Microstructures and Mechanical Properties of Al-Ni Eutectic Composite by Upward Continuous Casting

상향식 연속주조법으로 제조한 Ai-Ni 공정복합재료의 응고조직 및 기계적 성질

Continuous casting of the $Al-Al_3Ni$: eutectic composite was carried out by the upward continuous casting process. The morphology of the eutectic growth and the stability of solid-liquid interface were investigated under various growth conditions in an upward continuous casting. The effect of growth conditions on the mechanical properties of the $Al-Al_3$ Ni eutectic composit was also investigated, and the results were compared with those by the Bridgman method. As for the results, it was possible to get the planar solid-liquid interface at the condition of $G_L/R$＝$1.04{\times}10^3^{\circ}Csec/mm^2$. And the inter-rod spacing of $Al-Al_3Ni$ eutectic composite was decreased with the increase of pulling speed. The reduction of inter-rod spacing & value of $G_L/R$ caused the increase of ultimate tensile strength in $Al-Al_3Ni$: eutectic composite. The ultimate tensile strengths of $Al-Al_3Ni$ by the upward continuous casting were higher then those by the Bridgman method.