• 한국연소학회:학술대회논문집
• /
• 2012.04a
• /
• pp.37-40
• /
• 2012

In an entrained flow coal gasifier, predicting the reaction behavior of pulverized coal particles requires detailed information on devolatilization, char gasification, gaseous reactions, turbulence and heat transfer. Among the input parameters, the rate of devolatilization and the composition of volatile species are difficult to determine by experiments due to a high pressure (~40 bar) and temperature (${\sim}1500^{\circ}C$). This study investigates the effect of devolatilization models on the reaction and heat transfer characteristics of a 300 MWe Shell coal gasifier. A simplified devolatilization model and advanced model based on Flashchain were evaluated, which had different volatiles composition and devolatilization rates. It was found that the tested models produce similar flow and reaction trends, but the simplified model slightly over-predict the temperature and wall heat flux near the coal inlets.

• Textile Coloration and Finishing
• /
• v.20 no.4
• /
• pp.31-42
• /
• 2008

Tricrecyl phosphate(TCP)-containing polyurea microcapsules were prepared by interfacial polymerization using aromatic 2,4-toluene diisocyanate(TDI) and ethylenediamine(EDA) as wall forming materials. The effects of the protective colloids of polyvinylalcohol(PVA) and gelatin were investigated through experimentation. The mean size of prepared polyurea microcapsules was smaller and the surface morphology of the microcapsule prepared by the PVA as protective colloid was much smoother than the gelatin. As the concentration of protective colloid increased, the wall membrane of the polyurea microcapsules became more stable, the thermal stability of the wall membrane increased, the mean particle size became smaller, and the particle distribution was more uniform. PET containg microTCPs have a higher activation energy of decomposition, higher char content and lower heat of combustion.

• Journal of Energy Engineering
• /
• v.1 no.1
• /
• pp.76-86
• /
• 1992

A three-dimensional model has been developed for pulverized coal combusters and gasifiers. Coal devolatilization, heterogeneous char oxidation, gas particle interchange, radiation, gas phase oxidation, primary and secondary stream mixing, and heat losses are considered. A finite difference method was used to solve the ordinary non-linear differential equations. The effects of primary and secondary stream flow ratio and coal particle size are investigated.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.45 no.1
• /
• pp.42-51
• /
• 2013

In this study, oil palm biomass such as empty fruit bunch (EFB) and palm kernel shell (PKS) was used as raw materials for making pellets. Hardwood sawdusts were also mixed with EFB and PKS for making pellets. For improving a bad forming behavior in a pelletizer, 1 to 3 per cent of corn starch based on oven-dried weight biomass was added. The starch contributed to the decrease of dust generation in addition to the improvement of forming capability during pellet forming. Heating values of every pellets made of EFB and PKS were higher than 4,300 kcal/kg for the first grade pellet, irrespective of addition of sawdusts. However, the pellets made of EFB and PKS had ash contents over 3 per cent, which made it impossible to be applied for home use. Instead, they could be applied for industrial use. For studying their combustion characteristics, the pellets from the mixtures of EFB, PKS and sawdusts were analyzed using thermal gravimetric analyzer (TGA). From the TGA results, thermal decomposition of EFB and PKS occurred following three including endothermic reaction and dehydration, devolatilization of the major chemical components, and finally combustion of residual lignin and char.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2010.11a
• /
• pp.257-260
• /
• 2010

The purpose of this paper is to introduce a method to predict the case thermal insulation charred and erosion thickness as a function of the exposure time to combustion gases and in solid rocket motors. The sizing of the insulator requires a good estimation of the thermal and mechanical loads at the wall. The method is particularly suitable for internal insulation areas subjected to high radiative, convective heat fluxes and $Al_2O_3$ slag pool. The mathematical approach and lab-scale experiment were intentionally simplified in order to obtain some simple and rapid relationships particularly useful for trade-off studies and thermal insulation preliminary design. The method was utilized to compute the charred and erosion thicknesses of the insulation on the aft chamber domes. A comparison between theoretical and experimental insulator char thicknesses of the motor insulation is reported, indicating the applicability of the predictive method employed.

• Journal of the Korean Society of Safety
• /
• v.24 no.6
• /
• pp.63-71
• /
• 2009

In order to improve flame retardancy, the halogen free organic melamine phosphate(M-P) flame retardant was synthesized from melamine and phosphoric acid by the reaction of precipitation. The ignition test was carried out preparing hybrid flame retardant compound($H_bFRC$) consisting of organic M-P and inorganic Mg$(OH)_2$ as a flame retardant in the polyolefin resins. The flame retardancy and mechanical properties of flame retardant aluminum composite panel($H_bFRC$-ACP) were performed to investigate the possibility of the composite material, which was contained M-P, as a inner core for $H_bFRC$-ACP. For this study, the results of ignition test indicate that a char formation and drip suppressing effect, and combustion time reduced as the content of M-P increased. The limited oxygen index(LOI) values were measured 17.4vol% and 31.5vol% for LDPE only and $H_bFRC$-3(M-P content: 15wt%), respectively. And it was verified that the $H_bFRC$-3 was needed more oxygen quantity with the increase of M-P content when it combustion. Also, the results from thermogravimetric analysis were observed endothermic peak at $350^{\circ}C$ and $550^{\circ}C$, it was confirmed predominant thermal stability though the wide temperature range by the mixture of M-P and Mg$(OH)_2$. The LDPE-ACP (using only LDPE as a inner core), $35.13kW/m^2$ of heat release rate(HRR) and 13.43MJ/m2 of total heat release(THR) were measured while the $H_bFRC$-ACP, $10.44kW/m^2$ of HRR and 1.84MJ/m2 of THR were measured by results of cone calorimeter test. In case of $H_bFRC$-ACP, the average gas emission amount of CO and $CO_2$ could be decreased down to 25% and 20%, respectively, in comparison with LDPE-ACP. The mechanical properties such as tensile strength, bending strength and adhesion strength of $H_bFRC$-ACP were revealed slightly high values $54N/mm^2$, $152N/mm^2$ and 120N/25mm, respectively, compared with LDPE-ACP. It was confirmed that flame retardancy was improved with the synergy effect because of char formation by M-P and hydrolysis by Mg$(OH)_2$. The result of this study suggest that $H_bFRC$ can be applied for an adequate halogen free flame retardant composite material as a inner core for ACP.

• Elastomers and Composites
• /
• v.47 no.4
• /
• pp.355-363
• /
• 2012

A series of poly(hydroxyamide)s (PHAs) having trifluoromethyl group were prepared by direct polycondensation of aromatic diimide-dicarboxylic acids with 2,2-bis(3-amino-4-hydroxyphenyl)hexafluoropropane by thionyl chloride and triethyl amine in N-methyl-2-pyrrolidinone (NMP). The PHAs exhibited inherent viscosity in the range of 0.54-0.96 dL/g at $35^{\circ}C$ in DMAc solution. All PHAs were readily soluble in a variety of organic solvents, whereas the polybenzoxazoles (PBOs) were quite insoluble except partially soluble in sulfuric acid. PHAs were converted to PBOs by thermal cycling reaction with heat of endotherm. The maximum weight loss temperature of the PHAs occurred in the range of $559-567^{\circ}C$. The PBOs showed relatively high char yields in the range of 47-59%. Pyrolysis Combustion Flow Calorimeter (PCFC) results of the PBOs showed 12-19 W/g heat release rate (HRR), and 2.7-3.6 kJ/g total heat release (total HR). The HRR of PBO 1 showed the lowest value of 12 W/g, which was 37% lower than that of PBO 3 (19 W/g).

• Fire Science and Engineering
• /
• v.28 no.5
• /
• pp.71-79
• /
• 2014

This study was performed to test the combustive properties of Medium Density Fibreboards (MDFs) treated with chemicals of the bis-(dimethylaminomethyl) phosphinic acid (DMDAP), N,N-dimethylethylenediaminomethyl-bis-phosphonic acid (DMDEDAP), piperazinomethyl-bis-phosphonic acid (PIPEABP), and methylpiperazinomethyl-bis-phosphonic acid (MPIPEABP). MDFs were painted in three times with 15 wt% solution of the bis-(dimethylaminomethyl) phosphinic acid and alkylenediaminoalkyl-bis-phosphonic acids at the room temperature, respectively. After drying MDF treated with chemicals, combustive properties and volatile organic compounds (VOCs) contents were examined by the cone calorimeter (ISO 5660-1), test for flame retardant (NEMA Notice No. 2012034), and gas chromatography (KS M ISO 11890-2), respectively. It was indicated that the MDFs treated with chemicals showed the longer time to combustion time (CT) = (442~492) s than that of virgin plate by reducing the burning rate except for CT treated with DMDAP. In adition, the MDFs treated with chemicals showed both of the higher char area (44.33~61.33) kg/kg and char length (10.33~11.67) cm than those of virgin plate. Especially, the MDFs treated with chemicals showed the higher mean volatile organic compounds (VOCs) (0.188~0.333) g/L than that of virgin plate within the prescribed limits. Thus, It is supposed that the combustion- retardation properties were improved by the partial due to the treated chemicals in the virgin MDF.

• Journal of the Korean Institute of Gas
• /
• v.26 no.3
• /
• pp.27-37
• /
• 2022

With the recent increase in the spread of ESS (Electric Storage System), the damage to human life and property is also rapidly increasing due to continuous fires caused by ESS. In the manufacture of urethane sandwich panels used in ESS, it is necessary to improve the flame retardant performance. In this study, in order to realize the flame retardant properties of flexible polyurethane foam, the effect of the tissue density of the product due to the change of the isocyanate functional group parameter that changes the physical properties of the product on the fire performance was studied. The product was manufactured by changing the density of the urethane structure, and combustion performance tests, gas toxicity tests, and smoke density tests were performed. As a result, it was confirmed that the total amount of heat released had excellent performance when the isocyanate functional group was high, and had no correlation with the maximum heat release rate. When the value of the isocyanate functional group was 2.7 or more, the collapse of the shape could be prevented. In the gas hazard test, the performance was increased when the isocyanate functional group was relatively high, so a flame retardant for the Char system, which had a dense structure and easy to form a carbonized film, was added. confirmed to be. Therefore, as a result of this study, it is thought that it will be possible to lay the foundation for the development of a flame retardant to replace the cheap urethane sandwich panel used in the past.

• Journal of Aerospace System Engineering
• /
• v.11 no.5
• /
• pp.42-49
• /
• 2017

The solid rocket motor(SRM) consists of a motor case, igniter, propellants, nozzle, insulation, controller, and driving device. The liquid rocket propulsion systems(LRPSs) cools the nozzle by the fuel and oxidizer but SRM does not cool the nozzle. The nozzle of SRM is high temperature condition and high velocity condition so occurs the erosion by combustion gas. This erosion occurs the change of nozzle throat and reduces thrust performance of rocket. The material of Rocket nozzle is minimization of erosion and insulation effect and endure the shear force, high temperature and high pressure. The purpose of this study is to investigate the erosion characteristics of solid rocket nozzles by each combustion time. Through the structure inspection of Graphite and C-C composite, identify the characteristics of the microstructure before and after erosion.