• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.10a
• /
• pp.467-472
• /
• 2000

It is known that chloride ion in concrete destroys the passive film of reinforcement inside concrete and accelerates corrosion which is the most influencing factor to durability of concrete structures. In this thesis, a chloride ion diffusion model for blast furnace slag(BFS) concrete, which has better resistance to both damage due to salt and chloride ion penetration than ordinary portland cement concrete, is proposed by modifying existing model of normal concrete. Proposed model is verified by comparing diffusion analysis results with both results by indoor chloride penetration test for specimens and field test results for actual RC bridge pier. Also, the optimum resistance condition to chloride penetration is obtained according to degrees of fineness and replacement ratios of BFS concrete. As a result, resistance to chloride ion penetration for BFS concrete is more affected by replacement ratio than degree of fineness.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.283-286
• /
• 2005

Recently, the deterioration of concrete structures have been increased by the damage from salt, carbonization, freezing & thawing and the others. Reinforcement corrosion is the principal cause of deterioration of reinforced concrete. Unfortunately, full bond is assumed in all existing shear models, a condition which is often not fulfilled when assessing damaged structures. It is therefore very important to increase the understanding of how reduced bond influences the load carying capacity particularly for shear. Therefore in this study an equation is proposed to evaluate the residual shear strength considered deterioration.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.551-554
• /
• 2005

The durability of concrete is decreased by various deterioration factors such as a crack, spalling, corrosion. Many repair and rehabilitation methods have been introduced to extend service life of RC structure. An application of coating material is one of repair and rehabilitation methods. However, there is a problem due to reduction of bonding strength and damage of coating material in the case of existed coating material. Thus, this paper is aim to investigate the chloride resistance according to application method of coating material which improve the existed problem. According to the results, it is showed that application of coating material reduces diffusion of chloride into concrete. In special, application of MMA polymer showed the best resistance for chloride attack. However, variation of application method and number of times has a minor effect on chloride diffusion.

• KIEAE Journal
• /
• v.10 no.2
• /
• pp.57-62
• /
• 2010

In case of earth-covered storage, the condensation occurs on surface of wall and stores in summer with high humidity because of low temperature of constructional mass. Therefore, the preventive plans should be considered to protect stores from the damage by corrosion in earth-covered storages. This study aims to suggest the methods of forced ventilation by the air, to solve the problems of construction's surface condensation at the Magazine of igloo type which is similar to earth-covered storages. A fan was installed at the air outlet for exhaust gas to conduct forced ventilation. The surface and indoor temperature were measured, and then the influence of those on condensation was analyzed. The results of this research are follows; 1) Forced ventilation by a fan affects the rise in surface temperature of walls and stores. 2) The condensation on surface of walls and stores was reduced after operating a fan.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.61-66
• /
• 2001

Fracture behaviors of pipes with local wall thinning is very important for the integrity of nuclear power plant. In pipes of energy plants, sometimes, the local wall thinning may result from severe drosion-corrosion damage. However, effect of local wall thinning on strength and fracture behaviors of piping system were not well studied. In this paper, the monotonic bending tests were performed of full-scale carbon steel pipes with local wall thinning. A monotonic bending load was applied to straight pipe specimens by four-point loading at ambient temperature without internal pressure. From the tests, fracture behaviors and fracture strength of locally thinned pipe were manifested systematically. The observed failure modes were divided into four types; ovalization, ovalization+cracking, local buckling and local buckling+cracking. Also, maximum load was successfully evaluated.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.90-95
• /
• 2003

Fracture behaviors of pipes with local wall thinning are very important for the integrity of nuclear power plant. In pipes of energy plants, sometimes, the local wall thinning may result from severe erosion-corrosion (E/C) damage. However, the effects of local wall thinning on strength and fracture behaviors of piping system were not well studied. In this paper, the monotonic bending tests were performed of full-scale welded and unwelded carbon steel pipes with local wall thinning. A monotonic bending load was applied to straight pipe specimens by four-point loading at ambient temperature without internal pressure. The observed failure modes were divided into four types; ovalization, crack initiation/growth after ovalization, local buckling and crack initiation/growth after local buckling. Also, the strengths of welded and unwelded piping system with local wall thinning were evaluated.

• Journal of Power System Engineering
• /
• v.10 no.2
• /
• pp.89-92
• /
• 2006

In this study, the pressure vessel piping with corrosion used during long term were investigated from the time-frequency analysis method. The damage of piping could be evaluated the attenuation factor by ultrasonic parameters such as center frequency and echo waveform. Based on NDE analysis by time-frequency analysis method, it should also be possible to evaluate from various damages and defects in piping members.

• Proceedings of the KSR Conference
• /
• 2007.05a
• /
• pp.864-874
• /
• 2007

Suspension insulator in Catenary Trolley Wire Systems must have two characteristics, electric insulation and mechanical endurance. Because suspension insulator is used in supporting and insulating position between power supply parts and earth conducted supporting parts. The insulator's electric characteristics can be influenced by surface pollution and damage from the environment such as humidity, dust, smoke, salt. etc. And, the insulating parts can be electrically short. These electrically damaged insulator can cause serious accidents that have far-reaching effect. So appropriate management basis of suspension insulator is needed. And we present appropriate cleaning and the changing period of suspension insulator on the basis of actual data.

• Transactions of Materials Processing
• /
• v.14 no.2 s.74
• /
• pp.147-152
• /
• 2005

The objective of this study is to develop an optimal drawing die for the clad wire drawing process. Cu-clad wire, which has the advantages of the high strength of a steel core and the electro-conductivity, corrosion resistance of a copper layer, is widely being used in the field of the telecommunications, electric-electronic and military technology industries. It is important to obtain uniformly coated rate when producing clad wires. Drawing process of clad wire will be influenced on damage and coated rate of core and sleeve for process variables such as semi-die angle and reduction in area. Therefore, in this study, the finite-element result obtained in this study was analyzed to the effect of the various forming parameters, which included the semi-die angle and reduction in area. The coated rate will be predicted with observation of copper coated rate variation according to total reduction in area and the optimal pass schedule will be set up through proper reduction in area and semi-die angle variation.

• Journal of Industrial Technology
• /
• v.26 no.A
• /
• pp.139-146
• /
• 2006

Many concrete bridge decks develop transverse cracking shortly after construction. These cracks accelerate corrosion of reinforcing steel and lead to concrete deterioration, damage to components beneath the deck, unsightly appearance. These cracks shorten the service life and increase maintenance costs of bridge structures. In this study, VES-LMC overlay, which provides the same benefits as a conventional overlay, is designed to cure very quickly. Although the materials for VES overlays are more expensive, the cost is more than offset by the savings on traffic control and work zone safety measures. Otherwise, reaction of hydration occurs very rapidly in beginning step(concrete placing). As a results, thermal cracking can be occur by thermal stress in accordance with hydration-heat The purpose of this study was to estimate diagnosis of crack occurrence of VES-LMC through field tests at early-age.