• 한국주조공학회지
• /
• 제30권6호
• /
• pp.205-209
• /
• 2010

This study evaluates the influence of strontium addition and holding time on mechanical properties for Al-10.5wt%Si-2wt%Cu secondary die-casting alloy and the measured electrical conductivity of modified alloys. A general improvement in the mechanical properties of the alloy was observed after adding the strontium. Ultimate tensile strength, elongation and electrical conductivity of modified alloys were improved by increasing strontium content and holding time. From these results, the optimal strontium content and holding time were identified on the mechanical properties of Al-10.5wt%Si-2wt%Cu secondary die-casting alloys.

• 한국주조공학회지
• /
• 제41권2호
• /
• pp.127-131
• /
• 2021

고온 환경에 대한 우수한 특성을 바탕으로 산업 장비의 고온 재료에 Ti-48Al-2Cr-2Nb 합금이 사용된다. 본 연구에서는 Ti-48Al-2Cr-2Nb 합금 터보 차저 터빈 휠을 진공 원심 주조 방법으로 제작했다. 알루미나 몰드를 이용한 원심 주조시 터보 차저 터빈 휠 블레이드의 미스런 불량을 방지하기 위한 조건을 조사하였다. 진공 원심 주조로 제조된 합금의 미세 구조는 광학 현미경 (OM), 마이크로 비커스 경도 분석기 (HV), X- 선 회절 (XRD) 및 SEM-EDS로 연구하였다. 주조된 Ti-48Al-2Cr-2Nb 합금의 경도 및 SEM-EDS 결과는 산화층 (α- 케이스)의 두께가 일반적으로 50㎛ 미만임을 보여주었다. 예열 온도 1,100oC, RPM 260, 게이트 크기가 큰 알루미나 몰드의 경우 미스런 불량이 거의 없었다. 따라서 높은 예열 온도, 중간 RPM, 큰 게이트 크기 및 알파 케이스 형성 억제를 위한 알루미나 몰드를 통해 미스런이 적은 Ti-48Al-2Cr-2Nb 합금 터보 차저 터빈 휠을 얻을 수 있음을 확인했다.

• 한국주조공학회지
• /
• 제41권1호
• /
• pp.3-10
• /
• 2021

알루미늄 합금과 주철의 복합주조 공정 중에는 주철로부터 철 성분이 용해되어 알루미늄 용탕에 혼입될 수 있으므로 다양한 Fe함유 금속간 화합물이 형성되며, 이로 인해 알루미늄 합금의 인장 특성이 크게 저하 될 수 있다. 반면 불순물로 첨가되는 Fe와 는 달리 Cu의 경우 알루미늄 합금의 기계적 물성을 향상시키기 위해 첨가되는 합금원소이다. 본 연구에서는 Fe와 Cu의 첨가로 인한 알루미늄 합금의 미세조직 및 인장특성의 변화를 조사하였다. 첨가된 Fe 함량이 1% 이상일 경우 조대한 Al₅FeSi 상과 같은 Fe 함유 화합물들이 다량 형성되어 인장 특성이 현저히 감소하는 것으로 나타났다. Cu가 첨가 된 알루미늄 합금의 경우 Al2Cu 상이 추가로 형성되었으며, 인장 강도가 뚜렷하게 향상되는 결과를 보였다.

• 한국주조공학회지
• /
• 제14권5호
• /
• pp.464-470
• /
• 1994

The horizontal continuous casting method with the heated mold was applied to study the solidification structures of the pure Al and Al-0.5wt%Si and Al-1.0wt%Si alloy rods. The results could be summarized as follows: 1. The S/L interface structures of pure Al represented the hexagonal cells at the casting speed of 590 and 350mm/min, respectively. However, the hexagonal cells became irregular as the casting speed and(or) Si amount increased. 2. The striation increased as the Si amount and casting speed increased and was found to result from the occurrence of growth twin crystals by XRD analysis. 3. The striation did not affect the mechanical and electrical property of the drawn wire from the casted rod. This means the striation is not a serious defect which has to consider in the production of micro-sized fine wire in the drawing process.

• 대한금속재료학회지
• /
• 제50권7호
• /
• pp.531-538
• /
• 2012

In this study, we evaluated the fluidity of the Al-Zn based alloys which exhibit excellent mechanical properties. We conducted computer simulations of fluid flow using the results of DSC, DTA analysis and Java-based Materials Properties software (J. Mat. Pro). Such computer simulations were then compared with the results obtained from experimental observations. The computer simulation results and the experimental results were very similar in fluidity length. It was found that the fluidity length of Al-Zn alloys is improved by increasing the Zn content while decreasing the solidus temperature of an alloy. In addition, we elucidate the effect of Zn addition on variations in different mechanical properties and the microstructure characteristics of (Al-xZn3Cu0.4Si0.3Fe) x=20, 30, 40, and 45 wt% alloys fabricated by gravity casting.

• 한국주조공학회지
• /
• 제25권4호
• /
• pp.156-160
• /
• 2005

There are many factors that influence solidification behavior during continuous casting, e.g. include superheat, casting speed, cooling rate and holding time. However, when melt is stirred by electromagnetic force, there would be some changes in its solidification behavior compared to that of the ordinary casting process. In this study, the billets of A356 alloy with a diameter of 3 inch were fabricated with electromagnetic stirring under various conditions of superheat, casting speed and input voltage of electro magnetic stirring (EMS) device. The microstructure was also investigated under the various casting conditions and electromagnetic input voltages. When increase in input voltage, the microstructure was changed from dendritic to rosette type and finally to spheroidal. With pouring temperature, casting speed and electromagnetic input voltage were $650^{\circ}C$, 100 mm/min and 140 V, respectively, the billet with a diameter of 3 inch, which has a uniform dispersed spheroidal particles in the whole area of billet except for the surface area, was manufactured.

• 한국주조공학회지
• /
• 제33권1호
• /
• pp.22-31
• /
• 2013

In order to develop an aluminum alloy, that can combine high thermal conductivity and good castability and anodizability, aluminum alloys with low Si content, such as Al-(0.5~1.5)Mg-1Fe-0.5Si and Al-(1.0~1.5)Si-1Fe-1Zn, were designed. The developed aluminum alloys exhibited 170~190% thermal conductivity (160~180 W/mK), 60~85% fluidity, and equal or higher ultimate tensile strength compared with those of the ADC12 alloy. In each developed alloy system, the thermal conductivity decreased and the strength increased with the increment of Mg and Si, which are the significant alloying elements. The fluidity was in reverse proportion to the Mg content and in proportion to the Si content. The Al-(0.5~1.5)Mg-1Fe-0.5Si alloys exhibited better fluidity in thick-wall castings, while the Al-(1.0~1.5)Si-1Fe-1Zn alloys were better in thin-wall castability due to their lower surface energies. The fluidity behavior was complexly affected by the heat release for the solidification, viscosity, solidification range, and the type, quantity, and formation juncture of the main secondary phase.

• 열처리공학회지
• /
• 제36권6호
• /
• pp.359-366
• /
• 2023

Changes in microstructure and mechanical properties of Mg-1.0Al-1.0Zn-0.2Mn-0.5Ca (AZMX1100) alloy sheet manufactured by normal casting and twin roll casting process, were studied according to process and heat treatment. Non-uniform microstructure was observed in the initial sheet produced through both processes, and in particular, tilted dendrites and shifted central segregation were observed in the twin roll casting sheet. It was homogenized through hot rolling and heat treatment, and heat treated at 350℃ and 400℃ to compare the effect of heat treatment temperature. Both sheets were homogenized by the hot rolling process, and the grain size increased as the heat treatment temperature and time increased. It was confirmed that the grain size, deviation, and distribution of the second phase were finer and more homogenized in the TRC sheet. Accordingly, mechanical properties such as hardness, formability, and tensile strength also showed better values. However, unlike other previously reported AZMX alloy systems, it showed low formability (Erichsen value), which was judged by the influence of Al2Ca present in the microstructure.

• 한국주조공학회지
• /
• 제29권1호
• /
• pp.27-32
• /
• 2009

The microstructure of Al-7Si-0.4Mg-1Fe alloy mainly consists of aluminum dendrites, Al-Si eutectics, and $Al_5FeSi$ needles. When Mn was added to the alloy, the substantial amount of $Al_5FeSi$ phase was changed into Al(Mn,Fe)Si, however the needle-like morphology was almost unchanged. Combined additions of Cr or Sr with Mn to the base alloy resulted in rod-like Al(Mn, Fe,Si)Si phase. The tensile properties of as-cast alloys were enhanced by the Mn addition, especially when it was added with Sr. The tensile properties after T6 heat treatment was a little improved with 0.7%Mn addition, but Cr or Sr additions with Mn didn't show any positive effect on the properties of heat-treated alloys.

• 한국주조공학회지
• /
• 제37권6호
• /
• pp.186-192
• /
• 2017

The lost foam casting method was used to fabricate Al-Si alloy thin sheet specimens; the effects of chemical composition and process variables on the mold filling and mechanical properties were investigated. The mold filling capability was observed to be proportional to the pouring temperature, and both the vibration imposed during the casting and the application of a pattern coating had rather negative effects. The mold filling capability also decreased with the addition of Mg or TiB. When the Mg content increased, the tensile strength of the cast alloy was enhanced, but the elongation decreased. However, after T6 heat treatment, both the strength and the elongation were improved. TiB addition for grain refining or pattern coating did not significantly affect the tensile properties.