• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2012.05a
• /
• pp.73-75
• /
• 2012

In this study, basic physical properties and color development of the black concrete depending on CASB-SP dosages are investigated. According to results, It showed that the slump and air contents of the concrete containing CASB-SP meet all requirements of concrete except when CASB-SP 5.0 % is used. It also showed that the more the CASB-SP is used, the higher the compressive strength becomes. On the other hand, It is found that if the CASB-SP 5.0 % is used, the compressive strength was reduced as the more CASB-SP 5 % is used. In terms of color, it was found out that the more CASB-SP is used, the darker the black becomes.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.1 no.3
• /
• pp.181-188
• /
• 2013

This paper is to investigate experimentally an effect of carbon amino silica black-superplasticizer(CASB-SP)on the engineering properties and chromaticity of black color concrete with 0.45 of W/C(water to cement). CASB-SP and carbon black were applied for pigment of the concrete. To prevent efflorescence of concrete, four different water repellent agents were also applied. As results, it was found that use of CASB-SP increased the slump and air contents. Furthermore, the use of CASB-SP increased the compressive strength. As CASB-SP dosages increased, chromaticity was well developed. For the effect of water repellent agent, the use of epoxy type was effective for protection from efflorescence. Based on test results, it was evaluated that 0.5% of CASB-SP effectively improve the concrete quality as well as enhance the chromaticity with proper dosage.

• Journal of the Korea Institute of Building Construction
• /
• v.13 no.6
• /
• pp.627-633
• /
• 2013

This paper presents the result of a mock-up test and field application of concrete that is black in color thanks to the application of superplasticizer containing carbon amino silica black (CASB-SP). Mock-up specimen with a size of $3000{\times}1500{\times}40$ mm was fabricated with black concrete applying 0.5% of CSAB-SP with 27 MPa. After dividing the zone in wall mock-up specimen, three different water repelling agents were applied to verify its effect of efflorescence prevention. It was found that the use of CASB-SP with 0.5% made the black concrete develop a highly clear black color, and the epoxy type water repelling agent had better performance in efflorescence prevention. Based on mock-up test, field application was conducted with bridge member. It was also found that the application of CASB-SP showed favorable results in black color development.