• Journal of the Korean Magnetics Society
• /
• v.19 no.1
• /
• pp.12-16
• /
• 2009

Z-type barium ferrite [($Ba_{3}Co_{0.8}Zn_{1.2}Fe_{24}O_{41}$, $Ba_{3+{\delta}}Co_{0.8}Zn_{1.2}Fe_{24}O_{41}$ ${\delta}$ = 3, 5, 7, 13 wt%. $Ba_{3}Co_{0.8}Zn_{1.2}Fe_{24+{\delta}}O_{41}$ ${\delta}$ = 5, 7, 10 wt% )] were synthesized using co-precipitation method. The microstructure and magnetic properties of synthesized particles were investigated. In all prepared particles M-type Ba ferrite is identified with Z-type Ba ferrite together. It is found that particles having 7 wt% for Ba and 5 wt% for Fe excess addition revealed high saturation magnetization, respectively. All synthesized particles showed relatively high coercivity for device application. This result may be attributed to the contribution of M-type Ba ferrite. Ba and Fe excess addition was not affected to the structural change of CoZnZ Ba ferrite. The certain amount of excess additions of Ba and Fe and the 2 step heat-treatment may be beneficial to the improvement of soft magnetic properties of Z-type barium hexa-ferrite

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2002.11a
• /
• pp.25-25
• /
• 2002

• Journal of the Korean Magnetics Society
• /
• v.12 no.5
• /
• pp.195-200
• /
• 2002

Low temperature sintering of Co$_2$Z type Ba ferrites with various oxide additives has been studied. Co$_2$Z phase was obtained by 2 step calcination and XRD peaks showed a good agreement with the peaks of the standard Co$_2$Z phase, except for some minor extra peaks. ZnO-B$_2$O$_3$ glass, ZnO-B$_2$O$_3$ and CuO, ZnO-B$_2$O$_3$ and Bi$_2$O$_3$, and ZnO-Bi$_2$O$_3$ glass were added to lower sintering temperatures. Specimens were sintered at the temperature range between 900 $^{\circ}C$ and 1000 $^{\circ}C$. In the single addition of ZnO-B$_2$O$_3$ glass, the specimen with 7.5 wt％ showed the highest shrinkage. Specimens with complex addition of ZnO-B$_2$O$_3$ glass with CuO or Bi$_2$O$_3$ showed higher shrinkages and initial permeabilities than single addition of ZnO-B$_2$O$_3$ glass. Shrinkages and initial permeabilities of the specimens with ZnO-Bi$_2$O$_3$ glass were higher than those of ZnO-B$_2$O$_3$ glass addition.

• Journal of the Korean Ceramic Society
• /
• v.38 no.11
• /
• pp.1023-1029
• /
• 2001

Hexagonal ferrite $Co_2$Z(B $a_3$ $Co_2$F $e_{24}$ $O_{41}$ ) was prepared by various coprecipitation-oxidation methods. The formation of $Co_2$Z was studied in order to determine the optimal method. The $Co_2$Z composition hydroxides were prepared with the different oxidation and precipitation from the aqueous solution of $Ba^{2+}$, $Co^{2+}$ and F $e^{2+}$ chloride mixture. The coprecipitates were heat-treated at various temperatures, and their formation phases and microstructures were investigated from the analyses of DTA/TGA, powder XRD and SEM. The $Co_2$Z phase was observed in the case where the precursor will have the amorphous like oxyhydoxide($\delta$-FeOOH), and formed from $Ba_3$F $e_{32}$ $O_{51}$ , BaF $e_{12}$ $O_{19}$ (M-type) and $Ba_2$ $Co_2$F $e_{12}$ $O_{22}$ (Y-type). The $Co_2$Z was synthesized by the heat-treatment of the coprecipitate, which was prepared from the precipitation after oxidizing the chloride mixed solution, above 110$0^{\circ}C$.EX>.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.299-299
• /
• 2010

In this study, microwave properties with compositions and frequency of the $Ba_3Co_2Fe_{24}O_{41}$ ceramics with Zn substitution for Co were investigated. From the XRD patterns, hexagonal structure of Z-type phase was existed as main phase. Diffraction peaks of Z-type phase were shifted to lower angle by Zn substituted for Co site. The permittivity was increased with Zn additions. In all composition, loss tangent of permittivities were increased with frequency. Permeability and magnetic resonance frequency were increased with Zn additions. Permeability was increased and loss tangent of permeability was decreased rapidly over 600 MHz~800 MHz. The loss tangent of permeability did not changed with composition ratio. In the case of $Ba_3Co_{1.6}Zn_{0.4}Fe_{24}O_{41}$ ceramics sintered at $1250^{\circ}C$ for 3 hours, the permittivity, loss tangent of permittivity, permeability and loss tangent of permeability were 28.277, 0.193, 22.992 and 0.065 at 310 MHz, respectively.

• Journal of Industrial Technology
• /
• v.28 no.A
• /
• pp.119-123
• /
• 2008

Structural and magnetic properties of $CO_{1-x}Zn_xZ$ ($Ba_3Co_{1-x}Zn_xFe_{24}O_{41}$) hexa-ferrite are studied using XRD, VSM and SEM, respectively. Powder was prepared from co-precipitation and firstly heat treated at $1350^{\circ}C$ for 6 hours in $O_2$ atmosphere. Second heat treatment was performed at 900, 1000, $1100^{\circ}C$ for 6 hours in air, respectively. Saturation magnetization value of first heat treated powder is acceptable and coercivity is high for applying to device. These result may be originated from incomplete formation reaction from M and Y phases to Z phase. Second heat treatment leads to small value of coercivity.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.60 no.12
• /
• pp.2270-2275
• /
• 2011

The sintering behavior and microwave properties of ferrite ($Ba_3Co_{2-2x}Zn_{2x}Fe_{24}O_{41}$ ceramics) were investigated for microwave applications. Also PIFA type antenna with ferrite was simulated. All samples were prepared by the solid state reaction method and sintered at $1350^{\circ}C$. All ceramics had relatively density above of 92% compare with theoretical density of $Ba_3Co_2Fe_{24}O_{41}$ ceramics. From the XRD pattens, the Z-type phase was existed as main phase in $Ba_3Co_{2-2x}Zn_{2x}Fe_{24}O_{41}$ ceramics. The permittivity and permeability of $Ba_3Co_{2-2x}Zn_{2x}Fe_{24}O_{41}$ ceramics were increased with Zn additions and decreased rapidly over frequency of 200~600 MHz. Several PIFA type antennas with ferrite and FR4 were simulated. All antenna structure had return loss of less than -10 dB at each resonant frequency. Simulated antenna using both ferrite and FR4 showed size reduction of 25% without a significant decrement of efficiency.

• Journal of the Korean Magnetics Society
• /
• v.24 no.1
• /
• pp.1-10
• /
• 2014

$Co_2Z$-type barium ferrites ($Ba_3Co_2Fe_{24}O_{41}$) were synthesized using variation method. First, M-type, $Co_2Y$-type and $Co_2Z$-type synthesized by hydrothermal method. Second, M- and Y-type precursors for synthesis of $Co_2Z$ hexaferrite by hydrothermal and ball milling method. the morphology, structure and magnetic properties of the barium ferrite particles were characterized using XRD, FESEM, VSM, impedance. As a result, Single phase of M-type and $Co_2Y$-type were obtained. Manufactured powders of M+Y ball milling, M+Y hydrothermal were similar to single phase of $Co_2Z$-type hexaferrite, all powders were obtained theoretical magnetization (50 emu/g). The largest initial permeability were obtained $Co_2Z$ hexaferrite synthesized by reagent precusor, With increasing calcination temperature was lowered the initial permeability. In another synthesis didn't almost that little change could be found.

• Journal of Electrical Engineering and Technology
• /
• v.9 no.1
• /
• pp.273-279
• /
• 2014

Hexagonal Ba-ferrites are widely suggested as materials for small antennas. In this paper, the sintering behavior and magneto-electric properties of $Ba_3Co_{2-2x}Mn_{2x}Fe_{24}O_{41}$ ($0.1{\leq}x{\leq}0.5$) ceramics were investigated for small antenna application. All samples of $Ba_3Co_{2-2x}Mn_{2x}Fe_{24}O_{41}$ ceramics were prepared by the solid-state reaction method and sintered at $1250^{\circ}C$. From the XRD patterns of the sintered $Ba_3Co_{2-2x}Mn_{2x}Fe_{24}O_{41}$ceramics, the Z-type phases were found to be the main phases. The real part of permittivity and permeability of the $Ba_3Co_{2-2x}Mn_{2x}Fe_{24}O_{41}$ceramics decreased with frequency. On the other hand, loss tangents of permittivity and permeability tended to behave opposite to real part of permittivity and permeability. The real part of permeability was affected by Mn additions. The real part of permittivity, the loss tangent of permittivity and the real part of permeability, the loss tangent of permeability of $Ba_3Co_{0.2}Mn_{0.8}Fe_{24}O_{41}$ ceramics were 19.774, 0.176 and 15.183, 0.073, respectively, at 510 MHz. In order to investigate the effect of magneto-dielectric ceramics on antenna, PIFA (Planar Inverted F Antenna) was simulated with CST (Computer Simulation Technology). The operating frequency of antenna was decreased without considerable change of bandwidth by using the $Ba_3Co_{0.2}Mn_{0.8}Fe_{24}O_{41}$ ceramics as the carrier.