• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1998.05a
• /
• pp.65-65
• /
• 1998

• Journal of the Microelectronics and Packaging Society
• /
• v.28 no.1
• /
• pp.39-46
• /
• 2021

The quantitative measurement of interfacial adhesion energy (Gc) of multilayer thin films for Cu interconnects was investigated using a double cantilever beam (DCB) and 4-point bending (4-PB) test. In the case of a sample with Ta diffusion barrier applied, all Gc values measured by the DCB and 4-PB tests were higher than 5 J/㎡, which is the minimum criterion for Cu/low-k integration without delamination. However, in the case of the Ta/Cu sample, measured Gc value of the DCB test was lower than 5 J/㎡. All Gc values measured by the 4-PB test were higher than those of the DCB test. Measured Gc values increase with increasing phase angle, that is, 4-PB test higher than DCB test due to increasing plastic energy dissipation and roughness-related shielding effects, which matches well interfacial fracture mechanics theory. As a result of the 4-PB test, Ta/Cu and Cu/Ta interfaces measured Gc values were higher than 5 J/㎡, suggesting that Ta is considered to be applicable as a diffusion barrier and a capping layer for Cu interconnects. The 4-PB test method is recommended for quantitative adhesion energy measurement of the Cu interconnect interface because the thermal stress due to the difference in coefficient of thermal expansion and the delamination due to chemical mechanical polishing have a large effect of the mixing mode including shear stress.

• Korean Journal of Materials Research
• /
• v.16 no.4
• /
• pp.257-263
• /
• 2006

We have investigated the effect of silver added to Cu films on the microstructure evolution, resistivity, surface morphology, stress relaxation temperature, and adhesion properties of Cu(Ag) alloy thin films deposited on Mo glue layer upon annealing. In addition, pure Cu films deposited on Mo has been annealed and compared. The results show that the silver in Cu(Ag) thin films control the grain growth through the coarsening of its precipitates upon annealing at $300^{\circ}C{\sim}600^{\circ}C$ and the grain growth of Cu reveals the activation energy of 0.22 eV, approximately one third of activation energy for diffusion of Ag dopant along the grain boundaries in Cu matrix (0.75 eV). This indicates that the grain growth can be controlled by Ag diffusion along the grain boundaries. In addition, the grain growth can be a major contributor to the decreased resistivity of Cu(Ag) alloy thin films at the temperature of $300^{\circ}C{\sim}500^{\circ}C$, and decreases the resistivity of Cu(Ag) thin films to $1.96{\mu}{\Omega}-cm$ after annealing at $600^{\circ}C$. Furthermore, the addition of Ag increases the stress relaxation temperature of Cu(Ag) thin films, and thus leading to the enhanced resistance to the void formation, which starts at $300^{\circ}C$ in the pure Cu thin films. Moreover, Cu(Ag) thin films shows the increased adhesion properties, possibly resulting from the Ag segregating to the interface. Consequently, the Cu(Ag) thin films can be used as a metallization of advanced TFT-LCDs.

• Journal of the Microelectronics and Packaging Society
• /
• v.30 no.2
• /
• pp.52-59
• /
• 2023

The effects of dielectric curing temperature and temperature/humidity treatment conditions on the interfacial adhesion energies between Ti diffusion barrier/polybenzoxazole (PBO) dielectric layers were systematically investigated for Cu redistribution layer applications of fan-out wafer level package. The initial interfacial adhesion energies were 16.63, 25.95, 16.58 J/m² for PBO curing temperatures at 175, 200, and 225 ℃, respectively. X-ray photoelectron spectroscopy analysis showed that there exists a good correlation between the interfacial adhesion energy and the C-O peak area fractions at PBO delaminated surfaces. And the interfacial adhesion energies of samples cured at 200 ℃ decreased to 3.99 J/m² after 500 h at 85 ℃/85 % relative humidity, possibly due to the weak boundary layer formation inside PBO near Ti/PBO interface.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.4
• /
• pp.531-537
• /
• 1999

A copper based leadframe was oxidized in brown-oxide forming solution, then the growth characteristics of brown oxide and the effect of brown-oxide formation on the adhesion strength of leadframe to epoxy molding compound (EMC) were studied by using sandwiched double cantilever beam (SDCB) specimens. The brown oxide is composed of fine acicular CuO, and its thickness increased up to ~150 nm within 2 minutes and saturated. Bare leadframe showed alomost no adhesion to EMC, while once the brown-oxide layer formed on the Surface of leadframe, the adhesion strength increased up to ~80 J/$\m^2$ within 2 minutes. Correlation between oxide thickness, $\delta$ and the adhesion strength in terms of interfacial fracture toughness, $G_{c}$ was linear. Considering the above results, we might conclude that the main adhesion mechanism of brown-oxide treated leadframe to EMC is mechanical interlocking, in which fine acicular CuO plays a major role.e.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2006.08a
• /
• pp.1640-1644
• /
• 2006

The first issue that should be overcome in copper process is its poor adhesive strength between pure copper film and glass substrate. In this study, defining the adhesive strength of pure copper film on various substrates and clarifying the key deposition parameters are presented for the investigation of copper process. First, using different kinds of surface plasma treatments were studied and the results showed that the adhesive strength was not improved even though the roughness of glass substrate surface was increased. Second, adding an adhesive layer between glass substrate and pure copper film was used to enhance the adhesion. Based on the data in the present paper, adopting copper alloy film as an adhesive layer can have capability preventing peeling problem in copper process. Besides, Cu/Cu alloy structure could be etched with the same etchant with better taper angle than the one with single layer of Cu. Unlike Cu/Mo structure, there is no residual problem for Cu/Cu alloy structure during etching process. Finally, this structure was examined in electrical test without significant difference in comparison with the conventional metal process.

• Journal of the Microelectronics and Packaging Society
• /
• v.5 no.1
• /
• pp.7-18
• /
• 1998

In the flip chip interconnection on organic substrates using eutectic Pb/Sn solder bumps highly reliable Under Bump Metallurgy (UBM) is required to maintain adhesion and solder wettability. Various UBM systems such as 1$\mu$m Al/0.2$\mu$m Pd/1$\mu$m Cu, laid under eutectic Pb/Sn solder were investigated with regard to their interfacial reactions and adhesion proper-ties. The effects of numbers of solder reflow and aging time on the growth of intermetallic compounds (IMCs) and on the solder ball shear strength were investigated. Good ball shear strength was obtained with 1$\mu$m Al/0.2$\mu$m Ti/5$\mu$m Cu and 1$\mu$m Al/0.2$\mu$m ni/1$\mu$m Cu even after 4 solder reflows or 7 day aging at 15$0^{\circ}C$. In contrast 1$\mu$m Al/0.2$\mu$m Ti/1$\mu$m Cu and 1$\mu$mAl/0.2$\mu$m Pd/1$\mu$m 쳐 show poor ball shear strength. The decrease of the shear strength was mainly due to the direct contact between solder and nonwettable metal such as Ti and Al resulting in a delamination. In this case thin 1$\mu$m Cu and 0.2$\mu$m Pd diffusion barrier layer were completely consumed by Cu-Sn and pd-Sn reaction.

• Journal of the Semiconductor & Display Technology
• /
• v.3 no.3
• /
• pp.11-17
• /
• 2004

This research has been progressed for adhesive improvement of the Polyimide/Buffer layer/Cu at the COF(Chip On Film) which induced as the alternative plan about high concentration of a circuit or substrates according to demands of miniaturization and high efficiency of various electronic equipment. RF plasma equipment was applied to when plama pretreatment was performed for improvement of adhesive strength of PI and Cr as the buffer layer. Experimental fluents were a species of the buffer layer, depositied time and the ratio of $O_2$/Ar when performed to plasma pretreatment. The results are that Ni was superior to Cr at peel test according to a species of the buffer layer, peel strength and Cu THK were showed proportional relation to deposition structure of the same buffer layer and sample of the Cr depositied time(30 sec) and Cu depositied time(20 min) was showed good adhesion to peel test according to Cr's depositied time and Cu's depositied time. When perform PI's plasma pretreatment peel strength and $O_2$/Ar ratio were showed proportional relation. But $O_2$/Ar(2/5) was best condition since then decreased.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.4
• /
• pp.347-355
• /
• 2003

Roughening of metal surfaces frequently enhances the adhesion strength of metals to polymers by mechanical interlocking. When a failure occurs at a roughened metal/polymer interface, the failure prone to be cohesive. In a previous work, an adhesion study on a roughened metal (oxidized copper-based leadframe)/polymer (Epoxy Molding Compound, EMC) interface was carried out, and the correlation between adhesion strength and failure path was investigated. In the present work, an attempt to interpret the failure path was made under the assumption that microvoids are formed in the EMC as well as near the roots of the CuO needles during compression-molding process. A simple adhesion model developed from the theory of fiber reinforcement of composite materials was introduced to explain the adhesion behavior of the oxidized copper-based leadframe/EMC interface and failure path. It is believed that this adhesion model can be used to explain the adhesion behavior of other similarly roughened metal/polymer interfaces.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.2
• /
• pp.142-150
• /
• 2001

Due to naturally formed copper oxides, the adhesion strength between copper and epoxy resin is often very poor. To improve the adhesion strength between copper and epoxy resin, Cu-based leadframe sheets were oxidized in a brown-oxide forming solution. Then the effect of brown-oxide formation on the adhesion strength of leadframe to epoxy molding compound (EMC) was studied using pull-out specimens. After the pull-out test, fracture surfaces were analyzed using SEM, AES and EDS to determine failure path. The results showed that the failure path lay over inside the CuO and inside the EMC irrespective of the pull strength.