• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.224-225
• /
• 2006

$BaTiO_3$ powder를 epoxy/solvent에 혼합한 슬러리와 solvent에 혼합한 슬러리의 분산 특성을 평가하기 위하여 분산제인 silane을 $BaTiO_3$ powder 표면에 코팅한 powder를 이용하여 분산실험을 진행하였다. Silane 표면 코팅 량에 따른 $BaTiO_3$ 슬러리와 $BaTiO_3$/epoxy 복합 슬러리의 분산 특성은 서로 다른 경향으로 나타남을 확인하였으며, silanae 최적 첨가량은 $BaTiO_3$/solvent 슬러리의 경우 0.3~0.5 wt%, $BaTiO_3$/epoxy/solvent 슬러리의 경우 1wt% 이상 첨가한 조건이었다. 또한 분산성 측정의 방법으로 점도 측정 방법과 함께 표면 거칠기 측정 방법의 가능성을 확인하였다.

• Proceedings of the KIEE Conference
• /
• 2005.07c
• /
• pp.1850-1852
• /
• 2005

$SrTiO_3$ and $BaTiO_3$ sol-liquids and powders were prepared by the sol-gel method. $SrTiO_3/BaTiO_3$ heterolayered thin/thick films have been prepared on the $Al_2O_3$ substrates by screen printing and spin-coating method. The thin films were sintered at $750^{\circ}C$ in the air for 1 hour and the thick films sintered at $1325^{\circ}C$ in the air for 2 hours, respectively. The $SrTiO_3/BaTiO_3$ thin/thick films's structural and dielectric properties were investigated. Increasing the spin-coating times, (110), (200), (211) peaks of the $SrTiO_3$ were increased. The X-ray diffraction(XRD) patterns and SEM photographs indicated that the $SrTiO_3$ phase were formed in the surface of $BaTiO_3$ thick films. The average thickness of a $BaTiO_3$ thick films and $SrTiO_3$ thin films were $50{\mu}m$ and 400nm, respectively The dielectric constant and dielectric loss of the $SrTiO_3/BaTiO_3$ thin/thick films with $SrTiO_3$ coated 5 times were 1598 and 0.0436 at 10KHz.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.311-312
• /
• 2007

In this study, composite $BaSrTiO_3$ has been studied for high frequency device applications. Composite $Ba_{0.5}Sr_{0.5}TiO_3$ has high dielectric permittivity and low loss tangent at the relative frequency range from MHz to GHz. 10,30 and 50 wt% of epoxy doped $Ba_{0.5}Sr_{0.5}TiO_3$ powders were prepared with bisphenol A and F polymer employing ball milling process. Epoxy/($BaSrTiO_3$) composites thick films were screen printed on the Cu plated PCB substrates through screen printing methods. The specimens were designed for the embedded capacitor applications. Temperature dependent dielectric permittivity of Epoxy doped $BaSrTiO_3$ ceramics was measured.

• Journal of the Korean Ceramic Society
• /
• v.36 no.4
• /
• pp.343-353
• /
• 1999

Microwave(2.45 GHz) was used as energy source in hydrothermal reaction to fabricate ultrafine BaTiO3 powder. Using microwave of 700 W, crytal BaTiO3 began to fom after 5 min in microwave-autoclave sys-tem. The crystallinity was not noticeably increased with increasing longer reaction time than 10 min. On the other hand in microwave-reflux system crytal BaTiO3 began to form after 15min and the crystallinity was not noticeably increased with increasing longer reaction time than 1hr,. In either case particle size dis-tribution was considerably uniform due to the effect of homogeneous heating by microwave. In addition mi-crowave heating gave an extremely small degree of particle agglomeration compared to electric heating. Av-erage sizes of as-synthesized powders were 30-60nm. Ba/Ti ratio in sol played an important role in det-ermining the particle size. It seems that excess barium forms different phases such as Ba(OH)2 which makes thin layer on the surface of BaTiO3 powder. This thin layer would inhibit the agglomeration of Ba-TiO3 powders and keep the small grain size. In microwave-autoclave system tetragonal-BaTiO3 was formed directly by the reaction of only 15 min. In the case of microwave-reflux system tetragonal-BaTiO3 was formed by driyng over 25$0^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.31 no.10
• /
• pp.1240-1246
• /
• 1994

While sintering the Pb(Mg1/3Nb2/3)O3-PbTiO3-BaTiO3 system through solid-reaction route, pyrochlore(Pb3Nb4O13) phase while reduces the dielectric constant is inevitably formed. Substitution of Pb(Mg1/3Nb2/3)O3 with PbTiO3 and BaTiO3 can retard the occurrence of pyrochlore phase. The perovskite solid-solution without containing pyrochlore phase can be obtained when we consolidated the materials consisting of PbTiO3 and BaTiO3 at 1200℃ for 2 hours. The sintered body composed of 0.8Pb(Mg1/3Nb2/3)O3-0.1PbTiO3-0.1BaTiO3 composition showed the diffused phase transition(DPT) phenomena and the maximum value of dielectric constant at 0℃ (Tc') with the value of 1.3×104.

• Journal of the Korean Ceramic Society
• /
• v.41 no.11
• /
• pp.842-850
• /
• 2004

We have investigated on the preparation of BaTiO$_3$ powder at the system of BaO$_2$-TiO$_2$-Reduction ag.-PSCA by SHS. C and Mg were used as reduction agent, and NaCl was used as PSCA (Particle Size Control Agent). The effects of the various reduction agent and its concentration, particle size control agent, reaction mixture mass on the product in the preparation of BaTiO$_3$ powder at the optimum system by SHS were investigated. The optimum conditions for reaction system and composition were BaO$_2$+TiO$_2$+0.11 Mg +0.2C+0.75NaCl in the As atmosphere. NaCl as PSCA showed the effect of controlling the particle size of product as well as the combustion temperature. The particle size of BaTiO$_3$ synthesized at the optimum condition was about 0.5 ${\mu}{\textrm}{m}$. And as the mixture mass for the reaction was increased, the more stable combustion wave appeared. We have conducted the sintering experiment at the temperature of 130$0^{\circ}C$, the time of 2 h and the atmosphere of air to measure the dielectric properties of BaTiO$_3$ synthesised in this work, and the sample sintered in this condition showed 2,290 of dielectric constant at 10$0^{\circ}C$ and 13,890 at curie point (129$^{\circ}C$).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.05c
• /
• pp.127-130
• /
• 2001

The $BaTiO_3+xNb_2O_5$(x=6, 8, 10wt%) ceramics were prepared by conventional mixed oxide method. The structural properties of the $BaTiO_3+Nb_2O_5$ ceramics with the sintering temperature and addition of $Nb_2O_5$ were investigated by XRD and SEM. Increasing the sintering temperature, the $2{\theta}$ value of BT(110) peak was shifted to the lower degree and intensity of the $Ba_6Ti_2Nb_8O_{30}$ (133) peak was increased. Increasing the addition of $Nb_2O_5$, the intensity of $BaTiNb_4O_{13}$ (201) peak was decreased and $Ba_6Ti_2Nb_8O_{30}$ (133) peak was increased. The grain size of the $BaTiO_3+Nb_2O_5$ ceramics sintered at $1500^{\circ}C$ were almost uniform.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1097-1098
• /
• 2006

The Powder characteristics and sintering behavior of $SiO_2$ coated $BaTiO_3$ were studied. Silica coated $BaTiO_3$ powders were prepared by sol-gel method. The particle size of the $BaTiO_3$ powders were $\sim35$ nm and the thickness of the $SiO_2$ coating layer was $\sim5$ nm. As the $SiO_2$ content increased, the $SiO_2$ layers improved the powder dispersion. The Zeta potential of $SiO_2$ coated $BaTiO_3$ was getting close to that of pure silica with a more negative charge, compared with that of the uncoated $BaTiO_3$. The onset temperature of shrinkage curves shifted to higher temperatures with increasing $SiO_2$ contents

• Journal of the Korean Chemical Society
• /
• v.7 no.4
• /
• pp.254-256
• /
• 1963

A spectrochemical analysis was made to compare the major impurities in $BaTiO_3$ single crystals grown from $KF-BaTiO_3$ system and $TiO_2-BaTiO_3$ system respectively. The present technique was also extended, without any modifications, to the analysis of $SrTiO_3$ crystal.

• Journal of the Korean Ceramic Society
• /
• v.32 no.4
• /
• pp.448-454
• /
• 1995

The effect of WO3 addition on microwave dielectric properties of BaTiO3-3{(1-x)TiO2-xWO3} system was studied. Addition of WO3 to this system resulted in the formation of BaWO4 and Ba2Ti9O20 phases. Both the dielectric constant (K) and the temperature coefficientof resonant frequency (Tf) were decreased with the amount of WO3 addition. The value of Q$\times$f0 was increased as the amount of WO3 was increased up to x=0.0275, and then decreased when x exceeded 0.03. At x=0.0275, this ceramic showed excellent microwave proprties of K=34-35, Q$\times$f0=50,000-53,000, and near zero ppm/$^{\circ}C$ of Tf.