• Macromolecular Research
• /
• v.14 no.2
• /
• pp.194-198
• /
• 2006

Polystyrene, PS, particles of 450 nm diameter and poly(styrene-co-styrene sulfonate), PSS, particles of 140-160 nm diameter were prepared by emulsifier-free emulsion polymerization. The surfaces of the PS and PSS particles were coated with Ag nanoparticles for the application of antimicrobial agents by reduction of Ag ions using ${\gamma}$-irradiation. The Ag-PS and Ag-PSS were characterized by High-Resolution Transmittance Electron Microscopy (HR-TEM), Field-Emission Scanning Electron Microscopy (FE-SEM), and Energy Dispersive X-ray Spectroscopy (EDXS). The HR-TEM and EDXS data showed that the Ag nanoparticles were loaded on the surface of the PS and PSS particles, respectively. The antimicrobial efficiency of the Ag-PS and Ag-PSS particles (0.4 g) with ca. 100 ppm Ag, which was coated onto yam (KS K 0905-1996 rule), was tested against Staphylococcus aureus ATCC 6538 and Klebsiella pneumoniae ATCC 4352 after 100 washing cycles (KS K 0432-1999 rule). The antimicrobial efficiency of the Ag-PS particles against Staphylococcus aureus ATCC 6538 and Klebsiella pneumoniae ATCC 4352 was 99.9% after 100 cycles washing., confirming that the Ag-PS particles can be used as antimicrobial agents.

• Journal of the Korean institute of surface engineering
• /
• v.40 no.5
• /
• pp.225-233
• /
• 2007

Effects of alloying elements on the corrosion layer formation of Pb-grid/active materials interface has been researched for improvement of corrosion resistance of Pb-Ca alloy. For this research, various amounts of alloying elements such as Sn, Ag and Ba were added to the Pb-Ca alloys and investigated their corrosion behaviors. Batteries fabricated by using these alloys as cathode grids were subjected to life cycle test. Overcharge life cycle test was carried out at $75^{\circ}C$, 4.5 A, for 110 hrs. with KS standard (KSC 8504). And then, after keeping the battery with open circuit state for 48 hr, discharge was carried out at 300A for 30 sec. Corrosion morphology and interface between Pb-grid and active materials were investigated by using ICP, SEM, WDX, and LPM. Corrosion layer of Pb-Ca alloy got thicken with increasing Ca content. For Pb-Ca-Sn alloy, thickness of corrosion layer decreased as Sn and Ag content increased gradually. In case of Pb-Ca-Sn-Ba alloy, thickness of corrosion layer decreased up to 0.02 wt% Ba addition, whereas, it was not changed in case of above 0.02 wt% Ba addition.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.9
• /
• pp.802-807
• /
• 2007

We have developed red phosphorescent top emission organic light-emitting diodes with transparent metal cathodes deposited by using thermal evaporation technique. Phosphorescent guest molecule, BtpIr(acac), was doped in host CBP for the red phosphorescent emission, Ca/Ag, Ba/Ag, and Mg/Ag double layers were used as cathode materials of top emission devices, which were composed of glass/Ni/2TNATA(15 nm)/${\alpha}$-NPD(35 nm)/CBP:BtpIr(acac)(40 nm, 10%)/BCP(5 nm)/$Alq_3$(5 nm)/cathodes. The optical transparencies of these metal cathodes strongly depend on underlying Ca, Ba, and Mg layers. These layers also strongly affect the electrical conduction and emission properties of the red phosphorescent top emission devices.

• Bulletin of the Korean Chemical Society
• /
• v.14 no.5
• /
• pp.603-610
• /
• 1993

The crystal structure of dehydrated $Ag_{5.6}K_{6.4}-A$, zeolite A ion-exchanged with $K^+\;and\;Ag^+$ as indicated and dehydrated at 360$^{\circ}$C, has been determined by single-crystal X-ray diffraction techniques. Also determined were the structures of the products of the reactions of this zeolite with 0.1 Torr of Cs vapor at 250$^{\circ}$C for 48 h and 72 h, and with 0.1 Torr of Rb vapor at 250$^{\circ}$C for 24 h. The structures were solved and refined in the cubic space group Pm3m at 21(l)$^{\circ}$C (a= 12.255(l) ${\AA}$ , 12.367(l) ${\AA}$, 12.350(l) ${\AA}$, and 12.263(l) ${\AA}$, respectively). Dehydrated $Ag_{5.6}K_{6.4}$-A was refined to the final error indices $R_1= 0.044\;and\;R_2=0.037$ with 202 reflections for which I>3${\sigma}$(I). The crystal structures of the reaction products were refined to $R_1=0.087\;and\;R_2= 0.089$ with 157 reflections, $R_1=0.080\;and\;R_2= 0.087$ with 161 reflections, and $R_1= 0.071\;and\;R_2=0.061$ with 88 reflections, respectively. In the structure of $Ag_{5.6}K_{6.4}-A,\;K^+$ ions block all 8-oxygen rings, and one reduced Ag atom is found per sodalite cavity. Also, ca. 4.6 $Ag^+ ions\;and\;3.4 K^+ ions$ are found at 6-ring sites in the large cavity. The crystal structures of the reaction products show that all $K^+$ and $Ag^+$ ions have been reduced, and that all K^+$ atoms have left the zeolite. Cs or Rb species are found at three different crystallographic sites: 3.0 $Cs^+\;or\;3.0Rb^+$ ions per unit cell occupy 8-ring centers, ca. 8.0 $Cs^+ ions\;or\;5.7 Rb^+$ ions, are found on threefold axes opposite 6-rings deep in the large cavity, and ca. 2.5 $Cs^+\;or\;2.3 Rb^+ ions are found on threefold axes in the sodalite unit. Also, 1 $Rb^+$ ion lies opposite a 4-ring. Silver atoms, corresponding to 75% or 40% occupancy of hexasilver clusters stabilized by coordination to $Cs^+\;or\;Rb^+$ ions, are found at the centers of the large cavities. In the crystal structures of dehydrated Ag_{5.6}K_{6.4}-A$ reacted with Cs vapor, excess Cs atoms are absorbed and these form (locally) cationic clusters such as $(Cs_4)3^+\;and\;(Cs_6)4^+$.

• The Journal of Engineering Research
• /
• v.3 no.1
• /
• pp.189-197
• /
• 1998

Hyeroxyapatite(HAp) which has good biocompatibility was made by Wet Chemical Process. The surface of Ti-6Al-4V, coated with HAp by lon Beam Assisted Deposition (IBAD), was treated with 5ppm, 10ppm, 20ppm, and 100ppm of $AgNO_3$ solution. In this Ag impregnation process, $Ca^{2+}$ of HAp was substituted with $Ag^+$ of $AgNO_3$. In this study, the antimicrobial effect and biocompatibility of Ti-6Al-4V alloy which was coated with Ag-HAp were examined. The antimicrobial test was carried out with two kinds of bacteria(P. Aeruginosa, S. Epidermidis), which are highly infectious in a transplanting operation of implant materials. As a result of the test, it was observed that Ti-6Al-4V alloy which was treated by 20ppm of $AgNO_3$ solution has good biocompatibility. In order to observe the antimicrobial mechanism of $Ag^+$, E. coli which is the most common bacterium was treated by Ag-HAp. Then cell morphology of E. coli was observed by the transmission electron microscope(TEM). The destruction of cell wall and cytoplasm of E. coil were observed. A black spot appeared in the cytoplasm was analyzed by energy dispersive analysis X-ray (EDAX) and it showed a small amount of $Ag^+$. Thus, it was proved that $Ag^+$ destroys bacteria effectively and Ti-6Al-4V alloy which was impregnate with Ag ion show antimicrobial effect on infection bacteria.

• Journal of the Korean Ceramic Society
• /
• v.41 no.4
• /
• pp.334-339
• /
• 2004

Microstructures and mechanical properties of SPSed monolithic HAp, HAp-Ag, and HAp-ZrO$_2$sintered bodies were investigated by the XRD, SEM, and TEM techniques. The nano-sized HAp powders were successfully synthesized by precipitation of Ca(NO$_3$)$_2$4$H_2O$ and (NH$_4$)HPO$_4$solution. In the HAp-Ag composite, the shrinkage cavities were observed at the interfaces between HAp and large sized Ag particles due to the mismatch of their thermal expansion coefficients. However, no found the defect at the interfaces between HAp and fine-sized Ag particles. In the HAp-ZrO$_2$composite. nano-sized ZrO$_2$particles were almost dispersed at the grain boundaries of HAp phase. The fracture toughness of HAp-Ag and HAp-ZrO$_2$ composites were increased due to the plastic deformation and phase transformation mechanisms of the dispersed fine Ag and ZrO$_2$phase in the HAp matrix, respectively.

• Resources Recycling
• /
• v.25 no.5
• /
• pp.50-56
• /
• 2016

Extraction behaviour of silver from nitric acid solutions by Cyanex 301 as an extractant was examined. Detailed studies have been conducted to evaluate the effect of different variables influencing the extraction such as concentration of nitric acid and extractant, phase ratio(O/A) and synergism of mixed extractant. The extraction behaviour of associated metals namely Ca, Al, Fe, Zn and Sr has been investigated. The extraction results show that Ag can be extracted effectively by Cyanex 301 and selectively extracted from 3.0M $HNO_3$ using 5% Cyanex 301. Impurity metals loaded in organic phase can be effective scrubbed by 4.0M HCl. Finally, pure silver solution can be obtained efficiently by thiourea as a stripping reagent.

• Journal of Environmental Science International
• /
• v.10 no.6
• /
• pp.387-391
• /
• 2001

The hydroxyapatite(HAp) as a carrier the for ion exchange agent of $Ag^+$ions was prepared in semiconductor fabrication, The Ca/P molar ratio of the HAp was 1.65. The HAp is molded in shape of the antimcrobial ball and then sintered at 100$0^{\circ}C$ Ag-containing HAp(HAp-Ag) was prepared by incorporating $Ag^+$/ions in HAp crystals through an ion-exchange reaction in solutions containing 0.01M $AgNO_3$. The antimicrobial effect of HAp-Ag for bacteria such as Escherichial coli and Staphylococcus aureus has been Investigated. The concentrations of silver in the antimicrobial ball was determined by inductively coupled plasma and the amount of $Ag^+$ions was 9.0$\mu\textrm{g}$/g. The HAp-Ag exhibited excellent antimicrobial effect for bacteria such as E. coli and S. aureus. The bactericidal activity was considered to be caused by direct contact of bacteria with $Ag^+$ions in the HAp crystals. The HAp would likely to be possible as a carrier of antimicrobial metal ions such as Ag, Cu, and Zn by recycling of waste sludge in the semiconductor fabrication process.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.6
• /
• pp.535-538
• /
• 2002

Suspension effect has been studied by using superconductor of BiPbSrCaCuO ceramics containing $Ag_2()$. It has been clear that $Ag_2()$ acts as pinning center which plays an important role to the suspension effect. Magnetic repulsive force which affects a superconductor located in magnetic flux from toroidal magnet, has been investigated. It has been concluded that the suspension effect arises from the interaction between the pinning effect and the diamagnetic effect.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.101-103
• /
• 2001

Suspension effect has been studied by using superconductor of BiPbSrCaCuO ceramics containing $Ag_{2}O$ It has been cleared that $Ag_{2}O$ acts as pinning center which plays an important role to the suspension effect. Magnetic repulsive force which affects a superconductor located in magnetic flux from toroidal magnet has been investigated. It has been concluded that the suspension effect arises from the interaction between the pinning effect and the diamagnetic effect.