higher than that in crude extract. The native enzyme was a monomer with a molecular mass of 56,397.1 dalton. The optimum temperature and pH for the enzyme were $40^{\circ}C$ and 6.0, respectively. The enzyme was stable between 25 and $50^{\circ}C$. However, ${\alpha}$-galactosidase activity was lost rapidly below pH 4.5 and above pH 8.5. The enzyme activity decreased to 6.73% and 4.30% of the original activity by addition of $Cu^{2+}$ and $Hg^{2+}$, respectively. Other metal compounds did not affect the enzyme activity significantly. The enzyme liberated galactose from melibiose, raffinose, and stachyose. The rate of substrates hydrolysis was measured by HPLC. Raffinose, stachyose and melibiose were completely decomposed after 24 hr at $40^{\circ}C$.

• 한국재료학회지
• /
• 제3권2호
• /
• pp.103-110
• /
• 1993

금속동-흑연복합분말을 제조하기 위하여 염화동을 흑연주위에서 수소환원시킴으로써 흑연표면에 금속동을 석출시키는 새로운 방법으로 흑연-금속동 복합재료를 제조하고자 하였으며, 이를 위해 325 mesh이하의 KISH및 천연흑연을 모재로 하여 350-50$0^{\circ}C$의 환원온도에서 염화동을 환원시키는 실험을 실시하였다. 금속동의 분산도는 환원온도가 낮을수록 양호한 것으로 나타났으며, 금속동의 분산도를 높이기 위해서는 가능한한 환원온도를 낮게하는 것이 유리한 것으로 나타났다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 하계학술대회 논문집
• /
• pp.790-793
• /
• 2000

We have fabricated good quality superconducting YBa$_2$Cu$_3$$O_{7-x}$(YBCO) thin films on Hastelloy(Ni-Cr-Mo alloys) metallic substrates with CeO$_2$and BaTiO$_3$buffer layers in-situ by pulsed laser deposition in a multi-target processing chamber. YBCO film with CeO$_2$ single buffer layer shows T$_{c}$ of 71.64 K and the grain size less than 0.1 ${\mu}{\textrm}{m}$. When BaTiO$_3$is used as a single buffer layer, the grain size of YBCO is observed to be larger than that of YBCO/CeO$_2$by 200 times and the transition temperature of the film is enhanced to be about 84 K. CeO$_2$/BaTiO$_3$double buffer layer has been adopted to enhance the superconducting properties, which results in the enhancement of the critical temperature and the critical current density to be about 85 K and 8.4 $\times$ 10$^4$ A/cm$^2$ at 77 K, respectively mainly due to the enlargement of the grain size of YBCO film.ilm.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2005년도 제36회 하계학술대회 논문집 C
• /
• pp.2001-2003
• /
• 2005

Various organic acid were used in order to prepare new metalorganic deposition solution for high quality $REBa_2Cu_3O_{7-{\delta}}$ (RE=Y, Eu, Gd) films. Prepared fluorine free MO precursor solution was coated on single crystal (001) $LaAlO_3$ (LAO) by dip coating method. Processing parameters such as oxygen partial pressure, water vapor, ramping rate and pyrolysis temperature etc havebeen controlled in order to make high $J_c$ films with a good epitaxial relationship with substrate. 0.5 micron-thick film was obtained by single coating and no crack appeared after calcination. Oxygen partial pressure was varied in the range of $100{\sim}1,000 ppm$ and conversion heat treatment was carried out at the temperature of $725{\sim}765^{\circ}C$. A critical transition temperature $(T_{c0})$ of 90K and a critical transport current density $(J_c)$ of $>0.5MA/cm^2$ (77K and self-field) were demonstrated for the YBCO film on (001) oriented LAO substrates with a thickness of 0.5 micron. $I_c$ was determined by utilizing a transport measurement. SEM and XRD investigations confirmed that films were grown epitaxially onto the LAO single crystal substrate. It is thought that fluorine free new MOD solutionis promising for high quality REBCO films.

• 한국전기전자재료학회논문지
• /
• 제13권11호
• /
• pp.959-962
• /
• 2000

We have fabricated good quality superconducting YBa$_2$Cu$_3$$O_{7-x}$(YBCO) thin films on Hastelloy(Ni-Cr-Mo alloys) metallic substrates with CeO$_2$and BaTiO$_3$buffer layers in-situ by pulsed laser deposition in a multi-target processing chamber. YBCO film with CeO$_2$single buffer layer shows T$_{c}$ of 71.64 K and the grain size less than 0.1${\mu}{\textrm}{m}$. When BaTiO$_3$ is used as a single buffer layer, the grain size of YBCO is observed to be larger than that of YBCO/CeO$_2$by 200 times and the transition temperature of the film is enhanced to be about 84 K. CeO$_2$/BaTiO$_3$double buffer layer has been adopted to enhance the superconducting properties, which results in the enhancement of the critical temperature and the critical current density to be about 85 K and 8.4$\times$10$^4$ A/$\textrm{cm}^2$ at 77 K, respectively mainly due to the enlargement of the grain size of YBCO film.ilm.

• 조명전기설비학회논문지
• /
• 제27권3호
• /
• pp.107-112
• /
• 2013

Cu(In,Ga)$Se_2$ (CIGS) thin films were annealed on molybdenium/sodalime glass substrates of $300{\times}300mm^2$ by rapid thermal processing (RTP) with 2-step rising-temperature times in $N_2$ ambient. Morphological property, structural characteristics and chemical composition of the precursor of CIGS thin films were influenced directly with a change of $1^{st}$-step rising-temperature time in RTP whereas there is no significant difference with the different $2^{nd}$-step rising-temperature time (final crystallization temperature). The shorter $1^{st}$-step rising-temperature time in RTP obtained the higher photovoltaic cell efficiency from 7.469% to 8.479% even though the ideal composition in CIGS thin films could not be accoplished in this study.