• Journal of Welding and Joining
• /
• 제15권6호
• /
• pp.32-40
• /
• 1997

Solid state diffusion bonding is the joining process performed by creep and diffusion, which is accelerated by heating below melting temperature and proper pressing, in vacuum or shielding gas atmosphere. By this process we can obtain sufficient joint which can't be expected from the fusion welding. For Ti-6Al-4V alloy, the optimum solid state diffusion bonding condition and mechanical properties of the joint were found, and micro void morphology at bond interface was observed by SEM. The results of tensile test showed sufficient joint, whose mechanical properties are similar to that of base metal. 850$^{\circ}$C, 3MPa is considered as the optimum bonding condition. Void morphology at interface is long and flat at the initial stage. As the percentage of bonded area increases, however, small and round voids are found. Variation of void shape can be explained as follows. As for the void shrinkage mechanism, at the initial stage, power law creep is the dominant, but diffusion mechanism is dominant when the percentage of bonded area is increased.

• 한국전기전자재료학회논문지
• /
• 제22권8호
• /
• pp.625-631
• /
• 2009

In this thesis, lateral thermosonic bonding with ACFs was investigated as a process to make high reliability joints for FPD fabrication. Conditions for thermosonic and thermocompression bonding with ACFs were determined and used to make specimens in a driving test jig for testing of bond reliability by thermal shock. The results showed that thermosonic bonding temperature of $199\;^{\circ}C$ and bonding time of 1s produced bonds with good reliability. Additionally, thermosonic bonding temperature and time were reduced and thermal shock test results compared to this proposed curing condition. It is concluded that theromosonic bonding with ACFs can be effectively applied to reduce bonding temperature and time compared with that of thermocompression bonding.

• Journal of Welding and Joining
• /
• 제22권1호
• /
• pp.77-82
• /
• 2004

The effect of bonding condition on tensile properties of joints diffusion bonded spheroidal graphite cast iron, FCD60 to Cr-Mo steel, SCM 440 was investigated. Diffusion bonding was performed with various temperatures, holding times, pressures and atmospheres. All tensile specimens were fractured at the bonding interface. The tensile strength and elongation was increased with increasing bonding temperature. Especially, tensile strength of joints bonded at 1123K was higher than that of a raw material, FCD60, and tensile strength of joints bonded at 1173K was equal to that of a raw material, SCM440, but elongation of all joints was lower than those of raw materials. There was little the effect of holding time on the tensile properties. In comparison with bonding atmosphere, the difference of tensile strength was not observed, but elongation of joint bonded at vacuum(6.7mPa and 67mPa) was higher than that of Ar gas. Higher the degee of vacuum, elongation increased. Tensile properties of diffusion bonds depended on microstructures of cast iron at the interface and void ratio. Microstructures of cast iron at interface changed with temperature, because decarburizing and interdiffusion at the interface occurs and transformation of austenite-1 ferrite + graphite occurs on the cooling process. The void ratio decreased with increasing temperature, especially, effected on the elongation.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 춘계학술대회 논문집
• /
• pp.370-373
• /
• 1999

Si direct bonding (SDB) technology is very attractive for both Si-on-insulator(SOI) electric devices and MEMS applications because of its stress free structure and stability. This paper presents on- pre treatment conditions in Si wafer direct bonding, The paper resents on pre-bonding according to HF pre-treatment conditions in Si wafer direct bonding. The characteristics of bonded sample were measured under different bonding conditions of HF concentration, applied pressure and annealing temperature(200~ 100$0^{\circ}C$) after pre-bonding. The bonding strength was evaluated by tensile strength method. The bonded interface and the void were analyzed by using SEM and IR camera, respectively, Components existed in the interlayer were analyzed by using FT-IR. The bond strength depends on the HF pre-treatment condition before pre-bonding(Min 2.4kgf/$\textrm{cm}^2$~ Max : 14.kgf/$\textrm{cm}^2$)

• Journal of Welding and Joining
• /
• 제21권4호
• /
• pp.69-74
• /
• 2003

The mechanical properties of STD11 Joints by using TLP (Transient Liquid Phase Diffusion) bonding method employing MBF-30 and MBF-80 insert metals were investigated with concerning to the microstructural change. TLP bonding of STD 11 was carried out at 1323∼1423K for 0.6ks∼3.6ks in vacuum. The microstructure and the element distribution of the interlayer between tool steels and insert metals showed specific feature with bonding conditions. It was found that the width of the interlayer increased at initial bonding stage. However, the width of interlayer showed nearly constant value during the isothermal solidification. After isothermal solidification was completed, the joint showed homogeneous element distribution and similar microstructure with base metal because of the grain boundary migration to the bonded interlayer. The bonding strength measured by a tensile test has been varied with the bonding conditions. The maximum joint strength, 760MPa, was obtained with the condition of 1423K for 1.2ks using MBF30 insert metal in this experiment.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2002년도 하계학술대회 논문집 C
• /
• pp.2020-2022
• /
• 2002

SiC direct bonding technology is very attractive for both SiCOI(SiC-on-insulator) electric devices and SiC-MEMS fileds because of its application possibility in harsh environements. This paper presents on pre-bonding according to HF pre-treatment conditions in SiC wafer direct bonding using PECVD oxide. The PECVD oxide was characterized by XPS and AFM, respectively. The characteristics of bonded sample were measured under different bonding conditions of HF concentration and applied pressure, respectively. The bonding strength was evaluated by tensile strength method. Components existed in the interlayer were analyzed by using FT-IR. The bond strength depends on the HF pre-treatment condition before pre-bonding (Min : 5.3 kgf/$cm^2{\sim}$ Max : 15.5 kgf/$cm^2$).

• 대한치과기공학회지
• /
• 제33권1호
• /
• pp.47-54
• /
• 2011

Purpose: To investigate shear bonding strength between dental zirconia ceramics with different surface treatment and metal bracket. Methods: Zirconia ceramics(LAVA, 3M ESPE, USA) were divided to 4 groups according to their surface treatment; no surface treatment(G1), sand blasting(G2), silane coating(G3), and sand blasting+silane coating(G4). Specimens were bonded to metal bracket using resin bond($Transbond^{TM}XT$, 3M Unitek, USA). Shear bond strength was measured using universal test machine(3366 INSTRON. U.S.A) with cross head speed of 1 mm/min. Microstructural investigation for fracture surface was performed after shear test. Results: Shear bonding strengths of single surface treatment groups (G2 and G3) were higher than no treatment group(G1). Combined Treatment Group (G4) showed the highest shear bond strength of 9.15MPa. Microstructural observation shows that higher shear bonding strength was obtained when debonding was occurred at metal bracket/resin interface rather than zirconia ceramic/resin interface. Conclusion: Surface treatment of zirconia is necessary to obtain higher bonding strength. Combined treatment can be more effective when surface the surfaces are kept clean and homogeneous.

• Restorative Dentistry and Endodontics
• /
• 제20권1호
• /
• pp.97-112
• /
• 1995

The purpose of this study was to evaluate the effect of wetting condition made by drying time on bonding of resin cement to dentin. Freshly extracted bovine teeth were grinded to expose flat dentin surfaces. After the exposed dentin surfaces were treated with pretreatment agents and water rinse, each wetting condition of dentin surfaces was made according to drying times and methods including slight blow bry for I-second by air syringe, blow dry for 20-second by air syringe, and 12-hour dry in desiccator respectively. and then, previously made composite resin specimens were bonded onto each conditioned dentin surface of the specimen using Panavia-21(Kuraray Co.), Bistite(Tokuso Co.), and Choice(use with All bond-2, Bisco Inc.) resin cement according as manufacturer's instruction. Bonded specimens were stored in $37^{\circ}C$ distilled water for 24 hours, then the tensile bond strength was measured, cohesive failure rate was calculated, and fractured dentin surfaces and acrylic rod sides were examined under scanning electron microscope. The result were as follows ; In the group of bonding with Panavia-21 resin cement, higher tensile bond strength was seen in 12-hour dry group than in I-second and 20-second dry group(p<0.01). In the group of bonding with Bistite resin cement, higher tensile bond strength was seen in 1-second dry group than in 20-second and 12-hour dry group(p<0.01). In the group of bonding with Choice resin cement, no significant differences of bond strength under given drying time were seen. Cohesive failure rates derived from the groups of bonding with Panavia-21 and Choice resin cement were increased with the increase of tensile bond strength in each drying time. On SEM examination of fractured surface, adhesive failure mode with fractured resin tags was mostly seen in wet condition with I-second drying time in the group of bonding with Panavia-21 resin cement, mixed failure mode with shortened and fractured resin tag was seen in the group of bonding with Bistite resin cement, and regardless of drying time, and cohesive-adhesive mixed failure mode with fracture of 'Hollow' typed resin tags was mainly seen in the group of bonding with Choice resin cement.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 추계학술대회 논문집
• /
• pp.4-4
• /
• 2009

Surface analysis on defective wire-bonding pads are performed in flash memory assembly. Week wire bonding may cause a significant effect on the final product reliability, and the surface condition of the aluminum bond pads is critical in terms of product reliability. To find out possible week bonding on semiconductor interconnects, ball sheer test (BST) has been performed. On some defective or week bonded pads, we have investigated the surface contents, assuming that the week bonding is induced from the surface conditions. AES and XPS are employed for the quantitative surface analysis on defective dies.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.447-450
• /
• 2001

Abstract-Si direct bonding(SDB) technology is very attractive for both Si-on-insulator(SOI) electric devices and MEMS applications because of its stress free structure and stability. This paper presents on pre-bonding according to HF pre-treatment conditions in Si wafer direct bonding. The characteristics of bonded sample were measured under different bonding conditions of HF concentration, and applied pressure. The bonding strength was evaluated by tensile strength method. The bonded interface and the void were analyzed by using SEM and IR camera, respectively. Components existed in the interlayer were analysed by using FT-lR. The bond strength depends on the HF pre-treatment condition before pre-bonding (Min : 2.4kgf/cm$^2$∼Max : 14.9kgf/cm$^2$).