• Fibers and Polymers
• /
• v.4 no.2
• /
• pp.71-76
• /
• 2003

We evaluated the seam characteristics with finishing, seaming and sealing processes and seam Puckering behavior of the breathable waterproof fabrics with laser scan. There were differences in 99% significant level between the seamed fabric and the sealed fabric. Seam breakage was initiated with the breakage of sewing thread, so the seam strength after seaming was almost uniform. The sewn seam strength and elongation increased with sealing process in all finishing methods. Pucker grade of laminating type was generally much higher than that of the coating type. We confirmed that wave length and amplitude have more important meaning than the number of weave in the breathable waterproof fabrics. The puckering in breathable waterproof fabrics is mainly occurred by inherent and feeding pucker. The former if due to the insertion of sewing thread and the littler is caused by differential feeding when two pieces of fabric are fed into the gap between a press foot and needle plate.

• Korean Journal of Materials Research
• /
• v.14 no.1
• /
• pp.1-8
• /
• 2004

Laser weldability of aluminized steels for deep drawing application has been investigated. Test coupons for Nd:YAG laser welding and $CO_2$ laser welding were prepared trom the commercial steels. According to the test results, total penetration and back bead width of aluminized steels were sensitive to the welding conditions. Bead width at the half thickness of the overlap joint, however, was rather constant. Laser weldability of aluminized steels was superior to that of zinc coated steel. Weld microstructure revealed that overlap zone adjacent to the fusion line was filled with coated materials, which was thought to be desirable to protect weld from crevice corrosion. The aluminum coated materials was also found in the weld metal. Practically no spattering was observed in the laser welding of aluminized steels even when the welding was performed without joint gap. In the welding of zinc coated steel, however, spattering was so severe that it was difficult to get the acceptable weld. Bead quality of aluminized steel laser weld was smooth and stable.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.212.2-212.2
• /
• 2015

본 연구에서는 용액 공정을 통해 제작한 IGZO, ITZO 박막 트랜지스터의 전기적 특성을 비교, 분석하였다. 실험에 사용된 용액의 농도는 In:Zn:Ga, In:Zn:Sn = 1:1:1로 제작하여 Spin-Coating을 통해 증착하였다. 두 소자 모두 $350^{\circ}C$에서 열처리 공정을 진행한 뒤, 전기적 특성을 측정 및 분석하였다. IGZO 박막 트랜지스터의 경우, Threshold Voltage, S.Swing, Mobility, On/Off ratio가 각각 2.2 V, 0.42, $0.18cm^2/Vs$, $1.5{\times}$10^5로 측정되었으나 ITZO 박막 트랜지스터의 경우, -6.92 V, 0.91, $0.43cm^2/Vs$, $2.1{\times}$10^5 로 IGZO보다 Negative한 방향으로 이동하였다. 이는 Sn이 Ga에 비해 Band gap이 넓고, 산소와의 결합력이 작기 때문에, ITZO 박막 트랜지스터가 Oxygen vacancy형성을 통한 Carrier density가 높은 것으로 판단된다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.04b
• /
• pp.56-59
• /
• 2000

In this study, Ferroelectric $Pb(Zr_x,Ti_{1-x})O_3$(x=0.53) thin films were fabricated by the spin-coating on the Pt/Ti/$SiO_2$/Si substrate using the PZT metal alkoxide solutions with various excess Pb contents. Etching of PZT film was performed using planar inductively coupled Ar(20)$/Cl_2/BCl_3$ plasma. The etch rate of PZT film was 2450 ${\AA}/min$ at Ar(20)$/BCl_3$(80) gas mixing ratio and substrate temperature of $80^{\circ}C$. The leakage current densities of before etching and after etching PZT thin film were $6.25\times10^{-8}A/cm^2$, $8.74\times10^{-7}A/cm^2$ with electric field of 0.07MV/em, respectively.

• Journal of the Korean Graphic Arts Communication Society
• /
• v.16 no.3
• /
• pp.29-41
• /
• 1998

The ultraviolet(UV)-curable materials wildly have been used as a ink and coating materials. A according to measure UV polymerization phase separation of acryl groups 2,3,4-functional monomer, a few experiments were performed gel fraction, dynamic viscosity of alkyd resin blend system. Dependence of photoiniator concentration and various monomer, alkyd resin content investigated structural changes of films cured by UV irradiation. Curing rate measured UV irradiation under $25^{\circ}C$, cell gap 7cm and film thickness 100${\mu}{\textrm}{m}$. In results, it was through that the viscoelastic properties of films cured with increasing the ratios of monomer/alkydresin contents are network polymer in properties such as viscoelasticity.

• Proceedings of the KIEE Conference
• /
• 2006.07d
• /
• pp.2209-2210
• /
• 2006

In this paper, PZT(20/80) thick films were fabricated by the screen-printing method. And the PZT(80/20) coating solution was synthesized by the sol-gel method. PZT(20/80) thick films were screen-printed on the alumina substrates. PZT(80/20) thin film was spin-coaled on the PZT(20/80) thick films to obtain densification. And the structural and electrical properties of PZT thick films were investigated with variation of sintering temperature. The PZT specimen sintered at $650^{\circ}C$ showed good relative dielectric constant of 219 and dielectric loss of 2.45%. Also the remanent polarization and the coercive field wore 16.48 ${\mu}C/cm^2$ and 35.48kV/cm, respectively.

• Proceedings of the KIEE Conference
• /
• 2006.07d
• /
• pp.2211-2212
• /
• 2006

Ferroelectric PZT (70/30) thick films were fabricated by the screen printing method. And the PZT (30/70) precusor solution were infiltrated by the spin-coating method on the PZT thick films to obtain a densification. All PZT thick films were sintered at $1050^{\circ}C$ for 10 min. Structural properties, such as crystalline structure, microstructures and compositional ratio, of PZT thick films were investigated with the variation of the number of sol coatings using XRD, SEM and EDS, respectively. All PZT thick films exhibited a perovskite polycrystalline structure without a pyrochloer phase. The thickness of PZT thick films, 4-times screen-printed, was approximately $60{\mu}m$. And the densification of the PZT thick films increased with increasing the number of sol coatings.

• Proceedings of the KIEE Conference
• /
• 2006.07a
• /
• pp.577-578
• /
• 2006

In this paper, PZT(20/80) thick films were fabricated by the screen-printing method. And the PZT(80/20) coating solution was synthesized by the sol-gel method. PZT(20/80) thick films were screen-printed on the alumina substrates. PZT(80/20) thin film was spin-coated on the PZT(20/80) thick films to obtain densification. And the structural and electrical properties of PZT thick films were investigated with variation of sintering temperature. The PZT specimen sintered at 650f showed good relative dielectric constant of 219 and dielectric loss of 2.45%. Also the remanent polarization and the coercive field were 16.48${\mu}C/cm^2$ and 35.48kV/cm, respectively.

• Proceedings of the KIEE Conference
• /
• 2006.07a
• /
• pp.579-580
• /
• 2006

Ferroelectric PZT (70/30) thick films were fabricated by the screen printing method. And the PZT (30/70) Precusor solution were infiltrated by the spin-coating method on the PZT thick films to obtain a densification. All PZT thick films were sintered at $1050^{\circ}C$ for 10min. Structural properties, such as crystalline structure, microstructures and compositional ratio, of PZT thick films were investigated with the variation of the number of sol coatings using XRD, SEM and EDS, respectively. All PZT thick films exhibited a perovskite polycrystalline structure without a pyrochloer phase. The thickness of PZT thick films, 4-times screen-printed, was approximately 60fm. And the densification of the PZT thick films increased with increasing the number of sol coatings.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.212-213
• /
• 2006

BSCT(60/30/10) powder specimens were fabricated by sol-gel method and BSCT thick films were fabricated by screen-printing method. The coating and drying procedure was repeated 6 times. Then the structural properties as a function of the sintering temperature. As a result of the TG-DTA, exothermic peak was observed at around $670^{\circ}C$ due to the crystalline phase. The BSCT sintered at $1430^{\circ}C$ showed the cubic perovskite structure. The prosity and thickness of the BSCT thick films was decreased with sintering temperature. The thickness of BSCT thick films at $1420^{\circ}C$ was approximately $40{\mu}m$.