The purpose of this study is to enhance durability of concrete structures that uses this surface protecting material by carrying out the performance test of the surface protecting material of concrete, and as s result, we reached out the conclusion as follow. 1. As a result of the test measuring the stability and adhesive power of conductive film against ultraviolet, freezing & thawing, and damage from seawater that deteriorate the surface protecting material, it was turned out to meet the performance criteria specifying in the KS standard enough to gain a good evaluation to use as a surface protecting material. 2. As a result of the test identifying the neutralization-furtherance, it was assessed to be capable of protecting effectively concrete structures from carbonic acid gas by a very low depth of 0.1mm of neutralization. 3. As a result of the test identifying Penetrated Resistance Properties of chloride ion, as it was turned out to have a very low value of 819 Coulombs, it was assessed that even in the environment where the corrosion by chloride such sea environment is very affective, the film can effectively protect the concrete structure. 4. As a result of the test identifying freezing & thawing, as there was no change in reduction of mass after 400 cycle, it was assessed that the film has a good resistance against freezing & thawing. According to the results of study above, it is expected that this technology can extend its durability of concrete structure and be widely used for concrete structure through means (methods) to prevent the neutralization and damage from seawater as original purposes of the surface protecting material.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2009년도 추계 학술논문 발표대회
• /
• pp.117-120
• /
• 2009

It has been gradually increased with the use of resin based membrane forming agent for curing method, which plays a role in protecting moisture evaporation by forming resin membrane at the surface of concrete. In this paper, tests were carried out to examine moisture retention capability of cement mortar applying membrane forming agent. Dosages and types of the membrane forming agent were varied. It is found that sheet curing sealed with the surface of concrete closely has favorable moisture retention capability. However, the application of membrane forming curing method had superiority in moisture retention capability at early stage but at later age, its capability is deteriorated. Hence, further study regarding altering application method was necessary to secure enhanced moisture retention capability.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 춘계 학술발표회 제16권1호
• /
• pp.176-179
• /
• 2004

The latest concrete structure has showed that the deterioration of durability has been increased by the damage from salt, carbonization, freezing & thawing and the others. Therefore, the measures for the concrete which has deteriorated durability have been taken. Among them, it has been often used that surface treatment which cuts off the deterioration factors of durability by protecting the surface of concrete. This study was evaluated the surface improving agent for permeability, watertightness, air-permeability, chemical resistance and elution resistance.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 춘계 학술발표회 논문집(II)
• /
• pp.321-324
• /
• 2006

The latest concrete has showed that the deterioration of durability has been increased by the damage from salt, carbonation, freezing & thawing and the others. Therefore, it is needed to protect durability and performance according to the appropriate materials and methods in the concrete structures. In general, several types of polymer and silicate are used as protecting deterioration agents of concrete structures, but these agents have many problems because of low durability and properties. In this study, It developed the deterioration restraining agent using polycondensed silicate and monomer that can block a deterioration cause such as CO2 gas, salt and water from the outside and enhance waterproofing ability by reinforcing the concrete surface when applying it to concrete structures. Also, it evaluated improving concrete performance using a deterioration restraining agent.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 추계 학술발표회 제17권2호
• /
• pp.563-566
• /
• 2005

Concrete structures have been damaged by salt, carbonization, freezing and thawing and the others. Therefore, it is needed to protect durability and performance according to the appropriate materials and methods in the concrete structures. In general, several types of polymer and silicate are used as protecting deterioration agents of concrete structures, but these agents have many problems because of low durability and properties. In this study, It developed the deterioration restraining agent using polycondensed silicate and monomer that can block a deterioration cause such as $CO_2$ gas, salt and water from the outside and enhance waterproofing ability by reinforcing the concrete surface when applying it to concrete structures. Also, it developed the systems for improving concrete performance using a deterioration restraining agent.

• 한국구조물진단유지관리공학회 논문집
• /
• 제19권6호
• /
• pp.29-36
• /
• 2015

본 연구에서는 유황을 폴리머화하여 콘크리트 표면보호재로 활용가능성을 검토하기 위하여 내구성능 및 생물독성 평가를 실시하였다. 평가 결과, 콘크리트 표면보호재의 내화학성능은 산, 알칼리 용액에 대하여 화학저항성이 우수한 것으로 나타났다. 배합조건별 촉진내후성 실험 후 부착강도평가 결과 규사분말 및 플라이애시를 동시에 혼합한 배합에서 가장 우수한 강도특성을 나타내었다. 콘크리트용 표면보호재 시험체의 온냉반복 후에도 모든 배합조건에서 부착강도 1 MPa을 상회하였고, SFS배합에서 가장 높은 부착강도를 나타내었다. 표면보호재를 도포한 콘크리트의 촉진탄산화 및 염소이온침투저항성을 검토한 결과, 규사분말을 채움재로 사용한 표면보호재를 도포한 시험체에서 가장 우수한 내구성능을 나타내었다. 유황폴리머를 콘크리트 표면보호재로 사용시 생물독성 검토를 위해 어독성 실험을 수행한 결과, 유황폴리머는 생물에 미치는 영향은 없는 것으로 나타났다. 표면보호재의 내화학성, 동결융해저항성, 탄산화, 염소이온침투저항성 등을 모두 고려하여 볼 때, 본 연구범위에서는 유황폴리머에 채움재로서 규사분말과 플라이애시를 각각 20%씩 대체하는 것이 적절한 수준인 것으로 판단된다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제9권4호
• /
• pp.177-186
• /
• 2005

최근 콘크리트 구조물은 염해, 중성화 및 동결융해 등에 의한 내구성능 저하의 사례가 증가하고 있다. 이렇게 내구성능이 저하된 콘크리트에 대한 다양한 대책이 강구되고 있으며, 그 중에서도 콘크리트의 표면을 보호하여 내구성능 저하의 요인을 차단하는 표면처리공법이 많이 사용되고 있다. 그러나 에폭시 등 유기계 및 시멘트계 보수재는 콘크리트의 물성의 차이로 인하여 시간이 경과함에 따라 보수층의 파단 및 들뜸 등 문제가 발생하는 사례가 보고되고 있다. 저자들은 콘크리트의 물성과 동일한 무기계를 주성분으로 한 표면 성능 개선제를 콘크리트에 도포하면, 칼슘이온 등과 반응하여 콘크리트의 조직이 치밀해짐으로써 $CO_2$ 가스, 염소이온 및 물 등 내구성능 저하요인을 차단하는 보수재를 개발하고 있다. 본 연구에서는 개발된 표면성능 개선제의 침투성능, 수밀성능, 통기성능, 화학저항성능, 용출저항 성능 및 열화된 콘크리트에 대한 적용성에 대하여 평가하였다. 그 결과, 표면성능 개선제는 콘크리트의 내부로 10mm 이상 침투되며 콘크리트의 수밀성능 및 통기성능 등을 향상시키는 것으로 나타났다. 따라서, 본 연구에서 개발된 표면성능 개선제를 콘크리트 구조물에 도포하면 콘크리트의 내구성능 저하를 방지할 수 있을 것으로 판단된다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제18권5호
• /
• pp.1-8
• /
• 2014

본 연구에서는 유황을 폴리머화하여 내화학성능이 요구되는 구조물의 콘크리트 표면보호재로 활용할 수 있도록 성능을 검토하였다. 평가 결과, 유황폴리머 표면도포재의 중력식 스프레이가 적절한 것으로 나타났으며, 도포횟수는 왕복 3회 이상 도포했을 때 1MPa 이상의 부착강도 확보가 가능하였다. 표면보호재가 도포될 콘크리트 표면조건은 상온조건 ($20{\sim}30^{\circ}C$) 이상에서 높은 부착강도를 나타내었으며, 온도가 높을수록 부착강도가 증가하였다. 표면보호재의 채움재 혼입량에 따른 강도특성 평가결과, 20~40% 정도 혼입된 채움재는 유황폴리머의 수축을 저감시키는 효과를 나타내어 강도 향상에 기여하였다. 또한, 플라이애시 보다는 규사 혼입시 부착강도가 높았고, 동시 혼입시 가장 우수한 부착강도 특성을 나타내었다. 화학저항성은 플라이애시 및 규사를 각각 20% 대체한 배합에서 부착강도 저하가 최소로 되어 우수한 내화학성을 나타내었다. 염소이온 침투에 대한 성능평가를 수행한 결과, 표면보호재를 도포하지 않은 시험체에 비하여 유황폴리머 표면보호재를 도포한 경우, 29~48% 정도 염소이온침투저항성이 증대되었다. 표면보호재의 도포조건, 압축강도, 부착강도, 화학저항성, 염해저항성 등을 모두 고려하여 볼 때, 본 연구범위에서는 유황폴리머에 채움재로서 규사와 플라이애시를 각각 20%씩 대체하는 것이 적절한 수준인 것으로 판단된다.

• 콘크리트학회논문집
• /
• 제17권4호
• /
• pp.489-498
• /
• 2005

최근 콘크리트 구조물의 성능 저하는 염해, 중성화, 동결융해 및 기타 요인에 의해 증가하고 있고 콘크리트 성능 저하를 방지하기 위해 다양한 대책이 강구되고 있다. 이러한 콘크리트 성능 저하를 방지하기 위한 방법 중에 콘크리트 표면을 보호함으로써 성능 저하 요인을 차단할 수 있는 콘크리트 표면 처리제가 종종 사용되고 있다. 콘크리트 보수$\cdot$방수재료는 에폭시와 같은 유기계 재료가 많이 사용되고 있으며, 이런 재료는 초기접착력과 내약품성이 우수한 장점을 가지고 있다 그러나 이런 유기재료는 콘크리트와의 탄성계수 및 수축팽창율이 차이로 시간이 경과함에 따라 박리, 들뜸 현상이 발생하는 등 내구성에 문제가 있는 것으로 지적되고 있다. 한편 최근 콘크리트 구조물의 내구성 및 방수성능을 향상시키기 위해 무기질계 침투형 보수$\cdot$방수재의 사용사례가 증가하고 있다. 따라서 본 연구에서는 콘크리트 표면을 강화시켜 $CO_2$ 가스, 염화물 이온 등의 열화물질을 차단시키며 동시에 방수성능을 부여할 수 있는 콘크리트 침투형 성능개선제를 개발하였다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제10권5호
• /
• pp.157-163
• /
• 2006

본 연구는 콘크리트를 보호하기 위해서 발수성 프라이머와 마감 코팅재룰 사용한 이중 표면보호 방식을 평가하기 위한 것이다. 기존의 경우에는 발수제가 가장 마지막 도장재로 사용된다. 그러나 본 연구는 발수제가 자외선에 약한 결점을 보완하고자 발수제 도장 후에 마감재가 도장되는 순서로 시공하는 방법을 사용하였다. 본 연구에서는 이러한 조합의 표면 보호재와 기존 표면 보호재를 비교 평가하였다. 본 연구에서 사용된 표면 보호재의 부착 성능은 발수제 위에 보호재가 시공되어도 본 연구에서 사용된 다른 보호재와 마찬가지로 KS F 4936-' 03을 만족한 것으로 나타났다. 본 연구에서 사용된 모든 보호재는 콘크리트를 보호하는 성능이 우수한 것으로 나타났으며, 특히 발수성 프라이머와 마감 코팅재를 함께 도포한 경우 염소이온 침투 저항성 및 이산화탄소에 의한 중성화 저항성이 본 연구에서 사용된 다른 표면 보호재에 비해 우수한 것으로 나타났다.