• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1993년도 하계학술대회 논문집 B
• /
• pp.1081-1083
• /
• 1993

A superconducting multistranded cable is used to realize high current capacity for AC use. The critical current value of the cable to be less than the simple summation of individual critical current value of each strand. The causes for such a degradation of the critical current value have not been revealed. This paper investigates the current distribution in multistrands before and after their quenching by using $7{\times}7$-strand superconducting cable.

• International Journal of Safety
• /
• 제7권1호
• /
• pp.10-14
• /
• 2008

For evaluating the radiation degradation of cross-linked polyethylene (XLPE) cable insulation due to the irradiated oxidation, XLPE was irradiated with ${\gamma}$-ray. For each irradiated samples, TGA, DSC, FT-IR, and tensile tests were carried out. Regarding radiation degradation, oxidative process was predominant. TGA, DSC and FT-IR can be useful tools for evaluating the radiation degradation due to the irradiated oxidation because these analyses need only small amount of samples. The results of TGA, DSC and FTIR analyses showed the similar tendency for irradiated degradation. They can be useful tools for evaluating the oxidation of insulating material by non-destructive testing.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 춘계학술대회 논문집
• /
• pp.518-521
• /
• 1999

This paper describes the properties of discharge current and the residual voltage for $^{60}$ C$_{0}$ -${\gamma}$ irradiated cables using in nuclear power generating station. As these properties related with $^{60}$ C$_{0}$ -${\gamma}$ -irradiatiation dose, it is suggested that these properties can be utilized as a index of irradiation degradation. As the ratio of degradation increases, the residual voltage in the initial time range increases and the peak moves to the shorter time. Therefore, I know the degree of radiation degradation from the position of the peak.

• 한국초전도저온공학회:학술대회논문집
• /
• 한국초전도저온공학회 2003년도 추계학술대회 논문집
• /
• pp.274-277
• /
• 2003

Critical current(Ic) degradation of HTS tapes after bending is one of the hottest issues in HTS development and application studies. Many people are measuring Ic degradations for effect of bending radius. However even if the bending radius is larger than the breaking radius a HTS tapes can be damaged by repetitive bending, which is unavoidable in the winding processes. Therefore, We studied the Ic degradation after repetitive bending. at 77K with self-field, of Bi-2223 tapes processed by "Powder-in-Tube" technique, which was made by America Superconductor Corporation(AMSC) and superconductiing tapes that strain is imposed measured critical current by temperature difference of L$N_2$ and normal temperature. Like this, critical current could measure that degradation about 1~3％ by temperature difference. These results will amount the most important basis data in power electric machine of superconductivity cable, magnet, etc that winding work is require.

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 2002년도 춘계공동학술발표회요약집
• /
• pp.323-323
• /
• 2002

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2001년도 추계학술대회 논문집 전기물성,응용부문
• /
• pp.152-154
• /
• 2001

Recently the extensive use of composite insulators for transmission lines can ultimately be justified only on long-term qualification tests. Especially, it is possible for the Polymer insulator to be aged in according to the environment in which it is used this may bring about the decrease of the duration of voltage application. So, this paper deals with aging property of the polymer insulator installed at real transmission line in the industry area. The contact angle, arc test, tracking test were measured for acquiring the degradation characteristics of silicone rubber and the SEM, XRF, FT-IR tests were measured for analyzing the crack and components. Also the surface leakage current of the polymer insulator was compared with that of the porcelain insulator. Finally, we knew that the aging property was not appeared during seven months at real transmission line in the industry area.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1999년도 하계학술대회 논문집 E
• /
• pp.2377-2379
• /
• 1999

In order to analyze failure rates of underground transmission power cable systems in Korea, the survey has been performed for the failure cases of cables, joints, and terminations in CV, OF and POF cable systems which occurred from 1983 to 1998. During 16 years, the failure cases due to trips of the systems were 47 among the total 108 cases, These 47 cases could be divided into internal reasons(manufacture/installation, corrosion and degradation) of 16 cases and external reasons (external mechanical damages, lightning, fire. etc.) of 31 cases. For the 154 kV cable systems during 12 years from 1987 to 1998, total failure rate was 0.0057 [case/100C-km/year] and internal reason failure rate was 0.0020 [case/100C-km/Year], which is similar to those of foreign countries. Also, the many cases of internal reason failures occurred in the early stage after the operations due to incorrect installations. This implies that the installation process is very important and some diagnostic tests such as PD measurement are needed besides after laying test.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제55권12호
• /
• pp.570-575
• /
• 2006

In this paper, we have investigated thermal properties by changing the content of carbon nanotube, which is component part of semiconductive shield in underground power transmission cable. Heat capacity (${\Delta}H$), glass transition temperature (Tg) and melting temperature (Tm) were measured with the samples of eight, through DSC (Differential Scanning Calorimetry), and the measurement ranges of temperature selected from $-100[^{\circ}C]\;to\;100[^{\circ}C]$ with heating temperature selected per $4[^{\circ}C/min]$ Also, high temperature, heat degradation initiation temperature, and heat weight loss were measured by TGA (Thermogravimetric Analysis) in the temperature from $0[^{\circ}C]\;to\;700[^{\circ}C]$ with rising temperature of $10[^{\circ}C/min]$. As a result, the Glass transition temperatures of the sample were showed near $-20[^{\circ}C]{\sim}25[^{\circ}C]$, and the heat capacity and melting temperature from the DSC was increased according to increasing the content of carbon nanotube, while, thermal diffusivity was increased according to increasing the content of carbon nanotube. Also, heat degradation initiation temperature from the TGA results was increasing according to increasing the content of carbon nanotube with CNT/EEA. Therefore, heat stabilities of EVA, which contained the we VA (vinyl acetate), showed the lowest.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 춘계학술대회 논문집
• /
• pp.222-225
• /
• 1999

Degradation diagnosis of XLPE insulated URD cables was accomplished through out new method. which was to be analyzed non-electrical experiments and synthesized by degradation points. To supplement this method, it was also carried out using several electrical analyses. Breakdown voltages were measured and breakdown lifetimes were Predicted appling for Weibull distribution function. As a result, breakdown lifetime in failure cables was shorted up to 1/3 times than that in general cables. It was very available to estimate cable degradation using above method, but it needs further study on XLPE insulated URD cables in order to improve reliability.

• Elastomers and Composites
• /
• 제33권4호
• /
• pp.238-245
• /
• 1998

이 논문은 원자력발전소에서 사용되고 있는 부분적으로 방사선 조사된 EPR 전력 케이블의 방사선 절연열화 진단을 행하기 위해서 전기특성을 조사한 것이다. 본 연구에서는 방사선 조사량을 100Mrad부터 200Mrad까지 증가시킨 케이블 시료를 열화비율에 따른 방사선 조사량에 의한 충전전류 및 방전전류를 측정한 결과 $4.3{\times}10^{-9}$(A)로부터 $1.03{\times}10^{-7}$(A)로 증가함을 알 수 있었다. 또한 100% 일때의 충전전류 및 방전전류를 50%, 16.7% 일때를 비교하면 후자의 케이블은 열화된 부분의 길이가 1/2, 1/6로 되므로 충전전류 및 방전전류로 1/2, 1/6로 흐름을 알 수 있었다. 열화하지 않은 22m와 66m의 케이블을 조사한 결과 66m의 케이블 시료쪽이 충전전류 및 방전전류 값이 22m 케이블보다 3배나 크다는 것을 확인했다. 이들 결과로부터 방사선을 조사한 EPR 케이블의 절연열화 진단법으로 충전전류 및 방전전류를 측정하는 것이 가능하다는 것을 확인했다.