• Carbon letters
• /
• v.28
• /
• pp.38-46
• /
• 2018

Modified pitch A (MPA) and modified pitch B (MPB) were prepared by oxidative polymerization and thermal polycondensation reaction with refined pitch as the raw material, respectively. The toluene soluble components (TS-1 and TS-2) were obtained by solvent extraction from MPA and MPB, separately. The Flynn-Wall-Ozawa method and Kissinger-Akahira-Sunose method were used to calculate the pyrolysis activation energy of TS. The Satava-Sestak method was used to investigate the pyrolysis kinetic parameters of TS. Moreover, the optical microstructure of the thermal conversion products (TS-1-P and TS-2-P) by calcination shows that TS-1-P has more contents of mosaic structure and lower contents of fine fiber structure than TS-2-P. The research result obtained by a combination of X-ray diffraction and the curve-fitting method revealed that the ratios of ordered carbon crystallite (Ig) in TS-1-P and TS-2-P were 0.3793 and 0.4417, respectively. The distributions of carbon crystallite on TS-1-P and TS-2-P were calculated by Raman spectrum and curve-fitting analysis. They show that the thermal conversion product of TS-2 has a better graphite crystallite structure than TS-1.

• Transactions on Electrical and Electronic Materials
• /
• v.12 no.4
• /
• pp.164-168
• /
• 2011

Nanocrystalline cadmium sulphide (CdS) thin films were prepared using chemical bath deposition (CBD), and the structural, optical and photoconductive properties were investigated. The crystal structure of CdS thin film was studied by X-ray diffraction. The crystallite size, dislocation density and lattice constant of CBD CdS thin films were investigated. The dislocation density of CdS thin films initially decreases with increasing film thickness, and it is nearly constant over the thickness of 2,500 ${\AA}$. The dislocation density decreases with increasing the crystallite size. The Urbach energies of CdS thin films are obtained by fitting the optical absorption coefficient. The optical band gap of CdS thin films increases and finally saturates with increasing the lattice constant. The Urbach energy and optical band gap of the 2,900 A-thick CdS thin film prepared for 60 minutes are 0.24 eV and 2.83 eV, respectively. The activation energies of the 2,900 ${\AA}$-thick CdS thin film at low and high temperature regions were 14 meV and 31 meV, respectively. It is considered that these activation energies correspond to donor levels associated with shallow traps or surface states of CdS thin film. Also, the value of ${\gamma}$ was obtained from the light transfer characteristic of CdS thin film. The value of ${\gamma}$ for the 2,900 A-thick CdS thin film was 1 at 10 V, and it saturates with increasing the applied voltage.

• Journal of Electrochemical Science and Technology
• /
• v.13 no.4
• /
• pp.438-452
• /
• 2022

For cuboid and ellipsoid crystallites of LiFePO₄ powders, by X-ray diffraction (XRD) and microscopic (TEM) studies, it is possible to determine the anisotropic parameters of the crystallite size distribution functions. These parameters were used to describe the cathode rate capability within the model of averaging the diffusion coefficient D over the length of the crystallite columns along the [010] direction. A LiFePO₄ powder was chosen for testing the developed model, consisting of big cuboid and small ellipsoid crystallites (close to them). When analyzing the parts of big and small rate capabilities, the fitting values D = 2.1 and 0.3 nm²/s were obtained for cuboids and ellipsoids, respectively. When analyzing the results of cyclic voltammetry using the Randles-Sevcik equation and the total area of projections of electrode crystallites on their (010) plane, slightly different values were obtained, D = 0.9 ± 0.15 and 0.5 ± 0.15 nm²/s, respectively. We believe that these inconsistencies can be considered quite acceptable, since both methods of determining D have obvious sources of error. However, the developed method has a clearly lower systematic error due to the ability to actually take into account the shape and statistics of crystallites, and it is also useful for improving the accuracy of the Randles-Sevcik equation. It has also been demonstrated that the shape engineering of crystallites, among other tasks, can increase the cathode capacity by 15% by increasing their size correlation coefficients.

• Applied Chemistry for Engineering
• /
• v.21 no.2
• /
• pp.178-182
• /
• 2010

Simultaneous removal reaction for NOx, soot over Pt catalysts using various $TiO_2$ as support was studied. The catalytic tests ware carried out injectin NO, soot, NO and soot simultaneously on each catalysts. As results, it showed different NOx removal efficiency and soot oxidation rate according to various kinds of $TiO_2$. Onset temperature of soot oxidation has a correlation to $NO_2$ generated for the independently performed NOx. It was investigated that NO to $NO_2$ oxidation was intimately related to crystallite size and surface area, and it has a tremendous impact on Pt aggregation on the catalyst surface and catalyst' reducibility. Therefore, we concluded that major index of the reaction was physico-chemical properties of catalyst' supports.

• Korean Chemical Engineering Research
• /
• v.51 no.2
• /
• pp.195-202
• /
• 2013

$TiO_2$ powders were prepared from titanium (IV) sulfate ($Ti(SO_4)_2$) solution using ammonia solution at low reaction temperature ($80{\sim}100^{\circ}C$) and atmospheric pressure by hydrothermal precipitation method without calcination. The effect of reaction conditions, such as reaction temperature, initial concentration of titanium (IV) sulfate ($Ti(SO_4)_2$) solution, pH of mixture solution and the physical properties of the prepared $TiO_2$, such as crystallite structure, crystallite size were investigated. The photocatalytic activity of prepared $TiO_2$ was tested by the photolysis of brilliant blue FCF (BB-FCF) under the UV and the analysis of UV-VIS diffuse reflectance spectroscopy (DRS). The physical properties of prepared $TiO_2$ were examined by X-ray diffraction (XRD), scanning electron microscopy (SEM), photoluminescence spectrometer (PL), particle size distribution measurements. The crystallite size and crystallinity of prepared $TiO_2$ increased with increasing titanium (IV) sulfate ($Ti(SO_4)_2$) concentration, but photocatalytic activity decreased. The crystallite size decreased with increasing pH of mixture solution, but photocatalytic activity increased. The crystallinity and photocatalytic activity increased with increasing reaction temperature. The results showed that anatase type $TiO_2$ could be prepared by hydrothermal precipitation method using titanium (IV) sulfate ($Ti(SO_4)_2$) solution and ammonia solution at low reaction temperature and atmospheric pressure without calcination.

• Journal of the Mineralogical Society of Korea
• /
• v.21 no.2
• /
• pp.201-208
• /
• 2008

Ceria ($CeO_2$) becomes one of important functional nanomaterials and a key abrasive material for chemical-mechanical planarization (CMP) of advanced integrated circuits in silicon semi-conductor technology. Two synthetic crystalline ceria (RT735, RT835) are studied by the Rietveld structural refinement to determine crystallite size and microstrain. Rietveld indices of RT735 and RT835 indicate good fitting with $R_p(%)=8.50$, 8.34; $R_{wp}(%)=13.4$, 13.5; $R_{exp}(%)=11.3$, 11.5; $R_B(%)=2.21$, 2.36; S(GofF: Goodness of fit)=1.2, 1.2, respectively. $CeO_2$ with space group Fm3m show a=5.41074(2), 5.41130(6) ${\AA}$, V=158.406(1), 158.455(3)${\AA}^3$ in dimension. Detailed Rietveld refinement reveals that crystallite size and microstrain are 37.42(1) nm, 0.0026 (RT735) and 72.80(2) nm, 0.0013 (RT835), respectively. It also shows that crystallite size and microstrain of ceria are inversely proportional to each other.

• Korean Chemical Engineering Research
• /
• v.47 no.4
• /
• pp.424-429
• /
• 2009

The effects of $Na_2O$, $SiO_2$ and $H_2O$ contents of the synthetic mixtures prepared from water glass on the crystallinity and crystallite size of sodalite were studied. The composition of the synthetic mixtures described by $x\;Na_2O{\cdot}y\;SiO_2{\cdot}Al_2O_3{\cdot}z\;H_2O$ was varied within x=2.5~7.5, y=1.4~3.0, z=140~400. The hydrothermal reaction was carried out at $140^{\circ}C$ for 2 days. High content of $Na_2O$ resulted in the high crystallinity and small crystallite of sodalite. The $SiO_2/Al_2O_3$ molar ratios of around 2 were suitable for the synthesis of sodalite, and produced zeolite species were varied by the $H_2O$ content. Sodalite was mainly obtained with a high crystallinity from the synthetic mixtures with $SiO_2/Al_2O_3$ molar ratio of around 2 and high content of $Na_2O$. The high content of sodium ions caused a decrease in the particle sizes because of their role of structure directing agent.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.29-54
• /
• 2005

Consolidation of ceramic particles at room temperature. Reduction of crystallite size and formation of nano-crystalline. Applicable to Integrate functionalceramic materials with metals and Si structure and to fabricate MEMS devises

• Journal of Hydrogen and New Energy
• /
• v.31 no.1
• /
• pp.1-7
• /
• 2020

The synthesis and catalytic activities over vanadium carbides were examined for ammonia decomposition reaction to produce the hydrogen. In particular, the comparison of vanadium nitrides were made on the ammonia decomposition reaction. The experimental data exhibited that BET surface areas ranged from 5.2 ㎡/g to 25.6 ㎡/g and oxygen uptake values varied from 3.8 μmol/g to 31.3 μmol/g. It is general that vanadium carbides (VC) were observed to be superior to vanadium nitrides for ammonia decomposition reaction. The primary reason for these differences were thought to be related to the extent of electronegativity between these materials. Most of vanadium carbide crystallites were exceeded by Pt/C crystallite. We assumed that the activities for vanadium carbide crystallites (VC) were comparable to or even higher than that determined for the Pt/C crystallite.

• Journal of the Korean institute of surface engineering
• /
• v.38 no.1
• /
• pp.37-43
• /
• 2005

Nanosized titanium-colloid particles were prepared by sol-gel method. The physical properties, such as thermal stability, crystallite size and crystallinity according to synthesis condition have been investigated by TEM, XRD, SEM, TGA and DTA. In addition, Zinc phosphating has been studied in order to compare the phosphating characterization of prepared nanosized titanium-colloid particles. The major phase of all the prepared titanium-colloid particles was an amorphous structure regardless of synthesis temperature and the structure was composed of phoshate complex and titanium. The micrographs of HR- TEM showed that nanosized titanium-colloid particles possessed a spherical morphology with a narrow size distribution. The crystallite size of the titanium-colloid particles synthesized at 80℃ was 4-5 nm and increased to 8-10 nm with an increase of synthesis temperature (150℃). In addition, the coating weight increased with an increase of temperature of phosphating solution and when the concentration of titanium-colloid was 2.0 g/l, the coating weight was 1.0 g/㎡.