• 한국세라믹학회지
• /
• 제41권2호
• /
• pp.143-150
• /
• 2004

본 연구에서는 치아 수복에 사용되는 상용 글라스 세라믹들을 디스크 모양으로 열가압 성형하여 ball-on-3-bal에 의한 이축강도와 압입시험에 의한 파괴인성을 측정하였다. 시편들로부터 XRD, SEM, TEM을 이용하여 결정상과 미세구조를 분석하였다. 글라스 세라믹내의 결정들은 균열의 진행에 대하여 효과적인 저지를 하지 못하였으나 높은 결정화도가 기계적 성질의 향상에 기여하는 것으로 판단된다. Lithium disilicate결정의 글라스 세라믹은 상대적으로 결정함량이 낮은 leucite 세라믹에 비하여 유의하게 높은 이축강도와 파괴인성을 나타내어 치과용 글라스 세라믹으로서 높은 신뢰성이 기대된다.

• 대한의용생체공학회:의공학회지
• /
• 제17권3호
• /
• pp.327-336
• /
• 1996

This study was performed to investigate the effec% of immersion in water and thermal cycling on the mechanical peoperties of light cured restorative composite resins. Five commerically available light-cured composite resins(Photo Clearfil A : CA, Lite-Fil A . LF, Clearril Photo Posterior CP, Prisms AP.H.. PA, 2100 : ZH) were unto The specimens of 12 m in diameter and 0.7 m in thickness were made, and an immersion in $37^{\circ}C$ water for 7 days and a thermal cycling of 1000 cycles at 15 second dwell time each in $5^{\circ}C$ and $55^{\circ}C$ baths were performed. Biaxial flexure test was conducted using the ball-on-three-ball method at the crosshead speed of 0.5mm/min. In order to investigate the deterioration of composite resins during the thermal cycling test, Weibull analysis for the biaxial flexure strengths was done. Fracture surfaces and the surfaces before and after the thermal cycling test were examined by SEM. The highest Weibull modulus value of 10.09 after thermal cycling tests which means the lowest strength variation, was observed in the CP group, and the lowest value of 4.47 was obsered in the LF Group. Biaxial flexure strengths and Knoop hardness numbers significantly decreased due to the thermal cycling ($\textit{p}$< 0.01), however, they recovered when specimens were drie4 The highest biaxial flexure strength of 125.65MPa was observed in the ZH group after the thermal cycling test, and the lowest value of 64.86MPa was observed in the CA group. Biaxial flexure strengths of ZH and CP groups were higher than those of PA, CF, and CA groups after thermal cycling test($\textit{p}$< 0.05). Knoop hardness numbers of CP group after the thermal cycling test was the highest(95.47 $\pm$ 7.35kg/$mm^2$) among the samples, while that of CA group was the lowest(30.73 $\pm$ 2.58kg/$mm^2$). Knoop hardness numbers showed the significant differences between the CP group and others after the thermal cycling test(($\textit{p}$< 0.05). Fracture surfaces showed that the composite resin failure developed along the matrix resin and the filler/resin interface region, and the cracks propagated in the conical shape from the maximum tensile stress zone.

• 콘크리트학회논문집
• /
• 제23권4호
• /
• pp.479-486
• /
• 2011

이 연구에서는 휨인장강도 평가 방법에 따른 무근 콘크리트 원형패널의 휨거동을 비교하기 위해 유한요소해석과 실험을 수행하였다. 이를 위해 ASTM C 1550 round panel test(RPT) 시험법과 biaxial flexure test(BFT) 시험법을 적용하여 콘크리트 원형패널의 휨인장강도를 측정하였으며, 두 원형패널에 작용하는 응력 분포를 알아보기 위하여 패널의 아랫면 중앙에 두 개의 변형률 게이지가 직교하도록 부착하여 하중-변형률 관계를 측정하였다. 실험 결과 RPT 시험체와 BFT 시험체의 파괴 형상은 유사하게 관찰되었으며, 두 시험체 모두 중앙 아랫면의 하중-변형률 관계 또한 모든 방향에 일정한 것으로 나타나, 시험 시 등방성 휨인장응력 상태에 놓이는 것을 확인할 수 있었다. RPT 시험에 의한 평균 휨인장강도가 BFT의 경우보다 29% 더 큰 것으로 나타났다. 두 시험체의 휨인장강도 분포 모두 정규분포를 보이는 것으로 나타났으며, RPT 휨인장강도의 변동계수(coefficient of variation)와 BFT의 변동계수는 각각 8%와 6%로 측정되었다. 이는 BFT 시험을 통하여 신뢰할 수 있는 이방향 휨인장강도 측정이 가능한 것으로 판단된다.

• 구강회복응용과학지
• /
• 제17권3호
• /
• pp.199-204
• /
• 2001

This study was to investigate the reused possibility of zirconia reinforced glass-ceramic(IPS Empress Cosmo ceramic) with sprue button in the flexure strength and fracture toughness. 40 disk-shaped ceramic specimens (20 specimens: as-pressed material; 20 specimens: reused material) with approximately 1.7 mm thickness and 15 mm diameter were prepared by "lost wax" technique. The remnants(sprue buttons) were used for repressing. The surface treatments for the discs were gradually abraded with 320, 800, 1200, and 2000 grit SiC sandpaper. The specimens were evaluated their flexure strength with the biaxial flexure jig(ball-on-three balls) and their fracture toughness with Vickers Indentation-microfracture test. The Weibull moduli were calculated for biaxial flexural strength. The mean flexure strength and fracture toughness of each group were $122.2{\pm}18.3MPa$, $1.00{\pm}0.09MPa{\cdot}m^{0.5}$ (as-pressed ceramics), and $122.2{\pm}20.3MPa$, $1.01{\pm}0.10MPa{\cdot}m^{0.5}$ (reused ceramics). There were no significant differences in the strength and the fracture toughness between the as-pressed and the reused IPS Empress Cosmo ceramic (P>0.05). This implied zirconia reinforced glass-ceramic(IPS Empress Cosmo ceramic) could be used one more time by reusing of sprue button in the flexure strength and fracture toughness.

• 대한치과보존학회:학술대회논문집
• /
• 대한치과보존학회 2003년도 제120회 추계학술대회 제 5차 한ㆍ일 치과보존학회 공동학술대회
• /
• pp.575-575
• /
• 2003

The majority of studies comparing the mechanical properties of brittle dental restorative materials now include use of the Weibull Modulus (m). This modulus is determined from analysis of the statistical distribution of strength measurements, which can be determined using a variety of methods, including biaxial flexure, 3pt bend and 4pt bend. In comparing materials it is usually implicitly assumed that the modulus (m) is independent of test method although it is recognised to be highly dependent on flaw distributions. However, in some cases flaw distributions can be modified by sample preparation and test method may modify stressing patterns. This study investigated the pattern of strength and m in two light setting materials.

• 대한치과보철학회지
• /
• 제38권5호
• /
• pp.595-605
• /
• 2000

Dental ceramics have good aesthetics, biocompatibility, low thermal conductivity, abrasion resistance, and color stability. However poor resistance to fracture and shrinkage during firing process have been limiting factors in their use, particularly in multiunit ceramic restorations. A new method for making all-ceramic crowns that have high strength and low processing shrinkage has been developed and is referred to as the Vita In-Ceram method. This study was performed to investigate the effect of $CeO_2$ addition in borosilicate glasses on the strength of alumina-glass composites. Porous alumina compacts were prepared by slip casting and sintered at $1,100^{\circ}C$ for 2 hours. Dense composites were made by infiltration of molten glass into partially sintered alumina at $1,140^{\circ}C$ for 4 hours. Specimens were polished sequentially from #800 to #2000 diamond disk. and the final surface finishing on the tensile side was received an additional polishing sequence through $1{\mu}m$ diamond paste. Biaxial flexure test was conducted by using ball-on-three-ball method at a crosshead speed of 0.5mm/min. To examine the microstructural aspect of crack propagation in the alumina-glass composites, Vickers-produced indentation crack was made on the tensile surface at a load of 98.0 N and dwell time of 15 sec, and the radial crack patterns were examined by an optical microscope and a scanning electron microscope. The results obtained were summarized as follows; 1. The porosity rates of partially sintered alumina decreased with the rising of firing temperature. 2. The maximum biaxial flexure strength of 423.5MPa in alumina-glass composites was obtained with an addition of 3 mol% $CeO_2$ in glass composition and strength values showed the aspect of decrease with the increase of $CeO_2$ content. 3 The biaxial flexure strength values of alumina-glass composites were decreased with rising the firing temperature. 4. Observation of the fracture surfaces of alumina-glass composites indicated that the enhancement of strength in alumina-glass composites was due to the frictional or geometrical inter-locking of rough fracture surfaces and ligamentary bridging by intact islands of materials left behind the fracture front.

• Restorative Dentistry and Endodontics
• /
• 제31권1호
• /
• pp.58-65
• /
• 2006

이번 실험의 목적은 이축 굴곡 강도 시험의 복합레진에서의 적용가능성을 위해 기존의 3점 굴곡 강도 시험과 이축 굴곡 강도 시험을 이용하여 치과용 광중합형 레진의 강도를 측정하고, 이를 Weibull modulus를 이용하여 상대적 신뢰도를 비교하는 것이다. 이번 실험에 사용된 재료는 $MICRONEW^{TM},\;RENEW^{(R)}$ (Bisco, Schaumburg, USA)의 두 가지 광중합형 수복 재료이다. 이축 굴곡 강도 측정에는 International Organization for Standardization (ISO) 6872 규정에 따라 piston-on-3-ball test를 사용하였으며 검사 시편은 직경이 각각 12 mm (지지원의 반지름 3.75 mm), 16 mm (지지원의 반지름 5 mm), 두께가 각각 0.5 mm, 1 mm, 2 mm인 여섯 개의 군으로 나누어 제작하였으며 각 군당 시편을 20개씩 제작하였다. $MICRONEW^{TM}$와 $RENEW^{(R)}$의 실험 결과, 이축 굴곡 강도가 3점 굴곡 강도보다 높은 평균값을 나타내었고 이축 굴곡 강도의 모든 군이 3점 굴곡 강도보다 높은 Weibull modulus 값을 보여, 이축 굴곡 강도 시험이 상대적으로 실험적 오차의 영향을 적게 받는 방법으로 신뢰 할 수 있었다. 또한 이축 굴곡 강도 시험에서 시편의 두께가 2 mm일 때 가장 높은 Weibull modulus를 나타내었으며 이축 굴곡 강도시험군 중, $MICRONEW^{TM}$의 두께 2 mm군에서는 지지원의 반지름에 따른 굴곡 강도의 통계학적 유의차이가 없었고 (p>0.05), 이를 제외한 모든 군에서 시편의 두께와 지지원의 반지름에 따른 굴곡 강도의 통계학적 유의차이가 있었다 (p<0.05). 위의 결과로 미루어 볼 때 두께 2 mm군에서 이축 굴곡 강도는 기존의 3점 굴곡 강도 시험보다 우수한 것으로 추천할 수 있는 방법이다.

• Computers and Concrete
• /
• 제4권5호
• /
• pp.363-376
• /
• 2007

The paper presents the development of an adaptable strut-and-tie model that can be applied to the design or analysis of four-pile caps that support axial compression and biaxial flexure from a supported rectangular column. Due to an absence of relevant test data, the model is validated using nonlinear finite element analyses (NLFEA). The results indicate that the use of the proposed model would lead to safe and economical designs. The proposed model can be easily extended to any number of piles, providing a rational procedure for the design of wide range of pile caps.

• Structural Engineering and Mechanics
• /
• 제10권2호
• /
• pp.165-180
• /
• 2000

An analytical model with tension softening for the prediction of the capacity of prestressed concrete beams under pure torsion and under torsion combined with shear and flexure is introduced. The proposed approach employs bilinear stress-strain relationship with post cracking tension softening branch for the concrete in tension and special failure criteria for biaxial stress states. Further, for the solution of the governing equations a special numerical scheme is adopted which can be applied to elements with practically any cross-section since it utilizes a numerical mapping. The proposed method is mainly applied to plain prestressed concrete elements, but is also applicable to prestressed concrete beams with light transverse reinforcement. The aim of the present work is twofold; first, the validation of the approach by comparison between experimental results and analytical predictions and second, a parametrical study of the influence of concentric and eccentric prestressing on the torsional capacity of concrete elements and the interaction between torsion and shear for various levels of prestressing. The results of this investigation presented in the form of interaction curves, are compared to experimental results and code provisions.

• 구강회복응용과학지
• /
• 제30권2호
• /
• pp.102-111
• /
• 2014

목적: 본 연구의 목적은 air-blasting particle size를 달리하고 분사 압력과 시간을 통상보다 크게 증가시켜 표면에 큰 손상을 유발한 군을 상대적으로 작은 손상을 유발한 군과 비교하여 파절 저항과 접착 강도 차이를 보이는지 평가하는 데 있다. 연구 재료 및 방법: 지르코니아($LAVA^{TM}$) 디스크 표면에 각각 $30{\mu}m$- particle size (Cojet) 2.8 bar 15초, $110{\mu}m$- (Rocatec) 2.8 bar 15초, $110{\mu}m$- (Rocatec) 3.8 bar 30초로 조건을 달리하여 표면처리 후 각각 이축 굽힘하중 강도 실험과 접착 파절 하중 실험을 실행하였다. 접착은 상아질 유사 베이스에 $200{\mu}m$ 두께의 레진시멘트로 시행하여 인장력을 극대화하였으며 음향방출(AE) 센서로 실패하중을 검출하였다. 결과: 이축 굽힘하중 강도, 접착 파절하중은 세 군간 서로 유의성 있는 차이를 보이지 않았다(P > 0.05). 접착 시편의 균열은 대부분 radial crack이었다. 결론: 정하중 평가의 한계 내에서, air-blasting particle size와 압력에 의한 표면 손상은 크지 않았으며, 접착 파절하중 평가는 표면 손상과 접착 강도를 동시에 평가할 수 있는 방법이라 여겨진다.