• Journal of Welding and Joining
• /
• v.35 no.2
• /
• pp.23-29
• /
• 2017

Mechanical properties and hardness distributions in arc brazed joints of Dual phase steel using Cu-Al insert metal were investigated. The maximum tensile shear load was 10.4kN at the highest brazing current. It was about 54% compared to tensile load of base metal. This joint efficiency is higher than that of joint of DP steel using Cu-based filler metals which are Cu-Si, Cu-Sn. Fracture positions can be divided into two types. Crack initiation commonly occurred at three point junction among upper sheet, lower sheet and the fusion zone. However crack propagations were different with increasing the brazing current. In case of the lower current, it instantaneously propagated along with the interface between fusion zone and upper base material. On the other hand, in case of higher current, a crack propagation occurred through fusion zone. When the brazing current is low (60, 70A), the interface shape is flat type. However the interface shape is rough type, when the brazing current is high (80A). It is thought that the interface shapes were the reason why the crack propagations were different with brazing current. The interface was the intermetallic compounds which consisted of $(Fe,Al)_{0.85}Cu_{0.15}$ IMC formed by crystallization at $1200^{\circ}C$during cooling. Therefore the maximum tensile shear load and the fracture behavior were determined by a interface shape and effective sheet thickness of the fracture position.

• Korean Journal of Materials Research
• /
• v.12 no.2
• /
• pp.140-145
• /
• 2002

This study was conducted to investigate the brazing characteristics between Zircaloy-4 nuclear fuel cladding tubes and bearing pads with filler metals of amorphous $Zr_{1-x}Be_x$(0.3$\leq$x$\leq$0.5) binary alloy, in which they were produced in the ribbon form by the melt-spinning metod. The crystallization behavior, stability, hardness and micro-structure of brazed zone were examined by X-ray diffraction, differential scanning calorimetry, micro-Vickers hardness test, optical microscopy, and transmission electron microscopy. $Zr_{1-x}Be_x$(0.3$\leq$x$\leq$0.4) amorphous alloys were crystallized to $\alpha$-Zr with increasing the temperature, and the rest were transformed to ZrBe$_2$at higher temperatures. On the other hand, $Zr_{1-x}Be_x$(0.4$\leq$x$\leq$0.5) amorphous alloys were crystallized to $\alpha$-Zr and ZrBe$_2$, simultaneously. The thickness of the layer brazed with amorphous alloy was increased with increasing the beryllium content due to the higher diffusion of Be. The morphology of brazed layer with PVD Be filler metal showed dendrite while that brazed with amorphous alloys appeared globular. Micro-Vickers hardness of brazed zone increased as the beryllium content of filler metal was decreased.

• Korean Journal of Materials Research
• /
• v.12 no.4
• /
• pp.259-263
• /
• 2002

Three different ribbons of amorphous $Til_{1-x}Be_x$ alloys such as $Ti_{0.59}Be_{0.41},\;Ti_{0.61}Be_{0.39}\;and\;Ti_{0.63}Be_{0.37}$ were made by melt-spinning method to be used as brazing filler metals for joining Zircaloy-4 nuclear fuel cladding tubes, and their crystallization behavior as well as microstructure of the brazed zone were examined. The crystallization behavior was investigated in teams of thermal stability, crystallization temperature and activation energy. The crystallization of the $Ti_{1-x}Be_x$ alloys proceeded in two steps by the formation of ${\alpha}$-Ti at a lower temperature and of TiBe at a higher temperature. The crystallization temperature and activation energy of $Ti_{1-x}Be_x$ alloys were higher and larger than those of $Zr_{1-x}Be_x$ alloys and PVD Be. Those resulted thinner joining layer with $Ti_{1-x}Be_x$ alloys, which kept sound thickness of Zircaloy-4 nuclear fuel cladding tubes after brazing. But in the brazed zones made by $Ti_{1-x}Be_x$ filler metals, a little solid-solution layers composed of Zr and Ti were formed toward the Zr cladding tube and Zr was detected in the brazed zones. Microstructure of brazed zone was changed from globular to dentrite with decreasing Be content in the $Ti_{1-x}Be_x$ filler metal.

• Proceedings of the KWS Conference
• /
• 2003.05a
• /
• pp.228-230
• /
• 2003

Recently, lots of joining methods of thin metal sheets are being developed in order to improve joint quality and productivity in manufacturing area. Current existing welding methods are continuously challenged as new materials and smaller thickness of metal sheets are required. In this study, laser plug brazing process was investigated as a new joining method of thin metal sheets. A CO2 laser system with automatic feeding of filler metal wire and flux was developed, and laser plug brazing experiments were conducted. The brazed joints were analyzed using various methods.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.05a
• /
• pp.485-487
• /
• 2008

Aluminum brazing needs normally careful control of temperatures due to little difference between brazing temperatures and melting temperatures of base materials. Unsuitable processing conditions such as brazing temperature, gap between brazed materials, inadequate feeding of flux, etc. can lead to occur joining defects. In this study, A357 was used as a filler metal for the brazing of pure aluminum base materials. A357 was brazed at temperatures in the semi-solid state. Interface microstructures with base materials were observed using OM and SEM/EDS and compared to conventional aluminum brazing.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.12
• /
• pp.8679-8683
• /
• 2015

Using a surface modification technique, ion beam assisted deposition (IBAD) of Ti thin film it becomes possible to prepare an active ceramic surface to braze $Al_2O_3$-STS304 with conventional Ag-Cu eutectic composition filler metal. Researches on bonding formations at interfaces of ceramic joints were mainly related on the development of filler metals to ceramic, the process parameters, and clarifications of reaction products. From the results, the reactive brazing is a very convenient technique compared to the conventional Mn-Mo method. However melting point of reactive filler is still higher than that of Ag-Cu eutectic and it forms the brittle inter metallic compound. Recently several new approaches are introduced to overcome the main shortcomings of the reactive metal brazing in ceramic-metal, metal vapor vacuum arc ion source was introduced to implant the reactive element directly into the ceramics surface, and sputter deposition with sputter etching for the deposition of active material.

• Journal of the Korean Ceramic Society
• /
• v.55 no.5
• /
• pp.492-497
• /
• 2018

This paper reports the efficacy of tape casting using an Ag-10 wt% CuO filler for the successful joining of a sintered $Ce_{0.9}Gd_{0.1}O_{2-{\delta}}-La_{0.7}Sr_{0.3}MnO_{3{\pm}{\delta}}$ (GDC-LSM) ceramic with a SUS 460 FC metal alloy by reactive air brazing. The as-prepared green tape was highly flexible without drying cracks, and the handling was easy when used as a filler material for reactive air brazing. Heat treatment for the GDC-LSM/SUS 460 FC joint was performed at $1050^{\circ}C$ for 30 min in air. Microstructural observations indicated a reliable and compact joining. The room temperature mechanical shear strength of the as-brazed joints was $60{\pm}8MPa$ with a cohesive failure. The flexural strength of joints was measured from room temperature up to $850^{\circ}C$, where the strength retention revealed to be almost 100% at $500^{\circ}C$. However, the joints showed a degradation in strengths at 800 and $850^{\circ}C$, exhibiting strength retentions of 57% and 37%, respectively.

• Proceedings of the KWS Conference
• /
• 1994.10a
• /
• pp.161-162
• /
• 1994

No Abstract, See Full Text

• Proceedings of the KWS Conference
• /
• 1994.05a
• /
• pp.103-105
• /
• 1994

• Advances in materials Research
• /
• v.1 no.3
• /
• pp.183-190
• /
• 2012

Brazing Mo using Ti and Ti-15-3 foils has been investigated in the experiment. For traditional furnace brazing, solidification shrinkage voids cannot be completely removed from the joint even the brazing temperature increased to 2013 K and 160 ${\mu}m$ thick Ti foil applied in brazing. Similar results are observed from the joint using Ti-15-3 filler. In contrast, the quality of laser brazed joint is much better than that of furnace brazed joint. A sound joint is achieved after laser brazing. Tensile strengths of 418 and 373 MPa are obtained from laser brazed joints at the power of 800W and travel speed of 5 mm/s using Ti and Ti-15-3 fillers, respectively. All laser brazed joints are fractured at the brazed zone and cleavage dominated fractures are widely observed from their fractographs. The Ti base fillers show potential in laser brazing Mo substrate.