• Polymer(Korea)
• /
• v.37 no.6
• /
• pp.677-684
• /
• 2013

Zinc alginate films were prepared by a film maker from sodium alginate solutions of different weight ratios and then they solidified into 3 wt% content $ZnCl_2$ coagulation solution and washed and dried at a $60^{\circ}C$ oven for 20 min. The characteristics were measured by several methods (antimicrobial activity, viscosity, FTIR, TGA, SEM, EDS, contact angle, tensile strength and solubility) and the film properties were investigated. The antimicrobial test showed that the zinc alginate films result in excellent antimicrobial activity in the two strains (Klebsiella pneumonia, Staphylococcus). The surface of zinc alginate film from the solution of 9 wt% sodium alginate showed more uniform shape than any other films and the cross-section were hard and rough when the films were well-solidified by the $ZnCl_2$ solution. The tensile strength of zinc alginate films increased along with the concentration of sodium alginate solution due to the cross-linking, and the initial thermal decomposition temperature increased gradually.

• Transactions of the Korean hydrogen and new energy society
• /
• v.25 no.6
• /
• pp.561-569
• /
• 2014

Ceria ($CeO_2$) was used to increase the durability of the membrane in the polymer electrolyte membrane water electrolysis (PEMWE) circumstance. The sulfonated polyether ether ketone (SPEEK) as polymer matrix was prepared in the sulfonation reaction of polyether ether ketone (PEEK) to improve electrochemical characteristics. After sulfonation reaction, the organic-inorganic blended composite membranes were prepared by means of sol-gel casting method with loading the highly dispersed $CeO_2$ and Cs-substituted molybdophosphoric acid (Cs-MoPA) with cross-linking agent (tetrapropyl orthosilicate). Consequently, the composite membrane CL-SPEEK/Silane 4wt%/Cs-MoPA/Ceria(1%) showed the improved characteristics such as 82% of water content, 0.11136 S/cm of proton conductivity at $80^{\circ}C$, 55.50 MPa of tensile strength and 4.37% of breeding out of MoPA.

• Transactions of the Korean hydrogen and new energy society
• /
• v.26 no.3
• /
• pp.212-220
• /
• 2015

The engineering plastic of sulfonated polyether ether ketone (SPEEK) as a polymer matrix has been developed in this lab to replace Nafion, solid polymer electrolytes of perfluorosulfonic acid membrane which has several flaws such as high cost, and limited operational temperature above $80^{\circ}C$. The SPEEK was prepared in the sulfonation reaction of polyether ether ketone (PEEK). The organic-inorganic blended composite membranes were prepared by sol-gel casting method with loading the highly dispersed ceria and cesium-substituted tungstosilicic acid (Cs-TSiA) with cross-linking agent contents of 0.01 mL. In conclusion, CL-SPEEK/Cs-TSiA/ceria 1% membrane showed the optimum results such as 0.1882 S/cm of proton conductivity at $80^{\circ}C$, and 99.61 MPa of tensile strength which were better than Nafion 117 membrane.

• Transactions of the Korean hydrogen and new energy society
• /
• v.25 no.2
• /
• pp.151-160
• /
• 2014

CL-SPEEK/Cs-TPA/$CeO_2$ composite membrane was prepared for polymer electrolyte membrane water electrolysis (PEMWE). In order to improve the electrochemical, mechanical, durabilities and electrocatalytic characteristics, engineering plastic of polyether ether ketone (PEEK) as polymer matrix was sulfonated and the organic-inorganic blend composite membranes was prepared by loading cesium-substituted tungstophosphoric acid (Cs-TPA) by titration method with cross-linking agent contents of 0.01mL. Ceria ($CeO_2$) was used to scavenge free radicals which attack the membrane in the PEMWE circumstance and to increase the duration of the membrane. CL-SPEEK/$Cs_{(1)}$-TPA/CeriaIn conclusion, 1% membrane showed the optimum results such as 0.119 S/cm at $80^{\circ}C$ of proton conductivity and 62MPa of tensile strength.

• Polymer(Korea)
• /
• v.37 no.2
• /
• pp.167-176
• /
• 2013

Linear and cross-linked waterborne polyurethanes (WPUs) based on isophorone diisocyanate and mixed diols of poly(tetramethylene glycol)/hydroxyethyl-terminated polydimethylsiloxane (PDMS-OH) were synthesized with dimethylol propionic acid as an anionic component, trimethylolpropane as a cross-linking agent, and butanediol as a chain extender and characterized. The hydrophobicity, $T_g$, stress-strain behaviors of the linear or cross-linked siloxane-containing WPU (WPU-Si) films with different PDMS content were analyzed by using water contact shape analyzer, energy dispersive spectrometer, dynamic mechanical analyzer, and universal testing machine. The results reveal that as the PDMS content increased, the hydrophobicity of WPU-Si films increased, $T_g$ moved to higher temperature, the breaking stress increased, and the breaking strain decreased.

• Transactions of the Korean hydrogen and new energy society
• /
• v.23 no.5
• /
• pp.437-447
• /
• 2012

Ceria ($CeO_2$) was used to scavenge free radicals which attack the membrane in the polymer electrolyte membrane water electrolysis (PEMWE) circumstance and to increase the duration of the membrane. In order to improve the electrochemical, mechanical and electrocatalytic characteristics, engineering plastic of the sulfonated polyether ether ketone (SPEEK) as polymer matrix was prepared in the sulfonation reaction of polyether ether ketone (PEEK) and the organic-inorganic blended composite membranes were prepared by sol-gel casting method with loading the highly dispersed ceria and cesium-substituted tungstophosphoric acid (Cs-TPA) with cross-linking agent contents of 0.01 mL. In conclusion, CL-SPEEK/Cs-TPA/ceria (1%) membrane showed the optimum results such as 0.130 S/cm of proton conductivity at $80^{\circ}C$, 2.324 meq./g-dry-membrane of ion exchange capacity and mechanical characteristics, and 65.03 MPa of tensile strength which were better than Nafion 117 membrane.

• Elastomers and Composites
• /
• v.40 no.2
• /
• pp.136-142
• /
• 2005

Liquid crystalline poly(allylsulfone) networks having $SO_2$ in a main chain and mesogens in a side chain were synthesized and their gas permeability and permselectivity were determined. The monomer II having two allyl groups on the each end group was able to form polymer networks by polymerization reaction, while the monomer I having only one allyl group was not. Molecular motion of the poly(allylsulfone) networks were retarded with increasing the cross-linking density, and the segmental motion of networks was developed enough to show isotropic phase transition. Gas permeabilities of poly(II-5 $01/I-OCH_3$ 99) were 2.58 baller for $O_2$ and 18.4 barrer for $H_2$. It means that hydrogen gas are 7 times more permeable than oxygen. Its permselectivities were high as 23.9 for ${\alpha}(H_2/N_2)$. The permselectivity was increased with increasing the cross-linking density. For example, ${\alpha}(H_2/N_2)$ was 36.8 in poly(II-5 $10/I-OCH_3$ 90), which was shown to be the highest value among these poly(allylsulfone) networks.

• Polymer(Korea)
• /
• v.30 no.2
• /
• pp.140-145
• /
• 2006

The mort commonly available substrate material is glass in the display fibrication process. However, glass is not desirable due to its heaviness and fragility. Recently, plastics such polysulfone (PSF), polyethesulfone (PES), polycarbonate (PC), polyethylene terephthalate (PET) and cyclic olefin polymers (COP) have been investigated to replace glass as a substrate material for display fibrication. Plastic substrates are advantageous in that they are lightweight, huh impart resistance, flexibility, and ability for roll to roll manufacturing process. But many plastics have poor chemical resistance in organic solvent. The chemica resistance is also lequired because they are exposed to solvents for various chemical treatments din the manufacturing process. So, we have an interest in the chemical modification of PSF to improve chemical resistance. We introduced crosslinkable imide moieties using chloromethylation method for the modification of PSF which could be overcome above shortcomings for display substrate based on plastic film. We prepared the cross-linked polysulfone films which were represented chemical resistance in HeOH, THF, DMSO and NMP. The thermal properties were measured by TGA, DSC and TMA. As the results, we have confirmed to enhance of the thermal property. They had low coefficient of thermal expansion (CTE) which decreased to 15% and had increased $T_g\;from\;180^{\circ}C\;to\;252^{\circ}C$. Cross-linked polysulfone films with imide side-chain had good optical properties and chemical resistance so that they could be used as flexible display substrate.

• Journal of the Korean Ceramic Society
• /
• v.41 no.9
• /
• pp.684-689
• /
• 2004

Hexagonal sheet typed $\alpha$-Al$_2$O$_3$ nano particles were synthesized successfully at various conditions with the aluminum sulfate solution extracted from kaolin through the conventional and microwave assisted polyacrylamide (PAA) gel methods. Shorter gel time and higher yield were obtained in the microwave assisted PAA gel method, compared to conventional method. the size of nano particles was not changed by increasing the concentration of aluminum sulfate, but decreased with increasing the concentration of cross-linking agent in both the conventional and microwave samples. Above 0.01M concentration of cross-linking agent, the sizes of nano particles in the microwave samples were relatively larger than those in the conventional samples.

• Membrane Journal
• /
• v.17 no.2
• /
• pp.140-145
• /
• 2007

In this study, 3-(trihydroxysilyl)-1-propanesulfonic acid (THS-PSA) was added to poly(vinyl alcohol) (PVA) membranes crosslinked with poly(styrene sulfonic acid-co-maleic acid) (PSSA_MA) to improve the separation characteristics toward water vapors in the air. The prepared membranes varying both PSSA_MA and THS-PSA amounts were also synthesized at different cross linking temperatures. Then, in order to investigate the separation characteristics of the resulting membranes, the dynamic vapor sorption (DVS) and vapor permeation experiments were carried out. The increase of cross-linking temperature showed longer time to reach the equilibrium sorption state from the dynamic vapor sorption experiments. PVA/PSSA_MA (3%)/THA-PSA(7%) prepared at $120^{\circ}C$ gave the highest permeability of 480 barrer at $35^{\circ}C$.