• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.7 no.3
• /
• pp.213-221
• /
• 1987

To use fly ash as an additive for concrete, authors collected 15 kinds of domestic fly ashes and tested the chemical compositions and physical properties of the fly ashes. Fluidity of the fly ash paste was also investigated. The result shows that the chemical compositions of the fly ashes were in the range of regulation of Korean Industrial Standards except ignition loss and the following relationships in fly ash were studied; specific surface and residue in standard sieve, specific surface and unit weight, residue in standard sieve and ignition loss. For the given flow properties, fly ash paste required higher water-binder ratio than cement paste.

• Advances in concrete construction
• /
• v.6 no.4
• /
• pp.363-373
• /
• 2018

Portland cement pervious concrete (PCPC) is an effective pavement material to solve or reduce the urban waterlogging problems. The Mechanical properties, the permeability, the abrasion resistance and the frost resistance of PCPC without fine aggregate were investigated. The increase of porosity was achieved by fixing the dosage of coarse aggregate and reducing the amount of cement paste. The results show that the compressive strength and the flexural strength of PCPC decrease with the increase of porosity. The permeability coefficient and the wear loss of PCPC increase with the increase of the porosity. The compressive strength and the flexural strength of PCPC subjected to 25 freeze-thaw cycles are reduced by 13.7%-17.8% and 10.6%-18.3%, respectively. For PCPC subjected to the same freeze-thaw cycles, the mass loss firstly increases and then decreases with the increase of the porosity. The relative dynamic modulus elasticity decreases with the increase of freeze-thaw cycles. And the lower the PCPC porosity is, the more obvious the dynamic modulus elasticity decreases.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2005.05a
• /
• pp.93-98
• /
• 2005

The purpose of this study was to analyze the compression strength research by aerated concrete as mixing ratio This Study used foaming-agent and produced aerated concrete by pre-foam way that is used in construction site. An experiment changes unit cement amount, w/c and the glass fiber mixing rate and 'measured capacity change, unit capacity weight and compressive strength. The results obtained from experimental study are as following; Research to reduce unit capacity weight in condition more than unit cement amount 500kgf is considered should be gone side by side. The highest compressive strength result appeared in aerated concrete that cement amount 600kgf and w/c ratio $45\%$, $50\%$. compressive strength was increased maximum $34%$ when glass fiber $0.7\%$ addition cause by coherence enlargement to enlargement of cement paste and glass fiber addition per unit volume

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.85-88
• /
• 2006

This study describes the optimum mix proportion of the high strength and self-compacting concrete placed in main structures of LNG above tank. This concrete requires high strength level about $60{\sim}80MPa$, low hydration heat, balance between workability and consistency without vibrating in the actual work. For this purpose, low heat portland cement and fly ash are selected and design factors including water-binder ratio, replacement ratio of fly ash are tested. As experimental results, low heat portland cement shows lower the confined water ratio than another cement type and the optimum replacement ratio of fly ash in order to improve properties of the binder-paste shows 10% by cement weight considering test results of the confined water ratio$({\beta}p)$. Also, flowability of the high strength and self-compacting concrete by using fly ash about $10{\sim}20%$ is improved. The replacement ratio of fly ash 10% and water-binder ratio $25{\sim}27%$ are suitable to the design strength 80MPa and cost, In case of the design strength 60MPa, the replacement ratio of fly ash and water-binder ratio show 20% and $25{\sim}30%$ separately. Based on the results of this study, the optimum mix proportions of the high strength and self-compacting concrete will be applied to the construction of LNG above tank as a new type.

• Journal of the Korean Ceramic Society
• /
• v.44 no.1 s.296
• /
• pp.23-31
• /
• 2007

To examine the effects of chemical admixture on the fluidity and strength development of high chloride cement, experiments were conducted in which lignosulfonate (LS), naphthalenesulfonate (NS), and polycorboxylate (PC) were each added in standard and excessive amounts, and the results were as follows. 1. Because adding KCl to NS causes a decrease in flow, adding PC is better in maintaining high cement fluidity. 2. When cement contained much chloride comes in contact with water, hydration begins 4 h after contact and securing workability becomes difficult, but by adding PC, workability can be secured to 10 h. 3. The bound water ratio and compressive strength in aging 3 days occupy $70\sim80%$ of those in aging 28 days, and the early compressive strength increases not only by adding KCl, but also by chemical admixture. 4. Although compressive strength development is excellent in NS, PC, if NS is added excessively, hydration becomes slow and while the pore structures become slightly minute, the strength development decreases due to severe setting retardation.

• Proceedings of the Korean Society of Agricultural Engineers Conference
• /
• 2005.10a
• /
• pp.97-101
• /
• 2005

High strength concretes utilizing EVA with micro particles were prepared by varying polymer/binder mass ratio and curing conditions with a constant water/binder mass ratio of 0.3. The EVA modified concretes on the compressive and flexural strength, microstructure, ultrapulse modulus in curing condition(dry and water curing) were studied. Also, scanning electron microscope analysis(SEM) was performed to reveal the presence of polymer film and cement hydrates in the concrete. The compressive strength of the EVA modified concretes cured at water conditions ere higher than that of the EVA modified concretes cured at dry conditions. But, the flexural strength of the specimens cured at dry conditions were higher than that of the specimens cured at water conditions. Due to the interaction of the cement hydrates and polymer film, an interpenetrating network originated in which the aggregates were embedded. The curing of the polymer modified concrete involves two step of cement hydrates and polymer modification, and cement hydrates was promoted in water conditions and polymer film formation take place when water evaporates and was thereby was favored in dry conditions. By SEM analysis, influences of polymer modification was strengthening of the transition zone between the aggregate and the paste, and the porosity of transition zone decreases. By spring analysis, it could known that polymer film affects in porosity decrease and strengthening of transition zone.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2003.05a
• /
• pp.73.2-79
• /
• 2003

The purpose of this study is to provide the basic data on the optimum method for interfacial separation for an effective recycle of concrete waste by using the thermal properties of concrete. Therefore, this study is proceeded by dividing the interface of concrete into cement paste and fine aggregates or mortar and coarse aggregate, considering the aspect of recycled cement and aggregate as the recycling use of concrete waste. As results of the experiment, in case of recycle cement, the interfacial separation is easily appeared, but it is shown that the mixed amount of powder included in fine aggregate doesn't greatly decrease. But, in case of recycle coarse aggregate, the effect of interfacial separation by preliminary heating is predominant. Especially, the bonding rate of mortar is the lowest when it is heated 5 times for 120 minutes at $300^{\circ}C$. Hence, it is considered that it will be an excellent effect of quality control when the results of this study is applied to a manufacturing system of recycle coarse aggregate which is about to put into practical use.

• Restorative Dentistry and Endodontics
• /
• v.10 no.1
• /
• pp.71-83
• /
• 1984

The purpose of this study was to evaluate the transmission spectrum of the set calcium hydroxide dental cement (Dycal, L.D. Caulk Co. Milford, Del.) Cement was prepared for A T R spectra at a low powder-to-liquid ratio of 3.0gm/ml in order to retard the reaction and facilitate the manipulation of loading the cement into the cell. Spectra were recorded on an I R Spectrophotometer (MX-1, FT) at an agle of incidence of 55. The A T R cell was a RIIc Model TR5 with a hemisperical KRS-5 (Thallium-Bromide-Iodide). A spectrum was recorded within 3 minutes. Further spectra were recorded after 5,10,30 minutes and 1,5,24, 72 hours. The results were as follows; 1. The setting reaction between acid paste and base past would take place fastly within 10 minutes after mix, and that would be slow until 72 hours after mix. 2. In the set cements, some methyl salicylate and calcium hydroxide remained unreacted until 72 hours after mix. 3. The setting reaction and the reaction rate occuring at the surface and in the bulk cements were similar. 4. The chelates were bound together between calcium hydroxide and methyl salicylate.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.10a
• /
• pp.241-246
• /
• 1997

This paper tried to catch the fluidity and rheology nature of paste, using the W/P, flay-ash and additional amount of superplasticizing agent as experimental factor. Form result of experiment, as the amount of superplasticizing agent increased, fluidity increased and the rheology decreased. As the substitutional ratio increased fluidity decreased, the rheology tended to increase, additional amount of agent to gain high flowing range is different according to w/p, but this experiment shows about 0.5~1.0% in fly-ash 10~30% substitutional range, 1.0~1.5% in fly-ash 50%.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.171-172
• /
• 2017

In order to meet the high performance of the concrete, the viscosity increases with water binder ratio and amount of powder. because of these problems, we use high performance water reducing agent and low viscosity water reducing agent, but side effects may occur when using large amount of water reducing agent. Therefore, in this research, in order to increase the viscosity, I would like to analyze the change in viscosity and flow characteristics of paste by utilizing fly ash and lung limestone which are generally thrown away without using high performance water reducing agent.