• Journal of Powder Materials
• /
• v.21 no.3
• /
• pp.191-195
• /
• 2014

This study reports a simple way of fabricating the porous Cu with unidirectional pore channels by freeze drying camphene slurry with Cu oxide coated Cu powders. The coated powders were prepared by calcination of ball-milled powder mixture of Cu and Cu-nitrate. Improved dispersion stability of camphene slurry could be achieved using the Cu oxide coated Cu powders instead of pure Cu powders. Pores in the frozen specimen at $-25^{\circ}C$ were generated by sublimation of the camphene during drying in air, and the green bodies were sintered at $750^{\circ}C$ for 1 h in $H_2$ atmosphere. XRD analysis revealed that the coated layer of Cu oxide was completely converted to Cu phase without any reaction phases by hydrogen heat treatment. The porous Cu specimen prepared from pure Cu powders showed partly large pores with unidirectional pore channels, but most of pores were randomly distributed. In contrast, large and aligned parallel pores to the camphene growth direction were clearly observed in the sample using Cu oxide coated Cu powders. Pore formation behavior depending on the initial powders was discussed based on the degree of powder rearrangement and dispersion stability in slurry.

• Journal of Powder Materials
• /
• v.18 no.4
• /
• pp.327-331
• /
• 2011

In order to fabricate the porous metal with controlled pore characteristics, unique processing by using metal oxide powder as the source and camphene as the sublimable material is introduced. CuO powder was selected as the source for the formation of Cu metal via hydrogen reduction. Camphene-based CuO slurry, prepared by milling at $47^{\circ}C$ with a small amount of dispersant, was frozen at $-25^{\circ}C$. Pores were generated subsequently by sublimation of the camphene. The green body was hydrogen-reduced at $200^{\circ}C$ for 30 min, and sintered at $500-700^{\circ}C$ for 1 h. Microstructural analysis revealed that the sintered Cu showed aligned large pore channels parallel to the camphene growth direction, and fine pores are formed around the large pore. Also, it showed that the pore size was controllable by the slurry concentration.

• Journal of Powder Materials
• /
• v.19 no.4
• /
• pp.259-263
• /
• 2012

Dependence of the freeze-drying process condition on microstructure of porous W and pore formation mechanism were studied. Camphene slurries with $WO_3$ contents of 10 vol% were prepared by milling at $50^{\circ}C$ with a small amount of dispersant. Freezing of a slurry was done in Teflon cylinder attached to a copper bottom plate cooled at $-25^{\circ}C$. Pores were generated subsequently by sublimation of the camphene during drying in air for 48 h. The green body was hydrogen-reduced at $800^{\circ}C$ for 30 min, and sintered in the furnace at $900^{\circ}C$ for 1 h. After heat treatment in hydrogen atmosphere, $WO_3$ powders were completely converted to metallic W without any reaction phases. The sintered samples showed large pores with the size of about $70{\mu}m$ which were aligned parallel to the camphene growth direction. Also, the internal wall of large pores and near bottom part of specimen had relatively small pores with dendritic structure due to the growth of camphene dendrite depending on the degree of nucleation and powder rearrangement in the slurry.

• Journal of Powder Materials
• /
• v.19 no.6
• /
• pp.446-450
• /
• 2012

In order to fabricate the porous Mo with controlled pore characteristics, unique processing by using $MoO_3$ powder as the source and camphene as the sublimable material is introduced. Camphene-based 15 vol% $MoO_3$ slurries, prepared by milling at $50^{\circ}C$ with a small amount of dispersant, were frozen at $-25^{\circ}C$. Pores were generated subsequently by sublimation of the camphene during drying in air for 48 h. The green body was hydrogen-reduced at $750^{\circ}C$, and sintered at $1000-1100^{\circ}C$ for 1 h. After heat treatment in hydrogen atmosphere, $MoO_3$ powders were completely converted to metallic W without any reaction phases. The sintered samples showed large pores with the size of about $150{\mu}m$ which were aligned parallel to the camphene growth direction. Also, the internal wall of large pores and near bottom part of specimen had relatively small pores due to the difference in the camphene growth rate during freezing process. The size of small pores was decreased with increase in sintering temperature, while that of large pores was unchanged. The results are strongly suggested that the porous metal with required pore characteristics can be successfully fabricated by freeze-drying process using metal oxide powders.

• Korean Journal of Materials Research
• /
• v.28 no.2
• /
• pp.108-112
• /
• 2018

The present study demonstrates the effect of raw powder on the pore structure of porous W-Ni prepared by freeze drying of camphene-based slurries and sintering process. The reduction behavior of $WO_3$ and $WO_3-NiO$ powders is analyzed by a temperature programmed reduction method in Ar-10% H2 atmosphere. After heat treatment in hydrogen atmosphere, $WO_3-NiO$ powder mixture is completely converted to metallic W without any reaction phases. Camphene slurries with oxide powders are frozen at $-30^{\circ}C$, and pores in the frozen specimens are generated by sublimation of the camphene during drying in air. The green bodies are hydrogen-reduced at $800^{\circ}C$ and sintered at $1000^{\circ}C$ for 1 h. The sintered samples show large and aligned parallel pores to the camphene growth direction, and small pores in the internal wall of large pores. The strut between large pores, prepared from pure $WO_3$ powder, consists of very fine particles with partially necking between the particles. In contrast, the strut densification is clearly observed in the Ni-added W sample due to the enhanced mass transport in activation sintering.

• Journal of Powder Materials
• /
• v.21 no.5
• /
• pp.366-370
• /
• 2014

The present study demonstrates the effect of solidification condition on the pore structure in freeze drying process using the slurries of CuO/sublimable vehicles. Camphene and Camphor-45 wt% naphthalene based slurries with 14 vol% CuO powder were frozen into a mold at $-25^{\circ}C$, followed by sublimation at room temperature. The green bodies were hydrogen-reduced and sintered at $500^{\circ}C$ for 1 h. The porous Cu specimen, frozen the CuO/camphene slurry into the heated mold of the upper part, showed large pores with unidirectional pore channels and small pores in their internal wall. Also, it was observed that the size of large pores was decreasing near the bottom part of specimen. The change of pore structure depending on the freezing condition was explained by the nucleation behavior of camphene crystals and rearrangement of solid powders during solidification. In case of porous Cu prepared from CuO/Camphor-naphthalene system, the pore structure exhibited plate shape as a replica of the original structure of crystallized vehicles with hypereutectic composition.