• Journal of the Korean institute of surface engineering
• /
• v.54 no.3
• /
• pp.139-143
• /
• 2021

Cr-Al-N coatings were deposited onto WC-Co substrates using a cathodic arc evaporation (CAE) system. CAE technique is recognized to be a very useful process for hard coatings because it has many advantages such as high packing density and good adhesion to metallic substrates. In this study, the influence of deposition temperature as a key process parameter on film growth behavior and mechanical properties of Cr-Al-N coatings were systematically investigated and correlated with microstructural changes. From various analyses, the Cr-Al-N coatings prepared at deposition temperature of 450℃ in the CAE process showed excellent mechanical properties with higher deposition rate. The Cr-Al-N coatings with deposition temperature around 450℃ exhibited the highest hardness of about 35 GPa and elastic modulus of 442 GPa. The resistance to elastic strain to failure (H/E ratio) and the index of plastic deformation (H³/E² ratio) were also good values of 0.079 and 0.221 GPa, respectively, at the deposition temperature of 450℃. Based on the XRD, SEM and TEM analyses, the Cr-Al-N coatings exhibited a dense columnar structure with f.c.c. (Cr,Al)N multi-oriented phases in which crystallites showed irregular shapes (50~100nm in size) with many edge dislocations and lattice mismatches.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.8 no.1
• /
• pp.41-48
• /
• 2010

Uranium deposits from an electrorefining process contain about 30% salt. In order to recover pure uranium and transform it into an ingot, the salts have to be removed from the uranium deposits. Major process variables for the salt distillation process of the uranium deposits are hold temperature and vacuum pressure. Effects of the variables on the salt removal efficiency were studied in the previous study[1]. By applying the Hertz-Langmuir relation to the salt evaporation of the uranium deposits, the evaporation coefficients were obtained at the various conditions. The operational conditions for achieving above 99% salt removal were deduced. The salt distilled uranium deposits tend to form the eutectic melt with iron, nickel, chromium for structural material of salt evaporator. In this study, we investigated the hold temperature limitation in order to prevent the formation of the eutetic melt between urnaium and other metals. The reactions between the uranium metal and stainless steel were tested at various conditions. And for enhancing the evaporation rate of the salt and the efficient recovery of the distilled salt, the thermal analysis of the salt distiller was conducted by using commercial CFX software. From the thermal analysis, the effect of Ar gas flow on the evaporation of the salt was studied.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.11a
• /
• pp.83.2-83.2
• /
• 2010

평판형 고체산화물 연료전지(planar SOFC : Solid oxide Fuelcell)는 높은 전류 효율 및 출력밀도를 가지는 중,대형 발전용 전기소자이다. SOFC 스택을 600~800도에서 작동할 경우, 금속 분리판에서 휘발된 크롬에 의한 열화현상과 금속의 산화에 의한 표면 저항의 증가가 큰 문제점으로 알려져 있으며, 이를 개선하기 위한 많은 연구가 진행되고 있다. 본 연구에서는 금속 분리판의 열화를 억제하기 위한 여러 보호코팅의 특성을 밝히고, 특성차이의 원인을 분석하고자 하였다. 모재는 상용 STS444합금 (Nisshin steel 생산) 2.0mmt 박판을 사용하였으며, 표면 상태를 균일하게 하기 위하여 표면은 동일한 #1200 번 사포로 연마후 코팅하였다. 적용한 코팅은 전기도금 Ni 코팅, (MnCo)3O4 wet powder spray 코팅, (MnCo)3O4 ADM코팅 3종이었으며, 코팅층의 두께는 최적 공정조건에 따라 달리 하였다. 산화후 형성되는 표면 산화물의 전기적 특성을 평가하기 위하여 시험편의 비면적 저항 (ASR : area specific resistance)을 장시간 측정하였다. 측정편의 크기는 가로 4cm ${\times}$ 세로 4cm였으며, 100시간 공기중 산화후 측정하였다. 표면 접촉을 높이기 위하여 Pt paste를 40~50um도포하였으며, 1~0.1A인가된 전류에 대한 저항을 4전극법 (4-probe)으로 측정하였다. 표면 코팅층이 크롬 휘발을 억제하는 정도를 평가하기 위하여 크롬 휘발량을 측정하였다. 시편은 가로 1.5cm ${\times}$ 세로 1cm 였으며, 공급된 공기와 수분의 혼합가스와 응축기 표면에 흡착된 크롬의 양을 ICP-MASS법으로 측정하였다.