• Steel and Composite Structures
• /
• v.50 no.3
• /
• pp.363-374
• /
• 2024

The fatigue life of steel wire is affected not only by fatigue load, but also by corrosion environment in service period. Specially, the corrosion pit will lead to stress concentration on the surface of steel wire inducing the formation of fatigue cracks, and the fatigue cracks will accelerate the corrosion process. Therefore, the corrosion fatigue of steel wire is a coupling effect. In this study, the corrosion-fatigue coupling life curve is derived with considering corrosion-fatigue pitting stage, corrosion-fatigue short crack stage and corrosion-fatigue long crack stage. In addition, the stress concentration factors of different corrosion pits are calculated by COMSOL software. Furthermore, the effect of corrosion environment factors, that is, corrosion rate, corrosion pit morphology, frequency and action factor of fatigue load, on fatigue life of steel wire is analyzed. And then, the corrosion-fatigue coupling life curve is compared with the fatigue life curve and fatigue life curve with pre-corrosion. The result showed that the anti-fatigue performance of the steel wire with considering corrosion-fatigue coupling is 68.08% and 41.79% lower than fatigue life curve and fatigue life curve with pre-corrosion. Therefore, the corrosion-fatigue coupling effect should be considered in the design of steel wire.

• Journal of Ocean Engineering and Technology
• /
• v.1 no.2
• /
• pp.123-129
• /
• 1987

Corrosion fatigue fracture of dual phase steel(SS41) and raw material steel(SS41) were investigated in 3.5% NaCl aqueous solution at PH 4,6,9 and 11. The fatigue limit of dual phase steel is increased approximately 1.8 times larger than that of raw material in air. The corrosion fatigue life of dual phase steel is about 5-10 times larger than that of raw material in 3.5% NaCl aqueous solution. The reduction of fatigue life is larger for the acidsalt solution than for the alkali salt solution. The reduction of stress level on the reduction ratio of corrosion fatigue life is large as pH 6-11. The reduction ratio of corrosion fatigue life of dual phase steel and raw material is nearly coincided at pH 2. While at pH4-2 the reduction ratio of corrosion fatigue life only depends on the corrosion effect. It has been found that the corrosion resistance effect of dual phase steel is smaller than that of raw material in corrosion fatigue crack propagation rate. As pH below 6 is changed, it can be clearly observed from raw material that the brittle intergranular fracture is characterized, and from the above result, the influence of corrosion of dual phase steel is small.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.35 no.1
• /
• pp.46-51
• /
• 2007

In this study, test results for fatigue crack propagation of Al-2024-T3511 are presented considering corrosion effects, and fatigue lifes are compared for the cases of corrosion and non-corrosion. Higher corrosion environments show lower fatigue life and faster crack growth. To predict the corrosion fatigue life, a corrosion factor concept is newly introduced and applied in Paris' law. The predicted results show good agreement with experimental data and this corrosion fatigue model can be successfully used for the prediction of fatigue life of aluminum structure with corrosion effects.

• Journal of the Society of Naval Architects of Korea
• /
• v.44 no.4
• /
• pp.417-424
• /
• 2007

With regard to corrosion fatigue crack initiation life (Nc), it has been treated ambiguously for the member which doesn't have stress concentration area. In this research, in order to clarify the corrosion fatigue crack initiation life (Nc), corrosion fatigue tests were carried out. Reasonable and universal corrosion fatigue crack initiation life (Nc) was defined and corrosion fatigue crack initiation/propagation model was suggested also. As the fatigue crack which emanates from the pit is usually small, accordingly it is treated as a small crack. In addition, the observation of the corrosion fatigue fracture surfaces using SEM was conducted. And the fracture mechanics analysis using an intrinsic crack model was conducted for the treatment of the small crack. Finally, the followings were obtained. When there is no clear stress concentration point which seems to fall into a corrosion fatigue crack initiation life, the significance of the definition and suggestion of the moment of the reasonable and universal corrosion fatigue crack initiation life (Nc), at which the fatigue crack propagation rate becomes faster than the corrosion pit growth rate so that the fatigue crack initiates from the pit and propagates in earnest, has been clarified.

• Journal of Ocean Engineering and Technology
• /
• v.6 no.1
• /
• pp.140-147
• /
• 1992

Corrsion fatigue test was performed under rotated bending in 3.5% NaCl aqueous solution having a temperature from 278.deg.K in order to investigate the effects of aqueous solution remperature on the corrosion fatigue fracture of raw material steel(SS41) and dual phase steel that was produced from SS41 by a series of heat treatment. Corrosion fatigue life decreases remarkably with increase in solution temperature or with decrease in stress level. The corrosion fatigue life and the crack propagation rate at 303.deg.K show the similar behaviors with those at 318.deg.K, which is assumed to be caused by concentration polarization phenamena. The number and the lengths of microcracks increase with increase in solution temperature, so they lead to the decrease in corrosion fatigue life.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2005.11a
• /
• pp.228-229
• /
• 2005

The compressive residual stress, which is induced by shot peening process, has the effect of increasing the intrinsic fatigue strength of surface and therefore would be beneficial in reducing the probability of fatigue damage. However, it was not known that the effect of shot peening in corrosion environment. In this study, the effect of shot peening on corrosion fatigue crack growth of sping steel immersed in 6% $FeCl_3$ solution and corrosion characteristics with considering fracture mechanics. The results of the experimental study corrosion fatigue characteristics of spring steel are as follows; the fatigue crack growth rate of the shot peening material was lower than of the un peening material. And fatigue life shows more improvement in the shot peening material than un peening material. This is because the compressive residual stress of surface operate resistance of corrosion fatigue crack propagation. It is assumed that the shot peening process improve corrosive resistance and mechanical property.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.11 no.6
• /
• pp.867-876
• /
• 1987

Corrosion fatigue fracture with change in the grain size of M.E.F. dual phase steel is investigated in 3.5% NaCI aqueous solution at pH 2, 4, 6, 9, and 11. Generally speaking, decrease in corrosion fatigue life is strongly dependent on decrease in pH and slightly on the grain size. For the B material with the big grain size, the fatigue life is small due to its large reduction ratio of corrosion fatigue life. The influence of grain size on the reduction ratio of corrosion fatigue life is large at pH 11-6. Whi9le at pH 4-2 the reduction ratio of corrosion fatigue life only depends on the corrosion effect. The larger grain size and the lass pH result in the greater influence on corrosion fatigue crack propagation rate. As pH decreases, the plateau portion in the crack propagation rate curves of the B material are distinct. Crack propagation rate curves become slow down at high .DELTA.K range because crack closure effect by minute corrosion products inside crack causes the oxidation corrosion action less effective for a certain period of time. In A material with small grain size, fatigue life is increased in proportion with increase of martensite intergranular which brings forth restraining the crack propagation decreases crack propagation rate. Corrosion pit which is created in the surface of specimen is found at pH 6,4 and 2 which is noticeable and the unevenness of the surface of the specimen becomes severe as pH decreases. The unevenness of corrosion fatigue fracture surface is severe as the effect of pH increases i.e. as pH decreases. In proportion with increase in the grain size and decrease in pH, the aspect of brittle fracture becomes evident.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.220-225
• /
• 2003

In order to develop a method of corrosion fatigue design and estimate reliability of TMCP steel using as the material of heavy industries and plants, its corrosion susceptibilities and corrosion fatigue life considering corrosion degradation were investigated. From the results, the corrosion characteristic of TMCP steel is very susceptible in 3.5wt.% NaCl solution. Its susceptibility was linearly increased with the solution temperature increase. The potential difference due to the crack growth behavior in $25^{\circ}C$, 3.5wt.% NaCl solution is very susceptible. And it was found that stress amplitude has a linear relationship with the critical potential. Therefore, it is expected that the corrosion fatigue life of TMCP steel can be nondestructively predicted using the DCPD method.

• Proceedings of the KSR Conference
• /
• 2004.10a
• /
• pp.716-721
• /
• 2004

Corrosion highly affects to reduce lifetime and performance of machinery metallic components. The effects of shot peening on the fatigue life of metal material under corrosive environment are investigated in this paper. Experimental results show that the fatigue limit of shot peened specimen increases about 52$\%$. That means the fatigue life of metallic components is highly extended by shot peening. The corrosion greatly reduces the fatigue strength depending on the corrosive condition from one week up to one year. In case of shot peened specimen, the corrosion does not reduce the fatigue strength and fatigue life up to six months. It means that shot peening has superior effectiveness to reduce the influence of corrosion to the metallic materials.

• Journal of the Korean Society for Railway
• /
• v.8 no.6 s.31
• /
• pp.525-532
• /
• 2005

Fatigue life of catenary wires in various environments is reduced when stress is concentrated on some points, which are often found in corroded areas by surrounding pollutants. Therefore, the fatigue test were performed in order to investigate the effect of the surface corrosion on the destructive behavior in service environment and accelerated corrosion environment as well as th examine the corrosive property and mechanism of the catenary wires. In the fatigue test of the messenger stranded wire, the corrosion degraded materials showed 35~50% of fatigue life at a same stress amplitude compared to original material. Because the catenary wires have variable load by the interaction of periodic contacts with pantographs the maximum stresses of trolley wire and messenger wire calculated by simulation at the messenger wire during operation was estimated thought the corrosion behavior interpretation of variable stress and fatigue test.