• Journal of Welding and Joining
• /
• v.19 no.2
• /
• pp.176-181
• /
• 2001

Reflow soldering characteristics of Sn-3.5Ag and Sn-37Pb balls for BGA(Ball grid Array) were investigated. Diameter of 0.76mm ball was set on a Cu/Ni/Au-coated pad and reflowed in air with changing peak soldering temperature and conveyor speed. Peak temperatures were changed from 240 to 28$0^{\circ}C$ for Sn-3.5Ag, and from 220 to 26$0^{\circ}C$ for Sn-37Pb balls. As results, heights of solder balls increased and widths decreased with peak soldering temperature. Through aging treatment at 10$0^{\circ}C$ for 1.000 hrs, average hardness of Sn-3.5Ag balls bonded at 25$0^{\circ}C$ cecreased from 14.90Hv to 12.83Hv And with same aging conditions, average shear strength of Sn-3.5Ag balls bonded at 26$0^{\circ}C$ decreased from 1727gf to 1650gf.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.5
• /
• pp.386-392
• /
• 2003

The electroplating process for a solder bump which can be applied for a flip chip was studied. Si-wafer was used for an experimental substrate, and the substrate were coated with UBM (Under Bump Metallization) of Al(400 nm)/Cu(300 nm)Ni(400 nm)/Au(20 nm) subsequently. The compositions of the bump were Sn-Cu and eutectic Sn-Pb, and characteristics of two bumps were compared. Experimental results showed that the electroplated thickness of the solders were increased with time, and the increasing rates were TEX>$0.45 <\mu\textrm{m}$/min for the Sn-Cu and $ 0.35\mu\textrm{m}$/min for the Sn-Pb. In the case of Sn-Cu, electroplating rate increased from 0.25 to $2.7\mu\textrm{m}$/min with increasing current density from 1 to 8.5 $A/dm^2$. In the case of Sn-Pb the rate increased until the current density became $4 A/dm^2$, and after that current density the rate maintains constant value of $0.62\mu\textrm{m}$/min. The electro plated bumps were air reflowed to form spherical bumps, and their bonded shear strengths were evaluated. The shear strength reached at the reflow time of 10 sec, and the strength was of 113 gf for Sn-Cu and 120 gf for Sn-Pb.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.76-76
• /
• 2009

눈부신 전자산업의 발달로 대부분의 전자제품이 다기능/경박단소화 되고 있어, 고밀도 실장 기술인 양면 표면실장과 고집적 패키징 기술인 패키지 적층 공정의 적용이 점차 확대되고 있다. 따라서 양면 표면실장 및 패키지 적층 공정에 사용되는 저온 접합용 무연 솔더 즉, $183^{\circ}C$(Sn-37Pb 공정 솔더 융점) 이하의 융점을 가지는 저온 무연 솔더에 대한 관심이 높아지고 있다. 한편, 미세피치 적용 분야에 있어 ACF/P를 이용한 COG 접속 분야 외에도 최근 저온 접합용 무연 솔더를 이용한 접속 분야가 각광을 받고 있다. 따라서, 접속피치 미세화에 대응하기 위해 스크린 인쇄성을 향상시킬 수 있는 저온 무연 솔더 paste 제조 및 공정 기술의 개발이 필요한 실정이다. 현재 대표적인 저온 무연 솔더 조성은 Sn-Bi계($138^{\circ}C$ 융점)와 Sn-In계($120^{\circ}C$ 융점)이다. 하지만, 이들 조성의 신뢰성 등에 있어 개선의 여지가 있으므로 이를 해결하기 위한 무연솔더 조성의 개발이 필요하다. 이와 같은 관점에서, 본 연구는 $137^{\circ}C$의 융점을 갖는 Sn-57.6Ag-0.4Ag 저온 무연 솔더 paste를 $217^{\circ}C$의 융점을 갖는 Sn-3.0Ag-0.5Cu 솔더 paste와 비교하여 인쇄성, reflow 특성, void inspection, 미세조직 관찰 및 underfill 적용 등의 실험을 실시하였다.

• Journal of the Microelectronics and Packaging Society
• /
• v.22 no.3
• /
• pp.51-56
• /
• 2015

It has been used various pad finish materials to enhance the reliability of solder joint and recently Electroless Ni Electroless Pd Immersion Gold (the following : ENEPIG) pad has been used more than others. This study is about reliability according to being used in commercial Electrolytic Ni pad and ENEPIG pad, and was observed behavior of various Cu contents. After reflow, the inter-metallic compound (IMC) between solder and pad is composed of $Cu_6Sn_5$ (Ni substituted) by using EDS, and in case of ENEPIG, between IMC and Ni layer was observed the dark layer ($Ni_3P$ layer). Additional, it could be controlled the thickness of dark layer according to Cu contents. Investigated the different fracture mode between electrolytic Ni and ENEPIG pad after drop shock test, in case of soft Ni, accelerated stress propagated along the interface between $1^{st}$ IMC and $2^{nd}$ IMC, and in case of ENEPIG pad, accelerated stress propagated along the weaken surface such as dark layer. The unstable interface exists through IMC, pad material and solder bulk by the lattice mismatch, so that the thermal and physical stress due to the continuous exterior impact is transferred to the IMC interface. Therefore, it is strongly requested to control solder morphology, IMC shape and thickness to improve the solder reliability.

• Journal of the Microelectronics and Packaging Society
• /
• v.9 no.4
• /
• pp.1-9
• /
• 2002

The metallurgical reaction properties between the pad consisted of 0.5 $\mu\textrm{m}$Au/5 $\mu\textrm{m}$Ni/Cu layers on a conventional ball grid array (BGA) substrate and In-15 (wt.%)Pb-5Ag solder ball were characterized during the reflow process and solid aging. During the reflow process of 1 to 5 minutes, it was observed that thin $AuIn_2$ or Ni-In intermetallic layer was formed at the interface of solder/pad. The dissolution rate of the Au layer into the molten solder was about $2\times 10^{-3}$ $\mu\textrm{m}$/sec which is remarkably low in comparison with a eutectic Sn-37Pb solder. After solid aging treatment for 500 hrs at $130^{\circ}C$, the thickness of $Ni_{28}In_{72}$ intermetallic layer was increased to about 3 $\mu\textrm{m}$ in all the conditions nevertheless the initial reflow time was different. These result show that In atoms in the solder alloy were diffused through the $AuIn_2$ phase to react with underlaying Ni layer during solid aging treatment. From the microstructural observation and shear tests, the reaction properties between In-15Pb-5Ag alloy and Au/Ni surface finish were analyzed not to trigger Au-embrittlement in the solder joints unlike Sn-37Pb composition.

• Journal of the Microelectronics and Packaging Society
• /
• v.16 no.3
• /
• pp.11-17
• /
• 2009

The drop impact reliability comes to be important for evaluation of the life time of mobile electronic products such as cellular phone. The drop impact reliability of solder joint is generally affected by the kinds of pad and reflow number, therefore, the reliability evaluation is needed. Drop impact test proposed by JEDEC has been used as a standard method, however, which requires high cost and long time. The drop impact reliability can be indirectly evaluated by using high speed shear test of solder joints. Solder joints formed on 3 kinds of surface finishes OSP (Organic Solderability Preservation), ENIG (Electroless Nickel Immersion Gold) and ENEPIG (Electroless Nickel Electroless Palladium Immersion Gold) was investigated. The shear strength was analysed with the morphology change of intermetallic compound (IMC) layer according to reflow number. The layer thickness of IMC was increased with the increase of reflow number, which resulted in the decrease of the high speed shear strength and impact energy. The order of the high speed shear strength and impact energy was ENEPIG > ENIG > OSP after the 1st reflow, and ENEPIG > OSP > ENIG after 8th reflow.

• Journal of Welding and Joining
• /
• v.20 no.2
• /
• pp.77-81
• /
• 2002

Many kinds of Pb-free solder have been investigated because of the environmental concerns. Sn-Ag-Cu system is well blown as most competitive Pb-free solder. However, since Sn-Ag-Cu system has relatively high melting point compared to Sn-Pb eutectic, it may a limitation, the some application. In this study, Bi and In contained solder of $Sn_3Ag_8Bi_5In$ which has relatively lower melting point, $188~204^{\circ}C$, was investigated. $Sn_3Ag_8Bi_5In$ solder ball of $500\mu\textrm{m}$ diameter was set on the Ni/Cu/Cr-UBM and reflow soldered in the range of $220~240^{\circ}C$ for 5~15s. The maximum shear strength of the solder ball was around 170mN by reflowing at $240^{\circ}C$ for 10s. Intermetallic compound formed on the UBM of Si-wafer was analysed by SEM(scanning electron microscope) and XRD(X-ray diffractometer).

• Proceedings of the KWS Conference
• /
• 2004.05a
• /
• pp.75-77
• /
• 2004

Microstructure and mechanical property of In48Sn solder on electrolytic Au/Ni/Cu BGA substrate were investigated with the number of reflows. AuIn and AuIn$_2$ IMCs were formed at the interface solder and pad after 1reflow. An increase of the number of reflows changed AuIn into AuIn$_2$. AuIn$_2$ IMC layer at the interface broke and spalled away into the solder after 3reflows. Shear force decreased with the number of reflows because the weakness of the interface by the spalling of AuIn$_2$ IMC layer.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2003.11a
• /
• pp.68-71
• /
• 2003

The reaction of ultra-small eutectic 58Bl-42Sn solder bump with Au/Ni/Ti and Au/Cu/Ti UBMs during reflow was studied. The eutectic Bi-Sn solder bumps of $46{\mu}m$ diameter were fabricated by using the evaporation method and were reflowed using the rapid thermal annealing system. The intermetallic compound was characterized using a SEM, an EDS, and an XRD. The $(Cu_xAu_{1-x})_6Sn_5$ compounds formed at the interface between Bi-Sn solder and Au/Cu/Ti UBM. On the other hand, in the Bi-Sn solder bump on Au/Ni/Ti UBM, the faceted and rectangular intermetallic compounds were observed on the solder bump surface and inside the solder bump as well as at the UBM interface. These intermetallic compounds were Identified as $(Au_{l-x-y}Bi_xNi_y)Sn_2$ phase.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.18 no.2
• /
• pp.234-240
• /
• 2009

In this study, we found that it is important to have a specific management of standards which are the $12{\pm}3{\mu}m$ of plating thickness and $2{\pm}1%$ of tuning. To verify these standards, we checked the plating thickness and density of tuning through marginal valuation of each and checked size of a plating particle, adhesion of solder and condition of reflow after a section chief.