• Restorative Dentistry and Endodontics
• /
• 제26권1호
• /
• pp.16-22
• /
• 2001

The purpose of this study was to evaluate the marginal microleakage of condensable composite resin restorations according to flowable resin lining of internal cavity wall. The eighty extracted human molar teeth without caries and/or restorations are used The experimental teeth were randomly assigned into four groups of ten teeth each. Eighty caries-free extracted human molars were used in this study. The conventional class II cavities (box-shaped on mesial and distal surface, faciolingual width : 3mm, gingival wall depth : 1.5mm) were prepared 1mm below cementoenamel junction with a # 701 carbide bur. The teeth were divided into four groups, and then each group were subdivided into A & B group according to flowable resin & compomer lining ; Group 1-A : Tetric Ceram filling, Group 1-B : Tetric Flow lining and Tetric Ceram filling, Group 2-A Ariston pHc filling, Group 2-B : Tetric Flow lining and Ariston pHc filing, Group 3-A SureFil filling, Group 3-B : Dyract Flow lining and SureFil filling, Group 4-A : Pyramid filling, Group 4-B : Aeliteflo lining and Pyramid filling. To simulate as closely as possible the clinical situation during retoration placement, a "restoration template" was fabricated, and the condensable resin was filled using a three-sited light-curing incremental technique. All the materials used were applied according to the manufacturers' instructions. The specimens were stored in the 100% humidity for 7 days prior to thermocycling (100 thermal cycles of 5~55$^{\circ}C$ water with a 30-second dwell time) The specimens were immersed in 2% metyleneblue dye for 24 hours, and then embedded in transparent acrylic resin and sectioned mesiodistally with diamond wheel saw. The degree of marginal leakage was scored under stereomicroscope ($\times$20) and the data were analyzed by Kruskal-Wallis test and Wilcoxon signed ranks test. The results were as follows : 1. In the gingival margins of all the group, microleakage of subgroup B was less than subgroup A. 2. In the group 1, 2, 4, there was significant differences between subgroup A and B (p<0.05), but in the group 3, there was not significant different between group 3-A (SureFil) and group 3-B (Dyract flow/SureFil) (p>0.05). 3. In the subgroup A and B, there was significant different between all group except group 4 of subgroup A. From the results above, it was suggested that the cavity lining of flowable resin and flowable compomer in condensable resin restoration decrease microleakage at gingival margin, and does improve their ability to seal the gingival margin of class II preparation.

• 대한소아치과학회지
• /
• 제27권1호
• /
• pp.54-61
• /
• 2000

아말감은 널리 사용되어 온 대표적 치과재료이지만 치질과의 접착성이 없어 와동의 형태에 의해 유지되는 단점을 가진다. 아말감 수복물은 산화물에 의한 변연봉쇄가 일어나기 전까지 초기에 큰 미세누출을 보이며 수복초기에 이를 적절하게 예방하지 않으면 타액이나 미생물이 와동내에 침투하게 되고 이로 인해 수복 후의 과민반응, 충전물의 용해 및 파괴, 변연 변색과 2차 우식이 유발되어, 결과적으로 수복물의 수명이 단축되며 치수 병변이 발생될 수도 있다. 최근 기존 아말감 수복의 장점을 그대로 유지하면서 치질삭제를 줄이고 변연을 봉쇄하며 소와열구에 예방적 처치를 함께 할 수 있는 수복법이 제안되었는데 이를 이른바 sealed amalgam이라 한다. 이 술식은 예방적 확대 없이 병소만을 제거한 뒤 수복물 변연과 인접 소와열구에 치면열구전색재를 도포함으로서 소와열구의 예방적 충전은 물론 수복물 변연과 치질사이의 틈을 봉쇄하여 미세누출을 감소시킬 수 있다고 하였다. 이에 저자는 아말감 수복후 수복물의 마무리 처리와 전색재 적용시점을 달리 하여 sealed amalgam 수복과 기존의 아말감 수복과의 미세누출의 차이를 비교하고자 30개의 상, 하악 소구치를 준비하여 V급 와동을 소구치의 협, 설측에 형성하고 통상적 아말감 수복을 시행한 후 다음의 각 군으로 나누어 처리하였다. 제 1 군 : 24시간 후 연마 (대조군) 제 2 군 : 연마하지 않음, 즉시 전색재 적용 제 3 군 : 연마하지 않음, 열순환(thermocycling) 500회 후 전색재 적용 위의 처리 후 각 군을 $5^{\circ}C$와 $55^{\circ}C$의 온도변화를 30초씩 번갈아 주며 총 500회의 열순환을 실시한 후 1% methylene blue 용액에 침윤시켜서 100% 습도가 유지된 $37^{\circ}C$ 항온기에 24시간 보관하였다. 치아를 레진에 매몰한 후 협설측으로 치아 장축에 평행하게 절단하여 stereomicroscope를 사용해 색소침투도를 관찰하여 다음과 같은 결론을 얻었다. 1. 평균 미세누출은 연마하지 않고 바로 치면열구전색재를 도포한 2군이 가장 낮았고, 연마만 시행한 1군이 가장 높았다. 2. 실험군간의 미세누출 비교에서 연마만 시행한 1군은 2군에 비해 미세누출이 켰으며 통계적으로 유의성 있는 차이를 보였다(p<0.05). 3군은 1군보다 평균미세누출이 작았으나 통계적으로 유의한 차이가 없었다(p>0.05). 2군은 3군보다 평균 미세누출이 작았으나 통계적으로 유의한 차이가 없었다(p>0.05).

• 대한소아치과학회지
• /
• 제23권3호
• /
• pp.746-763
• /
• 1996

An alternative design to conventional class II cavity preparation for proximal carious lesions is the tunnel preparation. It preserves the marginal ridge intact, thus making it possible to maintain the natural contact relationship with the adjacent tooth and minimize tooth reduction. This in vitro study was purposed to evaluate the effect of the materials' elastic constants and shear-bond strength on the marginal ridge fracture resistance of teeth restored by the tunnel technique, and to find the materials of choice for tunnel restorations. $Resinomer^{(R)}$, $Ketac-silver^{(R)}$, $Miracle-Mix^{(R)}$, and Tytin were used as restorative material. The elastic constants of each restorative material were evaluated by ultrasonic pulse measurement. Young's modulus and bulk modulus of the restorative materials were evaluated in three specimens for each material type. The shear-bond strength of the restorative materials to the dentin surface was measured after thermocycling 400 times between 6 and $60^{\circ}C$, using ten specimens for each material type. For measuring marginal ridge strength, 60 sound extracted molar teeth were distributed into six groups by size. Sound molar teeth were used as a Control group and unfilled prepared teeth were grouped as Unrestored. Another four groups were named Resinomer group, Ketac-Silver group, Miracle Mix group, and Tytin group by type of restorative material. Tunnel cavity preparation was done with ' 1/2, 2, and 4 round burs in sequence. Initial access to proximal surface was made through an occlusal access preparation started at least 2mm from the marginal ridge, and the proximal opening was formed about 2.5mm below the marginal ridge. After restoration and thermocycling, marginal ridge strength was measured using a universal testing machine. The results were as follows: 1. The Young's modulus of $Tytin^{(R)}$ was 63.95 GPa, followed by $Ketac-Silver^{(R)}$ 27.60 GPa, $Miracle-mix^{(R)}$ 18.48 GPa, and $Resinomer^{(R)}$ 10.74 GPa showing significant differences between the groups(P<0.05). The bulk modulus of the materials showed the same order as Young's modulus. The value of $Tytin^{(R)}$ showed 59.57 GPa indicating that it will deform less than other materials under the same stress. It was followed by $Ketac-Silver^{(R)}$ 23.57 GPa, Miracle $Mix^{(R)}$ 12.50 GPa, and $Resinomer^{(R)}$ 11.60 GPa. 2. The Resinomer group had a shear-bond strength of 7.41 MPa which was significantly higher than those of the Ketac-Silver group (1.80 MPa) and the Miracle Mix group (2.84 MPa) (P<0.01). All the specimens of Tytin group detatched from the dentin surface during thermocycling. 3. The mean marginal ridge strength of the Unrestored group(46.14 kgf) was significantly lower than that of the Control group (84.24 kgf) (P<0.01). The marginal ridge strength of teeth restored by the tunnel technique was, in order, Ketac-Silver group 74.06 kgf, Miracle Mix group 73.36 kgf, Resinomer group 63.47 kgf, and Tytin group 58.76 kgf. The Ketac-Silver, Miracle Mix, and Resinomer groups showed no significant difference with the Control group (P>0.05), but the Tytin group showed significantly lower strength compared to the Control group(P<0.05). The results showed that the marginal ridge strength of the teeth restored by the tunnel technique was not significantly lower than that of sound teeth. They also demonstrated that the bonding strength of the restorative material to the tooth surface should be high and the modulus of elasticity should not be lower than that of the tooth in order to restore the marginal ridge strength to its natural condition.

• Restorative Dentistry and Endodontics
• /
• 제31권6호
• /
• pp.460-469
• /
• 2006

본 연구는 환자의 성별, 치료 부위 , 와동 형태 , 기존 수복물의 재료에 따른 구치부 재수복에 관하여 보고하고자 한다. 2003년 12월 1일부터 2004년 10월 31일까지 구치부의 재수복을 위해 보존과를 내원한 824명의 환자의 1206개의 치아를 실험재료로 택하였으며 영구치로 제한하였다. 환자의 성별 및 연령, 치료 부위, 와동 형태, 기존 수복물의 재료와 기존 수복물의 내원 당시 상태를 변연 적합성, 해부학적 형태, 이차 우식에 대해 modified Ryge criteria system으로 기록하였다. 환자 및 치아 요소에 따른 재수복율은 카이 제곱 검정으로, 각 재료별 기존 수복물의 상태는 One-way ANOVA로 분석하였다. 구치부 수복물의 재수복은 환자의 성별, 연령 , 치아 위치, 기존 수복 재료에 따른 차이가 존재함을 알 수 있었다.

• Restorative Dentistry and Endodontics
• /
• 제16권2호
• /
• pp.43-61
• /
• 1991

Present - day inlay casting procedures have been developed for more than 100 years and experimentation has focused on the perfect adaptation to the cavity preparation. Marginal adaptation is considered to be an important indicator of the acceptability of the cast restotration, especially on the gingival margin. The purpose of this study was to evaluate the effects of a dissecting microscope and burnishing on vertical discrepancies, horizontal discrepancies, and cement thicknesson master die. Extracted premolars were prepared for class II gold inlays and master dies were made with conventional techniques. The experiments consisted of 4 groups. Group 1 : unaided eye, no burnishing on master die. Group 2 : unaided eye, burnishing on master die. Group 3 : microscope, no burnishing on master die. Group 4 : microscope, burnishing on master die. Cemented inlays were embedded in the hard resin and sectioned with microcutter through the gingival margins. The sectioned surfaces were polished with emery paper and finally with aluminum oxide powders. The results of the experiments were measured for vertical discrepancies, horizontal discrepancied and cement thickness under the scanning electron microscpe at the beveled gingival margin. The results of the study were summarized as follows. 1. Group 1 showed the vertical discrepancies of $81.6{\mu}m({\pm}48.6{\mu}m)$, horizontal discrepancies of $60.1{\mu}m({\pm}41.1{\mu}m)$, and cement thickness of $59.6{\mu}m({\pm}24.6{\mu}m)$. 2. Group 2 showed the vertical discrepancies of $78.6{\mu}m({\pm}30.9{\mu}m)$, horizontal discrepancies of $36.9{\mu}m({\pm}20.7{\mu}m)$, and cement thickness of $54.0{\mu}m({\pm}21.6{\mu}m)$. 3. Group 3 showed the vertical discrepancies of $57.5{\mu}m({\pm}26.4{\mu}m)$, horizontal discrepancies of $28.4{\mu}m({\pm}17.5{\mu}m)$, and cement thickness of $37.2{\mu}m({\pm}17.4{\mu}m)$. 4. Group 4 showed the vertical discrepancies of $56.7{\mu}m({\pm}35.0{\mu}m)$, horizontal discrepancies of $31.8{\mu}m({\pm}24.2{\mu}m)$, and cement thickness of $45.6{\mu}m({\pm}19.8{\mu}m)$. 5. Vertical discrepancies were not significantly different at any groups(p>.050). 6. Microscope groups(Group 3, 4) showed significantly improved horizontal marginal adaptation (p<.050). 7. Although cement thickness showed the subset of Group 3. 4, 2 and Group 4, 2, 1. Group 3 showed significantly smaller thickness than Group l(p<.050). 8. Finishing and polishing by means of a microscope produced significantly smaller discrepancies than doing so with the unaided eye(p<.050).

• 구강회복응용과학지
• /
• 제32권3호
• /
• pp.184-193
• /
• 2016

목적: 중합 시간이 bulk fill 유동성 복합레진의 미세누출에 미치는 영향을 마이크로시티를 이용하여 평가하고자 하였다. 연구 재료 및 방법: 30개의 발거된 인간 대구치에 변형된 2급 와동인 vertical slot cavity를 형성하였다. SonicFill과 SureFil SDR flow을 단일 충전하였으며, 다른 중합시간(20, 40, 60초)으로 광중합 하였다. 모든 표본은 5000번의 thermal cycle을 시행하였다. 치아는 silver nitrate 용액에 24시간 동안 침전 후 8시간 동안 현상액에 침전하였다. 마이크로시티를 사용하여 시편을 촬영 후 침투된 silver nitrate solution을 3차원적으로 재건하여 그 부피를 측정하였다. 변연 누출 결과값의 통계 처리는 Mann-Whitney test를 사용하였다. 결과: 광중합 시간의 증가는 두 bulk fill 유동성 복합레진에서 변연 누출을 증가시켰다. 두 복합레진 사이 유의한 차이는 없었다. 결론: 중합 시간은 bulk fill 유동성 복합레진의 변연 누출을 증가시킬 수 있는 요인이었다. 또한 마이크로시티를 통해 레진-치아 계면에서 변연 누출의 양을 비파괴적 방법으로 3차원적으로 재건하여 측정할 수 있었다.

• 대한소아치과학회지
• /
• 제33권4호
• /
• pp.653-660
• /
• 2006

Fuji VII은 제 1, 2대구치의 조기보호를 목적으로 소개되었으며 기존의 글래스 아이오노머 시멘트보다 많은 양의 불소를 유리하면서도 점도가 낮아 흐름성이 우수하고 부가적인 산부식 과정이 필요 없는 특징 때문에 치은판개가 일부 덮인 제 1, 2대구치의 교합면이나 일부만 노출된 대구치 협면구의 우식 예방과 재광화에 유용하다고 하였다. 본 연구의 목적은 Fuji VII의 재광화 효과를 알아보고 기존의 글래스 아이오노머 시멘트, 레진 강화형 글래스 아이오노머 시멘트, 콤포머와 복합레진의 재광화 효과를 비교하고자 하였다. 이에 인공적으로 형성한 우식을 가진 42개의 치아에 Fuji VII, Fuji II, Fuji II LC improved F2000, $Filtek^{TM}$ Z250의 재료를 충전하고 편광현미경 상에서 충전 직후와 4주 후 탈회 면적을 측정하였으며 두 면적의 차이를 비교하여 다음의 결과를 얻었다. 1. 재광화 정도는 Fuji VII, Fuji II, Fuji II LC improved, F2000, 대조군, $Filtek^{TM}$ Z250 순으로 크게 나타났으며, 글래스 아이오노머 계통의 Fuji VII, Fuji II, Fuji II LC improved에서 F2000, $Filtek^{TM}$ Z250, 대조군에 비해 유의한 재광화가 나타났다(p<0.05). 2. Fuji VII과 Fuji II Fuji II LC improved 간에는 유의한 재광화 정도의 차이는 관찰되지 않았다(p>0.05).