• KSTLE International Journal
• /
• 제3권1호
• /
• pp.43-48
• /
• 2002

Dry sliding wear and friction test of CrN coaling on two types of aluminum alloy substrates,6061 Al and 7075 Al deposited by arc ion plating, was peformed with a ball-on-disk tribometer. The effects of normal Bead and the mechanical properties of substrate on the friction coefficient and wear-resistance of CrN coating were investigated. The worn surfaces were observed by SEM. The results show that surface micro-hardness of CrN- coated 7075 Al is higher than that of CrN-coated 6061 Al. With an increase in normal lead, wear volume increases, while the friction coefficient decreases. The friction coefficient of CrN-coated 6061 Al is higher than that of CrN-coated 7075 Al, while the wear-resistance of CrN-coated 6061 Al is lower than the CrN-coated 7075 Al's, which indicates that the substrate mechanical properties have strong inf1uences on the friction coefficient and wear of CrN coating. The main wear mechanism was fragments of CrN coating, which were caused by apparent plastic deformation of substrate during wear test.

• 한국재료학회지
• /
• 제14권8호
• /
• pp.558-564
• /
• 2004

In order to improve the low hardness and low wear resistance of Ti-6Al-4V alloy, plasma carburization treatment and CrN film coating were carried out. Effects of the plasma carburization and CrN coating were analyzed and compared with the non-treated alloy by mechanical and creep tests. After plasma carburization and CrN coating treatments, the carburized layer was about 150 ${\mu}m$ in depth and CrN coated layer was about 7.5 ${\mu}m$ in thickness. Hardness value of about $H_{v}$ 402 of the non-treated alloy was improved to $H_{v}$ 1600 and 1390 by plasma carburization and CrN thin film coating, respectively. Stress exponent(n) was decreased from 9.10 in CrN coating specimen to 8.95 in carburized specimen. However, the activation energy(Q) was increased from 242 to 250 kJ/mol. It can be concluded that the static creep deformation for Ti-6Al-4V alloy is controlled by the dislocation climb over the ranges of the experimental conditions.

• 한국표면공학회지
• /
• 제57권1호
• /
• pp.14-21
• /
• 2024

For this study, CrAlN multilayer coatings were deposited on SKD61 substrates using a multi-arc ion plating technique. The structural characteristics of the CrAlN multilayer coatings were evaluated using X-ray diffraction (XRD) and Scanning Electron Microscopy (SEM). Additionally, the adhesion of the coatings was assessed through scratch testing, and the mechanical strength was evaluated using nanoindentation and tribometric tests for frictional properties. The results show that the CrAlN multilayer coatings possess a uniform and dense structure with excellent mechanical strength. Hardness measurements indicated that the CrAlN coatings have high hardness values, and both the coating adhesion and wear resistance were found to be improved compared to CrN. The addition of aluminum is anticipated to contribute to enhanced durability and wear resistance.

• 한국표면공학회지
• /
• 제54권5호
• /
• pp.285-293
• /
• 2021

High-entropy TiAlCrSiN nano-composite coating was designed to improve mold life for high temperature liquid molding. Alloy design, powder fabrication and single alloying target fabrication for the high-entropy nano-composite coating were carried out. Using the single alloying target, an arc ion plating method was applied to prepare a TiAlCrSiN nano-composite coating had a 30 nm TiAlCrSiN layers are deposited layer by layer, and form about 4 ㎛-thickness of multi-layered coating. TiAlCrSiN nano-composite coating had a high hardness of about 39.9 GPa and a low coefficient of friction of less than about 0.47 in a dry environment. In addition, there was no change in the structure of the coating after the dissolution loss test in the molten metal at a temperature of about 1100 degrees.

• Corrosion Science and Technology
• /
• 제2권6호
• /
• pp.289-295
• /
• 2003

The corrosion behavior of Cr-N coated steels with different phases (${\alpha}-Cr$, CrN and $Cr_2N$) deposited by cathodic arc deposition on Hl3 steel was investigated in 3.5% NaCl solution at ambient temperature. Potentiodynamic polarization test, electrochemical impedance spectroscopy (EIS) and scanning electron microscopy (SEM) were the techniques applied to characterize the corrosion behavior. It was found that the CrN coating had a lower current density from potentiodynamic polarization test than others. The porosity, corresponding to the ratio of the polarization resistance of the uncoated and the coated substrate, was higher in the $Cr_2N$ coating than in the other Cr-N coated steels. EIS measurements showed, for the most of Cr-N coated steels, that the Bode plot presented two time constants. Also, the $Cr_2N$ coating represents the characteristic of Warburg behavior after 72hr of immersion. The coating morphologies were examined in planar view and cross-section by SEM analyses and the results were compared with those of the electrochemical measurement. The CrN coating had a dense, columnar grain-sized microstructure with minor intergranular porosity. From the above results, the CrN coating provided a better corrosion protection than the other Cr-N coated steels.

• 한국재료학회지
• /
• 제13권7호
• /
• pp.420-423
• /
• 2003

Coatings of TiCrN ion-plated on a steel substrate was oxidized at $800^{\circ}C$ in air, and their oxidation mechanism was presented. During oxidation, substrate elements and Ti and Cr in the coating always diffused outwardly to form the oxide scale. Simultaneously, oxygen from the atmosphere diffused inward1y to react with Ti and Cr to form $TiO_2$and $Cr_2$$O_3$, respectively. Also, the counter-diffusion of cations and oxygen resulted in some oxygen dissolution in the unoxidized TiCrN coating, and Fe dissolution in the oxide scale. When the Ti content in the coating was high, the $TiO_2$-forming tendency was strong, while when the Cr content was high, the $Cr_2$$O_3$-forming tendency was strong.

• 한국표면공학회지
• /
• 제43권6호
• /
• pp.278-282
• /
• 2010

In this research, the friction and wear characteristic behaviors of coating materials of TiAlN and CrAlN were investigated. The wear test was conducted in air and un-lubricated state using the reciprocating friction wear tester. Temperature were 50 and $120^{\circ}C$, and load were 3, 7, and 11 kgf for tests. By comparing the coefficient of friction and observing the wear microstructure, the friction and wear characteristic behaviors of TiAlN and CrAlN coating layers on SKD61 were investigated. The coefficient of friction of CrAlN coating was lower than that of TiAlN at all conditions. Therefore, CrAlN was suggested to be more advantageous coating than TiAlN for the extrusion mold of aluminum.

• Corrosion Science and Technology
• /
• 제22권4호
• /
• pp.232-241
• /
• 2023

The mechanical properties of the hydrogen valve responsible for supplying and blocking hydrogen gas in a hydrogen fuel cell electric vehicle (FCEV) were researched. Mechanical properties by hydrogen embrittlement were investigated by coating chromium nitride (CrN) and titanium nitride (TiN) on aluminum alloy by arc ion plating method. The coating layer was deposited to a thickness of about 2 ㎛, and a slow strain rate test (SSRT) was conducted after hydrogen embrittlement to determine the hydrogen embrittlement resistance of the CrN and TiN coating layers. The CrN-coated specimen presented little decrease in mechanical properties until 12 hours of hydrogen charging due to its excellent resistance to hydrogen permeation. However, both the CrN and TiN-coated specimens exhibited deterioration in mechanical properties due to the peeling of the coating layer after 24 hours of hydrogen charging. The specimens coated at 350 ℃ presented a significant decrease in ultimate tensile strength due to abnormal grain growth.

• 한국표면공학회지
• /
• 제42권5호
• /
• pp.220-226
• /
• 2009

Cr-O-N coatings having different oxygen contents were deposited on Si wafer and SUS 304 substrates by an arc ion plating technique using Cr target in $Ar/O_2/N_2$ gaseous atmosphere. As increasing oxygen content in the coating, the microstructure of Cr-O-N coating changed from polycrystalline having NaCl structure to amorphous structure. Further increase of oxygen content resulted in phase transformation from amorphous to rhombohedral structure. From the variations of d value and average grain size, it was revealed that the maximum solubility of oxygen in Cr-O-N coating was about 21 at.%. And the maximum micro-hardness of 2751HK was obtained in this composition. The lowest friction coefficient was measured in the coating having 34.8 at.% of oxygen. However, more narrow width of wear track was found in the coating having 30.1 at.% of oxygen.

• International Journal of Ocean System Engineering
• /
• 제2권2호
• /
• pp.106-115
• /
• 2012

In the present study, TiN and CrN films were coated by arc ion plating equipment onto aluminum alloy substrate, A2024. The film thickness was about 4.65 ${\mu}m$. TiN and CrN films were analyzed by X-ray diffraction and energy dispersive X-ray equipments. The Young's modulus and the micro-Vickers hardness of aluminum substrate were modified by the ceramic film coatings. The difference in Young's modulus between substrate and coating film would affect on the wear resistance. The critical load, Lc, was 75.8 N for TiN and 85.5 N for CrN. It indicated from the observation of optical micrographs for TiN and CrN films that lots of cracks widely propagated toward the both sides of scratch track in the early stage of MODE I. TiN film began to delaminate completely at MODE II stage. The substrate was finally glittered at MODE III stage. For CrN film, a few crack can be observed at MODE I stage. The delamination of film was not still occurred at MODE II and then was happened at MODE III. This agrees with critical load measurement which the adhesive strength was greater for CrN film than for TiN film. Consequently, it was difficult for CrN to delaminate because the adhesive strength was excellent against Al substrate. The wear process, which the film adheres and the ball transfers, could be enhanced because of the increase in loading. The wear weight of ball was less for CrN than for TiN. This means that the wear damage of ball was greater for TiN than for CrN film. It is also obvious that it was difficult to delaminate because the CrN coating film has high toughness. The coefficient of friction was less for CrN coating film than for TiN film.