• Journal of the korean academy of Pediatric Dentistry
• /
• v.33 no.4
• /
• pp.653-660
• /
• 2006

Fuji VII is a glass-ionomer cement specially targeted for early protection in erupting first and second molars. Properties of Fuji VII such as very high level of fluoride release, low viscosity and no need to preliminarily etch the substrate would be useful to erupting molars with primary pit and fissure caries or hypoplastic area for preventive goal or remineralization. The purpose of this study were to evaluate remineralization of Fuji VII glass ionomer cement and to compare with one of other restorative materials such as conventional glass ionomer cement, resin-modified glass ionomer cement, compomer and composite resin. Forty-two extracted human molars were used for this study. All teeth were immersed in demineralizing solution for 48 hours after Class V cavity preparation was made on sound proximal surface. The teeth were randomly divided into six groups and restored with Fuji VII, Fuji II, Fuji II LC improved, F2000, $Filtek^{TM}$ Z250 and control group was unrestored. The middle area with $130{\pm}20{\mu}m$ thickness was separated from specimen using microtome and demineralized area was photographed under polarized microscope. Separated area was relocated to specimen and stored in artificial saliva, After four weeks, changes of demineralized area were observed and compared to them restorated immediately. The results from the this study can be summarized as follows ; 1. Fuji VII, Fuji II, Fuji II LC improved have more prominent remineralization effect than F2000, $Filtek^{TM}$ Z250, control group. 2. No significant differences in remineralization effect are seen between Fuji VII and Fuji II, Fuji II LC improved.

• The Journal of Korean Academy of Prosthodontics
• /
• v.53 no.4
• /
• pp.295-300
• /
• 2015

Purpose: The aim of this study was to evaluate the shear bond strength between Ni-Cr alloy and composite resin using universal adhesive systems coMPared to conventional method using metal primers. Materials and methods: For this study, a total of 120 cast commercial Ni-Cr alloy (Vera Bond 2V) disks were embedded in acrylic resin, and their surfaces were smoothed with silicon carbide papers and airborne-particle abrasion. Specimens of each metal were divided into 6 groups based on the combination of metal primers (Metal primer II, Alloy primer, Metal & Zirconia primer, MKZ primer) and universal adhesive systems (Single Bond Universal, All Bond Universal). All specimens were stored in distilled water at $37^{\circ}C$ for 24 hours. Shear bond strength testing was performed with a universal testing machine at a cross head speed of 1 m/min. Data (MPa) were analyzed using one-way ANOVA and the post hoc Tukey's multiple comparison test (${\alpha}$=.05). Results: There were significant differences between Single Bond Universal, All Bond Universal, Metal Primer II and Alloy Primer, MKZ Primer, Metal & Zirconia Primer (P<.001). Conclusion: Universal Adhesive system groups indicated high shear bond strength value bonded to Ni-Cr alloy than that of conventional system groups using primers except Metal Primer II. Within the limitations of this study, improvement of universal adhesive systems which can be applied to all types of restorations is recommended especially non-precious metal alloy. More research is needed to evaluate the effect of silane inclusion or exclusion in universal adhesive systems.

• Restorative Dentistry and Endodontics
• /
• v.30 no.2
• /
• pp.112-120
• /
• 2005

This study was done to evaluate whether there were any differences in microleakage of class V composite restorations according to restoration site and cavity size. Total sixty-four restorations were made in molar teeth using Esthet-X. Small ($2\;{\times}\;2\;{\times}\;1.5\;mm$) and large ($4{\times}2{\times}1.5\;mm$) restorations were made at the buccal/lingual surface and the proximal surface each. After 1,000 times of thermocycling ($5^{\circ}\;-\;55^{\circ}C$), resin replica was made and the percentage of marginal gap to the whole periphery of the restoration was estimated from SEM evaluation. Thermocycled tooth was dye penetrated with $50\%$ silver nitrate solution. After imbedding in an auto-curing resin, it was serially ground with a thickness of 0.25 mm. Volumetric microleakage was estimated after reconstructing three dimensionally. Two-way ANOVA and independent T-test for dye volume, Mann-Whitney U test for the percentage of marginal gap, Spearman's rho test for the relationship between two techniques were used, The results were as follows : 1. The site and size of the restoration affected on the microleakage of restoration. Namely, much more leakage was seen in the proximal and the large restorations rather than the buccal/lingual and the small restorations. 2. Close relationship was found between two techniques (Correlation coefficient = 0.614/ P = 0.000). Within the limits of this study, it was noted that proximal and the large restorations leaked more than buccal/lingual and the small restorations. Therefore, it should be strictly recommended large exposure of margins should be avoided by reducing unnecessary tooth reduction.

• The Journal of Korean Academy of Prosthodontics
• /
• v.48 no.1
• /
• pp.8-15
• /
• 2010

Purpose: The purpose of this study was to evaluate the effect of various methods of dentin bonding agent application and air abrasion pretreatment on microtensile bond strength between dentin and resin, using a self-etching adhesive system. Material and methods: Thirty freshly extracted human molars were obtained and divided into 6 groups of 5 teeth. A 2-step self etching adhesive system (Clearfil SE Bond) was used for all groups. The control specimens were prepared using a direct immediate bonding technique. The delayed dentin sealing specimens were prepared using an indirect approach without dentin prebonding. The immediate dentin sealing specimens were prepared using dentin prebonding immediately following preparation. Immediate dentin sealing teeth and delayed dentin sealing teeth had provisional restorations using Fermit for two weeks. Then all specimens of each group were divided into two groups of three, depending on air abrasion pretreatment. Composite "crowns" were incrementally built on and specimens were stored in water for 24 hours. All teeth were prepared for a microtensile bond strength test. Bond strength data were analyzed with a one-way ANOVA test, and post hoc comparison was done using the Scheffe's test. Results: The mean microtensile bond strengths of all groups were not statistically different from each other. Conclusion: When preparing teeth for indirect restorations, IDS and DDS with Clearfil SE bond, have no difference on the microtensile bond strength between dentin and resin. Air abrasion pretreatment did not affect the microtensile bond strength when using IDS and DDS with Clearfil SE bond.

• Restorative Dentistry and Endodontics
• /
• v.20 no.2
• /
• pp.699-720
• /
• 1995

This study was conducted to evaluate the effect of benzalkonium chloride solution as a wetting agent instead of water on dentin bonding with NTG-GMA/BPDM system (All-bond 2, Bisco.) and DSDM system (Aelitebond, Bisco.). Benzalkonium chloride solution is a chemical disinfectant widely used in medical and dental clinics for preoperative preparation of skin and mucosa due to its strong effect of cationic surface active detergent. Eighty freshly extracted bovine lower incisor were grinded labially to expose flat dentin surface, and then were acid-etched with 10 % phosphoric acid for 15 second, water-rinsed, and dried for 10 second with air syringe. The specimens were randomly divided into 8 groups of 10 teeth. The specimens of control group were remoistured with water and the specimens of experimental groups were remoistured with 0.1 %, 0.5 %, and 1.0 % benzalkonium chloride solution respectively. And then, the Aelitefil composite resin was bonded to the pretreated surface of the specimens by use of All-bond 2 dentin bonding system or Aelitebond dentin bonding system in equal number of the specimens. The bonded specimens were stored in $37^{\circ}C$ distilled water for 24 hours, then the tensile bond strength was measured, the mode of failure was observed, the fractured dentin surface were examined under scanning electron microscopy, and FT-IR spectroscopy was taken for the purpose of investigating the changes of the dentin surface pretreated with benzal konium chloride solution followed by each primer of the dentin bonding systems. The results were as follows : In the group of bonding with NTG-GMA/BPDM dentin bonding agent(All-bond 2), higher tensile bond strength was only seen in the experimental group remoistured with 0.1 % benzal konium chloride solution than that in water-remoistured control group(p<0.05). In the group of bonding with DSDM dentin bonding agent (Aelitebond), no significant differences were seen between the control and each one of the experimental group(p<0.05). Higher tensile bond strength were seen in NTG-GMAIBPDM dentin bonding agent group than in DSDM dentin bonding agent group regardless of remoistur ization with benzal konium chloride solution. On the examination of failure mode, cohesive and mixed failure were predominantly seen in the group of bonding with NTG-GMAIBPDM dentin bonding agent, while adhesive failure was predominantly seen in the group of bonding with DSDM dentin bonding agent. On SEM examination of fractured surfaces, no differences of findings of primed dentin surface between the groups with and without remoisturization with benzal konium chloride solution. FT-IR spectroscopy taken from the control and the experimental group reve::.led that some higher absorbance derived from the primers binding to dentin surface was seen at the group pretreated with 0.1 % benzal konium chloride solution than at the control group of remoisturizing with water.

• The Journal of Korean Academy of Prosthodontics
• /
• v.57 no.2
• /
• pp.127-133
• /
• 2019

Purpose: The purpose of present study was to investigate fracture strength and mode of failure of endodontically treated teeth restored with metal cast post-core system, prefabricated fiber post system, and newly introduced polyetherketoneketone (PEKK) post-core system. Materials and methods: A total of 21 mandibular premolar were randomly grouped into 3 groups of 7 each according to the post material. Group A was for metal cast post core; Group B for prefabricated glass fiber post and resin core; and Group C for milled PEKK post cores. All specimens were restored with metal crown. The fracture strength of each specimen was measured by applying a static load of 135-degree to the tooth at 2 mm/min crosshead speed using a universal testing machine. After the fracture strength measurement, the mode of failure was observed. The results were analyzed using Kruscal-Wallis test and post hoc Mann-Whitney U test at confidence interval ${\alpha}=.05$. Results: Fracture resistance of PEKK post core was lower than those of cast metal post and fiber reinforced post with composite resin core. In the aspect of fracture mode most of the root fracture occurred in the metal post core, whereas the post detachment occurred mainly in the fiber reinforced post. In the case of PEKK post core, teeth and post were fractured together. Conclusion: It is necessary to select appropriate materials of post for extensively damaged teeth restoration and clinical application of the PEKK post seems to require more research on improvement of strength.

• Journal of the Korean Society for Marine Environment & Energy
• /
• v.16 no.1
• /
• pp.53-59
• /
• 2013

Since 1990s, the major recycling methods for mechanical recycling of FRP(Fiber Reinforced Plastics)boats has involved shredding and grinding of the scrap FRP in a new recycled product. But still it leads to secondary problem such as air pollution, unacceptable shredding noise level and few limited applications. This study is to propose a newly advanced method which is more efficient and environment friendly waste FRP regenerating system. As extracting FRP layer and making the recycled fiber for recycled-fiber reinforced concrete(RFRC) from waste FRP, the recycling process has some merits in a sense of the recycling energy and the environmental effects. In this study, for those tasks, spectro-chemical differentiation method and coloring water-soluble dye treatment makes the roving layer more distinguishable photophysically. Also that has remarkably reduced safety hazards and energy. Using the mechanical properties of polymers and composite, FRP with the orthotropic and laminated plastic structure has been easily separated in the new extracting system. Also the new method has introduced five kind of separating manuals for the some different compositions of FRP boats. The roving fiber of laminated glass-fiber layer is as good as the polyvinyl fiber which is cost-high commercial fiber to increasing strength of concrete products. The early study has shown the effectiveness of laminated glass-fiber layer which also is chemical-resistant due to the resin coating. These results imply that more efficient and environment friendly recycled glass fiber can be better applied to the fiber reinforced concrete(FRC) substitute and this study also has shown wide concrete applications with RFRC from the waste FRP boat.

• Restorative Dentistry and Endodontics
• /
• v.27 no.6
• /
• pp.561-568
• /
• 2002

Purpose of this research is estimating polymerization depth of different source of light. XL 3000 for halo-gen light, Apollo 95E for plasma arc light and Easy cure for LED light source were used in this study. Different shade (B1 & A3) resin composites (Esthet-X, Dentsply, U.S.A.) were used to measure depth of cure. 1, 2, and 3 mm thick samples were light cured for three seconds, six seconds or 10 seconds with Apollo 95E and they were light cured with XL-3000 and Easy cure for 10 seconds, 20 seconds, or 40 seconds. Vicker's hardness test carried out after store samples for 24 hours in distilled water. Results were as following. 1. Curing time increases from al1 source of lights, oui$.$ing depth increased(p<0.05). 2. Depth (that except 1mm group and 2mm group which lighten to halogen source of light) deepens in all groups, Vickers hardness decreased(p<0.05). 3. Vicker's hardness of A3 shade composite was lower in all depths more than B1 shade composites in group that do polymerization for 10 seconds and 20 seconds using halogen source of light(p<0.05), but group that do polymerization lot 40 seconds did not show difference(p>0.05). 4. Groups that do polymerization using Plasma arc and LED source of light did not show Vicker's hardness difference according to color at surface and 1mm depth(p>0.05), but showed difference according to color at 2mm and 3mm depth(p<0.05). The results showed that Apollo 95E need more polymerization times than manufacturer's recommendation (3 seconds), and Easy cure need polymerization time of XL-3000 at least.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.37 no.2
• /
• pp.179-185
• /
• 2010

Molar Incisor Hypomineralization(MIH) have recently gained intensive research interests and various clinical trials. Most prevalence, etiology, treatment studies in MIH were carried out in the European countries, and data from the Korean were seldom. This study aimed to investigate the prevalence of MIH and the status of dental caries and treatment on the first permanent molars in primary school children. For this study, 1,344 primary school students in Busan and Ulsan cities were examined directly the permanent incisors and first molars. The results of the survey were as follows: 81 MIH cases were identified among 1,344 cases. The prevalence of MIH in this group of children was 6.0%. Children with MIH showed a significantly higher DMFT value for permanent teeth than children without MIH. The mean number of decayed, missed, and filled in 1st permanent molars(DMFT index) was 1.17. The rate of children with restoration on 1st permanent molar was 13.6% and the sequence of restoration materials was as follows : composite resin, amalgam, gold inlay.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.36 no.1
• /
• pp.91-95
• /
• 2009

The use of stainless steel crowns are indicated for restoration of primary or permanent molars with proximal dental caries, extensive dental caries, or previous pulp treatment with increased danger of tooth fracture. Stainless steel crowns were introduced by Humphrey in 1950. For their improved durability, longevity, and success rate, they have been strongly considered for restoring extensive and multi-surfaced dental caries of molars in pediatric dentistry. However, they also have shortcomings, such as possibility of pulpal exposure or damaging proximal surface of adjacent teeth. In addition, when oversized stainless steel crowns are used, eruption of the adjacent permanent teeth may be disturbed by their prominent margin. As a means to compensate the shortcomings of stainless steel crowns, use of orthodontics bands may be considered. It is an alternative restoration method, where an orthodontic band is placed on a tooth first and cavity is restored with filling material, such as composite resin, glass ionomer, or amalgam. The use of an orthodontic band is indicated for molar restoration with cervical dental caries, extensive dental caries, enamel hypoplasia, or previous pulp treatment. Because it requires shorter chair time compared to stainless steel crown, its application is very useful for children with poor behavior. However, restoration using an orthodontic band requires good oral hygiene after its application. This case report illustrates the conservative restoration of primary molars and permanent molars with extensive dental caries using orthodontic bands.