• Electrical & Electronic Materials
• /
• v.10 no.10
• /
• pp.1041-1047
• /
• 1997

In this paper the dielectric properties of (0.8-x)Pb(Mb$_{1}$3//Nb/2/3)O$_3$/BaTiO$_3$-CaZrO$_3$(x=0.1, 0.15, 0.2, 0.25) ceramics were investigated. Specimens were prepared by the conventional mixed oxide method and sintering temperature and time were 1000~115$0^{\circ}C$ 2hr, respectively. The structural and dielectric properties with variation of sintering temperature and composition were investigated. All the specimens sintered at 115$0^{\circ}C$ for 2hr showed the highest value of 1043. With increasing the contents of CZ and frequency dielectric constant was decreased and which was decreased with increasing temperature from 3$0^{\circ}C$ to 15$0^{\circ}C$.

• Proceedings of the KIEE Conference
• /
• 2000.11c
• /
• pp.473-475
• /
• 2000

The (1-x)$MgTiO_3-xSrTiO_3$$(x=0.03{\sim}0.04)$ ceramics were fabricated by conventional mixed oxide method. The structural properties and microwave dielectric properties were investigated by XRD, SEM and HP8757D network analyzer. In the $0.96MgTiO_3-0.04SrTiO_3$ ceramics, the perovskite structure $SrTiO_3$ and ilmenite structure $MgTiO_3$ phases were coexisted. The dielectric constant(${\varepsilon}_r$ and temperature coefficient of resonant frequency(${\tau}_f$) was increased with addition of $SrTiO_3$. In the case of $0.96MgTiO_3-0.04SrTiO_3$ ceramics sintered at $1325^{\circ}C$, the dielectric constant, quality factor and temperature coefficient of resonant frequency were 20.13, 7956(at 7.27GHz), +1.7568ppm/$^{\circ}C$, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.05c
• /
• pp.123-126
• /
• 2001

The $0.98MgTiO_3-0.02BaTiO_3$ ceramics were prepared by the conventional mixed oxide method. The structural properties were investigated with sintering temperature and composition ratio by XRD, SEM and EDS. According to the X-ray diffraction patterns of the $0.98MgTiO_3-0.02BaTiO_3$ ceramics, the hexagonal $BaMg_6Ti_6O_{19}$ and ilmenite $MgTiO_3$ structures were coexisted. The dielectric constant$({\varepsilin}_r)$ and quality factor$(Q{\times}f_r)$ were decreased with increasing the sintering temperature in the range of $1275^{\circ}C{\sim}1350^{\circ}C$. In the case of the $0.98MgTiO_3-0.02BaTiO_3$ ceramics sintered at $1275^{\circ}C$, dielectric constant, quality factor and temperature coefficient of resonant frequency were 20.27, 76,845, $-46.6ppm/^{\circ}C$, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.05c
• /
• pp.127-130
• /
• 2001

The $BaTiO_3+xNb_2O_5$(x=6, 8, 10wt%) ceramics were prepared by conventional mixed oxide method. The structural properties of the $BaTiO_3+Nb_2O_5$ ceramics with the sintering temperature and addition of $Nb_2O_5$ were investigated by XRD and SEM. Increasing the sintering temperature, the $2{\theta}$ value of BT(110) peak was shifted to the lower degree and intensity of the $Ba_6Ti_2Nb_8O_{30}$ (133) peak was increased. Increasing the addition of $Nb_2O_5$, the intensity of $BaTiNb_4O_{13}$ (201) peak was decreased and $Ba_6Ti_2Nb_8O_{30}$ (133) peak was increased. The grain size of the $BaTiO_3+Nb_2O_5$ ceramics sintered at $1500^{\circ}C$ were almost uniform.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.51 no.8
• /
• pp.335-339
• /
• 2002

Ba(Mgl-xCox)TaO3[BMCT] ceramics were prepared by the conventional mixed oxide method. The ceramics were sintered at the temperature of 1525~$1625^{\circ}C$ for 5hr. in air. The crystal structure of BMCT ceramics was investigated by the XRD. The microstructure of the specimens were observed by SEM. The Microwave dielectric properties of BMCT specimens were investigated as a function of composition and sintering temperature. All BMCT ceramics sintered over 1575$^{\circ}C$ were showed a polycrystalline complex perovskite structure. The density of BMCT (90/10) specimen sintered at $1575^{\circ}C$ was 7.75g/㎤. As the Co contents decreased, the ordering parameter of B-site in BMCT increased. In the case of the BMCT(90/10) ceramics sintered at $1575^{\circ}C$ for 5 hours, dielectric constant, quality factor and temperature coefficient of resonant frequency for microwave dielectrics application were a good value o( 25, 17, 845 at 10㎓ and +2.4 ppm/${\circ}$, respectively.

• Proceedings of the KIEE Conference
• /
• 2000.07c
• /
• pp.1667-1669
• /
• 2000

The 0.8Ba($Zn_{1/3}Ta_{2/3})O_3$-0.2Ba($Co_{1/3}Nb_{2/3})O_3$ ceramics were prepared by conventional mixed oxide method. The structural properties of the 0.8BZT-0.2BCN ceramics with the sintering temperature were investigated by XRD and SEM. The 0.8BZT-0.2BCN ceramics had a superstructure reflection plane of (100), (200). Increasing the sintering temperature. the ordering parameter of B-site atoms were increased. The lattice constant of 0.8BZT-0.2BCN ceramics was 3.97${\AA}$. Increasing the sintering temperature, the average gram sizes were increased. In the case of the 0.8BZT-0.2BCN ceramics sintered at 1500$^{\circ}C$, the average grain size and bulk density were 1.56${\mu}m$, 6.93$g/cm^3$, respectively.

• Proceedings of the KIEE Conference
• /
• 2006.10a
• /
• pp.20-21
• /
• 2006

In this study, structural and microwave dielectric properties of the ${Ba_5}{B_4}{O_{15}}$ (B=Ta, Nb} cation-deficient perovskite ceramics with sintering temperature were investigated. All sample of the ${Ba_5}{B_4}{O_{15}}$ (B=Ta, Nb) ceramics prepared by conventional mixed oxide method and sintered at $1325^{\circ}C{\sim}1575^{\circ}C$. The bulk density and dielectric constant of the ${Ba_5}{Ta_4}{O_{15}}$ ceramics were increased continuously with increasing of sintering temperature. And the bulk density and dielectric constant of the ${Ba_5}{Nb_4}{O_{15}}$ ceramics was increased in $1375^{\circ}C{\sim}1400^{\circ}C$ but decerased in $1425^{\circ}C$. In the case of ${Ba_5}{Ta_4}{O_{15}}$ ceramics sintered at $1475^{\circ}C$ and ${Ba_5}{Nb_4}{O_{15}}$ ceramics sintered at $1400^{\circ}C$, The dielectric constant and quality factor, and temperature coefficient of the resonant frequency (TCRF) were 25.15, 53,105 GHz, $-3.06\;ppm/^{\circ}C$ and, 39.55, 28,052 GHz, $5.7\;ppm/^{\circ}C$ respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.383-386
• /
• 2000

The 0.6Ba(Zn$_{1}$3/Ta$_{2}$3/)O$_3$-0.4Ba(Co$_{1}$3/Nb$_{2}$3/)O$_3$ceramics were prepared by the conventional mixed oxide method. The structural properties of the 0.6BZT-0.4BCN ceramics with the sintering temperature were investigated by XRD, SEM. The 0.6BZT-0.4BCN ceramics had a complex-perovskite structure. Increasing the sintering temperature, the peak intensity of the superstructure reflection plane were increased and the density and ordering were increased. The density of the 0.6BZT-0.4BCN ceramics sintered at 1475$^{\circ}C$ was 6.455[g/cm$^3$].

• Journal of the Korean Ceramic Society
• /
• v.44 no.5 s.300
• /
• pp.173-178
• /
• 2007

The microstructure and microwave dielectric properties of dolomite type borates, $CaZr(BO_3)_2$ ceramics prepared by conventional mixed oxide method were explored. The sintering temperature of $CaZr(BO_3)_2$ ceramics could be reduced from $1150^{\circ}C\;to\;925^{\circ}C$ with little amount of sintering additives. Microwave dielectric properties of 3 wt% $Bi_2O_3-CuO$ added $CaZr(BO_3)_2$ ceramics sintered at $925^{\circ}C$ were $K{\approx}10.4,\;Q{\times}f{\approx}80,000GHz\;and\;TCF{\approx}+2ppm/^{\circ}C$. Thus obtained LTCC tape was co-fired with Ag paste for compatibility test and revealed no sign of Ag reaction with the ceramics. Therefore, $CaZr(BO_3)_2$ ceramics is considered as a possible candidate material for low temperature co-fired multilayer devices.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.60 no.11
• /
• pp.2093-2096
• /
• 2011

In this study, lead-free $(Na_{0.5}K_{0.5})NbO_3-BiTiO_3$ ceramics were fabricated by a conventional mixed oxide method. Structural and electrical properties of lead-free $(Na_{0.5}K_{0.5})NbO_3$ ceramics with the variation of $BiTiO_3$ were investigated. The results of X-ray diffraction analysis showed a typical polycrystalline perovskite structure without presence of the second phase in all specimens. Sintered density increased with an increasing of BTO and the specimen added with 0.07 mol% of $BiTiO_3$ showed the maximum value of 97.8%. Average grain size decreased and densification increased with an increasing of $BiTiO_3$ contents. The electromechanical coupling factor of the 0.01 mol% $BiTiO_3$ doped NKN specimens was 0.32. Dielectric constant, dielectric loss and Curie temperature of the 0.07 mol% $BiTiO_3$ doped NKN specimens were 1185, 0.145% and $400^{\circ}C$, respectively.