• Food Science and Preservation
• /
• v.8 no.4
• /
• pp.379-384
• /
• 2001

This study was conducted to investigate the changes in quality of soybean sprouts grown by ozone treatment during storage. Soybean spouts were cultivated under conditions of ozone water watering after soaking in water (W/W), watering after soaking in ozone water (O/W), ozone water watering after soaking in water (W/O) and ozone water watering after soaking in ozone water (O/O). The ozone concentration in soaking of soybean and watering of soybean sprouts was 0.3 ppm, respectively. No significant difference in shelf-life between W/W soybean sprouts and ozone treated samples showed. But shelf-life of soybean sprouts stored in 0.01 ㎜ polyethylene film at 10$\^{C}$ and 20$\^{C}$ prolonged 4 and 2 days, respectively. The slow growth of total microbe in the ozone treated samples stored at 10$\^{C}$ was observed, whereas that of products at 20$\^{C}$ showed rapid growth during storage. However, no great difference occurred among samples in the changes of moisture, vitamin C and chlorophyll content during storage. Higher hardness of soybean spouts stored at 10$\^{C}$ and 20$\^{C}$ was kept in the O/W and W/O products. Color, flavor and overall acceptability evaluated by sensory teat during storage had higher scores in O/W products as compared to the other samples.

• Proceedings of the KIEE Conference
• /
• 2006.07c
• /
• pp.1311-1312
• /
• 2006

This paper describes the ohmic contact formation between a TiW film as a contact material deposied by RF magnetron sputter and polycrystalline 3C-SiC films deposied on thermally grown Si wafers. The specific contact resistance (${\rho}_c$) of the TiW contact was measured by using 4he C-TLM. The contact phase and interfacial reaction between TiW and 3C-SiC at high-temperature were also analyzed by XRD and SEM. All of the samples didn't show cracks of the TiW film and any interfacial reaction after annealing. Especially, when the sample was annealed at $800^{\circ}$ for 30min., the lowest contact resistivity of $2.90{\times}10^{-5}{\Omega}{\cdot}cm^2$ of was obtained due to the improved interfacial adhesion.

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.3 no.3
• /
• pp.187-198
• /
• 1970

The author succeeded in rearing the young blue crab from the first stage of zoe ato the true crab shape, and during this time he observed their growth and metamorphosis. The relationships between the number of eggs carried by female crabs (E) and the carapace width (C) and body weight (W) are shown as follows: E= 27.9049C-281.8155, E=0.5682 W-116.4606. There are five zoeal stages and a megalopa in the complete larval development of the blue crab. Water temperature in rearing aquaria ranged from 21.4 to $25.2^{\circ}C$. The duration of each zoeal stage was two days on the average. After the fifth moulting, the zoea becomes megalopa and 5 to 6 days later the megalopa moults and develops into the first stage of adult crab shape. The carapace width of megalopa measured about 1.70 mm and the carapace length, from the tip of the rostrum to the posterior dorsal margin of the carapace, was about 2.78 mm on the average. The carapace width and length of the first crab, 18 days after hatching, measured about 4.48 mm and 2.62 mm respectively. After two days, the first crab moulted and grew into the second crab with about 6.47 mm in carapace width and 4.66 mm in carapace length. The larval rearing in the outdoor tank shelved better results than in the indoor aquarium. The highest mortality occurred when the first stage of zoea moulted into the second stage. Percentage of crabs which survived, from the first crab to the ninth crab stages, was about $55\%$. The relationships between rearing days (D) and the carapace width (C), carapace length (L) and body weight (W) of the crab stages during 40 days of rearing are shown as follows. Carapace width, Indoor: C=1.1250D+1.7227 Outdoor C=1.3465D -0.2449 Carapace length, Indoor: L=0.6654D+1.6712 Outdoor: L=0.7893D+0.6919 Body Weight, Outdoor: $$W=1.15e^{0.12423D}$$ Indoor: $$W=6.759\times10^{-2}D^{1.2598}$$ (9-19 day old crabs) Outdoor: $$W=4.136\times10^{-2}D^{1.6024}$$ (21-40 day old crabs) During the crab stage, the following relationships between the number of moulting times and the carapace width (C), carapace length (L) and body weight (W) were found as follows: $$C=5.2e^{0.28119N}$$ $$L=3.65e^{0.26372N}$$ $$W= 0.14e^{0.7037N}$$ The relationships between the carapace length (L) and the carapace width (C) and body weight (W) of the crab stages are shown as follows: Carapace length, mm Formula 2.62-27.17 L=1.6864C-1.0387 7.47-18.53 $$W=9.367\times10^{-5}C^{3.5567}$$ 22.11-27.17 $$W=3.406\times10^{-5}C{3.8571}$$

• Journal of Bio-Environment Control
• /
• v.17 no.2
• /
• pp.90-95
• /
• 2008

It has become a big matter of concerns that the skill and measures against reduction of energy and cost for heating a protected horticultural greenhouse were prepared. But in these days necessity of cooling a protected horticultural greenhouse is on the rise from partial high value added farm products. In this study, therefore, a horizontal type geothermal heat pump system with 10 RT scale to heat and cool a protected horticultural greenhouse and be considered to be cheaper than a vertical type geothermal heat pump system was installed in greenhouse with area of $240\;m^2$. And cooling performances of this system were analysed. As condenser outlet temperature of heat transfer medium fluid rose from $40^{\circ}C$ to $58^{\circ}C$, power consumption of the heat pump was an upturn from 11.5 kW to 15 kW and high pressure rose from 1,617 kPa to 2,450 kPa. Cooling COP had the trend that the higher the ground temperature at 1.75 m went, the lower the COP went. The COP was 2.7 at ground temperature at 1.75 m depth of $25.5^{\circ}C$ and 2.0 at the temperature of $33.5^{\circ}C$ and the heat extraction rate from the greenhouse were 28.8 kW, 26.5 kW respectively at the same ground temperature range. 8 hours after the heat pump was operated, the temperature of ground at 60 cm and 150 cm depth buried a geothermal heat exchanger rose $14.3^{\circ}C$, $15.3^{\circ}C$ respectively, but the temperature of ground at the same depth not buried rose $2.4^{\circ}C$, $4.3^{\circ}C$ respectively. The temperature of heat transfer medium fluid fell $7.5^{\circ}C$ after the fluid passed through geothermal heat exchanger and the fluid rejected average 46 kW to the 1.5 m depth ground. It analyzed the geothermal heat exchanger rejected average 36.8 W/m of the geothermal heat exchanger. Fan coil units in the greenhouse extracted average 28.2 kW from the greenhouse air and the temperature of heat transfer medium fluid rose $4.2^{\circ}C$after the fluid passing through fan coil units. It was analyzed the accumulation energy of thermal storage thank was 321 MJ in 3 hours and the rejection energy of the tank was 313 MJ in 4 hours.

• Electrical & Electronic Materials
• /
• v.4 no.2
• /
• pp.150-158
• /
• 1991

본 연구에서는 0.80Pb(F $e_{1}$2/N $b_{1}$2/) $O_{3}$-(0.20-x)Pb(F $e_{2}$3/ $W_{1}$3/) $O_{3-x}$Ba(C $u_{1}$2/ $W_{1}$2/) $O_{3}$ (x=0.01, 0.02, 0.03) 세라믹을 소결온도 및 시간을 각각 860~960[.deg.C], 2시간으로 하여 일반 소성법으로 제작하였다. 시편의 조성비와 소결온도에 따른 구조적, 유전적 특성을 조사하였으며 유전손실 특성의 개선을 위해 조성 0.80Pb(F $e_{1}$2/N $b_{1}$2/) $O_{3}$-0.18Pb (F $e_{2}$3/ $W_{1}$3/) $O_{3}$-0.02Ba(C $u_{1}$2/ $W_{1}$2/) $O_{3}$시편에 Mn $O_{2}$를 0~1.25[wt%]로 첨가한 후 유전특성의 변화를 관찰하였다. Mn $O_{2}$의 첨가량이 증가함에 따라 결정립의 크기와 유전상수는 점차 감소하였다. 소결밀도는 900[.deg.C]에서 소결시킨 시편의 경우 최대값을 나타내었다. Ba(C $u_{1}$2/ $W_{1}$2/) $O_{3}$의 양이 0.01에서 0.03[mol]로 증가함에 따라 상전이온도는 38[.deg.C]에서 2[.deg.C]로 감소하였다. 조성 0.80Pb(F $e_{1}$2/N $b_{1}$2/) $O_{3}$0.18Pb(F $e_{2}$3/ $W_{1}$3/) $O_{3}$-0.02Ba(C $u_{1}$2/ $W_{1}$2/) $O_{3}$에 Mn $O_{2}$가 0.25[wt%] 첨가된 시편의 20[.deg.C]에서의 유전상수는 16,700으로 최대값을 유전손실을 1.28[%]로 최소값을 나타내었다. 또한 모든 시편은 온도 및 주파수에 따라 유전상수가 완만하게 변화하는 유전이완 특성을 나타내었다.다.

• Nuclear Engineering and Technology
• /
• v.5 no.1
• /
• pp.3-12
• /
• 1973

Some physical and chemical properties of wood-plastic combinations(W.P.C.) made of domestic soft woods such as pinus densiflora, pinus rigida and poplus deltoides were measured. The rates of improvement in properties were roughly proportional to the contents of polymer or polymer mixtures in W.P.C. For the W.P.C. obtained by means radiation curing and containing 80% of polymer or polymer mixture, the hardness and water absorptirity were improved 2.2 times and 4 times those of the original wood, respectively. The improvement of hardness was especially remarkable in the W.P.C. made of pinus densiflora and polystyrene(120%) to show 7 times increased hardness. For the W.P.C. obtained by means of thermal curing and containing 80% of polymer or polymer mixture, the hardness and water absorptivity were improved 2.4 times and 3.4 times those of the non-treated woods, respectively. These data indicate that the properties of W.P.C. prepared by means of radiation curing are not much different from those of W. p. C. prepared by means of thermal curing. Both of acid resistancy and alkali resistancy of the W.P.C. were also improved remarkably in comparison with the non-treated wood.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.72-73
• /
• 2005

Stress behavior was studied to investigate the internal behaviors of boron, carbon, and nitrogen in the 1000${\AA}$-thick tungsten boron carbon nitride (W-B-C-N) thin films. The impurities in the W-B-C-N thin films provide stuffing effects that were very effective for preventing the interdiffusion between interconnection metal and silicon substrate during the subsequent high temperature annealing process. The resistivity of W-B-C-N thin film decreases as an annealing temperature increase. The W-B-C-N thin films have compressive stress, and the stress value decreased up to $4.11\times10^{10}dyne/cm^2$ as an $N_2$ flow rate increases up to 3 sccm.

• Elastomers and Composites
• /
• v.40 no.3
• /
• pp.174-180
• /
• 2005

Sonochemical synthesis of fullerene oxides $[C_{70}O_n](n=1{\sim}2)$ by fullerene$[C_{70}]$ and metal hexacarbonyl complexes $M(CO)_6$(M=Cr, Mo, W) took place under air atmosphere. The reactivity of fullerene$[C_{70}]$ and several metal hexacarbonyl complexes $M(CO)_6$(M=Cr, Mo, W) under same ultrasonic condition increased in the order of $Mo(CO)_6$ > $W(CO)_6$ > $Cr(CO)_6$. The MALDI-TOF-MS, UV-visible spectra, and HPLC analysis confirmed that the products of sonochemical reaction were $[C_{70}O_n](n=1{\sim}2)$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.406-407
• /
• 2006

This paper describes the ohmic contact formation between a TiW film as a contact material deposied by RF magnetron sputter and polycrystalline 3C-SiC films deposied on thermally grown Si wafers. The specific contact resistance (${\rho}_c$) of the TiW contact was measured by using the C-TLM. The contact phase and interfacial reaction between TiW and 3C-SiC at high-temperature were also analyzed by XRD and SEM. All of the samples didn't show cracks of the TiW film and any interfacial reaction after annealing. Especially, when the sample was annealed at $800^{\circ}$ for 30min., the lowest contact resistivity of $2.90{\times}10^{-5}{\Omega}cm^2$ was obtained due to the improved interfacial adhesion.

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.15 no.3
• /
• pp.211-218
• /
• 1982

The specific heat capacity and density of soybean oil and soy protein composing of the soybean curd were measured between $30^{\circ}C\;and\;-40^{\circ}C$. The thermal conductivity of soybean oil was measured to be 0.160 and 0.140, $W/m{\cdot}K$ at unfrozen and frozen states, respectively. The effective thermal conductivity of the soybean curd depended not only on its water content but also on its fat and protein contents.