• Proceedings of the KSME Conference
• /
• 2007.05a
• /
• pp.179-182
• /
• 2007

The compressive fatigue tests on the closed cell Al-Si-Ca alloy foams with two different thicknesses were performed using a load ratio of 0.1. The quasi-static and cyclic compressive behaviors were obtained respectively. The fatigue stress-life (S-N) curves were evaluated from the obtained cyclic compressive behaviors. S-N curves were presented for the onset of progressive shortening. It turned out that the fatigue strength showed higher value for the thicker foam and the onset of shortening of thinner foam took place earlier. The crushing was found to initiate in a single band which broadens gradually with additional fatigue cycles. Progressive shortening of the specimen took place due to a combination of low cycle fatigue failure and cyclic ratcheting.

• Journal of Korea Foundry Society
• /
• v.1 no.3
• /
• pp.19-29
• /
• 1981

An emphasis has been placed on the importance of selecting a sand for furan sand process, which ie affected by the properties of sand. Investigations have been carried out to use the domestic artificial sands for the furan sand process. For laboratory investigations, the sands have been prepared and tested for chemical analysis, loss on ignition, sieve analysis, AFS grain fineness number, grain shape, PH value, acid demand, surface shape, theoretical surface area, moisture absorption, crushing durability and compressive strength and S. S. I. of molding sands. Most commercial sands have been found to be able to be used. The main requirement of the sands has been shown to be that 3 or 4 screen sands, AFS no.40-70 (or 100), of low acid demand, good surface area and good grain shape require less resin and catalyst to give an adequate strength.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.421-426
• /
• 2003

For the replacement of deteriorated concrete decks or wider-span slab, composite slab could be very attactive due to higher stiffness and strength. Based on the previous research, a modified I-beam composite hollow slab was suggested. In order to investigate the static flexural behavior of the proposed composite slab and to suggest its flexural design method, experiments were performed. Judging from the tests, a composite slab with I-beam having a semi-circle hole showed better structural performance. The effect of web details on the flexural stiffness was negligible. Flexural stiffness, ultimate strength, and ductility of the composite slabs were significantly greater than the RC slab due to composite action. While the failure of the RC slab was punching shear failure, the composite hollow slab showed flexural cracking and failure by yielding of the I-beams and crushing of concrete. Therefore, the current one-way design concept is appropriate for the design of I-beam composite hollow slab.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2006.11a
• /
• pp.111-114
• /
• 2006

This paper is to investigate the chemical composition and physical properties of cements collected at different crushing process line of ordinary portland cement to verify the possibility for producing special purpose cement based on the particle distribution technique. According to test results, six different cement samples with different blaine were gathered. loss on ignition and chemical composition of cements gathered were satisfied with KS L 5201. Cement collected at line 5 had the lowest blaine value while cement at line 4 had the highest blaine value. The coarser the cement particle is, the larger the fluidity of cement is. The compressive strength of cement was highly affected by the blaine value of cement. It is confirmed that the use of cement produced by the process of particle distribution control may be applied for special purpose cement without modification of chemical composition.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.459-460
• /
• 2006

N-type $Bi_2Te_3-Sb_2Te_3$ solid solutions doped with 1$CdCl_2$ was prepared by melt spinning, crushing and vacuum sintering processes. Microstructure, bending strength and thermoelectric property were investigated as a function of the doping quantity from 0.03wt.% to 0.10wt.% and sintering temperature from $400^{\circ}C$ to $500^{\circ}C$, and finally compared with those of conventionally fabricated alloys. The alloy showed a good structural homogeneity as well as bending strength of $3.88Kgf/mm^2$. The highest thermoelectric figure of merit was obtained by doping 0.03wt.% and sintering at $500^{\circ}C$.

• Advances in materials Research
• /
• v.11 no.3
• /
• pp.211-224
• /
• 2022

The shrinkage and the mechanical properties of polypropylene hybrid fiber reinforced mortar PHFRM were investigated in this study. Mortars were prepared with limestone crushing sand, Portland cement and polypropylene hybrid fibers PHF. Two types of virgin fibers, having the same length (30 mm) were used for reinforcing test mortars, fibers in diameter of 0.45 mm, used by PLAST BROS factory of Bordj Bou Arreridj (Algeria) for the fabrication of brooms (for household cleaning) and fibers in diameter of 0.25 mm, available on the market, having multiple applications. In this investigation, it was aimed to study the total and autogenous shrinkage, the flexural and compressive strength of mortars based on hybrid fibers. As a result, PHF have negatively affected the mortar workability. However, shrinkage risk was reduced and coarser fibers (PF45) were most effective for reducing shrinkage risk. The mechanical performances and the ductility of PHFRM were also enhanced.

• Design & Manufacturing
• /
• v.17 no.2
• /
• pp.42-46
• /
• 2023

Currently, fossil resources are depleting rapidly. We are looking for energy to replace fossil fuels. They are trying to use electricity to replace internal combustion locomotives. Secondary battery raw materials and chemical additives are pulverized by the high-speed rotation of the grinding disc of the Classifier Separator Mill. Grinding Disc Assembly requires characteristics to withstand abrasion, corrosion, high-speed rotational force and impact. Domestic and foreign grinding discs were analyzed through abrasion resistance, hardness, bending strength, and tensile adhesion strength tests.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.6
• /
• pp.1903-1912
• /
• 1996

A quantitative study of impact damage of a soda-lime glass was carried out. An initiation and a propagation of cracks by the impact of two inds of steel ball was investigated. The fron, side and rear view of cracks were observed by a stereo-microscope. And the lowering of the benidng strength due to the impact of steel balls was examined through the 4-point bending test. A transparent glass is very helpful to understand and analyze the impact damage behavior of another brittle matereial. A deagdram about crack patterns according to the threshold impact velocity was sketched. A ring crack and a cone crack were formed at the low impact velocity. And as the impact velocity was higher, initial lateral crack was generated on the slanting surface of cone crack, and radial cracks were generated from the outermost ring crack. When the impact velocity of steel balls exceed a critical velocity, the contact site of specimens were crushed. According to the propagation of a cone crack, a rapid strength degradation occurred. In the specimen having crushed region, a bending strength was converged to a constant value instead of strength degradation.

• Steel and Composite Structures
• /
• v.35 no.2
• /
• pp.237-247
• /
• 2020

Shear connectors are essential elements in the design of steel-concrete composite systems. These connectors are utilized to prevent the occurrence of potential slips at the interface of steel and concrete. The two types of shear connectors which have been recently employed in construction projects are C- and L-shaped connectors. In the current study, the behavior of C and L-shaped angle shear connectors is investigated experimentally. For this purpose, eight push-out tests were composed and subjected to monotonic loading. The load-slip curves and failure modes have been determined. Also, the shear strength of the connectors has been compared with previously developed relationships. Two failure modes of shear connectors were observed: 1) concrete crushing-splitting and 2) shear connector fracture. It was found that the L-shaped connectors have less shear strength compared to C-shaped connectors, and decreasing the angle leg size increases the shear strength of the C-shaped connectors, but decreases the relative ductility and strength of L-shaped connectors.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.4
• /
• pp.75-81
• /
• 2012

In case of crushing rock to produce materials for lean concrete subbase layer in concrete pavement, natural sand is used for the gradation adjustment of aggregates, and the percentage of natural sand used is 30%~40% of the weight ratio of aggregate mix. The supply of natural sand that is used in lean concrete as a fine aggregate is getting harder due to the current of exhaustion of source, and the cost for the purchase of natural sand is included in the cost of roadway construction. This study, therefore, was conducted in order to resolve the exhaustion of materials and economize in construction expenditure by the application of screenings, which is by-product of crushing rock in quarry, as an alternative to natural sand. As a result of a comparative analysis on the application of screenings and natural sand with typical types of rock that is produced in domestic, which was conducted in the first year, It is found out that the use of screenings as a fine aggregate showed better unconfined compression strength. Verification of actual application of screenings was conducted in the second year, after test construction and follow-up investigation. The compressive strength, compaction density, settlement of screenings applied case was higher than that of natural sand. Thus, it is expected that application of screenings to construction in field will contribute to the cost saving, material recycling and the protection of environment.