• Journal of Mechanical Science and Technology
• /
• v.16 no.1
• /
• pp.39-45
• /
• 2002

Initiation and propagation of interfacial crack along bimaterial interface are considered in this study. A biaxial loading device for a single specimen is used for obtaining a wide range of mode-mixities. The specimen is an edge-cracked bimaterial strip of glass and epoxy; the biaxial loading device, being capable of controlling displacements in two perpendicular directions, is developed. A series of interfacial crack initiation and Propagation experiments are conducted using the biaxial loading device for various mixed modes. Normal crack opening displacement (NCOD) is measured near crack front by a crack opening interferometry and used for extracting fracture parameters. From mixed mode interfacial crack initiation experiments, large increase in toughness with shear components is observed. The behavior of interfacial crack propagation analyzed as a function of mode-mix shows that initial crack propagation is delayed with increase of mode-mixity, and its velocity is increased with positive mode-mixity but decreased with negative case. However, it is found that crack propagation is less accelerated with positive mode-mixity than the negative mode-mixity, which may be caused by contact and/or effects of friction between far field and near-tip Held along the interfacial crack.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05a
• /
• pp.378-381
• /
• 2006

Test results of four reinforced concrete two-span continuous deep beams are summarized. Main variables were the configuration of web opening reinforcement. Shear span-to-overall depth ratio and the size of the web opening were fixed by 1.0 and 0.5 a $\times$ 0.2 h, respectively. To control diagonal crack and enhance strength, it can be recommended that diagonal reinforcement crossing the crack plane joining between loading points and corner of openings should be provided.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.6 no.1
• /
• pp.45-50
• /
• 1997

It is not clearly known how surface defects or inclusions of a medium carbon steel affect a fatigue strength. In this study, we used SM35C specimens with spheroidized cementite structure to eliminate dependence of micro structure of fatigue crack. The investigation was carried out by behavior of crack closure at non-propagation crack and effect of the fatigue limit according to the artificial defects size. Experimental findings are obtained as follows : (1) Fatigue crack initiation point of medium carbon steel with spheroidized cementite structure is at the surface defects. (2) Non-propagating crack length of smooth specimen is equal to the critical size of defect. (3) Considering the opening and closure behavior of fatigue crack, the defect shape results in various crack opening displacement, while it does not affects the fatigue limit level of medium carbon steel with spheroidized cementite structure. (4) The critical length of the non-propagation crack of smooth specimen is the same as critical size of defect in transient area which determines threshold condition in steel with spheroidized cementite structure.

• International Journal of Precision Engineering and Manufacturing
• /
• v.2 no.3
• /
• pp.19-26
• /
• 2001

In order to investigate the effect of single tensile overload on the short crack growth behavior under the out-of-plane cyclic bending moment, crack opening stresses were continuously measured by an elastic compliance method using strain gages. The characteristics of short crack growth after the single tensile overload are analyzed by the effective stress range ratio. Futhermore, the investigation was carried out with respect to various fatigue crack growth behaviors such as the plastic zone size effect on crack retardation, the retarded crack length and the number of cycles.

• Journal of the Korean Institute of Gas
• /
• v.4 no.1 s.9
• /
• pp.55-62
• /
• 2000

A surface acoustic wave method for the evaluation of small fatigue crack initiated from a pit-type surface flaw is presented. In-situ ultrasonic experiments are performed for aluminum 2024-T3 alloy samples under the fatigue test. During the fatigue test, the surface acoustic wave reflection signal from the pit and crack is measured under different hold-stress levels. From the measured and predicted surface wave reflections the depths of fully and partially open cracks are determined and results are verified by comparing with SEM fractography The crack opening behavior of the fatigue crack is evaluated from the predicted effective crack depths. The method developed in this study can be applied to monitor and characterize crack initiation and propagation from pit-type surface flaws in the early stage of fatigue life.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.05a
• /
• pp.125-130
• /
• 2002

The most important material parameters are fracture energy and the stress-crack opening displacement($\sigma$-w) curve to determine the behavior of concrete. Especially, the relationship between the $\sigma$-w curve is strongly important to determine the load-displacement curve of concrete that has a major influence on the fracture behavior of a concrete. In this paper, notched plain concrete beams with different strength level were tested under three-point bending and fracture energy, the load-deflection curve, and the load-crack mouth opening displacement(CMOD) curve were obtained from the experimental data. Also, the fictitious crack model(FCM) was applied to determine the load-deflection curve of notched plain concrete beams using various types of $\sigma$-w curve model proposed by Petersson and we compared experimental results with numerical ones carried out by Finite Element Method(FEM).

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1996.10a
• /
• pp.194-197
• /
• 1996

The high-strength aluminum alloy 7075-T651 was used to observe the fatigue-crack-propagation behavior for the various stress ratios with constant amplitude loading and thus to predict the fatigue life. With a chevron notch in the specimen the fatigue-crack-propagation behavior of through crack was investigated. Crack propagation behavior of through crack in the depth direction and crack growth of weldments were experimentally studied. Base material heat affected zone and weld material were considered in the fracture of weldments. The change of crack-propagation length with respect to several parameters such as stress intensity factor range(ΔK) effective stress intensity factor range(ΔKeff)ration of effective stress intensity factor range(U) stress intensity factor of crack opening point(K op) maximum stress intensity factor(K max) and number of cycles(Nf)was determined. The crack length of through crack of weldments was 2.4mm and the remaining part was a base material. The experiment was accomplished by making the crack propagate near the base material.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.2 no.4
• /
• pp.67-72
• /
• 2003

In this study, to investigate the effects of 2-step shot peening at the surface of spring steel, crack growth tests are conducted on spring steel and shot peened specimens. And then the residual stresses and fractographs are examined. The crack growth equation that can describe the whole crack growth behavior is used to evaluate the experiment results. The results show that fatigue crack glows slowly in the shot peened specimen than in the unpeened. And in the case of the 2-step shot peened specimen the initial stress intensity factor range and the fracture toughness is higher than the unpeened specimen due to the compressive residual stress. Fractographs show that the compressive residual stress of the surface suppress the fatigue crack opening and consequently slow crack growth rates.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.40 no.12
• /
• pp.1021-1026
• /
• 2016

In this study, crack resistance is evaluated by the crack tip opening angle (CTOA) using a wedge splitting test (WST) on a viscoelastic particulate reinforced composite based on an HTPB binder. Generally, CTOA, as a function of crack extension, is used in order to determinate fracture resistance and has a steady state relative angle. Digital image correlation (DIC) is used to measure the crack tip opening displacement (CTOD) and crack extension for the critical crack tip opening angle (CTOAc). In these results, the CTOAc value of a particulate reinforced composite tends to approach a constant angle after a small amount of crack extension. The CTOAc value increases with decreasing temperature, from $50^{\circ}C$ to $-40^{\circ}C$. These CTOAc values may be used to measure fracture mechanics parameters for particulate reinforced composite.

• Journal of the Korean Society of Safety
• /
• v.9 no.1
• /
• pp.161-164
• /
• 1994

Computer aided unloading elastic compliance method was employed to measure the closure and the length of short cracks. The most significant factor that influences the fatigue growth behavior of short cracks is the crack closure Phenomenon. dc/dN-$\Delta$ $K_{eff}$ relationships of short cracks are found to coincide well with the corresponding long crack relationships. Non-propagating behavior of short cracks at notch root can be predicted from the crack opening SIF of short cracks, $K_{op}$ , and the growth equation of long cracks in Region I and II.n Region I and II.I.