• Korean Journal of Construction Engineering and Management
• /
• v.13 no.1
• /
• pp.118-128
• /
• 2012

As the bearing wall structure, which has been widely applied to domestic apartment buildings since the 1980s, cause many problems during remodeling of buildings, the government encourages constructors to adopt flat plate or rahmen structure through legal incentives. In line with such a trend, the green frame, an eco-friendly rahmen structure that has removed the shortcomings of previous structures, was developed to enhance structural safety, constructability, and eco-friendliness. The construction of green frame can reduce the labor cost and facilitate the composition of iron bars to reduce rebar loss through calculating the quality and establishing the bar bending schedule automatically on the precast concrete member data collected over the design phase. Therefore, the purpose of this study is to develop the algorithm to automate the calculation of iron bar volume for the green frame designed on composite precast concrete members. Automated algorithm to calculate concrete structural design information and design information. Practices through the application site should prove efficacy. The database established by the developed algorithm will automate the establishment of iron bar processing map and bar cutting list and the calculation of optimal composition and order volume to minimize the rebar loss. This will also reduce the expenses on management staff and overall construction cost through the minimization of rebar loss.

• Korean Journal of Materials Research
• /
• v.18 no.6
• /
• pp.339-346
• /
• 2008

Single-crystal $ZnIn_2S_4$ layers were grown on a thoroughly etched semi-insulating GaAs (100) substrate at $450^{\circ}C$ with a hot wall epitaxy (HWE) system by evaporating a $ZnIn_2S_4$ source at $610^{\circ}C$. The crystalline structures of the single-crystal thin films were investigated via the photoluminescence (PL) and Double-crystal X-ray rocking curve (DCRC). The temperature dependence of the energy band gap of the $ZnIn_2S_4$ obtained from the absorption spectra was well described by Varshni's relationship, $E_g(T)=2.9514\;eV-(7.24{\times}10^{-4}\;eV/K)T2/(T＋489K)$. After the as-grown $ZnIn_2S_4$ single-crystal thin films was annealed in Zn-, S-, and In-atmospheres, the origin-of-point defects of the $ZnIn_2S_4$ single-crystal thin films were investigated via the photoluminescence (PL) at 10 K. The native defects of $V_{Zn}$, $V_S$, $Zn_{int}$, and $S_{int}$ obtained from the PL measurements were classified as donor or acceptor types. Additionally, it was concluded that a heat treatment in an S-atmosphere converted $ZnIn_2S_4$ single crystal thin films into optical p-type films. Moreover, it was confirmed that In in $ZnIn_2S_4$/GaAs did not form a native defects, as In in $ZnIn_2S_4$ single-crystal thin films existed in the form of stable bonds.

• Steel and Composite Structures
• /
• v.21 no.5
• /
• pp.1017-1029
• /
• 2016

When a welded circular hollow section (CHS) tubular joint is subjected to brace axial loading, failure position is located usually at the weld toe on the chord surface due to the weak flexural stiffness of the thin-walled chord. The failure mode is local yielding or buckling in most cases for a tubular joint subjected to axial load at the brace end. Especially when a cyclic axial load is applied, fracture failure at the weld toe may occur because both high stress concentration and welding residual stress along the brace/chord intersection cause the material in this region to become brittle. To improve the ductility as well as to increase the static strength, a tubular joint can be reinforced by increasing the chord thickness locally near the brace/chord intersection. Both experimental investigation and finite element analysis have been carried out to study the hysteretic behaviour of the reinforced tubular joint. In the experimental study, the hysteretic performance of two full-scale circular tubular T-joints subjected to cyclic load in the axial direction of the brace was investigated. The two specimens include a reinforced specimen by increasing the wall thickness of the chord locally at the brace/chord intersection and a corresponding un-reinforced specimen. The hysteretic loops are obtained from the measured load-displacement curves. Based on the hysteretic curves, it is found that the reinforced specimen is more ductile than the un-reinforced one because no fracture failure is observed after experiencing similar loading cycles. The area enclosed by the hysteretic curves of the reinforced specimen is much bigger, which shows that more energy can be dissipated by the reinforced specimen to indicate the advantage of the reinforcing method in resisting seismic action. Additionally, finite element analysis is carried out to study the effect of the thickness and the length of the reinforced chord segment on the hysteretic behaviour of CHS tubular T-joints. The optimized reinforcing method is recommended for design purposes.

• Korean Journal of Materials Research
• /
• v.28 no.8
• /
• pp.466-473
• /
• 2018

Nickel oxide(NiO) thin films, nanorods, and carbon nanotube(CNT)/NiO core-shell nanorod structures are fabricated by sputtering Nickel at different deposition time on alumina substrates or single wall carbon nanotube templates followed by oxidation treatments at different temperatures, 400 and $700^{\circ}C$. Structural analyses are carried out by scanning electron microscopy and x-ray diffraction. NiO thinfilm, nanorod and CNT/NiO core-shell nanorod structurals of the gas sensor structures are tested for detection of $H_2S$ gas. The NiO structures exhibit the highest response at $200^{\circ}C$ and high selectivity to $H_2S$ among other gases of NO, $NH_3$, $H_2$, CO, etc. The nanorod structures have a higher sensing performance than the thin films and carbon nanotube/NiO core-shell structures. The gold catalyst deposited on NiO nanorods further improve the sensing performance, particularly the recovery kinetics.

• Applied Chemistry for Engineering
• /
• v.9 no.3
• /
• pp.342-347
• /
• 1998

Light-weight conductive polymer composites were prepared by incorporating polyheterocycles such as polypyrrole and polythiophene into pores of a highly porous cross-linked polystyrene, host polymer, to form a conductive network. The highly hydrophobic and porous host polymer was synthesized by concentrated emulsion polymerization method. Polypyrrole-based composites, prepared by employing ferric chloride-methanol system, showed a conductivity as high as 0.82 S/cm. Conductivity of polythiophene-based composites, prepared from ferric chloride-acetonitrile system, was 6.05 S/cm. Conductivity of compositivity was influenced by the initial molar ratio of oxidant to monomer as well. SEM micrographs of the composites showed that conducting polymer coated uniformly the inside wall of the porous host polymer. Shielding effectiveness of the polypyrrole-based composites and of the polythiophene-based composites were 15.2 dB and 22.5 dB at 2.0 GHz, respectively. In the temperature range from 20 to 300K, a polypyrrole impregnated composite exhibited seimiconducting behavior and followed the variable range hopping(VRH) model for charge transport.

• Korean Journal of Materials Research
• /
• v.16 no.3
• /
• pp.188-192
• /
• 2006

The microstructures and mechanical properties of continuously porous $SiC-Si_3N_4$composites fabricated by multi-pass extrusion were investigated at different Si levels added. Si-powder with different weight percentages (0%, 5%, 10%, 15%, 20%) was added to the SiC powder to make the raw mixture powders, with $6wt%Y_2O_3-2wt%Al_2O_3$ as sintering additives, carbon ($10-15{\mu}m$) as a pore-forming agent, ethylene vinyl acetate as a binder and stearic acid ($CH_3(CH_2)_{16}COOH$) as a lubricant. In the continuously porous $SiC-Si_3N_4$ composites, $Si_3N_4$ whiskers like the hairs of nostrils were frequently observed on the wall of the pores. In this study, the morphology of the $Si_3N_4$ whiskers was investigated with the silicon addition content. In the composites containing of 10 wt% Si, a large number of $Si_3N_4$ whiskers was found at the continuous pore regions. In the sample to which 15 wt% Si powder was added, maximum values of about 101 MPa bending strength and 57.5% relative density were obtained.

• Archives of Craniofacial Surgery
• /
• v.11 no.1
• /
• pp.13-18
• /
• 2010

Purpose: Nasal defect can be caused by excision of tumor, trauma, inflammation from foreign body reaction. Nose is located in the middle of face and protruded, reconstruction should be done in harmony with size, shape, color, and textures. We report various methods of nasal reconstruction using local flaps. Methods: From March 1998 to July 2008, 36 patients were operated to reconstruct the nasal defects. Causes of the nasal defects were tumor (18 cases), trauma (11 cases), inflammation from foreign body reaction (5 cases) and congenital malformation (2 cases). The sites of the defects were ala (22 cases), nasal tip (8 cases) and dorsum (6 cases). The thickness of the defects was skin only (5 cases), dermis and cartilagenous layer (7 cases) and full-thickness (24 cases). According to the sites and thickness of the defects, various local flaps were used. Most of alar defects were covered by nasolabial flaps or bilobed flaps and the majority of dorsal and tip defects were covered by paramedian forehead flaps. Small defects below $0.25 cm^2$ were covered with composite graft or full-thickness skin graft. Results: The follow-up period was 14 months. Partial flap necrosis was observed in a case, and one case of infection was reported, it was improved by wound revision and antibiotics. Nasal reconstruction with various local flaps could provide satisfactory results in terms of color and texture match. Conclusion: The important factors of nasal reconstruction are the shape of reconstructed nose, color, and texture. Nasolabial flap is appropriate method for alar or columellar reconstruction and nasolabial island flap is suitable for tip defect. The defect located lateral wall could be reconstructed with bilobed flap for natural color and texture. Skin graft should be considered when the defect could not afford to be covered by adjacent local flap. And entire nasal defect or large defect could be reconstructed by paramedian forehead flap.

• Steel and Composite Structures
• /
• v.15 no.1
• /
• pp.103-130
• /
• 2013

Fire performance and fire safety of high-rise buildings have become major concerns after the disasters of World Trade Center in the U.S. in 2001 and Windsor tower in Spain in 2005. Performance based design (PBD) approaches have been considered as a better method for fire resistance design of structures because it is capable of incorporating test results of most recent fire resistance technologies. However, there is a difficulty to evaluate fireproof performance of large structures, which have multiple structural members such as columns, slabs, and walls. The difficulty is mainly due to the limitation in the testing equipment, such as size of furnace that can be used to carry out fire tests with existing criteria like ISO 834, BS 476, and KS F 2257. In the present research, a large scale calorie meter (10 MW) was used to conduct three full scale fire tests on medical modular blocks. Average fire load of 13.99 $kg/m^2$ was used in the first test. In the second test, the weighting coefficient of 3.5 (the fire load of 50 $kg/m^2$) was used to simulate the worst fire scenario. The flashover of the medical modular block occurred at 62 minutes in the first test and 12 minutes in the second test. The heat resistance capacity of the external wall, the temperatures and deformations of the structural members satisfied the requirements of fire resistance performance of 90 minutes burning period. The total heat loads and the heat values for each test are calculated by theoretical equations. The duration of burning was predicted. The predicted results were compared with the test results, and they agree quite well.

• Membrane Journal
• /
• v.15 no.2
• /
• pp.105-113
• /
• 2005

Silica membranes were prepared on a porous metal sheet by ultrasonic spray pyrolysis method for gas separation at high temperatures. In order to improve the permselectivity, silica was deposited in the sol-gel derived $silica/\gamma-alumina$ intermediate layer by pyrolysis of tetraethyl orthosilicate (TEOS) at 873 K. The pyrolysis with forced cross flow through the porous wall of the support was very effective in plugging mesopores, Knudsen diffusion regime, that were left unplugged in the membranes. At permeation temperature of 523 K, the silica/alumina composite membrane showed $H_2/N_2$ and water/methanol selectivity as high as 17 and 16, respectively, by molecular sieve effect.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.1
• /
• pp.26-33
• /
• 2004

Self-etching priming bonding system was recently developed in order to simplify the clinical skills & save chair time after continuous improvements on dentin bonding agents. To test the magnitude of microleakage of a new "self-etching priming bonding agent" using sound premolar 4th, 5th, 6th generation dentin bonding agent was applied. Measure the magnitude of infiltration to the gap of enamel-restoration interface and dentin-restoration interface. After bonding of composite resin to sample surfaces according to the manufactures direction and 500 times thermocycling on dwell time 30 second, and microleakage was measured by the ratio of the depth to the axial wall and the magnitude of infiltration. Afterward analyzed by ANOVA test. The result were as follows ; 1. Enamel groups showed lesser microleakage (Group I, II, III, IV) than dentin groups(Group V, VI, VII, VIII). (p<0.05) 2. There are no statical differences among the dentin groups, in enamel groups, group IV showed more microleakage than group I, II, III. (p<0.05). For a clinical acceptance, better enamel marginal adaptation is required.