Abstract
We have implemented a system of falling weight impact tester in order to evaluate the impact energy absorbing characteristics and impact strength of CFRP laminate plates. The absorbed energy of T-300 orthotropic composites is higher than that of quasi-isotropic specimen over impact energy 7J, but in case of using T700 fiber, much difference does not show. Also, absorbed energy of T-300 orthotropic composites, which are composed of the same stacking number and orientation became more than that of T700 fiber specimen however there was no big difference in case of quasi-isotropic specimens. Delamination area of impacted specimens was measured with ultrasonic C-scanner to find correlation between impact energy and delamination area. Delamination area and frequency responses were evaluated between impacted and unimpacted specimens. There is a strong correlation between frequency responses and impact-induced delamination. The presence and scale of damages have been investigated based on the variations of frequency responses.
낙추충격 시험시스템을 제작하여 CFRP적층판의 충격흡수특성 및 충격강도가 평가가 가능하였다. 충격에너지 대략 7J이상에서는 동일한 T300 섬유와 적층배향으로 구성된 직교이방성 시험편이 의사등방성(quasi-isotropic)보다 높게 나타났으나 T700 섬유의 경우에는 크게 차이가 나타나지 않았다. 또한 동일한 T300섬유와 적층수로 구성된 시험편이 T700 섬유로 된 시험편보다 높게 나타났으나 T700섬유인 의사등방성 시험편의 경우에는 크게 차이가 나타나지 않았다 초음파 C-스캐너를 이용하여 내부손상영역을 관찰하여 시험편의 손상면적과 흡수에너지의 상관관계를 고찰하였으며, 충격손상유무에 따라 박리면적과 주파수응답계수를 평가하였다 주파수응답계수와 박리면적사이에는 상관관계가 있음을 알 수 있었으며 충격손상으로 인한. 손상의 유무 및 정도를 주파수응답계수로 평가가 가능하였다.