• 한국전기전자재료학회논문지
• /
• 제28권10호
• /
• pp.636-641
• /
• 2015

In this study, the partial discharge degradation properties for 2-core PVC cable($2cores{\times}1.5mm^2$ cross section, length of 10 cm, 20 cm, 30 cm) following immersion with the salt water that the 2%, 4%, 8% of NaCl is dissolved in 100 g of distilled water for 48 and 96 hours has been measured. The results of this study are as follows. When the degradation time in salt water of 2% NaCl is 48 hours, it found that the number of partial discharge increased as about 40 pps, 50 pps, 90 pps with increasing the length of cable to 10 cm, 20 cm, 30 cm. In case the concentration and degradation time is same, the inception and extinction voltage decreased with increasing the length of cable. When the degradation time in salt water is 96 hours and the length of cable is 20 cm, it found that the number of partial discharge decreased as 3,000 pps, 500 pps, 100 pps with increasing the concentration of NaCl to 2%, 4%, 8%.

• 품질경영학회지
• /
• 제45권4호
• /
• pp.969-980
• /
• 2017

Purpose: The purpose of this study was to estimate the lifetime, and verify the target lifetime at steady state temperature, of communication cable jackets used in nuclear power plants. Method: This study was completed according to test and analysis methods required by international standards. After measuring the residual elongation(%) of specimens at specific points in time with the accelerated degradation test, average failure time of each temperature was computed. Thus, the activation energy could be derived by applying the temperature-Arrhenius law to estimate cable jacket lifetime at steady state temperature. Results: The cable jacket lifetime was estimated as 363.8 years assuming a normal nuclear power plant operating temperature of $90^{\circ}C$. Conclusion: To ascertain stable operating conditions for a nuclear power plant, accelerated degradation tests were performed according to the Arrhenius law for components of the nuclear power plants. The lifetime was estimated from the degradation data collected during the accelerated degradation test.

• 한국전기전자재료학회논문지
• /
• 제24권3호
• /
• pp.208-214
• /
• 2011

In this thesis, the partial discharge according to applied voltage and variations of cross-sectional area and length of the conductor related to general condition for using cable was measured in order to study degradation diagnosis for 2-Core cable of the PVC insulator used in industrial fields for other safety installations. Also the thermal degradation conditions under various installation circumstances of cables were studied by assuming degradation conditions with each different degradation rate (50%, 67%, 100%) such as variation in degradated temperature, thermal exposure time, normal state, partially degradated state and overall degradated state for thermal degradation diagnosis. The quantity of electric discharge (V-Q) according to applied voltage was measured for measurement of inception voltage and extinction voltage. The quantity of electric discharge and the number of electric discharge (Q-N) were measured with applied voltage kept constantly. In addition, pictures were taken using SEM (scanning electron microscope) to compare the surface of external insulator to degradated state of internal insulator according to thermal degradation temperature and also compare the surface of external insulator to degradated surface state of internal insulator according exposure time of cables to thermal stress.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 춘계학술대회 논문집 유기절연재료 전자세라믹 방전플라즈마 일렉트렛트 및 응용기술
• /
• pp.233-236
• /
• 2002

This paper describes the properties of between the residual voltage for ${\gamma}$-irradiated in electric power cable using in nuclear power generating station. As these properties related with ${\gamma}$-irradiation dose, it is suggested that these properties can be utilized as a index of irradiation degradation. From theory and experiment We found the residual voltage is not influenced by cable length. We found that residual voltage of basic composite and practical composite have not a difference an occasion be the same cable length. As the ratio of degradation increases, the residual voltage in the initial time range increases and the peak moves to the shorter time. Therefore, We can know the degree of radiation degradation from the position of the peak.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1993년도 정기총회 및 추계학술대회 논문집 학회본부
• /
• pp.76-78
• /
• 1993

When an alternating current is supplied to a super-conducting multi-stranded cable, the quench current value of the cable was observed to be less than the simple summation of individual quench current value of each strand. One of the causes for such a degradation was attributed to the nonuniform of the current distribution in multi-stranded cable due to magnetic mutual coupling among the strands. The degradation of the superconducting cable is evaluated theoretically by taking into account the magnetic coupling among the strands.

• Transactions on Electrical and Electronic Materials
• /
• 제1권1호
• /
• pp.12-16
• /
• 2000

In this paper, we analyze self field effects of Bi-2223 tape-stacked cable assuming constant current density in the cross section of stacked cable. Generally, the critical current of Bi-2223 tape-stacked-cable in much less than the total summation of critical currents of each tape, which is mainly due to the self magnetic fields of the cable itself. Therefore, to predict the critical current of Bi-2223 tape-stacked-cable, we needs to analyze the self filed effects on the stacked cable as well as critical current density data(J$\_$C/) of one tape. To make it more complex, the critical current degradation of Bi-2223 tape is an-isotropic; the critical current is lower in the normal magnetic field(to the tape surface) than in the parallel field. In the paper, a novel approach to predict the critical current of a Bi-2223 tape-stacked-cable from a J$\_$C/-B curve of one tape is presented with the assumption of constant current density across the stacked cable, The approach basically includes the load analysis of the stacked tapes, and its usefulness is confirmed by the experimental data.

• Nuclear Engineering and Technology
• /
• 제36권5호
• /
• pp.475-484
• /
• 2004

Extending the lifetime of a nuclear power plant [(hereafter referred to simply as NPP)] is one of the most important concerns in the global nuclear industry. Cables are one of the long-life items that have not been considered for replacement during the design life of a NPP. To extend the cable life beyond the design life, it is first necessary to prove that the design life is too conservative compared with actual aging. Condition monitoring is useful means of evaluating the aging condition of cable. In order to simulate natural aging in a nuclear power plant. a study on accelerated aging must first be conducted. In this paper, evaluations of mechanical aging degradation for a neoprene cable jacket were performed after accelerated aging under tcontinuous and intermittent heating conditions. Contrary to general expectations, intermittent heating to the neoprene cable jacket showed low aging degradation, 50% break-elongation, and 60% indenter modulus, compared with continuous heating. With a plant maintenance period of 1 month after every 12 or 18 months operation, we can easily deduce that the life time of the cable jacket of neoprene can be extended much longer than extimated through the general EQ test. which adopts continuous accelerated aging for determining cable life. Therefore, a systematic approach that considers the actual environment conditions of the nuclear power plant is required for determining cable life.

• 전기학회논문지
• /
• 제65권10호
• /
• pp.1780-1785
• /
• 2016

This paper presents few case studies of state diagnosis of XLPE cables using very low frequency techniques. The power cables of 22.9kV which have installation fault were assessed using VLF technique in addition to other techniques like insulation resistance and DC voltage withstand test. From the experimental results, The dielectric loss($tan{\delta}$) values of degradation of the cable(joint, knife, needle) at $U_0$ were 5.839, 5.526 and 6.251, respectively and all values were "further study advised". VLF PD measurement was also found defective portion. These method was effective in defect to fault in the degradation of the cable. However, the breakdown did not occur in the degradation of the cable because of properties of XLPE insulation. Few case studies of using VLF $tan{\delta}$ diagnosis for fault are measured and analyzed. The $tan{\delta}$ values at $U_0$ were "further study advised" or "action required".

• 한국전기전자재료학회논문지
• /
• 제28권1호
• /
• pp.34-39
• /
• 2015

In this study, the characteristics of partial discharge was measured for the four core silicone cable (0.6/1.0 kV, $1.0SQ{\times}4C$) with insulated part of 15 cm and conductor of 1cm. The following results have been confirmed as a result of this study. When the first line of cable is connected to the positive electrode and the second, third line of cable is connected to the negative electrode, it found that the inception voltage and extinction voltage decreased with increasing the line of negative electrode, and the partial discharge charge quantity(Q) increases, while the number of discharge occurrence has decreased. The inception voltage and extinction voltage of partial discharge has decreased with increasing the degradation rate in the 33%, 67%, 100%. Also, it confirmed that the partial discharge charge quantity(Q) and the number of discharge occurrence has decreased.

• 대한기계학회논문집A
• /
• 제24권3호
• /
• pp.761-768
• /
• 2000

In order to investigate how the fatigue damage effects on the critical properties of superconductor, a fatigue test at room temperature and an Ic measurement test at 4.2K were carried out in this study, respectively, using a 9 strand Cu-Ni/NbTi/Cu composite cable. Through the fatigue test of a 9 strand Cu-NUNbTi/Cu composite cable, a conventional S-N curve was plotted even though there was a possibility of fretting among strands. It was found that the maximum stress corresponding to the inflection point on the S-N curve obtained was nearly the same value as the yielding strength of cable obtained from the static tensile test. However, the effect of cabling in multi-strands superconducting cable on the fatigue strength was not noticeable. The critical current(Ic) measurement was carried out at 4.2K in a NbTi strand out of the fatigued cable. It showed a degradation of lc at high stress amplitude regions over 380NTa, and the degradation became significant as the applied stress amplitude increased.