Bi-2212/Ag ROSAT용 와이어의 제작은 PIT법으로 제작된 단일 필라멘트가 사용되었다. 제작된 필라멘트를 압연하여 너비 8.6mm, 두께 2.15mm의 압연 테입을 제조한 후 4개씩 적층하여 3 부분의 마름모로 만들어 다시 내경 17.2mm의 Ag튜브에 적층하여 ROSAT 와이어를 약 150 mm로 제작하였다. 제작된 ROSAT 와이어는 산소분위기에서 약 60시간 동안 열처리 되었다. 이때 열처리 온도와 최고점에서의 유지시간에 따른 Bi-2212/Ag ROSAT 와이어의 전기적 특성을 평가 하였다. 기존의 Bi-2212/Ag 와이어에 비해 압연, 적층, 인발하여 제작된 동일한 크기의 ROSAT 와이어가 향상된 전기적 특성을 나타내었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.91-92
• /
• 2006

The important merit of Bi-2212/Ag wire is to apply cable as round wire state. Bi-2212 high Tc superconducting wires were fabricated in order to apply Rutherford cable near the future. Various Ag ratio from 0.22 to 0.42 of Ag tubes for PID (powder-In-Tube) process were used to investigate the workability and to prevent breakage of filaments during drawing. In order to find proper heat treatment condition, we investigated micro-structure of Bi-2212/Ag wires by using differential thermal analysis, XRD and SEM. The effect of atmosphere on the peritectic decomposition temperature of precursor was investigated. The shape of grain was observed by SEM to investigate Bi-2212 phase formation in filaments. The higher of Ag ratio of mono filament had the higher critical current density, Jc. The wire with 0.42 of Ag ratio showed 7,886 A/cm2 of Jc at 77K.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.238-239
• /
• 2007

The important merit of Bi-2212/Ag wire is to apply cable as round wire state. Bi-2212 high Tc superconducting wires were fabricated in order to apply Rutherford cable near the future. Various Ag ratio from 0.22 to 0.42 of Ag tubes for PID (powder-In-Tube) process were used to investigate the workability and to prevent breakage of filaments during drawing. KERI and Nexans Korea manufactured Rutherford cabling machine by ourselves. Rutherford cables with 20 - 30 strands could be fabricated by this machine. The shape of Rutherford cables were satisfied. The critical current of Bi2212/Ag round wire with 847 filaments showed 400 A at 4.2K and self field.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.163-164
• /
• 2005

Round shape Bi2212/Ag is isotropic and can be fabricated Rutherford cable to transport high current. Bi2212/Ag round wires with various Ag ratio were fabricated using powder-in-tube process. Double stacked 385 (55\times$7) filamentary wire of various wire diameter was heat-treated at various melting temperature. Wires which have Ag ratio of 0.3 and 0.42 of Ag tube for monofilament show similar critical current density. As average filament diameter decreases from 33 to 16 \mu$m, critical current density of wires increase, and in case of 16 ${\mu}m$ and $T_m$ 890$^{\circ}C$, critical current density was 2,062 $A/mm^2$ at 4.2 K, 0 T.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.527-530
• /
• 2002

A lot of efforts have been focused on the optimization of PIT parameters for Bi-2223/Ag wire. In this paper, initial annealing of Bi-2223/Ag wire to transform Bi-2212 orthorhombic from Bi-2212 tetragonal Precursor was investigated. This initial annealing step at low oxygen partial pressure were to transform Bi-2212 orthorhombic structure and to reduce the formation of second phases at superconducting wire. However Bi-2223 Phases were appeared at higher annealing temperature. Critical currents(Je) of Bi-2223/Ag tapes were sintered at low oxygen Partial pressure were higher than that of the wires sintered at atmosphere condition. In order to investigate the effect of rolling reduction ratio, Bi-2223/Ag HTS tapes were rolled with different reduction ratio. There were no clear difference of Je and filaments shape with various rolling reduction ratio.

• Progress in Superconductivity
• /
• v.9 no.1
• /
• pp.111-114
• /
• 2007

We have investigated the effect of different heat treatment processes on electrical and magnetic properties of Bi2212/Ag ROSAT wire. The ROSAT wire was fabricated by stacking and arranging 12 filaments Bi2212/Ag tapes in triple rotation symmetry in a Ag tube. ROSAT wires have been prepared using a partial melting method with changing $T_{max}$ and $T_a$ in oxygen atmosphere. The highest critical current density($J_c$) at 65 K under 0 T was $21,158\;A/cm^2$ for wire prepared $890\;^{\circ}C(T_{max})$ and $840\;^{\circ}C(T_a)$, respectively. SEM results indicated that the wire prepared at $890\;^{\circ}C(T_{max})$ and $840\;^{\circ}C(T_a)$ showed better directional phases than the other samples. However the result of magnetic susceptibility measurement indicates that the wire prepared $890\;^{\circ}C(T_{max})$ and $835\;^{\circ}C(T_a)$ had better superconducting phases than the other samples. It was revealed that heat treatment temperature was important factor for superconducting properties of the ROSAT wire.

• Progress in Superconductivity
• /
• v.8 no.1
• /
• pp.54-58
• /
• 2006

We have fabricated double stacked 385 filamentary Bi2212/Ag round wires which have different Ag ratios. The wires have been heat-treated at the maximum temperature($T_{max}$) of $882{\sim}896^{\circ}C$ for 0.5 h. Effect of heat treatment on critical current density and critical temperature on Bi2212/Ag round wires has been studied. Critical current density of the wire heat -treated at $890^{\circ}C$ showed 206,250 $A/cm^2$ at 4.2 K, 0 T and critical temperature of the wire was 83 K. Microstructure of the wires also has been studied via optical microscopy and SEM.

• 한국초전도학회:학술대회논문집
• /
• v.16
• /
• pp.62-62
• /
• 2006

• Progress in Superconductivity and Cryogenics
• /
• v.3 no.1
• /
• pp.6-10
• /
• 2001

Stress/stram dependencies of the critical current $I_c$ in AgMgNi sheathed multifilamentary Bi(2212) superconducting tapes were evaluated at 77K, 0T. The external reinforcement was accomplished by soldering Ag-Mg tapes to sin91e side or both sides of the sample. With the external reinforcement. the strength of tapes increased but $I_c$, decreased The $I_c$, degradation characteristic according to the external reinforcement was improved markedly in terms of the stress although it appeared less rectal.table on the basis of the strain. Effects of external reinforcement were discussed in a viewpoint of monitoring sensitivity of cracking in superconducting filaments by considering n-value representing the transport behavior of the current. It is closely associated with the location of them relative to the voltage-monitoring region in the tape.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1243-1244
• /
• 2006

Five kinds of double stacked 385 (55 x7) filamentary Bi2212/Ag round wires and 55 filamentary tapes with different Ag ratios (silver area/superconductor area) have been fabricated via PIT method, and the effects of Ag ratio and processing factors on critical current density were studied. The effects of the maximum temperature and average filament diameter on critical current density were also studied. The wire of 0.74 mm diameter having Ag ratio 3.7 showed critical current density of $2,218\;A/mm^2$ at 4.2 K, 0 T.