• Journal of the Korean Ceramic Society
• /
• v.34 no.8
• /
• pp.886-896
• /
• 1997

To investigate an effect of phase separation on precipitation characteristics of CuCl nanocrystals in CuCl doped nonlinear optical glasses, borosilicate glass systems with 9 different compositions with ~2wt% of CuCl were selected and CuCl doped glasses were prepared by melting and precipitation method. Microstructural properties of the CuCl doped glasses were analyzed by optical absorption spectroscopy, acid elution test, TEM, and EDXS. While phase separation did not occur in Glass A~D, interconnected and droplet microstructures due to phase separation were found in Glass E, F and Glass G~I, respectively. In the particular composition of the matrix glasses in this study, the precipitation of the CuCl particles was observed in the phase separable glasses, not in phase non-separable glasses. The CuCl particles were precipitated in both silica-rich phase region and boronrich phase region of the glass matrix. In the case of 7.7Na2O-36.6B2O3-52.7SiO2(mole%) glass, the larger CuCl particles than those in the silica-rich phase region were observed in the boron-rich phase region.

• Journal of the Korean Ceramic Society
• /
• v.36 no.9
• /
• pp.946-953
• /
• 1999

The etching characteristics of Er-doped sodium borosilicate glass film for the planar optical waveguides were investigated using reactive ion etching. The etch rate decreased as the pressure in creased but increased as the RF power increased. The etch rate increased as the flow rate C2F gas and the amount of O2 addition increased but decreased over critical point (C2F6 7,5 accm O2 20%) The etch rate was 180${\AA}$/min under C2F6 7.5 sccm O2 20% RF power 270 W, pressure 150 mTorr. With this optimum etching condition and subsequent heat treatment at 975$^{\circ}C$ for 30 minutes planar optical waveguides having improved sidewall roughness were fabricated successfully.

• The Korean Journal of Ceramics
• /
• v.1 no.2
• /
• pp.96-100
• /
• 1995

Recently, alumina/glass composites have been applied as a substrate material for hybrid IC and LSI multi-chip packaging. In this study, the characterization of sodium borosilicate glasses containing NaF and $AlF_3$ and the preparation of the resulted glass/alumina composites have been examined and the effect of the addition of fluorides on the thermal. and dielectric properties of the sintered composites have been studied. The sintering temperature of specimens was lowered by about 100-$150^{\circ}C$ by the addition of fluorine compared with the specimens without fluorine. The specimens containing fluorine showed slightly lower dielectric constants than those of the specimens without fluorine.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.45 no.3
• /
• pp.386-392
• /
• 1996

Zinc-Borosilicate is used as a side insulator wall to make high breakdown voltage with one Field Limiting Ring in a power p-n junction device in simulation. It is known that surface charge density can be yield at the interface of Zinc-Borosilicate glass / silicon system. When the glass is used as a side insulator wall, surface charge varied potential distribution and breakdown voltage is improved 1090 V under the same structure.The breakdown voltage under varying the surface charge density has a limit value. When the epitaxial thickness is varied, the position of FLR doesn't influence to the breakdown characteristic not only under non punch-through structure but also under punch-through structure. (author). 7 refs., 12 figs., 2 tabs.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1999.05a
• /
• pp.138-138
• /
• 1999

• Applied Chemistry for Engineering
• /
• v.27 no.6
• /
• pp.612-619
• /
• 2016

In this research, an alumino-borosilicate foamed glass with sound absorption property was prepared using the waste borosilicate glass obtained from the recycling process of waste liquid crystal display (LCD) panel. A 100 g of pulverized waste borosilicate glass with the particle size of under 325 mesh, was mixed with 0.3 g (wt/wt) of graphite, each 1.5 g (wt/wt) of $Na_2CO_3$, $Na_2SO_4$ and $CaCO_3$ as a foaming agent, and 6.0 g (wt/wt) of $H_3BO_3$ and 3.0 g (wt/wt) of $Al_2O_3$ as a pore control agent. Following mixture was under the foaming process for 20 minutes at a foaming temperature of $950^{\circ}C$. The result yielded the foaming agent with 45% of the opened porosity and 0.5-0.7 of the sound absorbing coefficient. This alumino-borosilicate foamed glass with the sound absorption property showed excellent physical and mechanical properties such as density of $0.21g/cm^3$, bending strength of $55N/cm^2$ and compression strength of $298N/cm^2$ which can be ideally used as sound absorption materials with heat-resisting and chemical-resisting property.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.371-374
• /
• 2004

저온동시 소성용(low temperature co-fired ceramics, LTCC) 마이크로파 유전체을 만들기 위해 $Ca(Li_{1/4}Nb_{3/4})O_3$ 마이크로파 유전체 세라믹스에 zinc-borosililcate glass를 첨가하여 소결 특성과 마이크로파 유전 특성을 조사하였다. $Ca(Li_{1/4}Nb_{3/4})O_3$과 $0.7Ca(Li_{1/4}Nb_{3/4})O_3-0.3CaTiO_3$에 zinc-borosilicate를 $5{\sim}30wt%$ 첨가하여 소결한 결과 $875{\sim}925^{\circ}C$에서 동시 소성이 가능한 것으로 확인되었으며 zinc-borosilicate glass의 함량이 증가할수록 저온에서 소성이 가능하였지만 과량의 액상과 2차상이 형성되면서 유전율과 품질계수가 저하되는 경향을 나타내었다. $Ca(Li_{1/4}Nb_{3/4})O_3$에 5wt%의 zinc-borosilicate를 첨가하여 $900^{\circ}C$에서 소성한 결과 가장 우수한 유전 특성$(\epsilon_r=17.45,\;Q{\times}f_0=5487)$을 나타내었고, 유전율을 높이기 위해 $CaTiO_3$를 0.3mol% 첨가한 $0.7Ca(Li_{1/4}Nb_{3/4})O_3-0.3CaTiO_3$에 10wt%의 zinc-borosilicate를 첨가하여 $925^{\circ}C$에서 소성한 결과 가장 우수한 유전특성$(\epsilon_r=44.92,\;Q{\times}f_0=5567)$을 나타내었다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.6
• /
• pp.524-530
• /
• 2006

$xCa(Li_{1/4}Nb_{3/4})O_{3}-(1-x)CaTiO_{3}$ ceramics were sintered under the presence of zinc-borosilicate(ZBS) glass and resultant microwave dielectric properties were investigated with a view to applying the composition to low-temperature co-fired ceramic(LTCC) technology. The addition of $5{\sim}15wt%$ ZBS glass ensured successful sintering below $900\;^{\circ}C$. In general, increased addition of ZBS glass increased sinterability but it decreased the quality factor($Q{\times}f_{0}$) significantly due to the formation of an excessive liquid and second phases. As for the addition of $CaTiO_3$, the dielectric constant(${\epsilon}_r$) and temperature coefficient of resonant frequency(${\tau}_f$) increased, while the quality factor($Q{\times}f_{0}$) did not show an apparent change. The sintered $0.9Ca(Li_{1/4}Nb_{3/4})O_{3}-0.1CaTiO_{3}$ specimen at $900\;^{\circ}C$ with 10 wt% ZBS glass demonstrated 39.6 in dielectric constant(${\epsilon}_r$), 4,400 in quality factor$(Q{\times}f_{0}),\;and\;-11ppm/^{\circ}C$ in temperature coefficient of resonant frequency(${\tau}_f$).

• Journal of the Microelectronics and Packaging Society
• /
• v.9 no.1
• /
• pp.49-52
• /
• 2002

This study demonstrated the feasibility of tape casting method to fabricate soda borosilicate glass-coated stainless steel electrostatic chucks(ESC) for low temperature semiconductor processes. Glass coating on the stainless steel substrate was 125 $\mu\textrm{m}$ thick. The adhesion of glass coating was found to be excellent such that it was able to withstand temperature cycling to over $300^{\circ}C$ without cracking and delamination. The electrostatic clamping pressure generally followed the theoretical voltage-squared curve except at elevated temperatures and high applied voltages. The deviations at elevated temperatures and high applied voltages are due to increased leakage current as the electrical resistivity of glass coating drops.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.1 no.1
• /
• pp.41-46
• /
• 2003

To understand the long-term leach behavior of a borosilicate Waste glass in a repository, the leaching experiment with three kinds of simulated borosilicate waste glasses has been carried out since the middle of 1997. The five years results indicate that a boron would be applied as an indicator of a long-term leaching of their borosilicate waste glasses and that their long-term leach rates have a tendency to be close to about 0.03g/$m^2$-day even though their compositions and their ratios of the surface area to the volume of leachate are different.