• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.4
• /
• pp.49-56
• /
• 2007

Effects of post-baking treatment conditions on the interfacial adhesion between electroless plated Ni and polyimide film were evaluated using $180^{\circ}C$ peel test. Measured peel strength values monotonically decrease from $38.6{\pm}1.1g/mm\;to\;26.8{\pm}2.2g/mm$ for the variations of post-baking treatment temperatures from $80^{\circ}C\;to\;180^{\circ}C$, respectively. Wet chemical treatment on the polyimide surface produces carboxyl and amide functional groups on the surface which is closely related to the change in interfacial adhesion between electroless Ni and polyimide films. It is speculated that interfacial adhesion seems to be controlled by carbonyl oxygen bonding near cohesive failure region during post-baking treatment.

• Journal of the Korean Vacuum Society
• /
• v.10 no.3
• /
• pp.298-302
• /
• 2001

Cleaning effect of RF/DC discharge to clean the surface of vacuum chamber was studied for various discharge conditions. Glow discharge cleaning without baking reduced the outgassing rate to 1/2, which was similar to that after the only baking treatment alone. Glow discharge cleaning treatment with baking improved the cleaning efficiency and then the outgassing rate was remarkably reduced to 1/20. It was found that the ion energy and the ion density were important factors in cleaning the surface. RF discharge cleaning was more effective than BC discharge cleaning.

• KOREAN JOURNAL OF PACKAGING SCIENCE & TECHNOLOGY
• /
• v.26 no.1
• /
• pp.1-9
• /
• 2020

We evaluated the applicability of baking soda, charco'al, coffee, and green tea as a natural deodorant in Kimchi packaging. Moreover, to evaluate the potential usage of these deodorants in packaging materials and confirm their applicability in high-temperature melt-extrusion processing, the thermal stabilities of the deodorants were investigated, and heat-treated deodorants were evaluated in terms of the deodorizing function compared with non-treated deodorants. Aroma patterns were decreased after deodorizing treatment with all-natural deodorants. Dimethyl disulfide, methyl trisulfide, and diallyl disulfide, the most significant odorous Volatile organic compounds (VOCs) of Kimchi, decreased after treatment with the deodorants. In particular, baking soda and charcoal showed the highest efficiency in removing odorous compounds and VOCs from Kimchi, even after high-temperature processing. The acetic acid removal rates for both baking soda and charcoal were 99.9±0.0%. The heating process increases the deodorizing effects of baking soda. Sensory evaluation results showed that there is a significant increase (p < 0.05) in the overall preference for Kimchi samples packaged with charcoal and baking soda. This study provides useful information for the deodorization effects of natural deodorants for Kimchi smell and their applicability for packaging materials.

• Korean Journal of Metals and Materials
• /
• v.49 no.12
• /
• pp.967-976
• /
• 2011

Conventional fracture tests of resistance spot welds have been performed without consideration of the paint baking process in the automobile manufacturing line. The aim of this paper is to investigate the effect of the paint baking process on load carrying capacity and fracture mode for resistance spot welded 590 dual phase (DP), 780DP, 980DP, 590 transformation in duced plasticity (TRIP), 780TRIP and 1180 complex phase (CP) steels. With paint baking after resistance spot welding, the l-shape tensile test (LTT) and nano-indentation test were conducted on the as-welded and paint baked samples. Paint baking increased the load-carrying capacity of the resistance spot welded samples and improved the fracture appearance from partial interfacial fracture (PIF) to button fracture (BF). Improvement in fracture appearance after LTT is observed on weldments of 780 MPa grade TRIP steels, especially in the low welding current range with paint baking conditions. The higher carbon contents (or carbon equivalent) are attributed to the low weldability of the resistance spot welding of high strength steels. Improvement of the fracture mode and load carrying ability has been achieved with ferrite hardening and carbide formation during the paint baking process. The average nano-indentation hardness profile for each weld zone shows hardening of the base metal and softening of the heat affected zone (HAZ) and the weld metal, which proves that microstructural changes occur during low temperature heat treatment.

• Transactions of Materials Processing
• /
• v.15 no.8 s.89
• /
• pp.621-627
• /
• 2006

Recently, micro-alloyed steels which could eliminate heat treatments after forging has been developed. These non heat-treated micro-alloyed steels have several advantages over the conventional quenched and tempered steel for cold forging. First of all, long components can be fabricated with a better dimensional accuracy since bending of long forged part after quenching treatment could be avoided. And it is possible to eliminate two energy consuming heat treatment steps, which are a spherodizing before forging and quenching/tempering after forging. Therefore, more cost effective and environment friendly process could be designed. However, there is non-uniform distribution of strain occurred across the forged part, since these non heat-treated micro-alloyed steel use strain hardening mechanism. In the present study, it was investigated how to lessen non-uniformity and increase strength together for cold forging when a baking heat treatment is applied in micro-alloyed steels. For this purpose, micro-alloyed steels developed by Se-A Besteel recently was used for the experiment.

• Transactions of Materials Processing
• /
• v.30 no.2
• /
• pp.61-68
• /
• 2021

As part of efforts to reduce the weight of automotive body-in-white, a hybrid center pillar with high strength 7075 aluminum alloy (AA7075) sheet and carbon fiber reinforced plastic (CFRP) has been recently studied. In the fabrication of the AA7075-CFRP hybrid center pillar, the AA7075 sheet might go through heating-forming-in-die quenching (HFQ), artificial aging, hybridizing, and then paint baking processes. In this study, we investigate the effects of the heat treatment history associated with each process on the tensile strength of the AA7075 sheet. Typical heat treatment conditions are HFQ for 20 minutes at 480℃ and then cooling down with die, artificial aging of T6 temper for 24 hours at 120℃, hybridizing for 10 minutes at 150℃, and paint baking for 20 minutes at 180℃. The tensile strength of the AA7075 sheet is continuously increased by a series of heat treatments of hybridizing and paint baking and is expected to have yield stress above 500MPa without artificial aging of T6 temper.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1996.04a
• /
• pp.697-703
• /
• 1996

Fatigue strength of high strengthsteels are variable with many different surface treatment. It is well known that residual compressive stress retard fatigue crack growth rate(or arrest crack). High strngth steels are manufactured by following process. Heat treatment, shot peening and chromium plating process. High strength steel(HRC40 or above) which are subjected to fatigue load and dynamic load, chromium plated parts shall be peened in accordance with requirements and baked after plating. The purpose of this paper is to compare and discuss the influence of surface treatment and hydrogen embrittlement on fatigue strength of high strength steel. Therefore, fatigue test was performed to investigate influence of surface treatment. The results shows that shot peening is very effect method in creasing fatigue life and after plating, baking process is essential to prevent hydogen failure. In this paper, the experimental investigation is made to clarify the influence of shot peening conditions and baking process on fatigue strength of high strength steel.

• Korean journal of food and cookery science
• /
• v.21 no.4 s.88
• /
• pp.490-495
• /
• 2005

Cooking is the final production stage of the food industry and is an essential part to define the distinctive feature. Consumers do not want to change their cooking styles because hey team the cooking styles as practices and customs from their region or their ancestor and they are skilled in their use. Corpulence is a major health concern in developed countries and developing countries alike. This study was conducted to suggest the arts of cooking for pork cutlet, a typical dish cooked by batter-fried food, and to decrease the intake of fat and calories. As a result, the fat contents of pork cutlet were lower (p<0.05) than when it was conducted with frying and oven baking. Especially, the pork cutlet cooked by oven baking showed a $10\%$ reduction in calories (p<0.05) compared to frying. The organic functional tests were satisfactory, and oven baking will help people who need dietary treatment.

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.222-222
• /
• 2000

PBGA(Plastic Ball Grid Array) is composed of some materials such as PCB(Printed Circuit Board), epoxy molding compound, die attach and so on. Reliability of PBGA package is weak compared with plastic packages. The weak points of reliability are the lower resistance to popcorn cracking, which is induced by moisture absorption in PCB, and the pressure cooker test corrosion, which is the basic problem due to the material characteristics of PCB. Introducing the PCB baking and the plasma treatment cleared the popcorn cracking phenomenon. The PCB baking and plasma treatment reduced the epoxy void by eliminating the source of moisture vaporization during the epoxy curing and enhanced the adhesion between PCB and epoxy. Also, plasma treatment enhanced the wettability of epoxy on PCB. The problem of corrosion is cleared using multi-functional epoxy. This type of EMC(Epoxy Molding Compound) is recommended in package using PCB as a substrate. (Received November 19, 1999)

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.244-249
• /
• 2008

It happened a failure on special bolt which supported main landing gear actuator up-lock rod of 00 aircraft. Fracture was occurred at end of center drilled hole and thread machined on bolt. Metallographic, fractographic, and other characteristics of embrittlement analysis and experiments carried out on the failed bolt to find out the reason. Bolt surface was cadmium electroplated(EP) to give lubrication and provide excellent corrosion resistance. Resultly, Bolt was failed due to cadmium embrittlement occurred during baking treatment as well as center drilled hole. for the failure that are relevant to failure analysis and prevention. For their successful functional application, cadmium EP bolts require proper and adequate baking treatment after electroplating, and is complete with no center drilled hole