• Proceedings of the Korea Concrete Institute Conference
• /
• 1989.10a
• /
• pp.25-30
• /
• 1989

In this paper, morter and concrete specimens made with four cements were immersed in Mgcl2, MgSO4 Solution and artifical Seawater which was corresponded with Seawater. The hydration products of immersed cement pastes were looked over by using SEM, EDS and X-ray diffraction method. The results show that the concrete made with domestic flyash cement and blast-frrnace slag cement is superior to that of ordinary portland cement in resistance to chloride and sulphate solution. Especially, it is found that the attack of Cl-ion on the concrete plays an important role of the deterioration of concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.04a
• /
• pp.83-88
• /
• 1998

II-anhydrite, slag, and fly ash produced as industrial by-product were reutilized for the manufacture of high strength admixtures for cement and concrete. The effects of these admixtures on the compressive strength of cement mortar and concrete were examined with those of domestic admixture. At the condition mortar and concrete. Especially, adding of II-anhydrite was very effective for the increasing of compressive strength. Therefore it is possible that these admixture as a high strength admixture apply to cement and concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1991.10a
• /
• pp.5-10
• /
• 1991

This study was performed to find out the effect about the spacing factor and durability factor to evaluate the durability of concrete in high-strength concrete with freezing and thawing as following each condition, 1) unit cement content : 500kg/$\textrm{m}^3$, 550kg/$\textrm{m}^3$ 2) water/cement ratio : 25%, 30%, 35% 3) air content : below 1.5%, 1.6~3.5%, 4~6%, over 7% From the results tested, a variation of air content was more effective to the durability of concrete than that of water/cement ratio and unit cement content.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.38 no.5
• /
• pp.95-105
• /
• 1996

This study was performed to evaluate the mechanical properties of permeable polymer concrete using fillers and unsaturated polyester resin. The following conclusions were drawn; 1. The unit weight was in the range of 1, 663~ l, 892kg/$cm^3$, the weights of those concrete were decreased 18~28% than that of the normal cement concrete. 2. The highest strength was achieved by fly ash filled permeable polymer concrete, it was increased 22% by compressive strength, 190% by tensile strength and 192% by bending strength than that of the normal cement concrete, respectively. 3. The external strength of permeable pipe was in the range of 3, 083~3, 793kg/m, the external strengths of those concrete were increased 2~26% than that of the normal cement concrete. Accordingly, these permeable polymer concrete pipe can be used to the members and structures which need external strength. 4. The static modulus of elasticity was in the range of $5.7{\times} 10^4 ~ 15.4{\times} 10{^4}kg/cm^2 $, which was approximately 35~64% of that of the normal cement concrete. Fly ash filled permeable polymer concrete was showed relatively higher elastic modulus. The poisson's number of permeable polymer concrete was less than that of the normal cement concrete. 5. The dynamic modulus of elasticity was in the range of $83{\times} 10^3 ~ 211{\times} 10{^3}kg/cm^2 $, which was approximately Ins compared to that of the normal cement concrete. Fly ash filled permeable polymer concrete was showed higher dynamic modulus. The dynamic modulus of elasticity were increased approximately 22~45% than that of the static modulus. 6. The ultrasonic pulse velocity was in the range of 2, 584 ~ 3, 587m/sec, . which was showed about the same compared to that of the normal cement concrete. Fly ash filled permeable polymer concrete was in the range of$0.58~8.88 {\ell}/cm^2/hr$, , and it was larglely dependent upon the mixing ratio. These concrete can be used to the structures which need water permeability.

• Journal of the Korea Institute of Building Construction
• /
• v.8 no.4
• /
• pp.79-85
• /
• 2008

The purpose of this study is to evaluate the mix design of pH reducing cement concrete which can be used for environment-friendly concrete. Cement pastes and concretes are prepared with water-binder ratios and various admixtures such as blast-furnace slag, fly ash and recycled cement, and tested for compressive strength and pH. pH is measured through pore solution expressed from hydrated cement paste by special apparatus. From the test results, regardless of water-binder ratio, The pH of expressed pore solution from hydrated cement paste which is made of ordinary portland cement with blast-furnace slag, fly ash is decreased with increasing of admixtures content, and compressive strength is also slightly improved. The compressive strength of cement paste made of recycled cement which is burnt at $1000^{\circ}C$, for 2 hours is considerably increased compared with that of none-burnt recycled cement due to restoration of hydraulic property, but pH is a little higher. Porous concrete with ordinary portland cement has high pH in the range of 12.22 to 12.59, however, that is reduced to the range of 8.95 to 10.39 by carbonation at the surface of porous concrete. The pH reduction of porous concrete is possible by various admixture addition, however their degrees are very slight. Therefore, to reduce the pH considerably, carbonation method of porous concrete is better in pH reduction methods for plant survival condition of pH of 9.0 or less. In this study, it is apparent that pH for the environment-friendly porous concrete products used in the construction field can be suppressed by this carbonation method and various admixtures addition.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.409-414
• /
• 2001

The hydration of cement paste occurs when the cement is mixed with water. During the hydration, hydration heat causes the thermal stress depending on the size of concrete and the cement content. Especially in the high-strength concrete, we must give care to the concrete due to its large cement content. In this study, conduction calorimeter and concrete insulation hydration heat meter were used to investigate the hydration heat characteristics of cement and concrete. To reduce hydration heat of high-strength concrete, several types of replacement of fly-ash and blast-furnace slag powder were used in this experiment.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.04a
• /
• pp.177-182
• /
• 1998

In this study, We compare material properties of Self-compacting concrete using Korean Belite cement with Japanese. Self-compacting concrete consolidates densely by virtue of its own weight at the location where concrete compaction cannot be carried out. Material properties of Korean and Japanese Belite cement are very similar but compatibility with superplasticizer and viscosity agent are some different. Before the batch mix, the compatibility must be checked as fresh concrete properties. For the concrete test results, Korean Beilite cement is suitable to product High performance concrete.

• Advances in concrete construction
• /
• v.7 no.2
• /
• pp.75-85
• /
• 2019

The present study is focused on the mechanical and durability properties of ternary blended cement concrete mix of different grades 30 MPa, 50 MPa and 70 MPa. Three mineral admixtures (fly ash, silica fume and lime sludge) were used as a partial replacement of cement in the preparation of blended concrete mix. The durability of ternary blended cement concrete mix was studied by exposing it to acids HCl and $H_2SO_4$ at 5% concentration. Acid mass loss factors (AMLF), acid strength loss factor (ASLF) and acid durability factor (ADF) were determined, and the results were compared with the control mix. Chloride ions penetration was investigated by conducting rapid chlorination penetration test and accelerated corrosion penetration test on control mix and ternary blended cement concrete. From the results, it was evident that the usage of these mineral admixtures is having a beneficiary role on the strength as well as durability properties. The results inferred that the utilization of these materials as a partial replacement of cement have significantly enhanced the compressive strength of blended concrete mix in 30 MPa, 50 MPa and 70 MPa by 42.95%, 32.48% and 22.79%. The blended concrete mix shown greater resistance to acid attack compared to control mix concrete. Chloride ion ingress of the blended cement concrete mix was low compared to control mix implying the beneficiary role of mineral admixtures.

• Cement
• /
• s.200
• /
• pp.54-59
• /
• 2013

2013년 봄호부터 시멘트지에 기고되었던 각 자료를 바탕으로 이를 재구성해 Cement knowledge 코너를 연재하고 있습니다. 이번 호는 마지막 순서로 콘크리트(concrete)에 대해 살펴봅니다.

• International Journal of Concrete Structures and Materials
• /
• v.5 no.2
• /
• pp.119-123
• /
• 2011

Presented in the paper are findings of a project that examined the effect of slag grade and cement source on the performance of concrete mixtures. Slag cement contents were 20, 40, and 60 percent of the total cementitious material content. Two grades of slag cement were examined (Gr. 100 and Gr. 120) along with two sources of Type I cement. Compressive strength, durability, and permeability were measured. The results showed that the cement source affected the early age strength of the mixtures. At 28 days of age, mixtures containing Gr. 120 slag cement had higher compressive strengths than mixtures containing Gr. 100 slag cement, but by 90 days of age, the trend reversed. As for the chloride ion penetrability, mixtures cast with Gr. 100 slag cement passed fewer coulombs at 28 and 90 days of age than similar mixtures containing Gr. 120 slag. Mixtures containing Gr. 120 slag had the greatest durability factors.