This study was conducted to evaluate the effect of substitution of the flour with coffee silver skin (at the levels of 0%, 3%, 5%, and 7%) on the characteristics of yellow layer cake. The specific gravity of batter increased significantly as the content of silver skin increased. The specific volume of cake decreased significantly as the content of silver skin increased. The volume index decreased significantly as the silver skin content increased, while the symmetry index and uniformity index were not influenced. It was found that control had the highest cake indexes. Texture analysis showed that control had the lowest hardness and highest springiness. Hardness value of cakes was increased by adding silver skin; however, the springiness value of cakes with silver skin decreased during storage. According to sensory evaluation, experiment groups scored the higher points in texture acceptance than control. Above all, SS5 scored the highest points in aroma, taste and SS3 scored the highest points in appearance and overall acceptance.

• Journal of Surface Science and Engineering
• /
• v.42 no.4
• /
• pp.161-168
• /
• 2009

Effects of TiN/Ti multilayer coating on the Ti-30Ta-xZr alloy surface were studied by using various experiments. The Ti-30Ta containing Zr (5, 10 and 15 wt%) were melted 10 times to improve chemical homogeneity by using a vacuum furnace. And then samples were homogenized for 24 hrs at $1000^{\circ}C$. The specimens were prepared for TiN/Ti coating by cutting and polishing. The prepared specimens were coated with TiN/Ti multilayers by using DC magnetron sputtering method. The analyses of coated surface and coated layer were carried out by field emission scanning electron microscope(FE-SEM), EDX, and X-ray diffractometer(XRD). From the microstructure and XRD analysis of Ti-30Ta-xZr alloys, The equiaxed structure was changed to needle-like structure with increasing Zr content. And $\alpha$-peak and elastic modulus increased as Zr content increased. The $\alpha$ and $\beta$ phase predominantly were found in the specimen containing high Zr content. According to the analysis of TiN/Ti coating layer, the surface defects and structures of Ti-30Ta-xZr were covered with TiN/Ti coating layer and surface roughness decreased.

• Korean Journal of Materials Research
• /
• v.18 no.10
• /
• pp.521-528
• /
• 2008

We present the structural, optical, and electrical properties of amorphous silicon suboxide (a-$SiO_x$) films grown on indium tin oxide glass substrates with a radio frequency magnetron technique from a polycrystalline silicon oxide target using ambient Ar. For different substrate-target distances (d = 8 cm and 10 cm), the deposition temperature effects were systematically studied. For d = 8cm, oxygen content in a-$SiO_x$ decreased with dissociation of oxygen onto the silicon oxide matrix; temperature increased due to enlargement of kinetic energy. For d = 10 cm, however, the oxygen content had a minimum between $150^{\circ}\;and\;200^{\circ}$. Using simple optical measurements, we can predict a preferred orientation of liquid crystal molecules on a-$SiO_x$ thin film. At higher oxygen content (x > 1.6), liquid crystal molecules on an inorganic liquid crystal alignment layer of a-$SiO_x$ showed homogeneous alignment; however, in the lower case (x < 1.6), liquid crystals showed homeotropic alignment.

• Journal of the Korea Society of Computer and Information
• /
• v.28 no.5
• /
• pp.49-56
• /
• 2023

Currently, e-commerce is changing from a digital twin to a metaverse world. The metaverse world is an intermediate form between virtual and real worlds and is operated as a coin-based meta-commerce. In this meta-commerce world, blockchain-based NFT coins are used when trading items (contents). In this study, we studied how to issue a large number of NFT coins (certification) rather than issuing a single type of NFT. The research method was designed to produce content layer-based and automatically create the desired quantity using a mass NFT index and automatic generation method. In this study, a layer overlap method (background, body, etc.) was used with a Phyton-based program for mass minting. As a result, it can be used as a blockchain-based certificate that can prove a group of many people. In addition, the content created with the NFT index was registered on the NFT sales site to confirm its utilization and value.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.45 no.3
• /
• pp.36-44
• /
• 2013

This study is focused on the debarking and xylem separation yield of Paper Mulberry. We investigated the most efficient manual on the automatic debarking and xylem separator machine. The bast tissues of Paper Mulberry were separated in three layers including black outer layer, green inner layer, and white inner layer. A target is to save the white inner layer of these three layers as much as possible. The experimental machine most characterize xylem separation and debarking by frictional force between the bulges and Paper Mulberry by the drum rotation. It is possible automatically to operate the machine by controlling the temperature sensor and the time. Debarking process can be know that removed black outer layer has beem accumulate and measured the weight. The content of the extract, holocellulose, lignin and ashes of the white inner layer was analyzed. It is result that conditions of optimum process of the experimental machine is 45 RPM, temperature at $60^{\circ}C$(60 min.) and $80^{\circ}C$(60 min.), mixing bulge of 10 mm(120ea) and 30 mm(120ea) and capacity of Paper Mulberry 10 kg.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.3 no.4
• /
• pp.319-324
• /
• 2002

The Integration of agent technology and security technology is needed to many application areas like electronic commerce. This paper suggests a model of extended multi-agent engine which supports privacy, integrity, authentication and non-repudiation on agent communication. Each agent which is developed with the agent engine is composed of agent engine layer and agent application layer. We describe and use the concepts self-to-self messages, secure communication channel, and distinction of KQML messages in agent application layer and messages in agent engine layer. The suggested agent engine provides an agent communication language which is extended to enable secure communication between agents without any modifications or restrictions to content layer and message layer of KQML. Also, in the model of our multi-agent engine, secure communication is expressed and processed transparently on the agent communication language.

• Journal of Advanced Marine Engineering and Technology
• /
• v.24 no.3
• /
• pp.43-51
• /
• 2000

The effect of time, temperature and gas composition on the case hardened thickness, hardness and nitride formation in the surface of ductile cast iron(GCD400) have been studied by micro-pulse plasma technique. Typically, external compound layer and internal diffusion layer which is much thicker than compound layer was observed in the nitride hardening of ductile cast iron. The relative amount kind of phases formed in the nitrided hardening changed with the change of nitriding conditions. Generally, only nitride phases such as $\gamma^'$($Fe_4N$), or $\varepsilon$($Fe_{2-3}N$) phases were detected in compound layer by XRD analysis. The thickness of compound layer increased with the increase of nitrogen content in the gas composition. The optimum nitriding temperature was obtained at $520^{\circ}C$. The nitrided hardening thickness parabolically with nitriding time(t) and thus, the case hardened layer(d) fits well with the typical parabolic equation ; d=kt. The material constant k for GCD400 nitrided at $520^{\circ}C$ was $0.04919\times10^3{\mu}m.hr^{-1/2}$.

• Korean Journal of Materials Research
• /
• v.16 no.1
• /
• pp.30-36
• /
• 2006

A novel method was proposed to grow an epitaxial $CoSi_2$ on (100)Si substrate. A $CoN_x$ interlayer was deposited by reactive sputtering of Co in an Ar+$N_2$ flow. From the Ti/Co/$CoN_x$/Si structure, a uniform and thin $CoSi_2$ layer was epitaxially grown on (100)Si by annealing above $700^{\circ}C$. Two amorphous layers were found at the $CoN_x$/Si interface, where the top layer has a silicon nitride (Si-N) bonding state with some Co content and the bottom layer has a Co-Si intermixing state. The SiNx amorphous layer seems to play a critical role of suppressing the diffusion of Co into Si substrate for the direct formation of epitaxial $CoSi_2$.

• Journal of Korea Foundry Society
• /
• v.17 no.4
• /
• pp.371-378
• /
• 1997

The study for direct synthesis of TaC carbide which was a reaction product of tantalum and carbon in the cast iron was performed. Cast iron which has hypo-eutectic composition was cast bonded in the metal mold with tantalum thin sheet of thickness of $100{\mu}m$. The contents of carbon and silicon of cast iron matrix was controlled to have constant carbon equivalent of 3.6. The chracteristics of microstructure and the formation mechanism of TaC carbide in the interfacial reaction layer in the cast iron/tantalum thin sheet heat treated isothermally at $950^{\circ}C$ for various time were examined. TaC carbide reaction layer was grown to the dendritic morphology in the cast iron/tantalum thin sheet interface by the isothermal heat treatment. The composition of TaC carbide was 48.5 at.% $Ti{\sim}48.6$ at.% C-2.8 at.% Fe. The hardness of reaction layer was MHV $1100{\sim}1200$. The thickness of reaction layer linearly increased with increasing the total content of carbon in the cast iron matrix and isothermal heat treating time. The growth constant for TaC reaction layer was proportional to the log[C] of the matrix. The formation mechanism of TaC reaction layer at the interface of cast iron/tantalum thin sheet was proved to be the interfacial reaction.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.1 no.1
• /
• pp.49-54
• /
• 2000

The effect of Particle size of coating Powder and coating temperature on the Properties of coating layer was studied by calorizing(or aluminizing). The surface properties of coating layer were fully characterized, using SEM and EDXS. Coating powders were separated according to the particle size by 3 steps and the coating temperature was varied from $950^{\circ}C$ to $980^{\circ}C$. Calorizing with pack cementation method carried under Ar atmosphere for 5 hrs. Results show that the thickness and Al content of coating layer increased as the size of coating powder decreased and coating temperature increased. And pores formed on the coating layer reduced and homogeneity of coating layer increased with smaller particle size of coating powder.