Absorbent polymer-cement composites were fabricated by the semi-powder mixing OPC(ordinary Portland cement) with an absorbent polymer. The effects of absorbent polymer on the mechanical properties and the hydration characteristics were observed and the polymer-cement interaction also discussed. Absorbent polymer-cement composites showed the value of total porosity of 8vol% the value of 28 days flexural strength was up to 280 Kgf/cm2 in the case of absorbent polymer-cement composite at 1 wt% absorbent polymer content and microstructure of absorbent polymer-cement composite has been observed more dense than that of OPC paste. Accordingly the permeability of compositewas improved and so the moisture resistance was also increased. Adding polymer did not retard the hydration of OPC. It was considered from the results of IR(infrared) analysis that the functional group of absorbent polymer would be changed from unidentate to bidentate during by the hydration of cement minerals.

• 한국세라믹학회지
• /
• 제37권1호
• /
• pp.70-76
• /
• 2000

In order to investigate the properties of the blended cement using coarsely ground blasturnace slag blended coements which were substituted from 10 to 70 wt% low Blaine slag powder (2,000 and 3,000 cm2/g) for porland cement clinker were prepared and Cal(OH)2 contents in hydrates hydration heat the fluidity and the compressive strength were measured. As the content of slag was increased the hydration heat and the early strength was decreased and the fluidity of the cement paste was improved. The heat evolution of the cement with 2,000cm2/g slag was lower than that of 3,000 cm2/g slag blended cement. Especially the heat evolution of 60wt% or above slag blended cement was similar to that of belite rich cement.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1998년도 가을 학술발표회 논문집(I)
• /
• pp.19-24
• /
• 1998

In this study, blended cement with low blaine(2000, 3000$\textrm{cm}^2$/g) blast-furnace slag power by 10-70wt.% was investigated through the measurement hydration heat, physical properties. The experiment results indicated compressive strength was decreased as low blaine slag blended, but hydration heat was reduced significantly and flow of the cement paste was increased.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 봄 학술발표회 논문집
• /
• pp.669-674
• /
• 2003

The purpose of this study is to identify the diffusion coefficients of carbon dioxide for various concrete mixtures. The test results indicate that the diffusion coefficient increases with the increase of water-cement ratio. The diffusion coefficient decreases with the increase of relative humidity at the same water-cement ratio. The diffusion of carbon dioxide reached the steady-state within about five hours after exposure. It was found that the diffusion coefficient of cement paste is larger then that of concrete or mortar. The quantitative values of diffusivity of carbon dioxide in this study will allow more realistic assessment of carbonation depth in concrete structures.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2019년도 추계 학술논문 발표대회
• /
• pp.176-177
• /
• 2019

As a result of the Rietveld analysis to determine the effect of carbon nanotubes on the hydration products of cement composites, the quantitative difference of hydration products according to the addition rate of carbon nanotubes was not significant. Ettringite, an early hydration product, was measured to be slightly higher than the planes with carbon nanotubes over all ages. Therefore, it seems that carbon nanotubes have no effect on the hydration production in cement paste.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 가을 학술논문 발표대회
• /
• pp.114-115
• /
• 2021

In this study, the effects of thermal activation on the compressive strength and water absorption of fly ash-cement systems were studied. The results show that the increase in curing temperature improves the early-age compressive strength and reduces its water absorption.

• International Journal of Concrete Structures and Materials
• /
• 제7권2호
• /
• pp.119-125
• /
• 2013

Carbonation is a natural ageing process for cement. This study focuses on how the carbonation rate varies with selected hydration times and atmospheric conditions during the early stages of reacting dried cement paste. Diffuse reflection Fourier transform infrared spectroscopy is shown to be a suitable technique to monitor the formation of carbonates in cement. Combined with a previously developed freeze drying technique, carbonation can be studied at specific hydration stages. In ambient air both calcium hydroxide and calcium silicate hydrate (C-S-H) in cement are carbonated. Increased hydration time enhances the carbon dioxide uptake, which indicates that the calcium in the hydration products reacts more easily than the calcium in the clinker phase. In a humid $CO_2$ atmosphere, the carbonation process is so pronounced that it decomposes C-S-H into calcium carbonate and silica. In a moist $N_2$ atmosphere no carbonation occurs, but the sulfate chemistry of the cement seems to be affected due to the formation of ettringite.

• 한국구조물진단유지관리공학회 논문집
• /
• 제26권5호
• /
• pp.95-102
• /
• 2022

최근, 전세계적으로 온실 가스의 저감에 관심이 높아지면서 건설 산업에서도 FA를 대량 치환하는 HVFAC의 사용을 위한 연구가 수행되고 있다. 시멘트의 수화도와 FA 반응도의 정량적인 측정은 HVFAC의 강도발현 메커니즘을 명확히 이해할 수 있게 한다. FA가 포함된 시멘트 페이스트의 수화 및 포졸란 반응은 매우 복잡하고 수화 생성물의 조성을 정확하게 결정할 수 없으므로 간단한 방법으로 반응도를 설명하는 것은 매우 어렵다. 따라서, 이 연구는 재령에 따른 하이볼륨 FA 시멘트의 수화 특성을 조사하였다. 시멘트의 수화도와 FA의 반응도는 재령에 따른 선택용해법과 페이스트의 비증발 수량을 통해 평가하였다. 또한 HVFA 모르타르 시편을 이용하여 연령에 따른 압축강도를 측정하였다. 실험결과 FA의 치환율이 증가할수록 시멘트의 수화도는 증가하나 FA의 반응성은 감소하는 것으로 나타났다.

• 콘크리트학회논문집
• /
• 제18권4호
• /
• pp.569-576
• /
• 2006

PC계 2원 공중합체를 분자량이 2080인 MPEG와 (polyethylene glycol methyl ether methacrylate, Mn=2080) 몰 비가 2, 3, 4인 mono-carboxylic aicd(AA acrylic acid)를 사용하여 합성하고, MPEG와 mono-carboxylic aicd에 dicarboxylic acid(ITA, MAL)를 추가하여 3원공중합체를 합성하였다. PC계 2, 3원 공중합체가 시멘트페이스트 수화 반응에 미치는 영향성을 평가하고, 분석하기위해 각각의 시편을 만들어 재령(1일, 3일, 28일)별로 적외선 분광법(FT-IR), X-선 회절분석(XRD), 시차주사열계량법(DSC), 주사전자현미경(SEM)을 사용하여 분석을 실시하였다. 2, 3원 공중합체 모두 재령 1일에서는 다소 수화 반응 속도가 지연되었으나, 시간 경과에 따라 수화 지연은 완화되었으며 3원공중합체보다 2원공중합체가 수화가 더 활발히 진행되었는데 이는 3원공중합체에 비해 상대적으로 2원 공중합체가 가진 낮은 카복실기 함량 때문이다. 2AA계를 적용한 PC계 2원 공중합체의 경우 재령 3일에서 수화반응이 가장 활발하게 일어났고, AA의 몰비가 증가할수록 2원 공중합체의 수화 지연성은 커지는 경향을 나타내었다.

• 콘크리트학회논문집
• /
• 제26권6호
• /
• pp.723-730
• /
• 2014

최근 고로슬래그 미분말의 사용량이 증가함에 따라 고로슬래그 미분말 혼입 시멘트의 수화반응 모델뿐만 아니라 압축강도, 수화생성물, 수화열 등 고로슬래그 미분말 혼입 시멘트 페이스트의 물성에 관한 연구가 활발히 진행되고 있다. 하지만 고로슬래그 미분말 혼입 시멘트 페이스트의 물성에 큰 영향을 끼치는 고로슬래그 미분말의 반응도에 대한 연구는 세계적으로도 부족하며 특히 국내에서는 전무한 실정이다. 따라서 본 연구는 선택적 추출법을 이용하여 시멘트 페이스트 내 고로슬래그 미분말의 반응도를 정량분석하고 물 바인더비, 치환율, 양생온도에 따라 압축강도, 화학결합수, $Ca(OH)_2$을 측정하여 비교 분석 하였다. 실험결과 시멘트 페이스트 내 고로슬래그 미분말의 반응도, 화학결합수, $Ca(OH)_2$은 치환율이 낮고 물 바인더비와 양생 온도가 높을수록 높게 나타났으며 특히 고로슬래그 미분말의 반응도는 최종적으로 약 0.3~0.4 값에 수렴하는 것으로 나타났다.