• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.32 no.6
• /
• pp.477-482
• /
• 2019

This study investigated the influence of the viscoelastic property of slag when producing glass fiber, MFS631 with 60% of manganese slag, 30% of steel slag, and 10% of silica stone. To fabricate the MFS631 glass bulk, slag materials were placed in an alumina crucible, melted at $1,550^{\circ}C$ for 2 h, and then annealed at $600^{\circ}C$ for 2 h. It was found that glass is non-crystalline through X-ray diffraction analysis. MFS631 fiber was produced at speed in the range of 100~300 rpm at $1,150^{\circ}C$. The loss modulus (G") and storage modulus (G') of the produced glass fiber were evaluated at high temperatures. G' and G" of MFS631 were greater than $893^{\circ}C$, and the modulus value was 136,860 pa. This is similar to the results of a general E-glass fiber graph. Therefore, it was concluded that its spinnability is similar to that of E-glass fiber; therefore, it can be commercialized.

• Journal of the Korean Ceramic Society
• /
• v.56 no.6
• /
• pp.526-533
• /
• 2019

Indialite/cordierite glass-ceramics demonstrate excellent microwave dielectric properties such as a low dielectric constant of 4.7 and an extremely high quality factor Qf of more than 200 × 10³ GHz when crystallized at 1300℃/20 h, which are essential criteria for application to 5G/6G mobile communication systems. The glass-ceramics applied to dielectric resonators, low-temperature co-fired ceramic (LTCC) substrates, and direct casting glass substrates are reviewed in this paper. The glass-ceramics are fabricated by the crystallization of glass with cordierite composition melted at 1550℃. The dielectric resonators are composed of crystallized glass pellets made from glass rods cast in a graphite mold. The LTCC substrates are made from indialite glass-ceramic powder crystallized at a low temperature of 1000℃/1 h, and the direct casting glass-ceramic substrates are composed of crystallized glass plates cast on a graphite plate. All these materials exhibit excellent microwave dielectric properties.

• Journal of the Korean Ceramic Society
• /
• v.50 no.1
• /
• pp.57-62
• /
• 2013

We investigated the thermal and electrical properties of the $B_2O_3-ZnO-Bi_2O_3$ glass system as a sealing material in sheath heater modules. A composition with over 90 wt% $Bi_2O_3$ in the $B_2O_3-ZnO-Bi_2O_3$ system was glassified by controlling the cooling rate. The glass transition temperature and thermal expansion coefficient in bismate glass could be controlled by the minor ingredients of ZnO, $SiO_2$, $BaO_2$, and $K_2O$. The $B_2O_3-ZnO-Bi_2O_3$ glass system bonded well to metal, and bismate glass insulating properties were comparable to those of bismate glass $B_2O_3-ZnO-PbO$ glass system in a sheath heater module.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.328-328
• /
• 2008

As a low K material for high frequency high integration modules, glass/ceramic composites were investigated. Glass composition were selected from $SiO_2-B_2O_3-Al_2O_3-R_2O$-RO system which having very low dielectric constant and cordierite was used as a ceramic filler. These composites were sintered at temperature range from $850^{\circ}$ to $950^{\circ}$ and XRD, SEM microstructure analysis of sintered bodies were performed for understanding sintering behavior. Any crystallization was not occurred and dense sintered bodies were attained. Dielectric and mechanical properties of these sintered glass/cordierite composites were analysed by network analyzer and UTM. Glass/ceramic composite with 50 wt% cordierite showing a dielectric constant (${\varepsilon}_r$) of 5.4, Q${\times}f_0$ (Q) of 1600 at 1 GHz and maximum bending strength of 163 MPa was attained.

• Journal of the Korean Ceramic Society
• /
• v.52 no.1
• /
• pp.23-27
• /
• 2015

Recently, the use of ion-exchange strengthened glass has increased sharply, as it is now used as the cover glass for smart phone devices. Therefore, many researchers are focusing on methods that can be used to strengthen ion-exchange glass. However, research on how the improved strength can be maintained under thermal environment of device manufacturing is still insufficient. We tested the degradation of the characteristics of ion-exchange soda-lime glass samples, including their surface compressive stress characteristics, the depth of the ion-exchange layer (DOL), flexural strength, hardness, and modulus of rupture (MOR) values. Degradation of the characteristics of the ion-exchange glass samples occurred when they were heat-treated at a temperature that exceeded $350^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.396-399
• /
• 2004

저온 동시소성용 glass-ceramics의 소결 경향성 연구를 위해 lead-borosilicate계 glass를 frit화하여 알루미나분말과 $TiO_2$분말을 $10{\sim}50\;vol%$로 각각 혼합한 후 여러 온도에서 소결하여 소결과 유전 특성을 조사하였다. 그 결과 glass의 연화온도(Ts)가 낮을수록 최대 치밀화 온도가 낮았으며, 반면에 소결밀도는 Ts가 높을수록 높았는데, 이는 glass-ceramicss에서의 결정화도와 관계하였다. 본 연구를 통해 glass-ceramic에서의 소결특성은 glass와 ceramic의 반응성에 의한 2상 석출 정도에 큰 영향을 받음을 알 수 있었으며, ceramic filler로서 알루미나와 $TiO_2$를 이용하여 $900^{\circ}C$에서 소성이 가능하였다. 알루미나의 경우 유전특성$({\epsilon}r=8.5,\;Q{\times}fo=6000)$이 기판용 저유전율 재료로 사용이 가능하였고, $TiO_2$의 경우도 유전특성($({\epsilon}r=17,\;Q{\times}fo=4000)$)이 필터용 고유전율 재료로 사용 가능하도록 높게 나타났다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.4
• /
• pp.619-625
• /
• 1998

The effect of softening point and glass amount of glass frit on the sintering behavior of low temperature cofirable glass/ceramic composites was studied and according to these results, glass/ceramic composites with high sintered density was fabricated. The density of composites was increased as the glass amount was increased. In case of using the glass with low softening point, the deformation of specimen was occurred though the ratio of the glass amount in the specimen was low. But, in case of using the glass with high softening point, the sintered density of composites was increased in accordance with glass amount. With the specimen of high softening point, the deformation was not happened. Therefore, it was found that the densification was progressed continuously in high glass amount. From the study on the effect of softening point of glass on sintering behavior, the suitable softening point and glass amount for fabrication of glass/ceramic composites can be anticipated. When glass frit with softening point of $790^{\circ}C$ was chosen according to this result, low temperature cofirable glass/ceramic composites with high density (97%) at $900^{\circ}C$ was fabricated.

• Korean Journal of Materials Research
• /
• v.29 no.11
• /
• pp.727-733
• /
• 2019

In this study, the glass melting properties are evaluated to examine the possibility of using refused coal ore as replacement for ceramic materials. To fabricate the glass, refused coal ore with calcium carbonate and sodium carbonate in it (which are added as supplementary materials) is put into an alumina crucible, melted at $1,200{\sim}1,500^{\circ}C$ for 1 hr, and then annealed at $600^{\circ}C$ for 2 hrs. We fabricate a black colored glass. The properties of the glass are measured by XRD (X-ray diffractometry) and TG-DTA (thermogravimetry-differential thermal analysis). Glass samples manufactured at more than $1,300^{\circ}C$ with more than 60 % of refused coal ore are found by XRD to be non-crystalline in nature. In the case of the glass sample with 40 % of refused coal ore, from the sample melted at $1,200^{\circ}C$, a sodium aluminum phosphate peak, a disodium calcium silicate peak, and an unknown peak are observed. On the other hand, in the sample melted at $1,300^{\circ}C$, only the sodium aluminum phosphate peak and unknown peak are observed. And, peak changes that affect crystallization of the glass according to melting temperature are found. Therefore, it is concluded that glass with refused coal ore has good melting conditions at more than $1,200^{\circ}C$ and so can be applied to the construction field for materials such as glass tile, foamed glass panels, etc.

• Journal of Auto-vehicle Safety Association
• /
• v.7 no.3
• /
• pp.14-18
• /
• 2015

Toughened glass is known to have about four times larger external impact resistance than that of original glass. This study is aimed to verify that ceramic-printed toughened glass does not meet of GTR(Global Technical Regulations) No. 6 and its strength is lower than that of original glass through tests. The tests were conducted on the test pieces of original glass, toughened glass, and ceramic-printed toughened glass from five glass manufacturers. In Test 1, a 227g steel ball was dropped from a height of 2 meters, and damage was checked according to the test method of GTR No. 6. In Test 2, a steel ball was freely dropped from different heights and limited damage height was determined. In the result of Test 1 according to the test method of GTR No. 6, while all five test pieces of toughened glasses were not damaged, all the ceramic-printed toughened glass from the five manufacturers were damaged. In the result of Test 2, none of the five test pieces of toughened glass were damaged by a 10m ball drop, meanwhile, the original glasses were damaged by an average of 3m ball drop. And the results of the tests show that the ceramic-printed toughened glass does not have the features of toughened glass due to its very low strength. Therefore, this study contributes to the safety of consumers by considering the GTR No. 6, and by revising the toughened glass test method.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2005.07b
• /
• pp.1229-1232
• /
• 2005

We report the method of preventing the grey color of Bi based glass frits caused by reduction of $Bi_2O_3$. To prevent reduction of $Bi_2O_3$, we controlled the melting temperature. Low melting temperature reduces the reduction of $Bi_2O_3$ and that makes clarity transparent glass cullets. After firing, glass frits that melted at lower temperature showed better transparency. To prevent the browning, we used some additives like CuO, $CeO_2$, CoO and $TiO_2$. The colors of glass cullets were varied according to additives. After firing, dielectric layer contained additives showed better transparency than the one without additives. In the point of reaction between dielectric layer and Ag electrode, CuO was the most effective additive in preventing the yellowing.