Ultrasonic evaluation of small surface fatigue cracks initiating in residual stress zone

잔류응력 영역에서 발생한 작은 피로균열의 초음파 평가

  • Kang Kae-Myung (Dept. of Safety Engineering, Seoul National University of Technology) ;
  • Kim Jin-Yeon (The Ohio Sate University, Industrial, Welding & Systems Engineering)
  • 강계명 (서울산업대학교 재료공학과) ;
  • 김진연 (오하이오주립대학교 용접공학과)
  • Published : 2000.03.01

Abstract

A surface acoustic wave method for the evaluation of small fatigue crack initiated from a pit-type surface flaw is presented. In-situ ultrasonic experiments are performed for aluminum 2024-T3 alloy samples under the fatigue test. During the fatigue test, the surface acoustic wave reflection signal from the pit and crack is measured under different hold-stress levels. From the measured and predicted surface wave reflections the depths of fully and partially open cracks are determined and results are verified by comparing with SEM fractography The crack opening behavior of the fatigue crack is evaluated from the predicted effective crack depths. The method developed in this study can be applied to monitor and characterize crack initiation and propagation from pit-type surface flaws in the early stage of fatigue life.

Pit형 표면결함으로부터 발생하는 작은 피로균열의 거동을 초음파의 표면파를 이용하여 이를 위하여 피로시험중인 Al 2024-T3를 시험재료, 피로시험도중 초음파를 이용하여 피로균열의 거동을 조사하였다. 즉, 피로시험에서 균열이나 Pit로부터 발생하는 작은 피로균열을 여러 응력조건하에서 나타나는 표면파의 반사특성에 관하여 연구하였다. 또한 이론적 결과와 실험적 결과를 상호 비교, 분석하였고, SEM을 사용하여 이들 작은 피로균열을 관찰하였다. 초음파를 이용한 피로균열의 균열 개구 거동에 관한 연구에서 피로균열의 유효균열 특성을 초음파법으로 평가 할 수 있었다.