• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.10 no.6
• /
• pp.48-56
• /
• 2001

In this paper, this study aims at the evaluation on the characteristics of CFRP laminate plates using a falling weight impact tester. The experiment was conducted on several laminates of different orientation. A system was built far measur- ing the impact strength of CFRP laminates in consideration of stress wave propagation theory using a falling weight impact tester. Delamination areas of impacted specimens for the different ply orientation were measured with ultrasonic C- scanner to find correlation between impact energy and delamination area. Absorbed energy of quasi-isotropic specimen having flour interfaces was higher than that of orthotropic laminates with two interfaces. The more interfaces, the greater the energy absorbed. The absorbed energy oft hybrid specimen containing a GFRP layer was higher than that of normal specimens.

• Composites Research
• /
• v.16 no.2
• /
• pp.9-17
• /
• 2003

We have implemented a system of falling weight impact tester in order to evaluate the impact energy absorbing characteristics and impact strength of CFRP laminate plates. The absorbed energy of T-300 orthotropic composites is higher than that of quasi-isotropic specimen over impact energy 7J, but in case of using T700 fiber, much difference does not show. Also, absorbed energy of T-300 orthotropic composites, which are composed of the same stacking number and orientation became more than that of T700 fiber specimen however there was no big difference in case of quasi-isotropic specimens. Delamination area of impacted specimens was measured with ultrasonic C-scanner to find correlation between impact energy and delamination area. Delamination area and frequency responses were evaluated between impacted and unimpacted specimens. There is a strong correlation between frequency responses and impact-induced delamination. The presence and scale of damages have been investigated based on the variations of frequency responses.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.21 no.3
• /
• pp.251-260
• /
• 2001

Damage Profess of CFRP laminates under monotonic tensile test was characterized by the correlation between Acoustic Emission(AE) and Ultrasonic Test(UT). The amplitude distribution of AE signal from a specimens is an aid to the determination of the extent of the different fracture mechanism such as matrix crack, debonding, fiber pullout and fiber fracture as load is increased. In addtion, the characteristics of ultrasonic amplitude attenuation are useful lot analysis of the different type of fracture mechanism. Different orientation of carbon fiber reinforced plastic specimens were used to investigate the AE amplitude range and ultrasonic amplitude attenuation. Finally, loading-unloading tests were carried out to check Felicity effect. During the tests, ultrasonic amplitude attenuation was investigated at the same time and compared with AE parameters. The result showed that two parameters of both AE and UT could be effectively used for analysis of fracture mechanism in CFRP laminates.

• Composites Research
• /
• v.13 no.6
• /
• pp.30-38
• /
• 2000

In this paper, a system of falling weight impact tester was built up to evaluate the impact energy absorbing characteristics and impact strength of CFRP laminate plates in consideration of stress wave propagation theory. Delamination area of impacted specimens for the different ply orientation was measured with ultrasonic C-scanner to find correlation between impact energy and delamination area. Absorbed energy of quasi-isotropic specimen having four interfaces was higher than that of orthotropic laminates with two interfaces. The more interfaces, the more absorbed energy. Hybrid specimen containing GFRP layer was higher than that of normal specimens.

• Composites Research
• /
• v.36 no.6
• /
• pp.441-447
• /
• 2023

Recently, as demand for high-strength, lightweight materials has increased, there has been great interest in joining with metals. In the case of mechanical bonding, such as bolting and riveting, chemical bonding using adhesives is attracting attention as stress concentration, cracks, and peeling occur. In this paper, surface treatment was performed to improve the adhesive strength, and the change in adhesive strength was analyzed. For the adhesive strength test were conducted with Carbon Fiber Reinforced Plastic(CFRP), CR340(Steel), and Al6061(Aluminum), and laser and plasma surface treatment were used. After plasma surface treatment, the adhesive strength improved by 7.3% and 39.2% in CFRP-CR340 and CFRP-Al6061, respectively. CR340-Al6061 was improved by 56.2% in laser surface treatment. Surface free energy(SFE) was measured by contact angle after plasma treatment, and it is thought that the adhesion strength was improved by minimizing damage through a chemical reaction mechanism. For laser surface treatment, it is thought that creates a rough bonding surface and improves adhesive strength due to the mechanical interlocking effect. Therefore, surface treatment is effect to improve adhesive strength, and based on this paper, the long-term fatigue test will be conducted to prevent fatigue failure, which is a representative cause of actual structural damage.

• Composites Research
• /
• v.36 no.1
• /
• pp.16-24
• /
• 2023

This paper presents a multi-scale progressive fatigue damage model incorporating the model for interfacial debonding between fibers and matrix. The micromechanics model for the progressive interface debonding was adopted, which defined the four different interface phases: (1) perfectly bonded fibers; (2) mild imperfect interface; (3) severe imperfect interface; and (4) completely debonded fibers. As the number of cycles increases, the progressive transition from the perfectly bonded state to the completely debonded fiber state occurs. Eshelby's tensor for each imperfect state is calculated by the linear spring model for a damaged interface, and effective elastic properties are obtained using the multi-phase homogenization method. The fatigue damage evolution formulas for fiber, matrix and interface were proposed to demonstrate the fatigue behavior of CFRP laminates under cyclic loading. The material parameters for the fiber/matrix fatigue damage were characterized using the chaotic firefly algorithm. The model was implemented into the UMAT subroutine of ABAQUS, and successfully validated with flat-bar UD laminate specimens ([0]₈,[90]₈, [30]₁₆) of AS4/3501-6 graphite/epoxy composite.

• Journal of Platform Technology
• /
• v.10 no.4
• /
• pp.3-10
• /
• 2022

In this study, damage resulting from internal flaws was investigated by finite element analysis for the safety evaluation of a non-destructive testing platform for hydrogen pressure vessels. A specimen was modeled and calculated using finite element analysis to determine material properties in accordance with the parameters of the composite material in order to assess the safety of the Type 4 hydrogen pressure vessel. Through this, flaws in the hydrogen pressure vessel were modeled, and test conditions were provided in accordance with rules to look into whether there was safety. Delamination, foreign object, and vertical cracks were modeled for internal flaws, and damage was examined in accordance with failure criteria. As the delamination defect approached the interior of the hydrogen pressure tank, it became more likely to cause damage. Additionally, as the crack depth grew in the case of vertical cracks, the likelihood of crack propagation rose. On the other hand, it was anticipated that the foreign item defect would suffer more damage from the outside in. A non-destructive testing platform will be used to assess the safety of fuel cell vehicles that are already in operation in future research.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.30 no.5
• /
• pp.429-436
• /
• 2010

Recently, (terahertz ray) applications have emerged as one of the most promising new powerful nondestructive evaluation (NDE) techniques. In this study, a new T-ray time-domain spectroscopy system was utilized for detecting and evaluating layup effect and flaw in FRP composite laminates. Extensive experimental measurements in reflection and thru-transmission modes were made to map out the T-ray images. Especially this was demonstrated in thick GFRP laminates containing double saw slots. In carbon composites the penetration of terahertz waves is limited to some degree and the detection of flaws is strongly affected by the angle between the electric field(E-field) vector of the terahertz waves and the intervening fiber directions. The artificial defects investigated by terahertz waves were bonded foreign material, simulated disbond and delamination and mechanical impact damage. The effectiveness and limitations of terahertz radiation for the NDE of composites are discussed.