• Computers and Concrete
• /
• v.10 no.4
• /
• pp.391-407
• /
• 2012

Utilization of supplementary cementing materials (SCM) by the cement industry, as a highly promising solution of sustainable cement development aiming to reduce carbon dioxide emissions, necessitates a more thorough evaluation of these types of materials on concrete durability. In this study a comparative assessment of the effect of SCM on concrete durability, of every cement type as defined in the European Standard EN 197-1 is taking place, using a software tool, based on proven predictive models (according to performance-related methods for assessing durability) developed and wide-validated for the estimation of concrete service life when designing for durability under harsh environments. The effect of Type II additives (fly ash, silica fume) on CEM I type of cement, as well as the effect of every Portland-composite type of cement (and others) are evaluated in terms of their performance in carbonation and chloride exposure, for a service life of 50 years. The main aim is to portray a unified and comprehensive evaluation of the efficiency of SCM in order to create the basis for future consideration of more types of cement to enter the production line in industry.

• Magazine of the Korea Concrete Institute
• /
• v.10 no.6
• /
• pp.169-178
• /
• 1998

Bond strength of reinforcing bar to high-perfomance concrete using belite cement is explored using beam end test specimens. The key parameters for the bond test are slump of concrete, top bar effect, and strength of concrete in addition to concrete cover. The test results show that the specimens with belite cement concrete show approximately 10% higer bond strength than those with portland cement concrete. The results also show that the bond strength from the high strength concrete is function of the square root of concrete compressive strength. Bond strength of the top bar is less than bond strength of bottom bar, but the ratios of the bond strength of bottom-cast bars to those for top-cast bars are much less than the modification factor for top reinforcement found in the ACI 318-95 code. Comparisons with other reported tests identified that belite cement increased bond strength while silica fume or flyash used in high strength concrete decreased bond strength. The high-strength and high-slump concrete with belite cement performs well in terms of bond strength to reinforcing steel.

• Structural Engineering and Mechanics
• /
• v.82 no.2
• /
• pp.133-149
• /
• 2022

This study investigates the resistance of sustainable ultra-high performance concrete (UHPC) on steel reinforcement corrosion. For enhancing the sustainability of UHPC, concrete mixes were prepared with ordinary Portland cement main binder, and mixes with moderate to high percentages of blast furnace cement (CEM III), fly ash (FA), and slag cement as partial replacements of the full quantity of the used cement. Linear polarization resistance technique was employed to estimate the electrochemical behavior of the concrete specimens. Results showed that the compressive strength and the resistance of steel to corrosion in marine environments can be enhanced by improving the sustainability of UHPC through incorporation of CEM III, FA, and slag cement. FA replacement of up to 50% with the addition of 15% SF content produced better compressive strength and steel corrosion resistance than slag cement whether with the use of ordinary Portland cement or blast furnace cement as the main binder.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.04a
• /
• pp.493-498
• /
• 1999

Many concrete pavements closed to the end of service life in out country need to repair. We investigated material and mix designs for thin bonded concrete overlay and applied it to concrete pavement rehabilitation. The concrete with Type III cement showed earlier strength and better durability than the concrete with Type I cement. Designed concrete mixture with TypeIII cement made it possible to open the road earlier against heavy vehicles, increased traffic despite of cold weather in winter. In the field examination after four month, there was no defects like as shrinkage crack, spalling, surface abrasion and scaling, and good traffic condition has been maintained.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.11a
• /
• pp.78-81
• /
• 2003

Recently, physical properties of concrete containing ternary blended cement were actively researching to develop durability, mobility, and atc. as well as strength increase of concrete. In this study, durability of concrete such as the resistance against chloride ion penetration, rebar corrosion, freeze and thaw, and sulfate were researched for concrete containing ordinary portland cement(OPC) and ternary blended cement(TBC), respectively. For this purpose, concrete specimens containing OPC and TBC, respectively, were made for 37.5% of W/C, and then various durability experiments described above were carried out. As a result, it was observed from the test that concrete containing TBC showed excellent durability than concrete containing OPC.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.10a
• /
• pp.408-415
• /
• 1997

Bond strength of reinforcing bar to high-performance concrete using Belite cement is explored using beam end test specimen. The key parameters for the bond test are slump of concrete, top bar effect, and strength of concrete in addition to concrete covers. Specimen failed in the typical brittle bond failure splitting the concrete cover as the wedging action. The test results show that for the group with portland cement I using superplasticizer additional slump does not decrease the bond strength of the top bar is less than bond strength of bottom bar, but the top bar factor satisfy the modification factor for top reinforcement. The result also show that bond strength is function of square root of concrete compressive strength and cover thickness. More detailed evaluation will be conducted from the test specimen with high strength concrete using the belite cement.

• Journal of the Korea Institute of Building Construction
• /
• v.2 no.2
• /
• pp.145-150
• /
• 2002

The hydration of cement paste occurs when the cement is miked with water. During the hydration, hydration heat causes the thermal stress depending on the site of concrete and the cement content. Especially in the high-strength concrete, we must give care to the concrete due to its large cement content. In this study conduction calorimeter and concrete insulation hydration heat meter were used to investigation the hydration heat characteristics of cement and concrete. To reduce hydration heat of high-strength concrete, several types of replacement of fly-ash and blast-furnace slag powder were used in this experiment. As a result of this study, it was found that hydration heat of high-strength concrete was reduced by replacement of fly-ash and blast-furnace slag powder. In case of high-strength concrete using blast-furnace slag powder, the max-heat arrival time was delayed but an effect of heat reduction was lower than a case of high-strength concrete using fly-ash, because it was considered that the heat-dependence property of blast-furnace slag powder was higher than that of fly-ash.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.04b
• /
• pp.747-750
• /
• 1998

The application of spent liquor(BSL) obtained from alkaline sulfite-anthraquinone cooking of pine bark to cement mortar significantly improved the water-reducing ability and decreased the rate of cement hardening. However, the compressive and flexural strength of BSL addition to cement mortar were lower than that of PLAIN. The application of 0.2% antifoamer to BSL slightly decreased water-reducing ability, but remarkably improved the compressive and flexural strength of cement mortar. On the other hand, BSL decreased the rate of hardening of cement, which exhibited the protperties of the lignosulfonated based retarding water-reducing type. but the setting time of cement could be controlled by addition of Na2CO3 could be used to convert BSL to normal or accelerating concrete admixtures.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1994.10a
• /
• pp.65-70
• /
• 1994

The aim of this study is to develop the High Workable Concrete which has not so large slump loss with time using blast-furnace cement and High range water reducing agent. Normal portland cement and blast-furnce cement was used as binders and water-binder ratio were ranging from 34% to 50%. 5 kinds of Superplasticizer and High range water reducing agent were used. Test results show that the blast-furmace cement was much higher flowability than normal portland cement and domestic High rang water reducing and AE agent had very small slump loss than others. The compactability of High Workable Concrete was also confirmed using model wall-form.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2014.05a
• /
• pp.252-253
• /
• 2014

This study is to XRD and image analysis of low carbon type recycled cement from waste concrete powder and cement raw materials. Waste concrete powder possible to low carbon type recycled cement in small part of additive materials. Also, low carbon type recycled cement using waste concrete powder is suitable for ordinary portland cement.