• 한국초전도ㆍ저온공학회논문지
• /
• 제4권1호
• /
• pp.21-25
• /
• 2002

The effect of Ca-doping on the superconducting properties of Nd-Ba-Cu-O bulk superconductors, fabricated by the oxygen-controlled melt growth process, has been systematically investigated. Various c-axis textured bulk samples were grown using precursors with the nominal compositions of $Nd_{1.8-x}Ca_{x]Ba_{2.4}Cu_{3.4}O_{y}$ (x= 0.00, 0.02, 0.05, 0.10, 0.15) in a reduced oxygen atmosphere of 1%O$_2$ in Ar. Magnetization measurements revealed that the critical temperatures(Tc) were almost linearly depressed from 95K to 86K with increasing the Ca dopant from x : 0.0 to 0.15, respectively, and thus critical current densities(Jc) at 77K and for H//c-axis of specimens were gradually degraded with increasing x. Compositional analyses revealed that although the amounts of the Ca dopant both in $NdBa_2Cu_2O_y(Nd123) and Nd_4Ba_2Cu_2O_{10}(Nd422)$,/TEX> were increased with increasing x, only less than half of the initial Ca compositions were detected in melt-grown Ca-doped Nd-Ba-Cu-O bulk crystals. The supression of Tc is attributed to an increased Nd substitution for the Ba site in the Nd123 superconducting matrix with increasing the amount of the Ca dopant.

• 한국초전도ㆍ저온공학회논문지
• /
• 제17권1호
• /
• pp.14-16
• /
• 2015

Due to the considerable development of the technology of second generation high-temperature superconductors and a significant improvement in their mechanical and transport properties in the last few years it is possible to use HTS tapes in the magnetic levitation systems. The advantages of tapes on a metal substrate as compared with bulk YBCO material primarily in the strength, and the possibility of optimizing the convenience of manufacturing elements of levitation systems. In the present report presents the results of the magnetic levitation force measurements between the stack of HTS tapes containing $n=2{\div}200$ of tapes $12mm{\times}12mm$ and NdFeB permanent magnet in the FC and ZFC regimes. It was found a non- linear dependence of the levitation force from the height of the array of stack in both modes: linear growth at small thickness gives way to flattening and constant at large number of tapes in the stack. Established that the levitation force of stacks comparable to that of bulk samples. The numerical calculations using finite element method showed that without the screening of the applied field the levitation force of the bulk superconductor and the layered superconductor stack with a critical current of tapes increased by the filling factor is exactly the same, and taking into account the screening force slightly different.

• Progress in Superconductivity
• /
• 제12권2호
• /
• pp.82-87
• /
• 2011

We studied the trapped field properties of bulk Y-Ba-Cu-O superconductors by applying 3 T of the permanent or $Nb_3Ti$ superconducting magnet. The 28 mm circular type of YBCO bulk superconductor was prepared and then hole at the center of bulk, parallel to the c-axis, was mechanically drilled. Typical size of hole in YBCO bulk was 10 mm in diameter. In order to examine the trapped field variation in terms of different impregnated materials, a hole in YBCO bulk was filled with resin and indium respectively. The trapped field decay due to flux flow was determined in terms of time. Our preliminary result indicates the trapped field value measured on the YBCO without hole after 30 minute by applying 3 T, was 6,500 G, which is much higher than that, 4,500 G, measured on YBCO with hole. Also, we confirmed that the tendency of a trapped field decrement with time was almost the same regardless of the impregnated materials in YBCO.

• Transactions on Electrical and Electronic Materials
• /
• 제10권1호
• /
• pp.31-34
• /
• 2009

The improvement of preparation process of ${YBa_2}{Cu_3}{O_x}$ superconductor and its conducting properties is important for practical applications. In this study, the additives such as $Ag_{2}O$ and PbO were used to improve the preparation conditions of ${YBa_2}{Cu_3}{O_x}$ superconducting bulk samples and the properties of ${YBa_2}{Cu_3}{O_x}$ superconductors prepared with powders using sol-gel method and solid state reaction method were studied. The effects of the different powders and the additives to the density, grain alignment, and porosity of samples, that affect the critical current density of superconductor, also have been investigated. It is found that the properties of ${YBa_2}{Cu_3}{O_x}$ prepared with sol-gel synthesized powder and the additives showed better superconductivities than those of conventionally prepared superconductors.

• 한국초전도ㆍ저온공학회논문지
• /
• 제24권1호
• /
• pp.18-22
• /
• 2022

The effect of electron beam (EB) irradiation on superconducting properties and microstructures of MgB₂ bulk superconductors were investigated. At E-beam doses of 1×10¹⁶ e/cm² and 1×10¹⁷ e/cm², the effect of irradiation on a superconducting transition temperature (T_c) of MgB₂ was weak. As a dose increases to 5×10¹⁷ e/cm², T_c decreases by 0.5 K. The critical current density (J_c) measured at 4.2 K and 20 K, and 0 T - 5 T increases slightly as exposure time increases. X-ray diffraction for the irradiation surface of MgB₂ shows that the diffraction intensity of (hkl) peaks decreases proportionally as the exposure time increases. This indicates that the crystallinity of MgB₂ was degraded by irradiation. TEM investigation for the irradiated sample showed distorted lattice structure, which is consistent with the XRD results. The J_c increase and T_c reduction of MgB₂ by irradiation are believed to be caused by the lattice distortion.

• 한국초전도ㆍ저온공학회논문지
• /
• 제16권2호
• /
• pp.36-41
• /
• 2014

Temperature dependence of magnetic moment (m-T) and the magnetization (M-H) at 5 K and 20 K of the in situ processed $MgB_2$ bulk pellets with/without carbon (C) doping were examined. The superconducting critical temperature ($T_c$), the superconducting transition width (${\delta}T$) and the critical current density ($J_c$) were estimated for ten test samples taken from the $MgB_2$ bulk pellets. The reliable m-T characteristics associated with the uniform $MgB_2$ formation were obtained for both $MgB_2$ pellets. The $T_cs$ and ${\delta}Ts$ of all test samples of the undoped $MgB_2$ were the same each other as 37.5 K and 1.5 K, respectively. The $T_cs$ and ${\delta}Ts$ of the C-doped $MgB_2$ were 36.5 K and 2.5 K, respectively. Unlike the m-T characteristics, there existed the difference among the M-H curves of the test samples, which might be caused by the microstructure variation. In spite of the slight $T_c$ decrease, the C doping was effective in enhancing the $J_c$ at 5 K.

• 한국재료학회지
• /
• 제22권11호
• /
• pp.569-574
• /
• 2012

Large single grain $Gd_{1.5}Ba_2Cu_3O_{7-y}$ (Gd1.5) bulk superconductors were fabricated by a top-seeded melt growth (TSMG) process using an $NdBa_2Cu_3O_{7-y}$ seed. The seeded Gd1.5 powder compacts with a diameter of 50 mm were subjected to the heating cycles of a TSMG process. After the TSMG process, the diameter of the single grain Gd1.5 compact was reduced to 43 mm owing to the volume contraction during the heat treatment. The superconducting transition temperature ($T_c$) of the top surface of the single grain Gd1.5 sample was as high as 93.5 K. The critical current densities ($J_cs$) at 77 K and 1T and 1.5 T were in ranges of 25,200-43,900 $A/cm^2$ and 10,000-23,000 $A/cm^2$, respectively. The maximum attractive force at 77 K of the sample field-cooled using an Nd-B-Fe permanent magnet (surface magnetic field of 0. 527 T) was 108.3 N; the maximum repulsive force of the zero field-cooled sample was 262 N. The magnetic flux density of the sample field-cooled at 77 K was 0.311T, which is approximately 85% of the applied magnetic field of 0.375 T. Microstructure investigation showed that many $Gd_2BaCuO_5$ (Gd211) particles of a few ${\mu}m$ in size, which are flux pinning sites of Gd123, were trapped within the $GdBa_2Cu_3O_{7-y}$ (Gd123) grain; unreacted $Ba_3Cu_5O_8$ liquid and Gd211 particles were present near the edge regions of the single grain Gd1.5 bulk compact.

• Progress in Superconductivity
• /
• 제9권1호
• /
• pp.107-110
• /
• 2007

Bi/CNT composite and resin/CNT were chosen to improve the mechanical properties of $YBa_2Cu_3O_7$(YBCO) superconductor. In order to elucidate the effects of Bi/CNT composite and resin/CNT in YBCO superconductors, melt texture superconductor were impregnated by mixed compound of Bi and CNT into the artificial holes parallel to the c-axis, which were drilled on the YBCO superconductor. Various amount of Bi/CNT and resin/CNT were impregnated to YBCO superconductor with different holes diameters. Typical artificial holes diameters were 0.5, 0.7, and 1.0 mm respectively. Result of three-point bending test measurement, the bending strength with resin/CNT impregnation was improved up to 59.64 MPa as compared with 50.79 MPa of resin/CNT free bulk. Resin/CNT impregnation has been found to be one of the effective ways in improving the mechanical properties of bulk superconductor.

• 한국초전도ㆍ저온공학회논문지
• /
• 제16권1호
• /
• pp.19-22
• /
• 2014

The effects of Mg content on the pore formation, density and critical properties were investigated in in-situ reacted $MgB_2$ superconductors. The $Mg_{1+x}B_2$, (x=-0.2, 0.0, 0.05, 0.3, 1.0) bulk samples with different Mg contents were heat-treated at $900^{\circ}C$ for 1 h in an Ar atmosphere. The dimensional changes of a pellet's mass and volume after heat-treatment were measured. After heat-treatment process, the sample mass was decreased by Mg evaporation, but the sample volume was expanded by pore formation at the Mg site; therefore, the apparent density was decreased. Spherical pores the same as Mg particles were developed after heat-treatment in all samples, and the pore density was increased with increasing Mg content. As the x of Mg content was increased to 1.0, the apparent density of $Mg_{1+x}B_2$ samples was decreased due to a relatively larger reduction in a mass change. The critical current density of Mg excessive sample of x=0.05 showed the highest values over the applied magnetic fields because the excessive Mg may compensate Mg loss and enhance grain connectivity.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2006년도 High Temperature Superconductivity Vol.XVI
• /
• pp.63-63
• /
• 2006