• The Journal of Advanced Prosthodontics
• /
• 제11권1호
• /
• pp.1-6
• /
• 2019

PURPOSE. The purpose of this in vitro study was to evaluate the effect of surface grinding and polishing procedures using high speed zirconia diamond burs with different grit sizes on the phase transformation and flexural strength of zirconia. MATERIALS AND METHODS. Forty disc shape specimens ($15{\times}1.25mm$) with a cylindrical projection in the center of each disc ($1{\times}3mm$) were fabricated with 3Y-TZP (Prettau, Zirkonzahn, Italy). The specimens were divided into 4 groups (n=10) according to the grinding and polishing procedures: Control group - grinding (coarse-grit diamond bur), Group 1 - grinding (coarse-grit diamond bur) + polishing, Group 2 - grinding (fine-grit diamond bur) + polishing, and Group 3 - grinding (fine grit diamond bur). Each specimen was analyzed by 3D-OM, XRD analysis, and biaxial flexural strength test. RESULTS. Based on the surface morphology by 3D-OM images, polished specimens showed smoother surface and lower roughness value (Ra). In the result of XRD analysis, partial phase transformation from tetragonal to monoclinic zirconia occurred in all groups. Control group, ground with a coarse grit diamond bur, showed more $t{\rightarrow}m$ phase transformation and lower flexural strength than Groups 1 and 2 significantly. CONCLUSION. The flexural strength in all specimens after grinding and polishing showed over 500 MPa, and those were clinically acceptable. However, grinding with a coarse grit diamond bur without polishing induced the phase transformation and low strength. Therefore, surface polishing is required for the occlusal adjustment using a high speed zirconia diamond bur to reduce the phase transformation and to prevent the decrease of flexural strength of zirconia.

• Journal of Oral Medicine and Pain
• /
• 제31권3호
• /
• pp.211-221
• /
• 2006

목적 전통적 고속 회전식 절삭기구 또는 Er:YAG 레이저로 삭제된 상아질에, 두가지 다른 접착 시스템을 적용한 후, 축조한 컴포지트 레진의 미세인장결합강도를 비교하고, 다양한 Er:YAG 레이저 에너지가 미세인장결합강도에 미치는 영향을 평가한다. 재료 및 방법 40개의 제3대구치를 사용하여, 평평한 상아질면을 만든 후 8개의 군으로 나누어, 4가지 절삭방법 (고속 회전식 절삭기구, 2 W, 3 W, 4 W 출력의 Er:YAG 레이저) 중 한 가지로 삭제하고, 2가지 접착 시스템 (Scotchbond Multipurpose Plus, Clearfil SE bond) 중 한 가지로 처리하여 컴포지트 레진을 축조하였다. 24시간의 저장 후, 각 시편을 결합면에 수직으로 자르고, 미세인장결합강도를 측정하였다. 각 군의 미세인장결합강도는 평균$\pm$표준 편차로 표현하였고, 통계분석을 위해 two-way ANOVA, one-way ANOVA, student-Newman-Keuls' multiple comparison test, 그리고 t-test가 사용되었다. 결과 및 결론 1. 접착시스템과 관계없이, 절삭방법에 따른 미세인장결합강도의 유의한 차이가 있었고, 높은 순서대로 나열하면 다음과 같다: 3 W, 2 W, Bur, 4 W (p<0.001). 2. 절삭방법과 관계없이, Scotchbond Multipurpose Plus로 처리한 군이 Clearfil SE bond로 처리한 군보다 유의하게 높은 미세인장결합강도를 나타냈다 (p<0.001). 3. Scotchbond Multipurpose Plus로 처리한 군 중에서, 3 W 레이저 절삭군이 가장 높은 미세인장결합강도를 나타냈고, 다음이 Bur, 2 W, 4 W 절삭군 순이었다 (p<0.001). 4. Clearfil SE bond로 처리한 군 중에서 3 W 레이저 절삭군이 가장 높은 미세인장결합강도를 나타냈고, 다음이 2 W, 4 W, Bur 절삭군 순이었다 (p<0.001). 5. 두 가지 접착 시스템 모두에서, 레이저로 절삭한 군의 미세인장결합강도의 차이가 있었고, 높은 순서대로 나열하면 3 W, 2 W, 4 W 순이었다 (p<0.001). :상아질에 접착된 컴포지트 레진의 미세인장결합강도는 절삭방법과 접착시스템의 상호작용에 의해 유의한 영향을 받았다. 임상에서 레진 수복시, 2 W-3 W 범위내로 Er:YAG laser를 사용한다면 전통적 핸드피스 못지않게 수복물의 우수한 결합강도를 얻을 수 있다. 특히 시술시간의 단축, 과도한 산부식에 따른 부작용의 예방을 위해 Clearfil SE bond를 포함한 self etching system을 사용하고자 한다면 bur보다 Er:YAG laser를 이용한 삭제방법이 더 유용한 결합력을 제공할 것이다.

• 대한소아치과학회지
• /
• 제35권1호
• /
• pp.11-17
• /
• 2008

본 연구는 Er:YAG laser에 의한 치수의 초기 조직반응과 calcitonin gene-related peptide (CGRP) 함유 신경섬유의 발현을 비교 평가하고자 시행하였다. Er:YAG laser와 conventional bur를 이용하여 상악 제1대구치의 교합면에 와동을 형성하였다. 와동형성 후 48시간 후에 조직을 처리하여 hematoxylin-eosin 염색과 CGRP 면역조직화학을 시행한 후 다음과 같은 결과를 얻었다. 1. Conventional bur를 이용하여 삭제한 경우, 상아질 바닥면은 균열이 없는 평면의 균일한 모양을 보였으며, Er:YAG laser의 경우에는 상아질의 면은 bur에 비해서 파동형의 불규칙적인 형태와 바닥면에서 상아세관의 주행방향을 따라 미세한 균열을 보였다. 2. Er:YAG laser에 의해 손상 받은 치수에서는 혈관확장과 노출된 치수의 손상부위를 따라 bur에서 손상 받은 치수보다 더 많은 염증세포의 침윤과 상아모세포층의 파괴를 보였다. 3. 노출손상 후에 치수신경 말단에서 CGRP 발현은 bur와 laser군 모두에서 손상을 받지 않은 정상 치수에 비해서 증가된 양상을 보였으며, 그 증가된 정도는 laser의 경우에서 더 강하였다. 위의 결과들을 종합하면, Er:YAG laser가 치수손상을 최소화하여 적용되면 치아우식 제거와 와동형성과 같은 여러 수복치료 시 유용하게 사용될 수 있으리라 사료된다.

• Restorative Dentistry and Endodontics
• /
• 제32권4호
• /
• pp.327-334
• /
• 2007

이 연구는 서로 다른 카바이드 버와 다이아몬드 버로 5급 와동을 형성 한 후 SE primer 접착 시스템인 Clearfil SE Bond를 이용한 복합레진 수복 시 버의 종류에 따른 법랑질과 상아질 변연에서의 미세누출 차이를 상호 비교하기 위하여 시행하였다. 4종의 삭제기구를 이용하여 각각 10개의 발거된 대구치의 협면 치경부에 5급 와동을 형성하였다. 1군은 plain-cut carbide fissure bur (no. 245)를 사용한 군, 2군은 cross-cut carbide fissure bur (no. 557)를 사용한 군, 3군은 fine diamond bur (TF-21F: 입자크기 $53\;-\;63\;{\mu}m$)를 사용한 군, 4군은 standard diamond bur (EX-41: 입자크기 $106\;-\;205\;{\mu}m$)를 사용한 군으로 분류하였다. 형성된 와동에 Clearfil SE Bond의 Primer와 Bond를 적용하고 Clearfil AP-X 복합레진을 충전하여 광중합한 후, Sof-Lex disc를 이용하여 마무리와 연마를 시행하였다. 수복된 치아를 2% methylene blue 용액에 24시간 동안 침적시킨 후 각 군의 치아를 협설로 절단하여 광학 입체현미경 하에서 법랑질과 상아질 변연에서의 미세누출 점수를 평가하여 다음과 같은 결과를 얻었다. Clearfil SE Bond와 복합레진을 이용한 5급 와동 수복 시 거친 다이아몬드 버의 사용은 카바이드 버나 미세한 다이아몬드 버에 비해 법랑질과 상아질 변연 모두에서 높은 미세누출을 나타내었다.

• The Journal of the Acoustical Society of Korea
• /
• 제22권2E호
• /
• pp.69-77
• /
• 2003

Correlations between acoustic properties and bone density have been investigated in bovine cancellous bone. Speed of sound (SOS), broadband ultrasonic attenuation (BUA), and broadband ultrasonic reflection (BUR) were measured in 10 defatted bovine cancellous bone specimens in vitro. SOS showed a significant correlation with the apparent density of the bone. A comparable correlation was observed between BUA and the apparent density. BUR was rather highly correlated with the apparent density. It was shown that BUR had a weak correlation with BUA and a significant correlation with SOS. This indicates that the parameter BUR can provide important information that may not be contained in BUA and SOS and, therefore, can be useful as an alternative diagnostic parameter of osteoporosis. As expected, a linear combination of all three ultrasonic parameters in a multiple regression model resulted in a significant improvement in predicting the apparent bone density.

• 한국정밀공학회지
• /
• 제16권4호통권97호
• /
• pp.148-154
• /
• 1999

This study was carried out to verify grinding performance of dental diamond bur and investigate the possibility of AE application in dentistry field. Workpieces were made of acryl and bovine respectively for the experiments in this study. Grinding test was conducted to get the data of grinding resistance and specific grinding energy of four different types of diamond bur by using tool dynamometer. AE signal was acquired to verify grinding process in the AE measuring system. Tool wear was observed to find parameters about grinding characteristics of diamond bur by means of SEM picture. It was found that the wear of dental diamond bur could be detected with polishing of grinding material, removal of adhesive parts, wear of particles neighboring cutting nose, loss of material and elevation of temperature. The wear of B, C, D type diamond bur is due to wear and fracture of grain size. Abnormal state can be found through the behavior of AE signal in the grinding working. As a result, it is expected that forecast of abnormal state is possible using AE equipments under real time process.

• 한국생산제조학회지
• /
• 제8권3호
• /
• pp.76-82
• /
• 1999

This study was carried out to verify finding performance of dental diamond bur and investigate the possibility of AE application in density field. Work pieces were made of acryl and bovine respectively for the experiments in this study. Grinding test was conducted to get the data of grinding resistance and specific finding energy of low different types of diamond bur by using tool dynamometer. AE signal was acquired to verify grinding process in the AE measuring system. AErms value was increased as the grinding velocity and depth were increasing, but it decreased as the feed rate was increasing. The case of the small value of AE signal is due to abnormal grinding in D type diamond bur. By analyzing AErms start and finish time of grinding working, abnormal grinding state can be confined. Abnormal state can be found through the behavior of AE signal in the finding working. As a result, it is expected that forecast of abnormal state is possible using AE equipments under real time process.

• The Journal of Advanced Prosthodontics
• /
• 제10권2호
• /
• pp.93-100
• /
• 2018

PURPOSE. The purpose of this study was to determine the changing frequency of a diamond bur after multiple usages on 3 different surfaces. MATERIALS AND METHODS. Human premolar teeth (N = 26), disc shaped direct metal laser sintered CoCr (N = 3) and zirconia specimens (N = 3) were used in this study. Groups named basically as Group T for teeth, Group M for CoCr, and Group Z for zirconia. Round tapered black-band diamond bur was used. The specimens were randomly divided into three groups and placed with a special assembly onto the surveyor. 1, 5, and 10 preparation protocols were performed to the first, second, and third sub-groups, respectively. The subgroups were named according to preparation numbers (1, 5, 10). The mentioned bur of each group was then used at another horizontal preparation on a new tooth sample. The same procedure was used for CoCr and zirconia disc specimens. All of the bur surfaces were evaluated using roughness analysis. Then, horizontal tooth preparation surfaces were examined under both stereomicroscope and SEM. The depth maps of tooth surfaces were also obtained from digital stereomicroscopic images. The results were statistically analyzed using One-Way ANOVA, and the Tukey HSD post-hoc tests (${\alpha}=.05$). RESULTS. All of the groups were significantly different from the control group (P<.001). There was no significant difference between groups Z5 and Z10 (P=.928). Significant differences were found among groups T5, M5, and Z5 (P<.001). CONCLUSION. Diamond burs wear after multiple use and they should be changed after 5 teeth preparations at most. A diamond bur should not be used for teeth preparation after try-in procedures of metal or zirconia substructures.

• 대한치과보철학회지
• /
• 제29권2호
• /
• pp.117-127
• /
• 1991

The purpose of this study was to evaluate the effect of surface treatment of fractured metal-ceramic crown on bond strength of porcelain repair resin. The specimens were divided into two groups for metal specimens add five groups for porcelain specimens by surface treatment methods. the metal specimens were treated by 2 methods. : micro-sandblasting with $50{\mu}m$ aluminum oxide and grinding with diamond bur. The porcelain specimens were treated by 5 methods : micro-sandblasting with $50{\mu}m$ aluminum oxide, grinding with diamond bur, etching with porcelain etching agent, combination of micro-sandblasting and etching procedure, and combination of grinding and etching procedure. After surface treatment, each specimen was bonded with composite resin and the bond strength was measured and the surface texture was observed by scanning electromicroscope(SEM). The results were as follows : 1. There was significant difference in shear bond strength between metal specimen and prorcelain specimen. 2. Bood strength of metal specimens treated with diamond bur was higher than that treated with $50{\mu}m$ aluminum oxide sandblasting. 3. Bond strength of porcelain specimen treated with diamond bur was higher than that treated with $50{\mu}m$ aluminum oxide sandblasting and porcelain etching agent. 4. There was no significant difference in shear bond strength between the group treated with diamond bur and combined treatment groups respectively. 5. The large undercuts were observed in group treated with diamond bur by SEM.

• 대한치과보철학회지
• /
• 제35권4호
• /
• pp.719-741
• /
• 1997

This study was undertaken to compare by Atomic Force Microscope the effects of various finishing and polishing instruments on surface roughness of filling and veneering composite resins. Seven composite resins were studied : Silux Plus (3M Dental Products, U.S.A.), Charisma (Heraeus Kulzer, Germany), Prisma THP (L.D.Caulk, Dentsply, U.S.A.), Photoclearfil (Kuraray, Japan), Cesead (Kuraray, Japan), Thermoresin LC (GC, Japan), Artglass (Heraeus Kulzer, Germany). Samples were placed and polymerized in holes (2mm thick and 8.5mm in diameter) machined in Teflon mold under glass plate, ensuring excess of material and moulded to shape with polyester matrix strip. Except control group (Polyester matrix strip), all experimental groups were finished and polishied under manufacturer's instructions. The finishing and polishing procedure were : carbide bur (E.T carbide set 4159, Komet, Germany), diamond bur (composite resin polishing bur set, GC, Japan), aluminum-oxide disc (Sof-Lex Pop-On, 3M Dental Products, U.S.A.), diamond-particle disc (Dia-Finish, Renfert Germany), white stone bur & rubber point( composite finishing kit, EDENTA, Swiss), respectively. Each specimens were evaluated for the surface roughness with Atomic Force Microscope (AutoProbe CP, Park Scientific Instruments, U.S.A.) under contact mode and constant height mode. The results as follows : 1. Except Thermoresin LC, all experimental composite resin groups showed more rougher than control group after finishing and polishing(p<0.1). 2. A surface as smooth as control group was obtained by $Al_{2}O_{3}$ disc all filling composite resin groups except Charisma and all veneering composite resin groups except Thermoresin LC(p<0.05). 3. In case of Thermoresin LC, there were no statistically significant differences before and after finishing and polishing(p>0.1). 4. Carbide bur, diamond bur showed rough surfaces in all composite resin groups, so these were inappropriate for the final polishing instruments.