• 한국대기환경학회지
• /
• 제22권3호
• /
• pp.373-381
• /
• 2006

The catalytic combustion of toluene was investigated on the Cu-Mn oxide catalysts prepared by the deposition-precipitation method. Experiment of toluene combustion was performed with a fixed bed flow reactor in the temperature range of $100{\sim}280^{\circ}C$. Among the catalysts, 1.29Cu/Mn showed the most activity at $260^{\circ}C$. The deposition-precipitation method may be showed the potential to enhance the activity of catalysts. The catalysts were characterized by BET, scanning electron microscopy (SEM), temperature-programmed reduction (TPR), X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD) techniques. On the basis of catalyst characterization data, the results showed that the surface of catalysts by deposition-precipitation method had uniform distribution and smaller particle size, which enhanced the reduction capability of catalysts. The XRD results showed that $Cu_{1.5}Mn_{1.5}O_{4}$ spinel phase was made by deposition-precipitation method, and increased catalyst activity and redox characteristic. It was assumed that the reduction step of $Cu_{1.5}Mn_{1.5}O_{4}$ spinel phase progressed $Cu_{1.5}Mn_{1.5}O_{4}\;to\;CuMnO_{2},\;and\;Cu_{2}O\;to\;CuMn_{2}O_{4}\;and\;Cu$.

• 한국자동차공학회논문집
• /
• 제10권1호
• /
• pp.32-44
• /
• 2002

Selective catalytic reduction of nitric oxide by methane in the presence of excess oxygen was investigated over copper and cobalt ion-exchanged ZSM-5 zeolites. Copper ion-exchanged ZSM-5(Cu-ZSM-5) has the limitations for commercial applications to lean-bum gasoline and diesel engines due to low thermal stability and resistance to water vapor and sulfur dioxide. But cobalt ion-exchanged ESM-5(Co-ZSM-5) is more active at high temperatures and also stable to water vapor and sulfur dioxide for catalytic reduction of nitric oxide by methane. The catalytic activity of Cu-ZSM-5 for NO reduction increases with increasing temperatures, reaches the maximum conversion of 23.0% at 350\"C. and then decreases with higher temperatures. In the meantime catalytic activities of Co-ZSM-5 show the maximum conversion of 25.8% at $500^{\circ}C$ Therefore Co-ZSM-5 catalysts have higher thermal stability at high temperatures. Catalytic activities of both zeolites were remarkably enhanced with the existence of oxygen in the exhaust. It is noted that the catalytic activity of Cu-ZSM-5 decreases with the increasing concentration of methane while the catalytic activity of Co-ZSM-5 decreases with increasing contents of methane in the exhaust. This may imply the existence of different paths of NO reduction by methane in the presence of excess oxygen fur Cu-ZSM-5 and Co-ZSM-5 catalysts. For binary metal ionexchanged ZSM-5, the primary ion-exchanged metal may be masked by secondary ion-exchanged component, which plays the important role for catalytic activities of binary metal ion-exchanged ZSM-5, Therefore CuCo-ZSM-5 catalysts show the similar volcano-shaped curves to Cu-ZSM-5 catalysts between the activity and temperature. It Is interesting that the activities of CoCu-ZSM-5 catalysts indicate almost no dependence on the concentration of methane in the exhaust.aust.

• 한국전기전자재료학회논문지
• /
• 제29권6호
• /
• pp.337-341
• /
• 2016

In this study, $ Ni_{0.79}(Mn_{2.21-x}Cu_x)O_4$ (x=0~0.25) specimens were prepared by using a conventional mixed oxide method. All specimens were sintered in air at $1,200^{\circ}C$ for 12 h and cooled at a rate of $2^{\circ}C/min$ to $800^{\circ}C$, subsequently quenching to room temperature. We investigated the structural and electrical properties of $ Ni_{0.79}(Mn_{2.21-x}Cu_x)O_4$ specimens with variation of CuO amount for the application of NTC thermistors. As results of X-ray diffraction patterns, all specimens showed the formation of a complete solid solution with cubic spinel phase. The relationship between ln ${\rho}$ and the reciprocal of absolute temperature(1/T) for the NTC thermistors was shown linearity, which exhibited the typical NTC thermistor properties. With increasing the amount of CuO, resistivity at room temperature, B-value, and temperature coefficient resistance decreased.

• 한국표면공학회지
• /
• 제22권4호
• /
• pp.179-184
• /
• 1989

This study seeks to the morphological changes in the oxide skin of the Al-10wt.%si alloy melts. These changes depend on the oxidation time and the temperature of the molten alloy, as well as the effects of adding Mg, Cu and Ni. Thess affects observed by X-ray diffractometer(XRD) and scanning electron microscope(SEM)' Very litte oxide skins on Al-10wtwt.%Si alloy melts can be detected by XRD because it is less than the measuring capabillity of the XRD, or the formation of noncrystalline oxide skins oxide skins canbe deteced by SEM. The addition of 1%Mg and 1%Cu-1%Mg-2.5%Ni to this base alloy crystallized the structure of the oxide skins and increased the oxidation in proportion to the length of time, but adding 3% had hardiy anyaffect at all on the crystal structure of the oxide skins.

• 문화기술의 융합
• /
• 제9권6호
• /
• pp.855-859
• /
• 2023

질산구리삼수화물염(copper(II) nitrate trihydrate) 수용액을 공업용 전분(starch)에 함침 시킨 전구체를 이용하여 산화구리(CuO) 나노 입자를 합성하였다. 주사전자현미경(SEM)을 통하여 질산구리삼수화물염 수용액이 함침된 전구체에 대한 구조를 분석하였고, 전구체에 대한 열처리 온도를 증가 시킴에 따라 생성되는 산화구리 입자의 입자 크기와 결정 구조를 X선회절분석법(XRD)과 주사전자현미경(SEM)으로 분석하였다. 분석 결과에 따르면, 전구체에서 유기물질이 완전히 열분해 되어지는 온도는 450-490℃이며, 열처리하는 온도가 증가함에 따라 생성되는 산화구리 입자의 크기와 결정성이 증가하는 것을 확인할 수 있었고, 또한 500-800℃에서 1시간씩 열처리하여 얻은 산화구리 입자의 크기는 100nm-2㎛인 것으로 나타났다. 하소 온도 400℃에서 산화구리 결정상이 형성되고, 800℃까지는 산화구리 단일상만 존재하며, 하소 온도의 증가에 따라 생성되는 입자의 크기가 커지는 것을 확인하였다.

• 한국재료학회지
• /
• 제9권4호
• /
• pp.335-340
• /
• 1999

The hot cracking phenomena and phase behaviors during hot working process of Cu-Ni bearing hot rolled steels were investigated by a $90^{\circ}$bending tests, BSE image analysis and EDS analysis. For aNi-free 1.2% Cu bearing steel, the surface hot cracking occurred about $1100^{\circ}C$ due to a liquid state Cu-enriched phase formed continuously at the interface between oxide scale and matrix. The liquid Cu-enriched phase penetrated into austenite grain boundaries and caused surface cracking during the hot working. In case of 0.6% Ni containing 1.2% Cu-Ni bearing steel, solid state Cu-Ni-riched phase existed at the scale/matrix interface as a discontinuous type. But the higher addition of 1.2% Ni, solid state Ni-Cu-riched phase was formed dominantly in the oxide scale. It was found that the addition of Ni suppressed the surface cracking of 1.2% Cu bearing steel by eliminating the liquid state Cu-enriched phase.

• Applied Microscopy
• /
• 제25권1호
• /
• pp.130-138
• /
• 1995

TEM specimen preparation methods have been examined to characterize Cu oxide particles in the polyimide film. Polyimide films were prepared by coating polyamic acid onto Cu films which had been deposited on TEM-mask and glass substrates and Cu foil, followed by thermal curing. In case of TEM-mask, direct observation was possible without further preparation. In other cases, TEM specimen were made by separating polyimide film from the substrate. Polyimide films were removed from glass and Cu foil by dissolving glass in HF solution and Cu foil in $H_{2}SO_{4}$ solution. TEM-mask observation confirms that fine $Cu_{2}O$ particles precipitate in the polyimide as a result of reaction of polyamic acid with Cu. However $Cu_{2}O$ particle reacts with HF and $H_{2}SO_{4}$ solution during dissolving the substrate and interpretation could be misled. It is concluded characterization of $Cu_{2}O$ particle in polyimide using TEM-mask is better than other methods.

• 한국재료학회지
• /
• 제27권4호
• /
• pp.221-228
• /
• 2017

Various morphologies of copper oxide (CuO) have been considered to be of both fundamental and practical importance in the field of electronic materials. In this study, using Cu ($0.1{\mu}m$ and $7{\mu}m$) particles, flake-type CuO particles were grown via a wet oxidation method for 5min and 60min at $75^{\circ}C$. Using the prepared CuO, AlN, and silicone base as reagents, thermal interface material (TIM) compounds were synthesized using a high speed paste mixer. The properties of the thermal compounds prepared using the CuO particles were observed by thermal conductivity and breakdown voltage measurement. Most importantly, the volume of thermal compounds created using CuO particles grown from $0.1{\mu}m$ Cu particles increased by 192.5 % and 125 % depending on the growth time. The composition of CuO was confirmed by X-ray diffraction (XRD) analysis; cross sections of the grown CuO particles were observed using focused ion beam (FIB), field emission scanning electron microscopy (FE-SEM), and energy dispersive analysis by X-ray (EDAX). In addition, the thermal compound dispersion of the Cu and Al elements were observed by X-ray elemental mapping.

• 한국세라믹학회지
• /
• 제32권1호
• /
• pp.83-89
• /
• 1995

YBa2Cu3O7-$\delta$, Y2BaCuO5, and binary compounds in the Ba-Cu-O system with the nominal composition of Ba2CuO3, BaCuO2, Ba3Cu4O7, Ba3Cu5O8 were synthesized to investigate the heat evolutions and crystalline phases in the hydration reaction of orthorhombic YBa2Cu3O7-$\delta$ phase. The observed crystalline phases were YBa2Cu3O7-$\delta$, Y2BaCuO5, and BaCuO2, or Ba2Cu3O5＋x, and some amount of noncrystalline phase in the Ba-Cu system comounds. In contact with distilled water, YBa2Cu3O7-$\delta$ and Y2BaCuO5 did not have considerable heat liberation, but in the binary compounds of the Ba-Cu-O system, the amount of total heat liberation was increased with respect to the Cu content. It might be that the reaction of high temperature superconductor YBa2Cu3O7-$\delta$ with water and/or moisture originated from the unusual oxidation state of Cu ion and the presence of amorphous Ba-Cu oxide compound. The degradation of high Tc superconductor by moisture and water could be controlled by restricting the heterogeneous distribution of Tc comlposition and the formation of second phase, such as stable Y2BaCuO5, and the resulting unstable Ba-Cu oxide compound.

• Journal of Electrochemical Science and Technology
• /
• 제11권4호
• /
• pp.399-405
• /
• 2020

Hollow copper oxide/multi-walled carbon nanotubes (CuO/MWCNT) composites were fabricated via an optimized infiltration-reduction-oxidation method, which is more facile and easy to control. The crystalline structure and morphology were characterized by X-ray diffraction (XRD), and transmission electron microscopy (TEM). The as-prepared CuO/MWCNT composites deliver an initial capacity of 612.3 mAh·g^-1 and with 80% capacity retention (488.2 mAh·g^-1) after 100 cycles at a current rate of 0.2 A·g^-1. The enhanced electrochemical performance is ascribed to the better electrical conductivity of MWCNT, the hollow structure of CuO particles, and the flexible structure of the CuO/MWCNT composites.