• 한국주조공학회지
• /
• 제17권3호
• /
• pp.252-257
• /
• 1997

The 8 mm dia: Sn-38%Pb eutectic alloy rods were produced by use of the horizontal continuous casting process with the heated mold and chill cast process. The cast rods were rolled into 2.0${\sim}$0.5 mm thick plates and structural and mechanical properties were examined. The results revealed that the plates produced by the continuous casting process with the heated mold show much higher superplasticity at ambient temperature (1550% elongation at 0.5mm thick plate and 0.5mm/min strain rate) than the plates procuced by chill cast process (630% elongation). Such a high superplasticity of the continuous cast plates is due to the high-quality plates free from any inside and surface defects with fine and uniform distribution of eutectic phases.

• 한국주조공학회지
• /
• 제25권6호
• /
• pp.259-264
• /
• 2005

The copper clad steel wire is used extensively as lead wires of electronic components such as capacitors, diodes and glass sealing lamp because the wire combines the strength and low thermal expansion characteristic of Fe-Ni steel with the conductivity and corrosion resistance of copper. In order to fabricate the copper clad steel wire, several processes including electro-plating, tubecladding extrusion process and dip forming process have been introduced and applied. The electroplating process for the production of copper clad steel wire shows poor productivity and induces environmental load generation such as electroplating solution. The dip forming process is suitable to mass production of copper clad steel such as trolley wire. and need expensive manufacturing facilities. The present paper describes the improvement of the conventional continuous casting process to fabricate copper clad steel wire, which its core metal is low thermal expansion Fe-Ni alloy and its sheath material is copper. In particular, the formation of intermetallic compound at interface between core and sheath was investigated in order to introduce optimum continuous casting process parameter for fabrication of copper clad steel wire with higher electrical conductivity. The mechanical strength of copper clad steel wire was also investigated through wiredrawing process with of 95% in total reduction ratio.

• 제어로봇시스템학회:학술대회논문집
• /
• 제어로봇시스템학회 1996년도 한국자동제어학술회의논문집(국내학술편); 포항공과대학교, 포항; 24-26 Oct. 1996
• /
• pp.1064-1067
• /
• 1996

This paper describes the design and implementation of an intelligent controller for continuous casting process. The proposed controller adopted a fuzzy control with feedback linearization. The simulation result shows that proposed intelligent controller is superior to the conventional PID controller.

• 대한기계학회논문집A
• /
• 제28권11호
• /
• pp.1629-1636
• /
• 2004

The continuous casting is primarily a heat-extraction process in which the heat transfer at various cooling zones profoundly influences quality of products. So development of numerical model is necessarily needed for more specific and clear investigations upon heat transfer mechanism at mold and secondary cooling zones. In this study, heat transfer coefficients which show the characteristic of heat transfer mechanism in mold are calculated for more exact analysis with temperature measured in bloom mold using optimal algorithm, and finally the validity of cooling conditions at secondary cooling zone actually used at field fur 30 Ton bloom type continuous casting of 0.187%C is investigated. From the results of solidification analysis, the characteristic of bloom mold shows a similar tendency with that of previous studies, and optimized cooling conditions for 0.187%C are presented.

• 대한기계학회논문집B
• /
• 제25권3호
• /
• pp.285-295
• /
• 2001

The transport phenomena in a wedge-shaped pool of twin-roll continuous caster are affected by the various operating parameters such as the melt-feed pattern, roll-gap thickness, melt-superheat, and casting speed. A computer program has been developed for analyzing the two-dimensional, steady conservation equations for transport phenomena during twin-roll continuous casting process in order to estimate the turbulent melt-flow, temperature fields, and solidification in the wedge-shaped pool. The turbulent characteristics of the melt-flow were considered using a low-Reynolds-number K-$\xi$ turbulence model. Based on the computer program, the effects of the different melt-feed patterns, roll-gap thicknesses, and superheats of melt on the variations of the velocity and temperature distributions, and the mushy solidification were examined. The results show that the liquidus line is located considerably at the upstream region, and in the lower region appear the well-mixed melt-flow and most widely developed mushy zone. Besides, the variation of melt-flow due to varying melt-feed patterns, affects mainly the liquidus line, and scarcely has effects on the solidus line in the outlet region.

• 한국주조공학회지
• /
• 제10권1호
• /
• pp.50-56
• /
• 1990

Continuous casting of the $Al-Al_3Ni$: eutectic composite was carried out by the upward continuous casting process. The morphology of the eutectic growth and the stability of solid-liquid interface were investigated under various growth conditions in an upward continuous casting. The effect of growth conditions on the mechanical properties of the $Al-Al_3$ Ni eutectic composit was also investigated, and the results were compared with those by the Bridgman method. As for the results, it was possible to get the planar solid-liquid interface at the condition of $G_L/R$＝$1.04{\times}10^3^{\circ}Csec/mm^2$. And the inter-rod spacing of $Al-Al_3Ni$ eutectic composite was decreased with the increase of pulling speed. The reduction of inter-rod spacing & value of $G_L/R$ caused the increase of ultimate tensile strength in $Al-Al_3Ni$: eutectic composite. The ultimate tensile strengths of $Al-Al_3Ni$ by the upward continuous casting were higher then those by the Bridgman method.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 1996년도 춘계학술대회논문
• /
• pp.165-171
• /
• 1996

Recently, to improve the productivity in the continuous casting process, thin slab continuous caster which is one of the new steelmaking technologies by a high speed casting has been introduced. In the process of the thin slab continuous cast, there is more possibility than convnetional one that the deformation be occurred by the bulging of solidified shell, since the thickness of soliidfied shell is very thin as much as 60mm after the casting is finished. In some cases of severe bulging, there might be more breakout. In this paper, using finite difference method , solification analysis of slab is made as well as the thicknessof solidified shell and temperature are calculated. Also, based on the data of the calculated temperature, the deformed behavior of solidified narrow face is anlayzed with the MARC which is a package program for finite element analysis.

• 한국생산제조학회지
• /
• 제7권2호
• /
• pp.9-14
• /
• 1998

One of the areas in the continuous casting process that up to this point, has not been definitively instrumented is a method of reliably locating the part of a continuously cast strand that remains liquid for a period after the outer portion has solidified. To solve the problem. Electromagnetic Trandsducers(EMAT) which operate across an air gap without the need for a coupling medium has been developed. The system was designed to employ a through transmission technique which enhanced the signal-to-noise ratio. The Al 75$\times$75mm and 75$\times$100mm simulators with 2, 4, 8, 16, 32 mm hole respectively has been produced in order to verify the developed EMAT system and to measure to liquid core in continuous casting strand. The system developed can be employed for the optimization of torch cutting speed and for the final cut length of the bloom as well as calculation of average bloom temperature.

• International Journal of Fuzzy Logic and Intelligent Systems
• /
• 제2권2호
• /
• pp.146-152
• /
• 2002

Mold level control has been a major control task for continuous casting plants. The system involves nonlinearities such as stick-slip friction in the sliding gate, time-delay, friction force variations between molten steel and the inner wall of mold, and nozzle logging/unclogging. These complex problems should be solved to control mold level for steel cast. In this paper, we propose a neural fuzzy mold level control technique for solving these complex problems and give experiment studies to show the mold level control in continuous casting process.

• 소성∙가공
• /
• 제13권4호
• /
• pp.319-325
• /
• 2004

Continuous casting machine has been experienced a rapid development to increase productivity with high casting speed and to meet consumer's strict demands for high quality. However, because most of defects and cracks are initially formed in mold and grown into surface cracks during the post process, more specific and clear investigations upon heat transfer mechanism between mold and solidified shell are necessarily needed. In this study heat transfer coefficients which shows the characteristic of heat transfer mechanism are calculated with temperatures measured in bloom mold using optimal algorithm, and thermal analysis are investigated using the calculated heat transfer coefficients. Finally uniformity of solidified shell is investigated for high carbon steel, 0.187%C from thermal analysis.