• International Journal of Automotive Technology
• /
• v.8 no.5
• /
• pp.623-628
• /
• 2007

Reliability analysis based on fracture mechanics requires knowledge of the on statistical parameters m and C in the fatigue crack growth law $da/dN=C({\Delta}K)^m$. The purpose of the present study is to investigate if it is possible to explain the change of parameter m by the fluctuation of C only. In this study, we apply the Paris-Erdogan law treating the parameter C as random and the parameter m as constant. Fluctuations in crack growth rate are assumed to be dependent only on C. The material resistance to fatigue crack growth(Z=1/C) is treated as a spatially random process, that varies along the crack path. The theoretical crack growth rates at various stress intensity factors are discussed. Additionally, the results of constant ${\Delta}K$ fatigue crack growth tests are reported for the structural steel, SM45C. The experimental data have been analyzed to determine the probability distribution of fatigue crack growth resistanc.

• Proceedings of the KSR Conference
• /
• 2004.06a
• /
• pp.702-709
• /
• 2004

Modified Gurson model (Gurson-Tvergaard-Needleman model) was used to analyze crack growth in M(T) and C(T) specimens. A commercial finite element code ABAQUS/Explicit is used to account for total failure of material point by cavity coalescence, and crack growth was simulated by finite element extinction. Crack growth resistance curve was obtained by calculating J-integral. Crack growth under residual stress was investigated.

• Journal of Ocean Engineering and Technology
• /
• v.14 no.1
• /
• pp.23-28
• /
• 2000

The fatigue crack growth behavior of the cold-rolled STS 304 steel developed for membrane material of LNG storage tank was examined experimentally at 293K, 153K and 111K. The fatigue crack growth rate(do/dN) tends to increase as the stress ratio (R) increases over the testing temperature when compared at the same stress intensity factor range($\Delta$K). The effect of R on do/dN is more explicit at low temperatures than at room temperature. The resistance of fatigue crack growth at low temperatures is higher compared with that at room temperature which is attributed to the extent of strain-induced martensitic transformation at the crack tip. The temperature dependence of fatigue crack growth resistance is gradually vanished with an increase in $\Delta$K which correlates with a decreasing fracture toughness with decreasing temperature. Fractographic examinations reveal that the differences of the fatigue crack growth characteristics between room and low temperature are mainly explained by the crack closure and the strengthening due to the martensitic transformation.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2000.04a
• /
• pp.40-45
• /
• 2000

Presented are the estimation of the probability distribution of fatigue crack growth life and reliability assessment of structures by simulating material resistance to fatigue crack growth along a crack path. The material resistance is treated as a Weibull stochastic process. A non-Gaussian stochastic fields simulation method proposed by Shimozuka, et al is applied with the statistical data obtained experimentally. Test results are obtained for $\Delta$K constant amplitude load in tension with stress ratio of R=0.2 and three specimen thicknesses of 6, 12 and 18mm. This simulation method is useful to estimate the probability distribution of fatigue crack growth life and the smallest life.

• Journal of Ocean Engineering and Technology
• /
• v.14 no.4
• /
• pp.73-78
• /
• 2000

Presented are the estimation of the probability distribution of fatigue crack growth life and reliability assessment of structures by simulating material resistance to fatigue crack growth along a crack path. The material resistance is treated as a Weibull stochastic process. A non-Gaussian stochastic fields simulation method proposed by shimozuka, et al is applied with the statistical data obtained experimentally. Test results are obtained for $\delta K$ constant amplitude load in tension with stress ratio of R=0.2 and three specimen thicknesses of 6,12 and 18mm. This simulation method is useful to estimate the probability distribution of fatigue crack growth life and the smallest life.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.04a
• /
• pp.219-222
• /
• 2004

The effects of short fiber and particle hybrid reinforcement on fatigue crack propagation behaviors in aluminum matrix composites have been investigated. Single and hybrid reinforced 6061 aluminum containing same 20 $Al_2O_3\;volume\%$ with four different constituent ratios of short fibers and particles were prepared by squeeze casting method and tested to check the near-threshold and stable crack growth behavior. The fatigue threshold of the composites increased with portion of particle contents and showed the improved crack resistance especially in low stress intensity range. Addition of particle instead of short fiber also increased fracture toughness due to increase of inter-reinforcement distance. These increase in both fatigue threshold and fracture toughness eventually affected the fatigue crack growth behavior such that the crack growth curve shift low to high stress intensity factor value. Overall experimental results were shown that particle reinforcement was enhanced the fatigue crack resistance over the whole stress intensity factor range.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.13 no.4
• /
• pp.174-181
• /
• 2005

In order to investigate the behavior of fatigue crack growth of SiC-particulate- reinforced Al-Si alloy composites, fatigue tests using single edge notched tension(SENT) specimens were performed. Composite materials were manufactured by using both permanent die casting and extrusion processes with different volume fractions of $10\%\;and\;20\%$. $SiC_p-reinfurced$ Al-Si composites showed the increased levels of threshold stress intensity factor range, ${\Delta}K_{th}$, for the increased volume fractions of SiC particles, which implies the increased fatigue crack growth resistance at the threshold or low ${\Delta}K$ levels, compared to the unreinforced Al-Si alloy. In the Paris region, however, the composites showed the increased rate of crack growth resulting in the unfavorable effects on the fatigue crack growth resistance. Critical stress intensity factor range at unstable crack growth leading to final fracture decreased as the volume fraction of SiC particle increased, because of the reduced fracture toughness of the composites. Extruded materials showed higher threshold and critical values than the cast materials.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.7 no.4
• /
• pp.441-450
• /
• 1983

A reasonable J-resistance curve determination procedure is suggested by correcting the amount of overestimation in J-value whose effect becomes significant when crack grows. Experiments using compact tension specimens of an alloy steel (SCM4, K.S. Designation) are performed. The value of J estimated according to this procedure is compared with that as obtained from the method by Merkle and Corten. The conditions for J controlled crack growth proposed by Hutchinson and Paris are examined for the material used here. It appears that J resistance curve, which is independent of crack ratio can be obtained for those specimens satisfying the conditions of J controlled crack growth.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.14 no.1
• /
• pp.103-111
• /
• 1990

This paper presents a methodology for predicting stable crack growth and instability of a cracked body under monotonically increasing load. It is based on a model that incremental crack extensions and load increments after fracture initiation occur by turns in sequence and the criterion that the crack grows by an incremebt .delta.a when the opening displacement at the current crack tip increases by a critical value V$_{c}$. It is shown that the value I$_{c}$ = V$_{c}$/ .delta. a is a material constant characterizing ductile crack growth resistance. Along with the fracture initiation toughness value, the constant is used for the calculation of the loads against crack extensions by adding up each increment. The specimen failure is defined to occur when the necessary load increment for crack extension is zero or when the limit load in the current ligament is reached. The predicted failure loads are in good agreement with the avaliable experimental failure loads for the compact and center-cracked tension specimens of 7075-T651, 2024-T351 aluminum alloys and 304 stainless steel.steel.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.18 no.9
• /
• pp.2374-2385
• /
• 1994

SiCw/Al composite material is especially attractive because of their superior specific strength, specific stiffness, corrosion fatigue resistance, creep resistance, and wear resistance compared with the corresponding wrought Al alloy. In this study, Fatigue crack growth behavior and fatigue crack path morphology(FCPM) of SiC whisker reinforced Al 6061 alloy with 25% SiC volume fraction and Al 6061 allay were performed. Result of the fatigue crack growth test sgiwed that fatigue crack growth rate of SiCw/Al 6061 composite was slower than that of Al 6061 matrix therefore it was confirmed that Sic whisker have a excellent fatigue resistance. And Al 6061 matrix had only FCPM perpendicular to loading direction. On the other hand SiCw/Al 6061 composite had three types in fatigue crack path morphology. First type is that both sides FCPM of artificial notch are perpendicular to loading direction. Second type is that a FCPM in artifical notch has slant angle to loading direction and the other side FCPM is perpendicular to loading direction. Third type is that both sides FCPM of notch have slant angle to loading direction. It was considered that this kinds of phenomena were due to non-uniform distribution of SiC whisker and confirmed by SEM observation for fracture mechanism study.