• Journal of Magnetics
• /
• 제10권4호
• /
• pp.145-148
• /
• 2005

Effect of vacuum annealing on the microstructures and magnetic properties of $Fe_{84}Si_6B_{10}$ films has been investigated as a function of annealing temperature. X-ray diffraction and transmission electron microscopy were employed to analyze crystallization behavior of the films. Permeability of the films was measured at various frequencies by one-turn coil method. When the films were annealed below 673 K, the coercivity of the films did not change a lot (${\~}$1500 A/m) although the grain size of a crystalline phase in the partially crystallized films increased gradually up to about 16 nm. It then increased rapidly as the films became almost fully crystalline mostly with $\alpha$-(Fe,Si) phase at and above 723 K. On the other hand, the electrical resistivity of the films decreased monotonically with the increase of annealing temperature. The permeabilities of the films annealed at 473${\~}$673 K were all over 1000, showing the optimum value of 3500 at 523 K, and almost constant up to 300 MHz. However, those of the as-deposited and fully crystallized films were lower than 1000 and unstable at the same frequency range.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.264-264
• /
• 2007

$B_2Mg_{2/3}/Nb_{4/3}O_7\;(B_2MN)$ thin films and $Bi_{3/2}MgNb_{3/2}O_7\;(B_{1.5}MN)$ thin films were deposited as a function of various deposition temperatures on Pt/$TiO_2/SiO_2$/Si substrates by radio frequency magnetron sputtering system. Both of their thin films are shown to crystalline phase at $500^{\circ}C$, deposition temperature, using 100W RF power. The composition of them and structural micro properties are investigated by RBS spectrum and SEM, AFM. 200 nm-thick $B_2MN$ thin films were deposited at room temperature had capacitance density of $151nF/cm^2$ at 100kHz, dissipation factor of 0.003 and had capacitance density of $584nF/cm^2$ at 100kHz, dissipation factor of 0.0045 at $500^{\circ}C$ deposition temperature. Both of their dielectric constant deposited at room temperature and at $500^{\circ}C$ were each approximately 40 and 100.

• 한국염색가공학회지
• /
• 제7권4호
• /
• pp.8-15
• /
• 1995

A series of thermotropic Polyurethanes mesogenic unit were synthesized by polyaddition of a para-type diisocyanate such as 2,5-tolylene diisocyanate(2,5-TDI) with 4-4'-bis($\omega$-hydroxyalkoxy) biphenls(BPm: $HOCmH_{2m}OC_{6}H_{4}OC_{m}H_{2m}OH$ : m is the carbon number of the hydroxyalkoxy group) in DMF. Intrinsic viscosities of the polymers were in the range of 0.41~0.99dL/g DSC thermograms for these polymers exhibited two endothermic peaks corresponding to phase transitions of melting and isotropization. For examplem polyurethane 2,5-TDI/BPll with [η]=0.99 prepared from 2.5-TDI and 4,4'-bis[11-hydroxyundecaoxy biphenyl(BP11) a liquid crystalline phase from 156 to 173$^{\circ}C$. The thermotropic properites of liquid crystalline polyurethanes have been investigated by wide-angle X-ray scatter(WAXS), infrared (IR) spectroscopy, and differential scanning calorimetry (DSC). The mesomorphic behavior of the polyurethanes was concluded to be greatly dependent on the intermolecular hydrogen bonds through the urethane.

• 대한금속재료학회지
• /
• 제48권5호
• /
• pp.449-455
• /
• 2010

To enhance the efficiency of dye sensitized solar cells, we proposed crystalline anatase-$TiO_{2}$ by using a low temperature process ($150^{\circ}C{\sim}250^{\circ}C$). We successfully fabricated 30 nm-$TiO_{2}$ at a fixed atomic layer deposition condition of 1.0 sec of TDMAT pulse, 20 sec of TDMAT purge, 0.5 sec of H$_{2}$O pulse, and 20 sec of H$_{2}$O purge. In order to examine the microstructure, phase, and band-gap of the TiO$_{2}$ respectively, we employed a Nano-Spec, transmission electron microscope, high resolution XRD, Auger electron spectroscopy, scanning probe microscope, and UV-VIS-NIR. We were able to fabricate a crystalline anatase-phase of 30 nm-TiO$_{2}$ successfully at temperatures above $180^{\circ}C$. Our results showed that our proposed low temperature ALD process (below $200^{\circ}C$) might be applicable to glass and flexible polymer substrates.

• Bulletin of the Korean Chemical Society
• /
• 제12권5호
• /
• pp.490-494
• /
• 1991

The ${\beta} to {\alpha}$ phase transition in silver iodide is studied with the (N, V, E) and (N, P, T) molecular dynamics (MD) method. In experiments, the phase transition temperature is 420 K. Upon heating of ${\beta}$ form, the iodine ions undergo hcp to bcc transformation and silver ions become mobile. MD simulations for the ${\beta}$ and ${\alpha}$ phases are carried out at several temperatures and the radial distribution functions (rdf) are obtained at those temperatures in the (N, V, E) ensemble. But the phase transition is not found in our calculation. Next the phase transition is studied with the (N, P, T) MD and we find some evidences of phase transition. At 3 Kbars and 2 Kbars the phase transition temperatu re is about 300 K. For 3.55 Kbars, the phase transition is higher (420 K) than the low pressure case. The phase transition temperature is somewhat dependent on the pressure in our calculations.

• KIEE International Transactions on Electrophysics and Applications
• /
• 제4C권4호
• /
• pp.181-184
• /
• 2004

Thin films of single phase, polycrystalline silicon germanium (Si$_{1-x}$ Ge$_{x}$) were prepared by ion-beam evaporation (IBE) using Si-Ge multi-phase targets. After irradiation of the targets by a pulsed light ion beam with peak energy of 1 MV, 450 and 480 nm thick films were deposited on Si single crystal and quartz glass substrates, respectively. From XRD analysis, the thin films consisted of a single phase Si$_{1-x}$ Ge$_{x}$, whose composition is close to those of the targets.rgets.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1999년도 제29회 춘계학술대회
• /
• pp.119-126
• /
• 1999

The rolling fatigue lives (RFL) of five kinds of silicon nitride balls were investigated. Four kinds of Si$_3$N$_4$ balls were fabricated using different raw materials, sintering aids and sintering conditions, Commercially available Si3N4 ball was also studied for comparison. All the balls were finished up to the dimensional accuracy of Grade 10 defined in KS B 2001 (Steel Balls for Ball Bearings) with a size of 9.525mm. RFL tests were then conducted under the initial theoretical maximum contact stress 6.38 GPa and the spindle speed 10,000 rpm. Gear oil was provided by oiled race as lubricant. The results of RFL test indicated the prerequisitic conditions for the long rolling life of Si$_3$N$_4$ball : (1) the high density, (2) mjcrostructures consisted of small uniformly distributed grains, (3) little glassy phase in grainboundary, and (4) little crystalline phase and secondary phase that induces residual thermal stress due to the differences of thermal expansion coefficient with Si$_3$N$_4$Phase.

• 한국세라믹학회지
• /
• 제29권11호
• /
• pp.870-876
• /
• 1992

Lead lanthanum zirconate titanate (PLZT, 6/65/35) powders, crack-free and dense thin films have been prepared by polymeric sol-gel process. Pyrolysis of the gel, crystallization and optical transmittance behavior of the PLZT thin film onto sapphire substrate have been studied. Esterification occurs during synthesis of PLZT complexation. Crystalline Pb phase was transiently formed near 450$^{\circ}C$. Content of perovskite phase in the films were increased with increasing thickness of film, but the kinetics of formation of perovskite phase in films was slower than that of powders. Transmittance of the films was decreased with increasing the temperature of heat treatment. Ferroelectric hysteresis loop measurements indicated increments of remanent polarization and coercive field for plenty more of perovskite phase.

• 대한화장품학회지
• /
• 제25권4호
• /
• pp.65-74
• /
• 1999

We have studied the stability of W/O high internal phase emulsions(HIPE) containing water, cetyl dimethicone copolyol and oils varying magnesium sulfate in the range 0 to 0.5 wt% and oil polarities, respectively. The rheological consistency was mainly destroyed by the coalescence of the deformed water droplets. The greater the increase of complex modulus was, the less coalescence occurred and the more consistent the concentrated emulsions were. The increasing pattern of complex modulus versus volume fraction has been explained with the resistance to coalescence of the deformed interfacial film of water droplets in concentrated W/O emulsion. The stability is dependent on: (i) the choice of the oil is important, the requirements coincide with the requirements for the formation of the rigid liquid crystalline phases; and (ii) addition of salts the aqueous phase opposes the instability due to coalescence. Increasing the salt concentration increases the refractive index of the aqueous phase. It lowers the difference in the refractive index between the oil and aqueous phases. This decreases the attraction between the water domains, thus increasing the stability.

• Applied Microscopy
• /
• 제43권2호
• /
• pp.98-101
• /
• 2013

In the present study, formation of yard and shell has been investigated in as-melt-spun $Gd_{30}Ti_{25}Al_{25}Co_{20}$ alloy using a variety of transmission electron microscopy techniques. The phase separation during cooling leads to the formation of the microstructure consisting of amorphous droplets with different size scales embedded in the amorphous matrix. Due to the interdiffusion at the interface after the first-step phase separation, ~50 nm-thick yard develops on the surface of the primary droplet particle. Due to the critical wetting phenomenon, ~5 nm thickness shell enveloping the droplet forms. The sell is enriched in Co and Ti, implying that the composition is close to that of the droplet.