$LiNbO_3$ congruent 조성이 성장결정과 잔류융액의 Curie 온도$(T_c)$측정에 의해 조사되어졌다. 결정성장시 원료의 조성은 48.45에서 48.60mole%$Li_2O$ 까지 변화되어졌다. $LiNbO_3$의 $T_c$는 조성에 따라 크게 변하였고 Tc=10.4184C2-962.996C+23342에 따름을 알 수 있었다. $T_c$측정에는 DSC-1500를 사용하였고, $iNbO_3$내 $Li_2O$의 분배계수가 결정과 융액조성의 관계에 따라 구해졌다. $ iNbO_3$의 congruent조성은 48.52mole%$Li_2O$임이 밝혀졌고 그때의 $T_c$는 $1145{\pm}^1{\circ}C$이었다.

• 한국결정성장학회:학술대회논문집
• /
• 한국결정성장학회 1997년도 Proceedings of the 12th KACG Technical Meeting and the 4th Korea-Japan EMGS (Electronic Materials Growth Symposium)
• /
• pp.179-181
• /
• 1997

When grown the oxide single crystal including Li-ion, optimum oxygen condition is needed. Color and crack are caused in single crystal according too the change in the condition of the oxygen. LiTaO₃ crystals grown from off-composition of congruent melt composition under oxygen deficieny condition didn't generate any crack. LiNbO₃. LiTaO₃ crystals grown from congruent melt composition under optimum oxygen condition caused pale yellow color or colorless with no crack. Color gradually became colorless and generated cracks according to Oxygen excess.

• 한국결정성장학회지
• /
• 제3권2호
• /
• pp.99-106
• /
• 1993

열분석(DTA : Differential Thermal Analysis) 방법에 의한 퀴리온도$(T_c)$ 측정방법으로부터 48.50에서 49 $Li_2O$ mole %까지의 퀴리온도$(T_c)$와 $Li_2O$ mole %(C)의 관계식 $(T_c = -17.869C^2+1840.2C-46623)$을 구하였다.$LiTaO_3$ 단결정의 congruent 조성을 결정하기 위하여 48.60 부터 48.70 mole %까지의 영역에서 쵸크랄스키법으로 $LiTaO_3$ 단결정을 육성하고 Top과 Tail 결정에서의 퀴리온도 차이,${\Delta}{T_c} (T_{c(Top)}-T{_c(Tail)})$ 그리고 결정성장 초기와 말기의 융액과 결정의 조성비로부터 분배계수(k)를 구하였다. 이 결과로부터 결정된 congruent 조성은 48.65 mole %였으며 그때의 $(T_c)$ 값은 $610{\pm}1^{\circ}C$였다.

• 한국결정성장학회지
• /
• 제9권3호
• /
• pp.267-272
• /
• 1999

Czochralski법으로 성장시킨 조화용융조성(48.6 mol%$LiNbO_3$)의 undoped 및 MgO-doped $LiNbO_3$ 단결정 내의 미소결함을 광학현미경 및 주사/투과 전자현미경을 이용하여 정밀분석하였다. Dopant 첨가 및 성장된 부위(g)에 따른 분역구조의 변화와 결함밀도를 측정함으로써 결함양상을 분석하고 최적 결정성장조건과의 상관관계를 고찰하였다. 강자성 분역벽 주변의 높은 결함밀도는 이 근처가 응력이 집중된 영역임을 반영하고, 특히 한쪽 방향의 분역벽에만 결함이 밀집된 결함구조를 가지고 있음을 확인하였다.

• 한국결정성장학회:학술대회논문집
• /
• 한국결정성장학회 1998년도 PROCEEDINGS OF THE 14TH KACG TECHNICAL MEETING AND THE 5TH KOREA-JAPAN EMGS (ELECTRONIC MATERIALS GROWTH SYMPOSIUM)
• /
• pp.111-114
• /
• 1998

Lithium Niobate {{{{ { LiNbO}_{ 3} }}}} single crystals grown by Czichralski method at the congruent composition, have ferroelectric microdomains. These microdomins were investigated by chemical etching with hydrofluoric acid (HF) AND NITRIC ACID ({{{{ { HNO}_{3 } }}}}), and by us ing optical microscopy, scanning electron microscopy and atomic force microscopy

• 한국광학회:학술대회논문집
• /
• 한국광학회 1999년도 제16회 광학 및 양자전자 학술발표회Proceedings of 16th Optics and Quantum Electronics Conference, 1999
• /
• pp.220-221
• /
• 1999

Single crystals of Yttrium Calcium Oxyborate (YCOB) doped with different concentrations of Er3+ and Yb3+ ions were growth by Czochralski method. High qualities of crystals in morphology and transparency were obtained . Analysis on crystal structure and lattice parameters were performed by X-ray diffraction method. It was found that congruent melting composition is YCA4.2O1.2(BO3)3. Absorption and fluorescence properties of grown crystals were also reported.

• 한국세라믹학회지
• /
• 제31권1호
• /
• pp.39-46
• /
• 1994

LiTaO3 single crystals were growth without cracking using Pt-Rh crucible and Ir crucible. The starting composition to get the melt of congruent melting composition, which has been dependent upon the experimental procedure, was taken after fixing the total growing process by the result of preliminary experiments. The Rh contamination from the Pt-Rh crucible was to be neglected if the crystal had been grown under inert atmosphere, which resulted in the crystal color being slightly yellow. This color was decolored after 24 hour's annealing at 1200℃ under air atmosphere. The optimum conditions for the crystal growing and the diameter control were so dependent upon the crucible material in spite of using the crucible of the same size. The liquid-solid interface of LiTaO3 crystal of 1" diameter has been flat if the rotation speed was 45rpm.

• 한국결정성장학회지
• /
• 제12권1호
• /
• pp.50-55
• /
• 2002

$LiNbO_3$ 단결정에 $Nd_2O_3$0.2~0.5 wt.%를 칭량하여 결정을 성장 시켰다. 그리고 광손상을 억제하기 위해 ZnO 2~8 mole%를 첨가하여 광손상에 대한 저항성을 높였다. 본 연구에서는 Nd가 doping된 단결정을 성장시켜 주기적인 domain을 만들고자 하였다

• 한국결정성장학회지
• /
• 제7권1호
• /
• pp.6-17
• /
• 1997

Czochralski법으로 용융상태에서의 조성이 congruent(48.6 mol%$Li_2O$), stoichiomet-ric(50.0 mol%$Li_2O$), Li-rich(54.6 mol%$Li_2O$, 58 mol%$Li_2O$), 한 결정과 congruent한 조성에 $K_2$O를 6wt.% 첨가한 결정을 c-축 방향으로 성장시켰다. 성장된 결정들은 분말 X-선 회절 실험에 의해 확인하고 편광 현미경과 투과 X-선 Laue법에 의해 축을 결정한 후 절단하여 65 mol%$Li_2O$의 Li-rich 2-phase powder에서 VTE 처리한다. VTE 처리한 시료는 상온에서 결정내 $Fe^{3+}$ 이온에 대한 EPR 스펙트럼과 UV-스펙트럼을 측정하고 이 온도에서의 IR-스펙트럼은 $OH^-$ 이온 농도를 증가시키기 위하여 수증기 분위기에서 열처리한 후 측정한다. 측정 결과를 as grown 상태의 결정에 대한 결과와 비교 분석한다. 상온에서의 결정내 $Fe^{3＋}$ 이온에 대한 EPR 실험 결과 VTE 처리한 시료들의 EPR 스펙트럼은 허용되지 않은 천이에 의한 스펙트럼이 사라지고 허용된 천이에 의한 스펙트럼은 세기가 증가하며 lineshape가 거의 대칭적으로 되고 선폭도 훨씬 줄어든다. 상온에서의 각 시료에 대한 UV-스펙트럼의 흡수단은 VTE 처리하면 단파장쪽으로 이동하며 VTE 처리한 모든 시료의 흡수단이 거의 동일하다. $OH^-$이온에 의한 IR-흡수 스펙트럼은 VTE 처리한 시료의 경우 $3465\textrm{cm}^{-1}$ 성분 스펙트럼이 현저하게 중가한다. 이 결과에 의하면 본 실험과 같은 조건에서 VTE 처리한 시료들은 결정내 [Li]/[Nb] 비가 거의 1인 stoichiometric한 결정이 되었음을 알 수 있다.

• 한국결정성장학회지
• /
• 제2권1호
• /
• pp.20-29
• /
• 1992

전영역에 결쳐서 고용영역이 존재하는 $BaTiO_3-NaNbO_3$계에서, congruent melting composition인 $30BaTiO_3{cdot}70NaNbO_3$조성의 고용체 단결정을 Czochralski법에 의하여 육성하였다. 직경 15-50mm, 길이 20-30mm인 단결정이 결정인상속도 2.0mm/h, 결정회전수 5.0-1-rpm에서 육성되었다. 그러나 결정 육성중 육성되는 결정의 열전도도가 낮기 때문에, 발생하는 잠열(latent heat)의 방출이 충분치 않아 고-액계면이 평탄하게 유지되지 않았고 그결과로 육성된 결정중에는 corestructures가 관찰되었다. 육성된 결정에서 core 부분을 제외한 다른 부분은 inclusion등이 없는, 광학적으로 균질한 단결정이었고 가시광 영역에서 양호한 광투과율을 보였다.